FORD WSK-M4G329-A-2014 SEALER CAULKING COMPOUND SOLVENT FREE TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD WSK-M4G329-A-2014 SEALER CAULKING COMPOUND SOLVENT FREE TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WSK-M4G329-A-2014 SEALER CAULKING COMPOUND SOLVENT FREE TO BE USED WITH FORD WSS-M99P1111-A .pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 5 2014 10 20 N Status No replacement named L. Sinclair, NA 2011 07 13 Revised Odor Requirements added W. Janitschke, EU 1998 11 05 Revised Added B3; Completely revised W. Scholz Controlled document at www.MATS Copyright 2014, Ford Global

2、 Technologies, LLC Page 1 of 4 SEALER CAULKING COMPOUND, SOLVENT FREE WSK-M4G329-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a caulking compound based on synthetic rubber which can be applied in an extruded (strip) form or in an unshaped form in two hardnes

3、s grades. 2. APPLICATION This specification was released originally for sealing purposes and to eliminate noise in cable openings, screw-fastening holes as well as screw held flanges. The material is applied to oiled, primed or painted metal. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION

4、MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COLOR Gray to white or according to Engineering drawing with additional suffix (see para 4.3). 3.3 SOLIDS 99 % min (FLTM BV 150-10) 3.4 DENSITY AT 20 C 1.

5、6 - 1.9 kg/L (ASTM D 1475) 3.5 PENETRATION-HARDNESS GRADE (see para 4.2) 4 - 5 mm Test Method: Test apparatus as described in ASTM D 217, total weight force 1.5 N, 5 s time delay. The material under test is transferred into a container 75 mm in diameter, avoiding entrapment of air bubbles during fil

6、ling. Fill the container up to the rim and condition for 16 h at room temperature prior to test. The results of tests on a min of 5 samples are to be determined in mm and must not deviate more than 10 % from the average value. 3.6 PAINT STAINING (FLTM BZ 150-11, Method A) No staining or any other de

7、leterious effects on the painted surface. Test Method: 200 mm long strips of the test material are placed on panels (300 x 100 mm) oiled according to FLTM BZ 150-11, Method A , and pressed down lightly. The test specimens are then painted according to FLTM BI 103-02, Method C, and conditioned for 1

8、h at room temperature. Following this, half of each specimen is masked and exposed in the Fluorescent Sunlamp Cabinet (FLTM BU 152-02) for 96 h. Evaluated for evidence of staining by comparing the exposed area of the specimen with the unexposed. ENGINEERING MATERIAL SPECIFICATION WSK-M4G329-A Copyri

9、ght 2011, Ford Global Technologies, LLC Page 2 of 4 3.7 AGING No breaking, no cracking Test Method: a) Expose 200 x 20 x 6 mm strips of material under test for 72 h at 100 +/- 2 C. b) Condition test specimens for 1 h at room temperature. c) Bend each specimen through an angle of 180 deg in 2 s aroun

10、d a 50 mm diameter mandrel. 3.8 COLD RESISTANCE No breaking, no cracking Test Method: a) Expose 200 x 20 x 6 mm strips of material under test and a 50mm diameter mandrel for 4 h at - 40 +/- 1 C. b) While still in the cold box bend each specimen through an angle of 180 deg 2 s around the mandrel. 3.9

11、 WATER RESISTANCE The material must not become soluble or show any loss of cohesion. Test Method: The material shall be kneaded between the fingers under running tap water for 1 minute at room temperature. 3.10 ADHESION STRENGTH The test specimen must when placed in an upside down position adhere to

12、 the test panels for 30 s. Test Method: A test specimen is placed on a grease free body steel panel 300 x 100 mm in size without applying any pressure. After a storage time of 5 minutes at room temperature the panel is turned upside down so that the strip is held only by means of its own adhesion st

13、rength. 3.11 FORM STABILITY The extensibility of the material shall constitute the measure of its form stability. 3.11.1 Extensibility as Received 10 % max 3.11.2 Extensibility After Aging (para. 3.7) 15 % max Test Method: A 250 mm long section of the caulking strip on its release foil is cut out. T

14、he caulking strip is then drawn off from the release foil at an angle of approximately 135 deg at a speed of approximately 500 mm/s. The length of the specimen strip so separated from the release foil shall then be measured to an accuracy of 1 mm. The increase in length is the extensibility. 3.12 CL

15、EANING The material shall be easily removed. Test Method: Apply a strip of caulking compound with finger pressure to freshly enameled panels (prepared according to FLTM BI 103-02, Method C, using currently released light colored production paint). Condition for 1 h at room temperature. Remove materi

16、al and then wipe panels with a rag soaked with white spirit (80 - 120). ENGINEERING MATERIAL SPECIFICATION WSK-M4G329-A Copyright 2011, Ford Global Technologies, LLC Page 3 of 4 3.13 SALT SPRAY RESISTANCE The material shall not become brittle or disintegrate. Test Method: a) Apply a 300 x 20 x 2 mm

17、strip of caulking compound between two 300 x 40 mm angle body steel panels (prepared according to FLTM BZ 150-11, Method A). The steel panels are angled in 15 x 25 mm with 300 x 15 mm areas. Screw both parts together with three M 5 X 20 mm in 100 mm distance with 5 Nm using a torque wrench. b) Phosp

18、hate and E-coat the test assemblies under production conditions. c) Condition one assembly for 1 h at room temperature and expose to the max heat curing cycle per FLTM BV 150-05, for each individual region d) After 1 h at room temperature expose both assemblies for 240 h in the salt spray cabinet pe

19、r ASTM B 117. 3.14 STORAGE STABILITY 12 months min From date of receipt at Ford Motor Company when stored in sealed unopened containers out of direct sunlight at ambient temperatures between 5C and 28C. 3.15 QUALITY The material shall be of uniform quality, free from foreign materials and properties

20、 detrimental to normal production use. 3.16 ODOR Rating 3 max (FLTM BO 131-03, cured material per min cycle as in FLTM BV 150-05, for the individual region, for interior application only) 4. GENERAL INFORMATION This information given below is provided for clarification and assistance in meeting the

21、requirements of this specification. Contact for questions concerning Engineering Material Specifications. Suffix abbreviations following the specification number. 4.1 PENETRATION-GRADE (SECOND SUFFIX) A = 4 - 5 mm ENGINEERING MATERIAL SPECIFICATION WSK-M4G329-A Copyright 2011, Ford Global Technolog

22、ies, LLC Page 4 of 4 4.2 DIMENSIONS (THIRD SUFFIX) The dimensions are denoted by an additional suffix letter. It is preferred to utilize the following dimensions: A = 3 mm diameter N = 25 x 2 mm B = 5 mm diameter O = 25 x 2.5 mm C = 8 mm diameter P = 25 x 5 mm D = 12 mm diameter Q = 10 x 2 mm E = 20

23、 mm diameter R F S G = 15 x 2 mm T H = 15 x 3 mm U = unshaped J = 15 x 4 mm V K = 20 x 2 mm W = 4 mm diameter L = 20 x 4 mm X = 6 mm diameter M = 20 x 6 mm Y = 7 mm diameter Z = special shape Z is considered a special shape, the dimensions of which shall be quoted on the drawing. 4.3 COLOR SUFFIX (F

24、OURTH SUFFIX) Without additional suffix = white to gray, according to BS 2660/ 9-102 to 9-093 to 9-095. S = black, according to BS 2260/ 9-103 to 9-097 Example: S-M4G4632-AANS where AANS denotes Caulking Compound specification suffix A, penetration-grade A, 4 - 5 mm, Dimensions N, 25 x 2 mm, color black (S). 5. SUMMARY OF REVISIONS 2011 07 13 Added Odor Requirement. Editorial changes for clarification. Removed inactive spec WSK-M4G329-B3 from document.