1、Designation: D 4261 05Standard Practice forSurface Cleaning Concrete Masonry Units for Coating1This standard is issued under the fixed designation D 4261; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A

2、 number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice covers surface cleaning of concrete ma-sonry units to remove dust, dirt, mortar spatter, oil, and greaseprior to the ap

3、plication of coatings. Procedures include vacuumcleaning, air-blast cleaning, water cleaning, detergent waterwash, steam cleaning, and mechanical cleaning.1.2 This practice may alter the surface profile of theconcrete but is primarily intended to clean the surface.1.3 This standard does not purport

4、to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use. For specific hazardstatements, see Section 5.2. R

5、eferenced Documents2.1 ASTM Standards:2D 4258 Practice for Surface Cleaning Concrete for CoatingD 4262 Test Method for pH of Chemically Cleaned orEtched Concrete SurfacesD 4263 Test Method for Indicating Moisture in Concrete bythe Plastic Sheet Method2.2 Other Standard:ACI Specification 531.7-76 Spe

6、cification for Concrete Ma-sonry Construction33. Summary of Practice3.1 Surface cleaning is intended to provide a clean,contamination-free surface suitable for the application ofcoatings.3.2 Acceptable surfaces shall be free of dust, dirt, mortarspatter, oil, grease, and other contaminants. Mortar j

7、oints shallbe struck flush or tooled with a round jointer and shall be freeof rough edges and nibs (see ACI 531.1-76).3.3 Vacuum cleaning, air blast cleaning, water cleaning,detergent water wash, steam cleaning, hand tool, and mechani-cal cleaning are acceptable cleaning methods.3.4 Any one or a com

8、bination of listed cleaning proceduresmay be used to achieve acceptably cleaned surfaces.4. Significance and Use4.1 Surface cleaning is to be used to prepare concrete unitmasonry surfaces for applying coatings intended for light dutyservice, splash and spillage of water and chemical solutions,radiat

9、ion exposure, decontamination, and repeated washdownswith alkaline cleaners.5. Cautions5.1 Moisture in concrete unit masonry may be detrimentalto coating adhesion. Moisture content shall be in compliancewith the coating manufacturers recommendations (see TestMethod D 4263 for moisture test method).6

10、. Procedures6.1 Steam CleaningThis procedure is intended to removeheavy deposits of grease and oil, as well as other water solublesurface contaminants and emulsifiable materials, with a jet ofhigh pressure steam, in accordance with Practice D 4258.6.2 Detergent Water WashThis procedure is intended t

11、oremove water soluble surface contaminants, oils, grease, andother emulsifiable materials with an aqueous solution ofdetergent or nonsolvent emulsifier in accordance with PracticeD 4258.6.3 Water CleaningThis procedure is intended to removedust, dirt, and water soluble contaminants with a stream ofw

12、ater under pressure, in accordance with Practice D 4258.6.4 Mechanical Tool Cleaning:6.4.1 The intent of this procedure is to remove mortarspatter, efflorescence, and similar dry, firmly adhering foreignmaterial prior to performing either cleaning operation.6.4.2 This procedure shall consist of scra

13、ping, abrading,brushing, or stoning to dislodge mortar and similar materialsfrom the surface.6.4.3 Clean in accordance with Practice D 4258 to removedust and loose particles.1This practice is under the jurisdiction of ASTM Committee D33 on ProtectiveCoating and Lining Work for Power Generation Facil

14、ities and is the directresponsibility of Subcommittee D33.05 on Application and Surface Preparation.Current edition approved Dec. 1, 2005. Published January 2006. Originallyapproved in 1983. Last previous edition approved in 1999 as D 4261 83 (1999).2For referenced ASTM standards, visit the ASTM web

15、site, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from American Concrete Institute (ACI), P.O. Box 9094, FarmingtonHills, MI 48333.1Copyright ASTM Int

16、ernational, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.6.5 Vacuum CleaningThis procedure is intended to re-move surface dust and other debris by vacuum cleaning inaccordance with Practice D 4258.6.6 Air Blast CleaningThis procedure is intended toremove debris

17、, dust, dirt, and loosely adhering material by airblast cleaning in accordance with Practice D 4258.7. Inspection7.1 Visually examine prepared surface for the presence ofdebris, dust, dirt, oil, grease, loose particles, mortar spatter, andother contaminants.7.2 Test surfaces cleaned with detergent o

18、r non-solventemulsifying agents for pH in accordance with Test MethodD 4262.7.3 Moisture content may be determined in accordance withTest Method D 4263.8. Acceptance8.1 Acceptable surfaces shall be free of dust, dirt, mortarspatter, oil, grease, and other contaminants.9. Keywords9.1 coating; concret

19、e unit masonry; surface cleaningpreparationASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and

20、the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision

21、 of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shou

22、ldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D4261052