ASTM B676-2003(2014) Standard Specification for UNS N08367 Welded Tube《UNS N08367焊接管的标准规格》.pdf

《ASTM B676-2003(2014) Standard Specification for UNS N08367 Welded Tube《UNS N08367焊接管的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM B676-2003(2014) Standard Specification for UNS N08367 Welded Tube《UNS N08367焊接管的标准规格》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B676 03 (Reapproved 2014)Standard Specification forUNS N08367 Welded Tube1This standard is issued under the fixed designation B676; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in

2、 parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers UNS N083672welded tube forgeneral corrosion applications.1.2 This specification covers outside diameter and nominalwal

3、l tube.1.2.1 The tube sizes covered by this specification are18 to 5in. (3.2 to 127 mm) in outside diameter and 0.015 to 0.320 in.(0.38 to 8.13 mm), inclusive, in wall thickness.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalc

4、onversions to SI units that are provided for information onlyand are not considered standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including tho

5、se identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3A1016/A101

6、6M Specification for General Requirements forFerritic Alloy Steel, Austenitic Alloy Steel, and StainlessSteel TubesB751 Specification for General Requirements for Nickel andNickel Alloy Welded TubeB899 Terminology Relating to Non-ferrous Metals and Al-loys3. Terminology3.1 Terms defined in Terminolo

7、gy B899 shall apply unlessotherwise defined in this standard.4. General Requirement4.1 Material furnished in accordance with this specificationshall conform to the applicable requirements of SpecificationB751 unless otherwise provided herein.5. Classification5.1 Class 1Welded, cold worked, solution

8、treated, andeach piece of each lot subjected to one of the following fourtests: hydrostatic, pneumatic (air underwater), eddy current, orultrasonic.5.2 Class 2Welded, cold worked, solution treated, andeach piece of each lot leak tested (hydrostatic or pneumatic)plus electric tested (eddy current or

9、ultrasonic).6. Ordering Information6.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for material ordered under thisspecification. Examples of such requirements include, but arenot limited to, the following:6.1.1 Alloy name or UNS number,6.1.2 ASTM designati

10、on and year of issue,6.1.3 Dimensions:6.1.3.1 Outside diameter and nominal wall thicknesses,NOTE 1Tube produced to outside diameter and minimum wallthickness may be furnished upon agreement between the manufacturer andthe purchaser.6.1.3.2 Length (specific or random),6.1.4 Class (Section 5),6.1.5 Qu

11、antity (feet or number of pieces),6.1.6 CertificationState if certification is required,6.1.7 Samples for Product (Check) AnalysisState whethersamples for product (check) analysis should be furnished, and6.1.8 Purchaser InspectionIf the purchaser wishes towitness tests or inspection of material at t

12、he place ofmanufacture, the purchase order must so state indicating whichtests or inspections are to be witnessed.1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and

13、 Their Alloys.Current edition approved Oct. 1, 2014. Published October 2014. Originallyapproved in 1980. Last previous edition approved in 2009 as B676 03 (2009).DOI: 10.1520/B0676-03R14.2New designation established in accordance with Practice E527 and SAE J1086,Practice for Numbering Metals and All

14、oys (UNS).3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive

15、, PO Box C700, West Conshohocken, PA 19428-2959. United States17. Material and Manufacture7.1 Tube shall be made from flat-rolled alloy by an auto-matic welding process with no addition of filler metal. Subse-quent to welding and prior to final solution treatment Class 1and Class 2 material shall be

16、 cold worked either in both weldand base metal or in weld metal only.NOTE 2The recommended heat treatment shall consist of heating to aminimum temperature of 2025F (1105C) for Type N08367 and quench-ing in water or rapidly cooling by other means.7.2 Tube shall be furnished with oxide removed. Whenso

17、lution treatment is performed in a protective atmospheredescaling is not necessary.8. Chemical Composition8.1 The material shall conform to the requirements as tochemical composition prescribed in Table 1. One test isrequired for each lot as defined in Specification B751.8.2 If a product (check) ana

18、lysis is performed by thepurchaser, the material shall conform to the product (check)analysis variations specified in Specification B751.9. Mechanical Properties and Other Requirements9.1 Mechanical PropertiesThe material shall conform tothe mechanical properties prescribed in Table 2. One test isre

19、quired for each lot as defined in Specification B751.9.2 Flattening Test Requirements:9.2.1 One flattening test per lot shall be performed inaccordance with Specification B751.9.3 Flange Test Requirements:9.3.1 Flange test specimens shall show no cracking or flaws.9.3.2 For tube less than 0.093 in.

20、(2.36 mm) in insidediameter and tube having a wall thickness equal to or greaterthan the inside diameter, the flange test shall not be required.9.4 Reverse-Bend Requirements:9.4.1 One reverse-bend test as defined in SpecificationA1016/A1016M shall be performed on each lot of tubing.9.4.2 Reverse-ben

21、d test specimens shall show no evidenceof cracks or lack of penetration in the weld, or of overlapsresulting from the reduction in thickness of the weld areas bycold working.9.4.3 The reverse-bend test is not applicable when thespecified wall is 10 % or more of the specified outsidediameter, or the

22、wall thickness is 0.134 in. (3.4 mm) or greater,or the outside diameter size is less than 0.375 in. (9.5 mm).Under these conditions the reverse flattening test of Specifica-tion A1016/A1016M shall apply.9.4.4 The lot definition for the reverse-bend test shall be1500 ft (450 m) of finished tubing.9.5

23、 Nondestructive Test Requirements:9.5.1 Tube shall be subjected to a pressure test or nonde-structive electric test in accordance with Specification B751.10. Keywords10.1 UNS N08367; welded tubeTABLE 1 Chemical RequirementsElementComposition Limits, %N08367Carbon 0.030 maxManganese 2.00 maxSilicon 1

24、.00 maxPhosphorus 0.040 maxSulfur 0.030 maxChromium 20.00 to 22.00Nickel 23.50 to 25.50Molybdenum 6.00 to 7.00Nitrogen 0.18 to 0.25IronAremainderCopper 0.75 maxAIron shall be determined arithmetically by difference.B676 03 (2014)2ASTM International takes no position respecting the validity of any pa

25、tent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revisio

26、n at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your com

27、ments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyright

28、ed by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-

29、mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 2 Mechanical PropertiesType Condition (Temper) GageTensile Strength,min, ksi (MPa)Yield Strength, 0.2 %Offset, min, ksi (MPa)Elongation in2 in. or 50mm (or 4 D), min, %N08367Solution treated (Class 1and Class 2)#316316100 (690)95 (655)45 (310)45 (310)3030B676 03 (2014)3