SAE AS 3563D-2013 NUT SELF-LOCKING DOUBLE HEXAGON SOLID FILM LUBRICATED EXTENDED WRENCH PAD 160 KSI 800 DEGREE F UNS S66286《UNS S66286 800℉ 160 KSI 延长的扳手衬垫 固体膜润滑 双精度型六角型 自锁定式螺母》.pdf

《SAE AS 3563D-2013 NUT SELF-LOCKING DOUBLE HEXAGON SOLID FILM LUBRICATED EXTENDED WRENCH PAD 160 KSI 800 DEGREE F UNS S66286《UNS S66286 800℉ 160 KSI 延长的扳手衬垫 固体膜润滑 双精度型六角型 自锁定式螺母》.pdf》由会员分享，可在线阅读，更多相关《SAE AS 3563D-2013 NUT SELF-LOCKING DOUBLE HEXAGON SOLID FILM LUBRICATED EXTENDED WRENCH PAD 160 KSI 800 DEGREE F UNS S66286《UNS S66286 800℉ 160 KSI 延长的扳手衬垫 固体膜润滑 双精度型六角型 自锁定式螺母》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、AEROSPACE STANDARD NUT, SELF-LOCKING, DOUBLE HEXAGON, SOLID FILM LUBRICATED, EXTENDED WRENCH PAD, 160 KSI, 800 F, UNS S66286 AS3563Copyright 2013 SAE International All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any m

2、eans, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org

3、 ISSUED 1995-10REVISED 2013-08THIRD ANGLE PROJECTION CUSTODIAN: E-25 REV.DFEDERAL SUPPLY CLASS 5310 AS3563SHEET 1 OF 3REV. DPROCUREMENT SPECIFICATION: AS4393 /2/SAE Technical Standards Board Rules provide that: “This report ispublishedby SAE toadvance thestate of technicalandengineering sciences. Th

4、euse ofthis report is entirely voluntary, andits applicability and suitability forany particular use,including any patent infringement arising therefrom, isthe soleresponsibilityofthe user.”SAE reviews eachtechnicalreport at least every five years at which time itmay berevised, reaffirmed, stabilize

5、d, orcancelled. SAE invites yourwrittencomments andsuggestions. SAE values your input. To provide feedbackon this Technical Report, please visit http:/www.sae.org/technical/standards/AS3563DRATIONALE RESTORE MARKING SPECIFICATION TO AS478, REVISE FPI NOTE, MINOR EDITORIAL AND REFERENCE UPDATES, FIGU

6、RE 1 REDRAWN. FIGURE 1 - NUT AEROSPACE STANDARD AS3563SHEET 2 OF 3REV. DNUT, SELF-LOCKING, DOUBLE HEXAGON, SOLID FILM LUBRICATED, EXTENDED WRENCH PAD, 160 KSI, 800 F, UNS S66286 TABLE 1A - PART NUMBERS AND DIMENSIONS D, B, AS870 DASH NO., E, F, AB, H, AND K PARTNUMBER THREAD D BNOM AS870DASHNO. EMAX

7、FMINAB HMINKMAXAS3563-09 .1900-32UNJF-3B .2500 08 .340 .325 .190 - .220 .045 .305 AS3563-10 .2500-28UNJF-3B .3125 10 .450 .410 .250 - .280 .045 .400 AS3563-11 .3125-24UNJF-3B .3750 12 .525 .495 .312 - .342 .060 .455 AS3563-12 .3750-24UNJF-3B .4375 14 .600 .560 .375 - .405 .070 .520 AS3563-13 .4375-2

8、0UNJF-3B .5625 18 .690 .650 .438 - .468 .080 .595 AS3563-14 .5000-20UNJF-3B .6250 20 .780 .740 .500 - .532 .100 .680 AS3563-15 .5625-18UNJF-3B .6875 22 .880 .840 .562 - .597 .110 .758 AS3563-16 .6250-18UNJF-3B .7812 25 .970 .925 .625 - .660 .120 .850 AS3563-17 .7500-16UNJF-3B .9375 30 1.230 1.180 .7

9、50 - .785 .130 1.032 TABLE 1B - DIMENSIONS L, N, T, P, R, AH AND APPROX. MASS. PARTNUMBER LNMAXTMINP R AH APPROX MASSLB/100 AS3563-09 .190-.210 .262 .082 .004 .006 .0014 .28 AS3563-10 .250-.270 .326 .130 .005 .007 .0014 .51 AS3563-11 .312-.332 .392 .170 .005 .008 .0016 .83 AS3563-12 .375-.395 .458 .

10、210 .005 .009 .0016 1.34 AS3563-13 .438-.458 .588 .230 .005 .010 .0020 2.74 AS3563-14 .500-.520 .654 .260 .006 .012 .0020 3.34 AS3563-15 .562-.582 .720 .320 .006 .014 .0020 4.92 AS3563-16 .625-.645 .817 .370 .007 .015 .0020 7.12 AS3563-17 .750-.770 .980 .500 .007 .016 .0020 13.01 NOTES: 1. MATERIAL:

11、 CORROSION AND HEAT RESISTANT STEEL PER AMS5731 OR AMS5734 (UNS S66286). HEAT TREATMENT: AFTER FORMING, NUTS SHALL BE HEAT TREATED PER AMS2759/3 TO MEET THE HARDNESS SPECIFIED IN NOTE 3. /2/ PROCUREMENT SPECIFICATION: AS4393 EXCEPT AS FOLLOWS: a. COATING: SOLID FILM LUBRICANT PER AS1701, TYPE VI, IN

12、 LIEU OF SILVER PLATE PER AMS2411. b. PRETREATMENT: PRIOR TO APPLYING THE SOLID FILM LUBRICANT, NUTS MAY BE PLATED WITH COPPER (AMS2418) OR NICKEL (AMS2403) OR BOTH TO .00025 MAXIMUM THICKNESS. c. DIMENSIONS APPLY AFTER PRETREATMENT PLATING AND BEFORE COATING WITH SOLID FILM LUBRICANT. d. BAKE AT 80

13、0 F 15 F IN LIEU OF 1200 F FOR NUTS TESTED AFTER BAKE. 3. HARDNESS: 32-42 HRC. 4. BREAK SHARP EDGES .003 TO .015, UNLESS OTHERWISE SPECIFIED. AEROSPACE STANDARD AS3563SHEET 3 OF 3REV. DNUT, SELF-LOCKING, DOUBLE HEXAGON, SOLID FILM LUBRICATED, EXTENDED WRENCH PAD, 160 KSI, 800 F, UNS S66286 5. FLUORE

14、SCENT PENETRANT INSPECTION PER ASTM E1417/E1417M, TYPE 1, SENSITIVITY LEVEL 2 MIN, PRIOR TO PRETREATMENT OR COATING. ACCEPTANCE CRITERIA PER AS3071. 6. SURFACE TEXTURE: SYMBOLS PER ASME Y14.36M. REQUIREMENTS PER ASME B46.1. UNLESS OTHERWISE SPECIFIED, SURFACES TO BE 125 MICROINCHES Ra. 7. DIMENSIONI

15、NG AND TOLERANCING: ANSI Y14.5M-1982 (ASME PUBLICATION). 8. DIMENSIONS ARE IN INCHES. 9. DO NOT USE UNASSIGNED NUMBERS. 10. CLASSIFICATION: a. 160 KSI MINIMUM AXIAL STRENGTH AT ROOM TEMPERATURE. b. 800 F MAXIMUM BAKE TEMPERATURE FOR NUTS TESTED AFTER BAKING. 11 A CHANGE BAR (l) LOCATED IN THE LEFT M

16、ARGIN IS FOR THE CONVENIENCE OF THE USER IN LOCATING AREAS WHERE TECHNICAL REVISIONS, NOT EDITORIAL CHANGES, HAVE BEEN MADE TO THE PREVIOUS ISSUE OF THIS DOCUMENT. AN (R) SYMBOL TO THE LEFT OF THE DOCUMENT TITLE INDICATES A COMPLETE REVISION OF THE DOCUMENT, INCLUDING TECHNICAL REVISIONS. CHANGE BARS AND (R) ARE NOT USED IN ORIGINAL PUBLICATIONS, NOR IN DOCUMENTS THAT CONTAIN EDITORIAL CHANGES ONLY. AS AND AMS ARE SAE INTERNATIONAL PUBLICATIONS. ASTM IS AN ASTM INTERNATIONAL PUBLICATION. ASME IS AN AMERICAN SOCIETY OF MECHANICAL ENGINEERS PUBLICATION.