FORD FLTM BN 128-1-2001 RESISTANCE OF VINYL COATED FABRICS TO COLD CRACKING (Replaces FLTM BN 028-01).pdf

《FORD FLTM BN 128-1-2001 RESISTANCE OF VINYL COATED FABRICS TO COLD CRACKING (Replaces FLTM BN 028-01).pdf》由会员分享，可在线阅读，更多相关《FORD FLTM BN 128-1-2001 RESISTANCE OF VINYL COATED FABRICS TO COLD CRACKING (Replaces FLTM BN 028-01).pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、FORD LABORATORY TEST METHOD BN 128-01 2001 10 31 2000 03 02 RESISTANCE OF VINYL COATED FABRICS TO COLD CRACKING Revised Editorial - no technical change A. Cockman Revised Editorial - no technical change A. Cockman Application This procedure is used to determine the resistance of vinyl coated fabrics

2、 to cold cracking Apparatus Required Specimen Block Shall consist of a foam block held to the top (100 x 100 mm) surface of a hardwood block by means of any suitable adhesive. 1. Hardwood Block (1 O0 x 1 O0 x 25 mm) This block shall have an M 4.2 x 13 mm round head wood screw driven into the geometr

3、ic center of each of the four 1 O0 x 25 mm sides of the block to such a depth that the bottom of the head stands 3 mm from the block. 2. Foam Block (1 O0 x 1 O0 x 50 mm) The foam shall be made from a high resilient polyurethane (WSB-M2D402-A3, ESB-M4D113 or equivalent) with a density of 32 - 42 kg/m

4、3, and a load deflection at 25 % compression of 12 - 17 kPa. Oven Shall be capable of maintaining 80 +/- 2 OC. The oven used shall conform to IS0 188/ASTM E 145 Type HA, normal oven,l50 +/- 50 air changes per hour, and provide a minimum oven of 2 L/1 O0 cm2 of sample size. Freezer Thermostatically c

5、ontrolled and capable of maintaining +/- 1 OC. I Date I Action I Revisions I I 19940928 I I Copynght02001, Ford Global Technologies, Inc FORD LABORATORY TEST METHOD BN 128-01 Testing Machine As shown in Figure 1 or an equivalent device that shall consist of the following parts: A frame to support th

6、e weight guiding tube, the weight release shaft and the specimen block. A vertically mounted weight guiding metal tube at least 340 mm long with an outside diameter of 75 mm and an inside diameter of 72 mm. The lower end of the tube shall be 90 mm above the specimen block seat on the frame. A 1.8 kg

7、 drop weight and chain of the design and materials shown on Figure 1. A weight release shaft mounted on the frame so that one edge of the shaft is vertical over the center of the tube. The shaft shall be equipped with a pin placed directly over the center of the tube over which the weight chain can

8、be hooked to suspend the weight and a latch so arranged that the weight can be released at any time during the test. Conditioning and Test Conditions All test values indicated herein are based on material conditioned in a controlled atmosphere of 23 +/- 2 “C and 50 +/- 5 % relative humidity for not

9、less than 24 h prior to testing and tested under the same conditions unless otherwise specified. Procedure 1. Cut five specimens 190 mm square from the sample and punch a 6 mm hole in each corner 22 mm on center from the nearest edge (refer to Figure 2). 2. Mount the specimen grain side up on the po

10、lyurethane foam side of the specimen block with the holes of the specimen placed over the screws in the sides of the block. 3. Place the testing apparatus in the freezer and allow it to remain for such time as required for the cabinet and the specimen temperature (as determined by means of thermocou

11、ples) to have reached and maintained for a minimum of one hour the temperature specified for the type of material being tested. The test apparatus and specimens remain in the freezer until testing is completed. 4. Lift the weight on the apparatus and secure on the pin of the release mechanism. 5. Po

12、sition the mounted specimen in the apparatus so the center of the specimen is directly under the center of the tube. Page 2 of 5 Copynght02001, Ford Global Technologies, Inc FORD LABORATORY TEST METHOD BN 128-01 6. Adjust the height of the weight to obtain the impact indicated in the specification.

13、a. A weight height“ at 75 mm = 1.35 J b. A weight height“ at 150 mm = 2.70 J C. A weight height“ at 230 mm = 4.05 J “ Bottom of the drop weight to top surface of test sample. 7. Release the weight and allow it to fall on the specimen. 8. Remove the specimen from the apparatus and examine for cracks

14、in the coating as per the applicable Engineering Material Specification. 9. Repeat the above procedure for specimens having been subjected to oven aging at 80 +/- 2C for 7 days. Chemicals, materials, parts, and equipment referenced in this document must be used and handled properly. Each party is re

15、sponsible for determining proper use and handling in its facilities. Page 3 of 5 Copynght02001, Ford Global Technologies, Inc FORD LABORATORY TEST METHOD BN 128-01 RESISTANCE OF VINYL COATED FABRICS TO COLD CRACKING I COLD IMPACT TESTER 75 mm 0.0. 72 mm 1.0. I 105 mm & Weight 1.8 kg 77 mm 9.5 mm Radius 69 mm rJmm 100 mm Figure 1 Page 4 of 5 Copynght02001, Ford Global Technologies, Inc FORD LABORATORY TEST METHOD BN 128-01 RESISTANCE OF VINYL COATED FABRICS TO COLD CRACKING 22 mm o o o TEST SPECIMEN Figure 2 -22mm Page 5 of 5 Copynght02001, Ford Global Technologies, Inc