DIN EN 14499-2015 Textile floor coverings - Minimum requirements for carpet underlays German version EN 14499 2015《铺地织物 地毯衬垫的最低要求 德文版本EN 14499-2015》.pdf

《DIN EN 14499-2015 Textile floor coverings - Minimum requirements for carpet underlays German version EN 14499 2015《铺地织物 地毯衬垫的最低要求 德文版本EN 14499-2015》.pdf》由会员分享，可在线阅读，更多相关《DIN EN 14499-2015 Textile floor coverings - Minimum requirements for carpet underlays German version EN 14499 2015《铺地织物 地毯衬垫的最低要求 德文版本EN 14499-2015》.pdf（12页珍藏版）》请在麦多课文档分享上搜索。

1、June 2015 Translation by DIN-Sprachendienst.English price group 8No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 59

2、.080.60!%CZe“2325566www.din.deDDIN EN 14499Textile floor coverings Minimum requirements for carpet underlays;English version EN 14499:2015,English translation of DIN EN 14499:2015-06Textile Bodenbelge Mindestanforderungen an Teppichunterlagen;Englische Fassung EN 14499:2015,Englische bersetzung von

3、DIN EN 14499:2015-06Revtements de sol textiles Exigences minimales pour les thibaudes de moquette;Version anglaise EN 14499:2015,Traduction anglaise de DIN EN 14499:2015-06SupersedesDIN EN 14499:2005-02www.beuth.deDocument comprises 12 pagesIn case of doubt, the German-language original shall be con

4、sidered authoritative.06.15 DIN EN 14499:2015-06 2 A comma is used as the decimal marker. National foreword This document (EN 14499:2015) has been prepared by Technical Committee CEN/TC 134 “Resilient, textile and laminate floor coverings” (Secretariat: NBN, Belgium). The responsible German body inv

5、olved in its preparation was the DIN-Normenausschuss Kunststoffe (DIN Standards Committee Plastics), Working Committee NA 054-04-09 AA Prfung und Verwendungsbereichs-einstufung von textilen Bodenbelgen. The European Standards referred to in this document have been published as DIN EN or DIN EN ISO S

6、tandards with the same number. For the International Standards referred to in this standard there are no national standards available unless they have been published as DIN ISO standards with the same number. Amendments This standard differs from DIN EN 14499:2005-02 as follows: a) Clause 3 “Terms a

7、nd definitions” has been revised; b) the content of the former Clause 5 “Requirements” has been extended and transferred to a new Clause 5 “Performance” and Clause 6 “Classification”; c) Annex B (normative) “Determination of work of compression of underlay” has been added; d) the standard has been e

8、ditorially revised. Previous editions DIN EN 14499: 2005-02 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 14499 April 2015 ICS 59.080.60 Supersedes EN 14499:2004English Version Textile floor coverings - Minimum requirements for carpet underlays Revtements de sol textiles - Exigences minimales

9、 pour les thibaudes de moquette Textile Bodenbelge - Mindestanforderungen an Teppichunterlagen This European Standard was approved by CEN on 28 February 2015. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard th

10、e status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, Fren

11、ch, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria,

12、 Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey

13、and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2015 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref.

14、 No. EN 14499:2015 EEN 14499:2015 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative references 4 3 Terms and definitions .4 4 Sampling .5 5 Performance .5 6 Classification 6 7 Marking .7 Annex A (normative) Method for determination of resistance to breaking and cracking .8 A.1 Principle 8 A.2 App

15、aratus .8 A.3 Test specimen 8 A.4 Procedure .8 A.5 Test report 8 Annex B (normative) Determination of work of compression of underlay 10 DIN EN 14499:2015-06 EN 14499:2015 (E) 3 Foreword This document (EN 14499:2015) has been prepared by Technical Committee CEN/TC 134 “Resilient, textile and laminat

16、e floor coverings”, the secretariat of which is held by NBN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by October 2015, and conflicting national standards shall be withdrawn at the latest by Oc

17、tober 2015. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 14499:2004. The main technical changes with re

18、spect to the previous edition are: The scope has been extended to include breaking and cracking resistance, which is in line with the requirement clauses; A number of editorial and technical inaccuracies in the text and the figures were corrected. According to the CEN-CENELEC Internal Regulations, t

19、he national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latv

20、ia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. DIN EN 14499:2015-06 EN 14499:2015 (E) 4 1 Scope This European Standard specifies minimum performance requirements for fibrous, non-fibrous

21、 and combined underlays as well as demands for the breaking and cracking resistance. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For u

22、ndated references, the latest edition of the referenced document (including any amendments) applies. EN 1471, Textile floor coverings Assessment of changes in appearance EN ISO 13934-1, Textiles Tensile properties of fabrics Part 1: Determination of maximum force and elongation at maximum force usin

23、g the strip method (ISO 13934-1) ISO 1765, Machine-made textile floor coverings Determination of thickness ISO 1957, Machine-made textile floor coverings Selection and cutting of specimens for physical tests ISO 2094, Textile floor coverings Determination of thickness loss under dynamic loading ISO

24、3415, Textile floor coverings Determination of thickness loss after brief, moderate static loading ISO 3416, Textile floor coverings Determination of thickness loss after prolonged, heavy static loading ISO 10361, Textile floor coverings Production of changes in appearance by means of Vettermann dru

25、m and hexapod tumbler tester BS 4098, Method for the determination of thickness, compression and recovery characteristics of textile floor coverings 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. 3.1 needlefelt fibrous underlay material made who

26、lly of fibres entangled or matted together by needling of a fibre batt 3.2 impregnated fibrous underlay material made of fibres consolidated by impregnation with a binding agent Note 1 to entry: A woven, nonwoven or film scrim may be included in a fibrous underlay for support during manufacture. 3.3

27、 cellular rubber underlay material formed of a vulcanized rubber foam, with or without a carrier or backing material bonded thereto 3.4 cellular plastics underlay material formed of a polymeric foam, e.g. polyurethane, with or without a carrier or backing material bonded thereto DIN EN 14499:2015-06

28、 EN 14499:2015 (E) 5 3.5 rubber crumb underlay material formed of crumb vulcanized rubber with or without a carrier or backing material bonded thereto 3.6 combined underlay material composed of one or more layers of any fibrous underlay combined with one or more layers of any non-fibrous (rubber or

29、plastics) underlay 3.7 initial thickness thickness measured under a pressure of 2 kPa 3.8 compression change in thickness of the underlay when the pressure is increased from 2 kPa to 100 kPa (see Annex B) 4 Sampling Sampling shall be carried out in accordance with ISO 1957. A full-width sample 1 m i

30、n length in the machine production direction shall be taken. For non-fibrous underlays, a minimum period of 3 days shall be allowed between manufacture and testing. 5 Performance All underlays shall conform to the minimum performance requirements specified in Table 1. Table 1 Minimum requirements Ch

31、aracteristic Requirement Test Method Breaking Strength (maximum force) 30 N in each direction EN ISO 13934-1 aElongation 15% for applied force of 30 N EN ISO 13934-1 Thickness loss of static loading long term after 24 h recovery ISO 3416 Fibrous underlay Non-fibrous underlay Combined underlay 40 % 1

32、5 % 40 % Thickness loss of static loading short term after 1 h recovery ISO 3415 Fibrous underlay Non-fibrous underlay Combined underlay 40 % 15 % 40 % Thickness loss of dynamic loading ISO 2094 Fibrous underlay Non-fibrous underlay Combined underlay 40 % 15 % 20 % Thickness 4,0 mm ISO 1765 b DIN EN

33、 14499:2015-06 EN 14499:2015 (E) 6 Characteristic Requirement Test Method Thickness deviation a) mean from nominal ISO 1765 Fibrous or combined underlay Non-fibrous underlay 15 % 12 % b) from max to min Fibrous or combined underlay Non-fibrous Underlay 4 mm 3mm Resistance to breaking or cracking No

34、cracks greater than 50 mm along the fold No cracks in backing Annex A Compression after dynamic loading Minimum 2 mm, maximum 8 mm ISO 2094 cand BS 4098 Work of compression after dynamic loading Minimum 50 J/m2, maximum 200 J/m2Retention of original work of compression 40 % Appearance/use No negativ

35、e effect dISO 10361 aThe requirement in EN ISO 13934-1 to include at least 20 threads in the test specimen need not be met. bThickness is measured in accordance with ISO 1765 at 10 equally spaced intervals across the full width of the underlay, using a presser foot area between 700 mm2and 1 000 mm2.

36、 cCompression and work of compression are determined in accordance with BS 4098 with following modifications: a presser foot of between 700 mm2and 1 000 mm2is used and loading of the specimen is only up to 100 kPa. Compression and work of compression are calculated between 2 kPa and 100 kPa (see Ann

37、ex B) before and after dynamic loading for 1 000 cycles in accordance with ISO 2094. Certain carpet thickness gauges may require modification and the manufacturers advice should be sought. dA carpet is tested, with and without the underlay in a Vettermann Drum for 22 000 cycles (or Hexapod Tumbler T

38、ester for 12 000 cycles) according to ISO 10361 and subsequently assessed according to EN 1471. There should not be a negative effect of the specimen tested over underlay compared to the specimen without underlay. 6 Classification All underlays shall be classified as suitable for different intended

39、use/applications in accordance with the performance levels shown in Figure 1 for work of compression after dynamic loading versus compression after dynamic loading. The designations and the descriptions of intended use/application are described in Table 2. Underlays should initially be specified for

40、 that particular application. Table 2 Designation and description of intended use/application Designation Description of intended use/application LD/U Light domestic use, not suitable for stairs GD/U General domestic use L/U Luxury use, domestic locations, where high energy absorption is desirable G

41、C/U General contract use, suitable for normal foot and wheel traffic HC/U Heavy contract use, suitable for heavy foot and wheel traffic and castor chairs DIN EN 14499:2015-06 EN 14499:2015 (E) 7 Key X-axis work of compression (in J/m) Y-axis compression (in mm) For a description of each designation,

42、 see Table 2. Figure 1 Classification of underlays (work of compression after dynamic loading, versus compression after dynamic loading, in accordance with BS 4098 7 Marking Underlays shall be provided with a label or other means giving at least the following information: a) number and date of this

43、document; b) manufacturers or suppliers identification or trade mark; c) classification of underlay. DIN EN 14499:2015-06 EN 14499:2015 (E) 8 Annex A (normative) Method for determination of resistance to breaking and cracking A.1 Principle A rectangular piece of underlay is folded at each end. One e

44、nd is placed under a weight-piece, whilst the other is folded without an added weight. After 1 h, the weight-piece is removed and each fold of the test specimen is visually assessed for signs of cracking. This test is applicable to all types of underlay except those of wholly fibrous construction. A

45、.2 Apparatus Rectangular rigid metal plate of dimensions (80 1) mm x (40 1) mm; Weight-piece, such that the combined mass of the rigid metal plate and the weight piece is (2,5 0,1) kg; Single-sided adhesive carpet tape, 50 mm wide. A.3 Test specimen The test specimen shall have dimensions of (240 5)

46、 mm x (120 5) mm. A.4 Procedure Fold the test specimen as shown in Figure A.1, so that, when folded, the edges of the test specimen meet and the backing material, if any, is innermost. Tape the edges of the test specimen together and then turn the test specimen over so that the edges where the folds

47、 meet are on the underside. Place the metal plate on the folded test specimen as shown in Figure A.2. Place the weight-piece on top of the metal plate and leave for 1 h. Remove the weight-piece and metal plate and immediately examine the folded specimen for signs of cracking and breaking. A.5 Test r

48、eport Report the number of cracks or breaks and their length and location relative to the position of the metal plate during loading. DIN EN 14499:2015-06 EN 14499:2015 (E) 9 All dimensions in millimetres Key 1 fold A 2 fold B Figure A.1 Arrangement of folds in test specimen for resistance to breaking and cracking test Key 1 fold A 2 metal plate 3 fold B Figure A.2 Location of metal plate on folded test specimen for resistance to breaking and cracking test DIN EN 1449