ASTM D4496-2013 Standard Test Method for D-C Resistance or Conductance of Moderately Conductive Materials《中等导电材料直流阻抗或导电性的标准试验方法》.pdf

《ASTM D4496-2013 Standard Test Method for D-C Resistance or Conductance of Moderately Conductive Materials《中等导电材料直流阻抗或导电性的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D4496-2013 Standard Test Method for D-C Resistance or Conductance of Moderately Conductive Materials《中等导电材料直流阻抗或导电性的标准试验方法》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D4496 13 An American National StandardStandard Test Method forD-C Resistance or Conductance of Moderately ConductiveMaterials1This standard is issued under the fixed designation D4496; the number immediately following the designation indicates the year oforiginal adoption or, in the cas

2、e of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the determination of electricalresistance and electrical resistivit

3、y of materials that are gener-ally categorized as moderately conductive and are neither goodelectrical insulators nor good conductors.1.2 This test method applies to the materials that exhibitvolume resistivity in the range of 100to 107-cm or surfaceresistivity in the range of 103to 107 (per square)

4、.1.3 This test method is designed for measurements atstandard conditions of 23C and 50 % relative humidity, but itsprinciples of operation can be applied to specimens measuredat lower or higher temperatures and relative humidities.1.4 This standard does not purport to address all of thesafety concer

5、ns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use. Specific precau-tionary statements are given in 8.3.2. Referenced Documents2.1 ASTM

6、 Standards:2D257 Test Methods for DC Resistance or Conductance ofInsulating MaterialsD374 Test Methods for Thickness of Solid Electrical Insu-lation (Withdrawn 2013)3D991 Test Method for Rubber PropertyVolume Resistiv-ity Of Electrically Conductive and Antistatic ProductsD1711 Terminology Relating t

7、o Electrical InsulationD6054 Practice for Conditioning Electrical Insulating Mate-rials for Testing (Withdrawn 2012)32.2 ASTM Adjuncts:Carbon black test cell (two drawings)43. Terminology3.1 Definitions:3.1.1 moderately conductivea solid material having vol-ume resistivity between 100and 107cm.3.1.2

8、 For definitions of the terms used, but not defined inthis standard, refer to Terminology D1711.3.2 Definitions of Terms Specific to This Standard:3.2.1 steady statefor the purpose of this test method,steady-state is attained if any rate of change in the observedresistance (or conductance) averages

9、less than 0.25 %/s.4. Summary of Test Method4.1 Specimens of the test material are conditioned at pre-scribed conditions and subjected to direct-voltage stress. Re-sistance or conductance is measured and used with the dimen-sional aspects of the specimen to compute the resistivity of thematerial. Th

10、e apparatus and techniques used in this test methodare selected in accordance with the general principles set forthin Test Methods D257.5. Significance and Use5.1 This test method is useful for the comparison ofmaterials, as a quality control test, and for specificationpurposes.5.2 This test method

11、is useful in the selection and use ofmaterials in wires, cables, bushings, high-voltage rotatingmachinery, and other electrical apparatus in which shielding orthe distribution of voltage stress is of value.5.3 Commercially available “moderately conductive” mate-rials frequently are comprised of both

12、 conductive and resistivecomponents (that is, cellulose fibers with colloidal carbonblack particles attached to portions of the surfaces of thosefibers, or discrete conductive particles adhered to the surfacesof electrical insulating polymers). Such commercially availablematerials are often manufact

13、ured in a manner that results in1This test method is under the jurisdiction of ASTM Committee D09 onElectrical and Electronic Insulating Materials and is the direct responsibility ofSubcommittee D09.12 on Electrical Tests.Current edition approved May 1, 2013. Published July 2013. Originally approved

14、in 1985. Last previous edition approved in 2004 as D4496 041, which waswithdrawn in January 2013 and reinstated in May 2013. DOI: 10.1520/D4496-13.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandard

15、s volume information, refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.4Available from ASTM International Headquarters. Order Adjunct No.ADJD4496.Copyright ASTM International, 100 Barr Harbor Drive, PO

16、 Box C700, West Conshohocken, PA 19428-2959. United States1anisotropy of electrical conduction. Hence, the significance oftests using this test method depends upon the orientation of thespecimen tested to the direction of the electric field and therelationship between this orientation and the orient

17、ation of thematerial in the electrical apparatus, which uses these materials.6. Apparatus6.1 Use apparatus conforming to the general requirementsset forth in Test Methods D257.6.2 Power SourceCapable of limiting the magnitude ofthe direct voltage applied to the specimen. (See Appendix X1for discussi

18、on of voltage stress and specimen heating.)6.3 Test cells, that have been found to be satisfactory aredepicted in Fig. 1, Fig. 2, and Fig. 3.4NOTE 1Conductive paint is a suitable electrode material for speci-mens of certain materials and testing such specimens does not require testcell assemblies si

19、milar to ones shown in Fig. 1, Fig. 2, and Fig. 34(seeAnnex A1 for additional information).7. Specimen Preparation and Selection7.1 Take specimens from a sample of material that has beenobtained in a random manner. Take care to protect the sampleand the specimens from any contamination, which will a

20、ffectthe results of the resistance or conductance tests. Such con-tamination can include, in particular, salts or moisture fromhuman hands. Be aware of elevated temperatures, extremes ofhigh or low humidity, and the presence of chemical vapors, etc.7.2 Prior to testing, condition all specimens to eq

21、uilibriumin the standard laboratory atmosphere prescribed in PracticeD6054. For many materials the time of conditioning toequilibrium will require only a few hours (that is, less than 24h). Equilibrium with standard laboratory conditions is declaredattained if two consecutive volume resistance measu

22、rements onthe same specimen agree within 61 %. The two consecutivemeasurements are to be made at the intervals separated at leastby4h.7.3 Determine the dimensions of the test specimens towithin6 2 % on material in equilibrium with the standardlaboratory atmosphere. Make all thickness measurements in

23、accordance with Method D of Test Methods D374 using theappropriate procedure for the material being tested.7.4 For specimens incorporating conductive paint electrodessee Annex A1.7.5 For anisotropic materials, label and prepare specimensfor testing in each of the principal directions of anisotropy.N

24、OTE 2Moderately conductive paper exhibits three axes of anisot-ropy. The principal axes in paper are machine direction (MD); cross-machine direction (CMD); and thickness direction (TD). Extruded poly-meric materials frequently show anisotropy with the axis of extrusion(direction of flow) compared to

25、 the axis of the material at right angles tothat direction of flow.8. Procedure8.1 Unless otherwise specified, make all measurementsusing an electrification time of less than 1 min. The electrifi-cation time shall be long enough to attain a “steady state” andthe magnitude of the voltage shall not be

26、 so great as to causeheating of the test specimen. See Appendix X1 for discussionof time effects of voltage application and specimen heating.8.2 Do not apply to the test specimen a power inputexceeding 1 W. For very conductive materials it is useful toincrease the size of a specimen or to decrease t

27、he test voltageby one or more orders of magnitude below 500 V in order toavoid the specimen overheating.8.3 Test a minimum of five specimens from each sample ineach of the principal directions of anisotropy. Use caution inhandling the specimens to avoid contaminating the surfaces.8.4 Place the speci

28、men in the test cell or attach the leads tothe painted-on electrodes. If mercury electrodes are used, takespecial care in handling the mercury.8.4.1 WarningMercury metal-vapor poisoning has longbeen recognized as a hazard in the industry. The maximumFIG. 1 Cell For Volume Resistivity 1-in.2Electrode

29、 (Mercury)D4496 132exposure limits are set by the American Conference of Gov-ernmental Industrial Hygienists.5The concentration of mercuryvapor over spills from broken thermometers, barometers, orother instruments using mercury can easily exceed theseexposure limits. Mercury, being a liquid and quit

30、e heavy, willdisintegrate into small droplets and seep into cracks andcrevices in the floor. The use of a commercially availableemergency spill kit is recommended whenever a spill occurs.The increased area of exposure adds significantly to themercury vapor concentration in the air. Mercury vapor con

31、cen-tration is easily monitored using commercially available sniff-ers. Spot checks are to be made periodically around operationswhere mercury is exposed to the atmosphere. Thorough checksare to be made after spills.8.5 Measure the conductance, resistance, or voltagecurrentvalues, depending upon the

32、 type of apparatus shown in TestMethods D257, that is being used. Record each observedmeasurement.8.6 Calculate the resistivity in accordance with Section 9.9. Calculation9.1 If the voltmeter-ammeter method of Test Methods D257is used in 8.5, calculate the resistance for each specimen usingthe equat

33、ion:R 5 VI (1)where:R = resistance, ,V = applied direct voltage, V, andI = magnitude of the direct current, A.9.2 If the direct method of resistance of Test Methods D257is used, use the values observed and calculate the resistivity asfollows:9.2.1 Volume Resistivity = v(in cm)5Available from the Ame

34、rican Conference of Governmental IndustrialHygienists, Building No. D-7, 6500 Glenway Ave., Cincinnati, OH 45211.AMass for applying contact force between current electrodes and the specimen (300 N/m times the specimen width in metres) (Note 1).BMass for applying contact force between potential elect

35、rodes and the specimen (60 N/m times specimen width in metres) (Note 2).CThe specimen.DCurrent electrodes.EPotential electrodes.FDistance between the current and potential electrodes (20 mm minimum).G Distance between potential electrodes depends on specimen size.HWidth of current electrode, 5 to 8

36、mm (0.2 to 0.3 in.).XElectrical insulating material (10 tera cm volume minimum resistivity).Note 1For a specimen 150 mm (6 in.) wide, mass is approximately 4.5 kg (10 lb).Note 2For a specimen 150 mm (6 in.) wide, mass is approximately 0.9 kg (2 lb).Note 3Fig. 2 is taken from Test Method D991.The ele

37、ctrode assembly (Fig. 2) shall consist of a rigid base made from an electrical insulating material having a volume resistivity greater than 10 T cm (for example,hard rubber, polyethylene, polystyrene, etc.) to which a pair of potential electrodes are fastened in such a manner that the four electrode

38、s are parallel and their top surfacesare in the same horizontal plane. Another pair of current electrodes identical with the first pair shall be fastened to a second piece of insulating material so that they canbe superimposed on the specimen directly above the first pair. The current electrodes sha

39、ll have a length at least 10 mm (0.4 in.) greater than the specimen width, a widthbetween 5 and 8 mm (0.2 and 0.3 in.), and a height uniform with 0.05 mm (0.002 in.) between 10 and 15 mm (0.4 and 0.6 in.). The potential electrodes shall have a lengthand height equal to the current electrodes, and sh

40、all be tapered to an edge having a radius of 0.5 mm (0.02 in.) maximum at the top surface. The distance between thepotential electrodes shall be not less than 10 mm (0.4 in.) nor more than 66 mm (2.6 in.) and shall be known within+2%.Thecurrentelectrodes shall be equidistant outsidethe potential ele

41、ctrodes by at least 20 mm (0.8 in.). The electrodes shall be made from a corrosion-resistant metal such as brass, nickel, stainless steel, etc. Insulationresistance between electrodes shall be greater than 1 T.FIG. 2 Electrode AssemblyFIG. 3 Cell For Surface Resistance Assembly PhotoD4496 133v5 RvAt

42、(2)where:Rv= volume resistance, ,A = area of the electrodes, cm2, andt = distance between the electrodes, cm.9.2.2 Surface Resistivity in (per square) ss5 RsW/L! (3)where:Rs= surface resistance, L = length of the specimen between electrodes, andW = width of the specimen.NOTE 3The ratio (W/L) is anal

43、ogous to the (P/g) ratio shown in TestMethods D257.NOTE 4L and W must be measured in the same units of distance. Theunit of surface resistivity is ohms (or megohms). It is common practice torefer to surface resistivity as ohms per square.10. Report10.1 Include in the report:10.1.1 Complete identific

44、ation of the material tested.10.1.2 Average and the standard deviation of the resistivitiescomputed shall be reported as the resistivity of the sample.10.1.3 Median (or central value) of the resistivities com-puted is often of interest and shall be reported.10.1.4 High and low (or the range of ) res

45、istivities.10.1.5 Average, and the high and low (or the range of)resistivity for each principal direction of anisotropy if aniso-tropic material is tested.10.1.6 Listing of any deviations from the prescribed testconditions.10.1.7 Type of test cell used.10.1.8 Fact that conductive paint was used, if

46、applicable.10.1.9 Voltage applied to the test specimen.10.1.10 Thickness of the specimens tested.11. Precision and Bias11.1 The measurements have been done using the test cellshown in Fig. 1 and a voltage stress below 10 direct VDC/mil(400 kVDC/m). The results in a single laboratory by threedifferen

47、t operators showed agreement within 6 3 % of theaverage value of volume resistivity.The moderately conductivematerials tested were carbon-black cellulose papers havingvolume resistivities 103to 105cm at 23C and 50 % relativehumidity.11.2 Using the test cell shown in Fig. 2 and a voltage stressof app

48、roximately 20 kVDC/m, the surface resistivity showedagreement within 610 % of the average value. The moderatelyconductive carbon-black cellulose paper ranged from 104to106 per square at 23C and 50 % relative humidity. Thesurface resistance using silver paint electrodes was not signifi-cantly differe

49、nt from the resistance using the test cell of Fig. 2and strips cut 1-in. wide.11.3 The bias of this test method has not been determined.12. Keywords12.1 electrical shielding; moderately conductive; semicom;surface resistivity; volume resistivityANNEX(Mandatory Information)A1. INFORMATION PERTINENT TO MEASUREMENTS OF SPECIMENS WITH ELECTRODES OF CONDUCTIVE PAINTINTRODUCTIONIt has been found practical to make resistance measurements with conductive paint applied to thesurface of a specimen to provide an electrode that has intimate co