ASTM B894-2009 Standard Specification for ACuZinc5 (Zinc-Copper-Aluminum) Alloy Die Castings.pdf

《ASTM B894-2009 Standard Specification for ACuZinc5 (Zinc-Copper-Aluminum) Alloy Die Castings.pdf》由会员分享，可在线阅读，更多相关《ASTM B894-2009 Standard Specification for ACuZinc5 (Zinc-Copper-Aluminum) Alloy Die Castings.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B894 09Standard Specification forACuZinc51(Zinc-Copper-Aluminum) Alloy Die Castings2This standard is issued under the fixed designation B894; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A

2、 number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers ACuZinc5, zinc-copper-aluminum alloy die castings. (UNS Z46541).31.2 The values stated in inch-pound units

3、are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibili

4、ty of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulator

5、y limitations prior to use.2. Referenced Documents2.1 The following documents of the issue in effect on dateof order acceptable form a part of this specification to theextent referenced herein:2.2 ASTM Standards:4B892 Specification for ACuZinc5 (Zinc-Copper-Aluminum) Alloy in Ingot Form for Die Cast

6、ingsB899 Terminology Relating to Non-ferrous Metals andAlloysE10 Test Method for Brinell Hardness of Metallic MaterialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE88 Practice for Sampling Nonferrous Metals and Alloys inCast Form for Determinatio

7、n of Chemical CompositionE527 Practice for Numbering Metals and Alloys in theUnified Numbering System (UNS)E536 Test Methods for Chemical Analysis of Zinc and ZincAlloysE634 Practice for Sampling of Zinc and Zinc Alloys forOptical Emission Spectrometric Analysis2.3 Federal Standards:5Fed. Std. No. 1

8、23 Marking for Shipment (Civil Agencies)2.4 IS Standards:6IS 3815-1 Zinc and zinc alloys Part 1: Analysis of solidsamples by optical emission spectrometryIS 3815-2 Zinc and zinc alloys Part 2: Analysis byinductively coupled plasma optical emission spectrometry2.5 Military Standard:7MIL-P-116 Methods

9、 of PreservationMIL-STD-129 Marking for Shipment and Storage2.6 NADCA Standard:8NADCA Product Specification Standards for Die Castings3. Terminology3.1 Terms shall be defined in accordance with TerminologyB899.3.2 Definitions of Terms Specific to This Standard:3.2.1 die casting, na casting process i

10、n which moltenmetal is injected under high velocity and pressure into a metaldie and solidified, also a product produced by such a process.Alternately known as pressure die casting.4. Ordering Information4.1 Orders for die castings shall include the following basicinformation:4.1.1 This specificatio

11、n number and date,4.1.2 Quantity and delivery schedule, as required,1ACuZinc and ACuZinc5 are registered trade names of the General MotorsCorporation.2This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02

12、.04 on Zinc and Cadmium.Current edition approved Oct. 1, 2009. Published November 2009. Originallyapproved in 1999. Last previous edition approved in 2003 as B894 - 03. DOI:10.1520/B0894-09.3See Footnote B in Table 1.4For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact AST

13、M Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.5Available from U.S. Government Printing Office Superintendent of Documents,732 N. Capitol St., NW, Mail Stop: SDE, Washington, DC 20401, http:/

14、www.access.gpo.gov.6Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.7Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/www.dodssp.daps.mil.

15、8Available from North American Die Casting Association 241 Holbrook DrWheeling, Illinois 60090-5809, http:/www.diecasting.org.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United

16、States.4.1.3 Part name and number,4.1.4 Alloy (Table 1), and4.1.5 Drawing of die casting, when required, giving allnecessary dimensions and showing latest revisions and allow-ances for machining, if any. Location of ejector pin marks orparting lines shall be at the option of the producer, unlessspec

17、ifically designated on the drawing.4.2 Additional tests, options and special inspection require-ments as provided below should be justified only on the basisof need. These shall be specified in the contract or purchaseorder, as additional procedures and extended delivery time maybe involved.4.2.1 Ch

18、emical analysis (7.1.1),4.2.2 Quality assurance (Section 6),4.2.3 Special proof tests or mechanical properties (Section8),4.2.4 General quality options for internal soundness or forfinish (Section 10),4.2.5 Source inspection (Section 11),4.2.6 Certification (Section 13),4.2.7 Marking for identificat

19、ion (Section 14), and4.2.8 Special packaging (Section 15).5. Materials and Manufacture5.1 The metal used in the manufacture of die castings shallbe zinc alloy of a specified chemical composition conformingto the requirements of Specification B892.5.2 The material covered by this specification shall

20、be ofuniform quality and shall be free of harmful contamination.6. Quality Assurance6.1 Responsibility for InspectionWhen specified in thecontract or purchase order, the producer or supplier is respon-sible for the performance of all inspection and test require-ments specified herein. Except as othe

21、rwise specified in thecontract or order, the producer or supplier may use his own orany other suitable facilities for the performance of the inspec-tion and test requirements specified herein, unless disapprovedby the purchaser. The purchaser shall have the right to performany of the inspections and

22、 tests set forth in this specification.Quality assurance standards shall be agreed upon between theproducer or supplier and purchaser at the time a contract ororder is placed.6.2 For normal inspection purposes, an inspection lot shallconsist of the production from each die during a singleproduction

23、run, as defined and recorded by the producer, andshipped, or available for shipment, at one time.6.2.1 The producer or supplier shall examine each diecasting of a randomly or statistically selected sample todetermine conformance to the requirements of the contract,purchase order, or part drawing. Th

24、e results of this inspectionshall be recorded.6.2.1.1 Unless otherwise specified in the contract, purchaseorder, or part drawing, detailed dimensional conformance shallnormally be determined on one or more production samples.6.2.2 When specified in the contact, purchase order, or partdrawing, specia

25、l inspection lot definitions may be established,for a specific part.7. Chemical Requirements7.1 LimitsThe die casting shall conform to the require-ments as to chemical composition in Table 1. Conformanceshall be determined by the producer by analyzing samplestaken at the time castings are made. If t

26、he producer hasdetermined the chemical composition of the metal during thecourse of manufacture, he shall not be required to sample andanalyze the finished product.7.1.1 When a detailed chemical analysis is required with ashipment, is shall be called for in the contract or purchaseorder.7.1.2 If the

27、 producers or suppliers method of compositioncontrol is acceptable, sampling for chemical analysis may bewaived at the discretion of the purchaser.7.2 Number of SamplesWhen required, samples for deter-mination of chemical composition shall be taken to representthe following:7.2.1 A sample shall be t

28、aken from each of two representa-tive castings selected from each lot defined in 6.2.7.3 Methods of SamplingSamples from die castings fordetermination of chemical composition shall be taken inaccordance with one of the following methods:7.3.1 Samples for chemical analysis shall be taken from themate

29、rial by drilling, sawing, milling, turning or clipping arepresentative piece or pieces to obtain a weight of preparedsample not less than 100 g. Sampling shall be in accordancewith Practice E88.7.3.2 By agreement, an appropriate spectrographic samplemay be prepared at time of manufacture in accordan

30、ce withPractice E634.7.3.3 The method of sampling cast products for spectro-chemical and other methods of analysis shall be suitable for theform of material being analyzed and the type of analyticalmethod used.7.4 Method of AnalysisThe determination of chemicalcomposition shall be made in accordance

31、 with suitable chemi-cal Test Methods E536, IS 3815-1, IS 3815-2, or other meth-ods. In case of dispute, the results secured by Test MethodE536, IS 3815-1,orIS 3815-2 shall be the basis of acceptance.TABLE 1 ACuZinc5 Chemical Requirements, Composition, Zinc-Copper-Aluminum Die CastingsAElementsCompo

32、sition, %(Z46541)BCopper 5.0 to 6.0Aluminum 2.5 to 3.3Magnesium 0.025 - 0.05Iron 0.075 maxLead 0.005 maxCadmium 0.004 maxTin 0.003 maxZinc RemainderCAThe following applies to all specified limits in this table: For purposes ofdetermining conformance with this specification, the observed value or cal

33、culatedvalue obtained from analysis shall be rounded off to the nearest unit in the lastright-hand place of figures used in expressing the specified limit, in accordancewith the rounding method of Practice E29.BUNS designations were established in accordance with Practice E527.CDetermined arithmetic

34、ally by difference.B894 0928. Mechanical Properties and Tests8.1 Unless specified in the contract or purchase order, orspecified on the detail drawing, acceptance of die castingsunder this specification shall not depend on mechanical prop-erties determined by tension or impact tests.8.1.1 Tensile st

35、rength, yield strength and elongation valuesshown in Table 1 are Weibull analysis values to be used fordesign guidance. They are B50and B1values with 50 %confidence and were obtained from tests on 5.3 mm diameterseparately cast test bars which had a 25.4 mm gage length. Thebars were tested in the as

36、-cast condition.NOTE 1The property values of test bars cut from castings will varydepending on the solidification rate of the individual casting. Solidifica-tion and cooling rate are significantly influenced by casting section size.Also due to cooling rate and section size variation, the properties

37、of barsmachined from castings may vary from those of separately cast test bars.For these reasons, acceptance or rejection of the casting shall be based onchemistry. Hardness and mechanical properties may be used when agreedby the purchaser and supplier, and specified on the engineering drawing.8.1.2

38、 Hardness (Test Method E10)The hardness shall bedetermined on the casting unless otherwise specified on thepart drawing. A Brinell hardness test will be performed using a500 kg load and a 10 mm ball unless otherwise specified andagreed to by supplier and user. If the part is too small for aBrinell t

39、est, a Rockwell F or K hardness test is suggested.9. Permissible Variations in Dimensions9.1 Permissible variations in dimensions shall be within thelimits specified on the drawings or in the contract or purchaseorder.9.1.1 Any dimensions for which a tolerance is not specifiedshall be in accordance

40、with NADCA Product SpecificationStandards for Die Castings.9.2 Dimensional tolerance deviations waived by the pur-chaser shall be confirmed in writing to the producer or supplier.10. General Quality10.1 Internal SoundnessWhen specified, the soundness ofdie castings shall conform to standards or requ

41、irements agreedupon between the producer or supplier and the purchaser. Thenumber and extend of imperfections shall not exceed thosespecified by the purchaser. The standards or requirements mayconsist of radiographs, photographs, or sectioned die castings.10.2 Imperfections inherent in die castings

42、shall not because for rejection provided it is demonstrated that the diecastings are in accordance with the requirements and standardsagreed upon.10.3 WorkmanshipDie castings shall be of uniform qual-ity, free of injurious discontinuities that will adversely affecttheir serviceability.10.4 FinishWhe

43、n specified in the contract or purchaseorder the as-cast surface finish required shall conform tostandards agreed upon between the purchaser and the producer,supplier, or as prescribed in NADCA Product SpecificationStandards for Die Castings.10.5 Pressure TightnessWhen specified in the contract orpu

44、rchase order the pressure tightness of die castings shallconform to standards agreed upon between the purchaser andthe producer or supplier, or as prescribed in NADCA ProductSpecification Standards for Die Castings.11. Source Inspection11.1 If the purchaser desires that his representative inspector

45、witness the inspection and testing of the product prior toshipment, such agreement shall be made by the purchaser andproducer or supplier as part of the contract or purchase order.11.2 When such inspection or witness of inspection andtesting is agreed upon, the producer or supplier shall afford thep

46、urchasers representative all reasonable facilities to satisfyhim that the product meets the requirements of this specifica-tion. Inspection and tests shall be conducted so there is nounnecessary interference with the producers operations.12. Rejection and Retest12.1 When one or more samples, dependi

47、ng on the ap-proved sampling plan fail to meet the requirements of thisspecification, the represented lot is subject to rejection exceptas otherwise provided in 12.2.12.2 Lots rejected for failure to meet the requirements ofthis specification may be resubmitted for test provided:12.2.1 The producer

48、has removed the nonconforming mate-rial or the producer has reworked the rejected lot as necessaryto correct the deficiencies.12.3 Individual castings that show injurious imperfectionsduring subsequent manufacturing operations may be rejected.The producer or supplier shall be responsible only for re

49、place-ment of the rejected castings to the purchaser. As much of therejected original material as possible shall be returned to theproducer or supplier.13. Certification13.1 The producer or supplier shall, when called for in thecontract or purchase order, furnish to the purchaser a certificateof inspection stating that each lot has been sampled, tested, andinspected in accordance with this specification, and has beenfound to meet the requirements specified.14. Identification Marking14.1 When specified in the contract or purchase order, or inthe detail drawing,