FORD ESB-M4D279-A-2009 LAMINATE POLYVINYL FLOURIDE POLYVINYL CHLORIDE - METAL TO BE USED WITH FORD WSS-M99P1111-A 《聚氟乙烯-聚氯乙烯-金属层压板 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD ESB-M4D279-A-2009 LAMINATE POLYVINYL FLOURIDE POLYVINYL CHLORIDE - METAL TO BE USED WITH FORD WSS-M99P1111-A 《聚氟乙烯-聚氯乙烯-金属层压板 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M4D279-A-2009 LAMINATE POLYVINYL FLOURIDE POLYVINYL CHLORIDE - METAL TO BE USED WITH FORD WSS-M99P1111-A 《聚氟乙烯-聚氯乙烯-金属层压板 与标准FORD WSS-M99P1111-A一起使用 》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 07 28 N-STATUS No Replacement Named Y. Bankowski, NA 2005 01 28 Revised Inserted 3.0; Deleted 3.6 & 4 1968 10 28 Released AY1-290 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1 of 4 LAMINATE, POLYVINY

2、L FLOURIDE ESB-M4D279-A POLYVINYL CHLORIDE - METAL NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a composite of clear weatherable, ultraviolet absorbing, polyvinyl fluoride (PVF) film, and a pigmented polyvinyl chloride (PVC) film, laminated to a metal substrat

3、e. 2. APPLICATION This specification was released originally for material used for station wagon side rails and parts of similar construction. The polyvinyl fluoride is laminated to the polyvinyl chloride. This composite is laminated to aluminum with the polyvinyl fluoride film being the weather exp

4、osed surface. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 CONSTRUCTION 3.1.1 Substrate Aluminum, or as specified on engineering drawing. 3.1.

5、2 Polyvinyl Chloride The pigmented vinyl (PVC) film shall have the necessary flexibility and elongation characteristics to allow it to be easily formed without delamination, color change, crazing, cracking or excessive loss of embossing. 3.1.3 Polyvinyl Fluoride This material (PVF) is back printed w

6、ith light fast inks to obtain the specified color and grain pattern. Refer to para. 5.1. 3.1.4 Lamination Suitable adhesives shall be used to bond the polyvinyl fluoride and polyvinyl chloride films to each other and to the metal substrate. It is not intended to limit the type of adhesives used, and

7、 any bonding system which provides laminations meeting the requirements of this specification is acceptable. 3.2 METAL SUBSTRATE As specified on engineering drawing. ENGINEERING MATERIAL SPECIFICATIONESB-M4D279-APrinted copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of

8、4 3.3 FILM THICKNESS 3.3.1 Polyvinyl Chloride Film, min 0.0040 in (0.102 mm) 3.3.2 Polyvinyl Fluoride Film, min 0.0010 in (0.025 mm) (FLTM BI 117-01, Permascope or ASTM D 1000) 3.4 POLYVINYL CHLORIDE-POLYVINYL FLUORIDE LAMINATE, Less Substrate 3.4.1 Tensile Strength, min 4,000 psi (27.6 MPa) (ASTM D

9、 882) 3.4.2 Elongation, min 100% (ASTM D 882) 3.4.3 Tear Strength, min 150 lb/in (26 kN/m) (ASTM D 1938) of thickness 3.4.4 Adhesion, Polyvinyl Chloride to Polyvinyl Fluoride, min (1 in (25 mm) wide sample, 180 pull, 12 in (300 mm/) min) 3.4.4.1 Original as Received 2 lb/in (350 N/m) 3.4.4.2 Aged 14

10、 days at 88 +/- 1 C 2 lb/in (350 N/m) 14 days at 38 +/- 1 C 2 lb/in (350 N/m) (95 - 100% R.H.) 14 days water immersion 2 lb/in (350 N/m) (FLTM BI 104-01) Cycle Test 2 lb/in (350 N/m) (10 cycles in sequence indicated) 4 h at 88 +/- 1 C 4 h at 38 +/- 1 C, 95 - 100% R.H. 16 h at -29 C 1600 h Weatherome

11、ter 2 lb/in (350 N/m) (FLTM BO 101-01) Florida Exposure 1.5 lb/in (260 N/m) (1 year in Miami, Florida, 45 facing South.) 3.4.5 Adhesion Polyvinyl Chloride to Metal (FLTM BI 106-01, Method “B“, condition panels 24 h at 23 +/- 2 C prior to testing.) 3.4.5.1 Original as Received No evidence of removal

12、ENGINEERING MATERIAL SPECIFICATIONESB-M4D279-APrinted copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 3 of 4 3.4.5.2 Aged 14 days at 88 +/- 1 C No evidence of removal 14 days water immersion No evidence of removal (FLTM BI 104-01) 14 days at 38 +/- 1 C No evidence of remov

13、al (95 - 100% R.H.) Cycle Test No evidence of removal (10 cycles in sequence indicated) 4 h at 88 +/- 1 C 4 h at 38 +/- 1 C, 95 - 100% R.H. 16 h at -29 C 1600 h Weatherometer No evidence of removal (FLTM BO 101-01) Florida Exposure No evidence of removal (1 year in Miami, Florida, 45 facing South.)

14、3.5 FINISHED PARTS 3.5.1 Color The color and grain shall match the Ford Motor Companys styling master as specified on engineering drawing. 3.5.2 Gloss (FLTM BI 110-01, 60 glossmeter) The gloss shall match the Ford Motor Companys styling master as specified on engineering drawings. 3.5.3 Surface Qual

15、ity The color and grain film (PVC) and the protective surface film (PVF) shall be smooth and free from wrinkles, folds, orange peel, cracks, pinholes, blisters, delaminations or other defects as defined by engineering acceptance standards. 3.5.4 Abrasion Test (FLTM BN 108-02, CS-10 wheels, 1,000 g l

16、oad) After 1,000 cycles, the abraded area may show dulling, but no loss of print design as compared to the unabraded area. 3.5.5 Resistance to Elevated Temperatures There shall be no evidence of shrinkage, loss of grain, color change, or delamination of the film after 30 min exposure at 121 +/- 1 C

17、in a mechanical convection oven. ENGINEERING MATERIAL SPECIFICATIONESB-M4D279-APrinted copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 4 of 4 3.5.6 Water Resistance, min 240 h (FLTM BI 103-01) No blistering or loss of adhesion. 3.5.7 Salt Spray Resistance, min 240 h (FLTM

18、BI 103-01) No blistering or loss of adhesion. 3.5.8 Gasoline Resistance, min 15 minutes Neither the polyvinyl chloride nor polyvinyl fluoride film shall exhibit softening, dulling, color change or loss of adhesion (intercoat or to substrate) after immersion in reference fuel. Test Method: Immerse pa

19、nel to which film has been applied in 40% aromatic reference fuel (40% para-xylene, 60% iso-octane) for 15 min at 21 C min. Wipe the film with a soft cloth and examine for film damage, dulling, or color change. 3.5.9 Weathering Resistance The film shall show a minimum degree of fade, chalking or dul

20、ling. No increase in brittleness nor loss of adhesion is permitted, and the material shall be completely free from evidence of cracking, checking, blistering or peeling when exposed as follows: Florida Exposure, min 2 years (Miami area, 45 facing South) Accelerated Weathering, min 1,000 h (FLTM BO 101-01) 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 MATERIAL REFERENCE ESB-M4D239-A, “Weatherable Polyvinyl Fluoride Film - Ultraviolet Absorbing“.