FORD WSS-M2F202-A-2014 FABRIC VINYL COATED (PVC) WELL LINING TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD WSS-M2F202-A-2014 FABRIC VINYL COATED (PVC) WELL LINING TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M2F202-A-2014 FABRIC VINYL COATED (PVC) WELL LINING TO BE USED WITH FORD WSS-M99P1111-A .pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2014 11 24 N Status No replacement named D. Murtonen, NA 2006 05 03 Activated C. McComb Copyright 2014, Ford Global Technologies, LLC Page 1 of 2 FABRIC, VINYL COATED (PVC), WELL LINING WSS-M2F202-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The

2、material defined by this specification is a calendered polyvinyl chloride copolymer film laminated to a poly/cotton knit. 2. APPLICATION This specification was released originally for material used as a well lining for convertible tops. 3. REQUIREMENTS Material specification requirements are to be u

3、sed for initial qualification of materials. In addition to the requirements listed herein, this material shall meet all requirements of the WSS-M8P3-D3, PERFORMANCE, FLEXIBLE POLYMERIC FILM, INTERIOR QUALITY material performance specification. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Mater

4、ial suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 MATERIAL CHARACTERISTICS Construction is a PVC facing to a poly/cotton backing. polyester: 65% cotton: 35% 3.3 APPEARANCE (FLTM BI 109-01) The color, pattern and finish

5、shall match the approved master sample, or shall be as specified on the engineering drawing. 3.4 WEIGHT, range (ASTM D 751, Sample Method) LSL USL Coating 641 g/m2 711 g/m2 Fabric 68 g/m2 98 g/m2 Total 709 g/m2 809 g/m2 ENGINEERING MATERIAL SPECIFICATION WSS-M2F202-A Copyright 2014, Ford Global Tech

6、nologies, LLC Page 2 of 2 3.5 RESISTANCE TO TEAR, Trapezoid, min (ASTM D 1117) Warp 22 N Fill 22 N 3.6 BREAKING STRENGTH, min (ASTM D 751, Grab Method) Warp 222 N Fill 198 N 3.7 ADHESION OF VINYL FILM TO BACKING FABRIC, min (FLTM BN 151-05, Method A/ISO 2711) Warp 18 N Fill 18 N 3.8 FILTERED XENON WEATHEROMETER, min (FLTM B0 116-01/ISO 105-A02/AATCC Evaluation Procedure 1) 451.2 kJ Rating 4 4. GENERAL INFORMATION The information below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 RECYCLING CODE PVC,LF