BS ISO 1924-3-2005 Paper and board - Determination of tensile properties - Constant rate of elongation method (100 mm min)《纸和纸板 抗张性能的测定 恒速拉伸法(100 mm min)》.pdf

《BS ISO 1924-3-2005 Paper and board - Determination of tensile properties - Constant rate of elongation method (100 mm min)《纸和纸板 抗张性能的测定 恒速拉伸法(100 mm min)》.pdf》由会员分享，可在线阅读，更多相关《BS ISO 1924-3-2005 Paper and board - Determination of tensile properties - Constant rate of elongation method (100 mm min)《纸和纸板 抗张性能的测定 恒速拉伸法(100 mm min)》.pdf（20页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD BS ISO 1924-3:2005 Paper and board Determination of tensile properties Part 3: Constant rate of elongation method (100 mm/min) ICS 85.060 BS ISO 1924-3:2005 This British Standard was published under the authority of the Standards Policy and Strategy Committee on 3 October 2005 BSI 3

2、 October 2005 ISBN 0 580 46553 5 National foreword This British Standard reproduces verbatim ISO 1924-3:2005 and implements it as the UK national standard. The UK participation in its preparation was entrusted to Technical Committee PAI/11, Methods of test for paper, board and pulps, which has the r

3、esponsibility to: aid enquirers to understand the text; present to the responsible international/European committee any enquiries on the interpretation, or proposals for change, and keep UK interests informed; monitor related international and European developments and promulgate them in the UK. A l

4、ist of organizations represented on this committee can be obtained on request to its secretary. Cross-references The British Standards which implement international publications referred to in this document may be found in the BSI Catalogue under the section entitled “International Standards Corresp

5、ondence Index”, or by using the “Search” facility of the BSI Electronic Catalogue or of British Standards Online. This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. Compliance with a British Standard does not of

6、 itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, the ISO title page, pages ii to v, a blank page, pages 1 to 10, an inside back cover and a back cover. The BSI copyright notice displayed in this document indicates when the

7、 document was last issued. Amendments issued since publication Amd. No. Date Comments Reference number ISO 1924-3:2005(E)INTERNATIONAL STANDARD ISO 1924-3 First edition 2005-07-01 Paper and board Determination of tensile properties Part 3: Constant rate of elongation method (100 mm/min) Papier et ca

8、rton Dtermination des proprits de traction Partie 3: Mthode gradient dallongement constant (100 mm/min) BS ISO 1924-3:2005ii BS ISO 1924-3:2005 iii Contents Page Foreword iv Introduction v 1 Scope . 1 2 Normative references . 1 3 Terms and definitions. 1 4 Principle . 2 5 Apparatus 2 6 Calibration a

9、nd adjustment of apparatus. 4 7 Sampling and preparation of test pieces . 4 7.1 Sampling 4 7.2 Conditioning 4 7.3 Preparation of test pieces 4 8 Procedure 4 9 Calculation and report 5 9.1 Tensile strength 5 9.2 Tensile index . 6 9.3 Strain at break . 6 9.4 Tensile energy absorption . 6 9.5 Tensile e

10、nergy absorption index. 7 9.6 Tensile stiffness 7 9.7 Tensile stiffness index . 8 9.8 Modulus of elasticity 8 10 Precision 8 10.1 Repeatability 8 10.2 Reproducibility 8 11 Test report . 9 Bibliography . 10 BS ISO 1924-3:2005 iv Foreword ISO (the International Organization for Standardization) is a w

11、orldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented

12、on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafte

13、d in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Stand

14、ard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 1924-3 was prepared b

15、y Technical Committee ISO/TC 6, Paper, board and pulps, Subcommittee SC 2, Test methods and quality specifications for paper and board. ISO 1924 consists of the following parts, under the general title Paper and board Determination of tensile properties: Part 2: Constant rate of elongation method 1)

16、 Part 3: Constant rate of elongation method (100 mm/min) Part 1: (Constant rate of loading method) was withdrawn in 2004 as it was considered obsolete. 1) In Part 2, a constant rate of elongation of 20 mm/min is used. v Introduction This part of ISO 1924 has been developed in order to specify the co

17、nditions for determining the tensile properties of paper, including tensile stiffness and tensile stiffness index, using a higher rate of elongation than specified in ISO 1924-2, which is the most commonly used part where tensile strength, stretch at break, tensile energy absorption and modulus of e

18、lasticity are measured. In ISO 1924-2, the tensile properties are measured at a constant rate of elongation of 20 mm/min at a test span of 180 mm. For the measuring of tensile stiffness in this part of ISO 1924, a higher accuracy in the recording of elongation, compared to ISO 1924-2, is also requir

19、ed. This part of ISO 1924 specifies the fastest of the two methods. In addition to the properties measured in ISO 1924-2, the tensile stiffness is also measured. The tensile properties are measured at a constant rate of elongation of 100 mm/min at a test span of 100 mm, and the elongation is recorde

20、d with a higher accuracy than the accuracy in ISO 1924-2. This part of ISO 1924 differs from existing standards for testing tensile properties in that the test span, i.e. the distance between the clamping lines, is 100 mm irrespective of the kind of sample to be tested. The rate of elongation has be

21、en increased to 100 mm/min in order to reduce the testing time, thus making it possible to test a greater number of samples within a given time period. NOTE The results of tensile tests depend on the rate of elongation applied and the test span. The rate dependence and the effect of test span may va

22、ry with paper grade and are different for tensile strength, strain at break, tensile energy absorption and tensile stiffness. In a study within SCAN-test, comparing the results achieved using ISO 1924-2 and this part, the tensile strength increased by 5 % to 15 % when the rate of elongation was incr

23、eased from 20 mm/min (at a test span length of 180 mm) to 100 mm/min (at a test span length of 100 mm). It is not possible to predict the exact relationship between the results for any particular paper whose tensile properties are determined using ISO 1924-2 and this part of ISO 1924. This relations

24、hip may only be determined by laboratory experimentation. In this part of ISO 1924, the same terminology and symbols are used as in general literature concerning physics and mechanics of materials. BS ISO 1924-3:2005blank1 Paper and board Determination of tensile properties Part 3: Constant rate of

25、elongation method (100 mm/min) 1 Scope This part of ISO 1924 specifies a method for measuring the tensile strength, strain at break, tensile energy absorption and tensile stiffness, using a testing machine operating with a constant rate of elongation (100 mm/min). This part of ISO 1924 also specifie

26、s equations for calculating the tensile index, the tensile energy absorption index, the tensile stiffness index and the modulus of elasticity. When tensile stiffness is to be determined, a greater accuracy is required in the elongation measurement than when the other tensile properties are to be det

27、ermined. If the elongation is determined with the lower accuracy, the tensile stiffness value obtained is not in accordance with this part of ISO 1924. This part of ISO 1924 is applicable to all papers and boards, including papers of high extensibility, such as creped papers and extensible sack pape

28、rs, but with the exception of low-density papers such as tissue papers and tissue products for which ISO 12625-4 2is recommended. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. Fo

29、r undated references, the latest edition of the referenced document (including any amendments) applies. ISO 186, Paper and board Sampling to determine average quality ISO 187, Paper, board and pulps Standard atmosphere for conditioning and testing and procedure for monitoring the atmosphere and cond

30、itioning of samples ISO 534, Paper and board Determination of thickness, density and specific volume ISO 536, Paper and board Determination of grammage 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. 3.1 tensile strength maximum tensile force per

31、 unit width that paper and board will withstand before breaking under the conditions defined in this standard test method 3.2 tensile index tensile strength divided by the grammage BS ISO 1924-3:20052 3.3 elongation increase in length of a test piece 3.4 strain ratio of the elongation of a test piec

32、e to the initial test length NOTE The initial test length of the test piece is the same as the initial span between the clamping lines. 3.5 strain at break strain at the maximum tensile force 3.6 tensile energy absorption amount of energy per unit surface area (test length width) of a test piece whe

33、n it is strained to the maximum tensile force 3.7 tensile energy absorption index tensile energy absorption divided by the grammage 3.8 tensile stiffness maximum slope of the curve obtained when tensile force per unit width is plotted versus strain 3.9 tensile stiffness index tensile stiffness divid

34、ed by the grammage 3.10 modulus of elasticity tensile stiffness divided by the thickness 4 Principle A test piece of given dimensions is strained to break at a constant rate of elongation using a testing machine that automatically records both the tensile force and the elongation. From the recorded

35、data, the tensile strength, the strain at break, the tensile energy absorption and the tensile stiffness are calculated. 5 Apparatus 5.1 Tensile testing machine, including means of determining the force (i.e. a load-cell), the elongation and the area between the force-elongation curve and the elonga

36、tion axis. The testing machine is designed to strain a test piece at a constant rate of elongation of 100 mm/min 10 mm/min, and to record both the tensile force and the elongation. NOTE 1 The true elongation rate is less than the rate of movement of the moving clamp due to the deflection of the load

37、-cell and the testing machine. This rate difference has, however, normally a negligible effect on the strength values. The testing machine shall have two clamps for holding the test piece. Each clamp shall be designed to grip the test piece firmly, but without damage, along a straight line across th

38、e full width of the test piece (the clamping line), and have a means of adjusting the clamping force. BS ISO 1924-3:20053 NOTE 2 The clamping line is the contact zone resulting from gripping the test piece between a cylindrical and a flat surface or between two cylindrical surfaces whose axes are pa

39、rallel. For certain grades of paper, “line contact” clamps may not be appropriate and it may be necessary to replace them with another type of gripping surface. Other types of clamps may be used, provided no slippage of, or damage to, the test piece occurs during the test. When the test piece is cla

40、mped, the clamping lines shall be parallel to each other within an angle of 1, see Figure 1. During the test, the angle between the clamping lines shall not change by more than 0,5 in the plane of the test piece. The centre-line of the test piece shall be perpendicular to the clamping lines within a

41、n angle of 1. If there is any suspicion that the test piece slips, a test with different clamping forces shall be carried out. If the clamping force influences the strain at break, this means that the test piece may be slipping in the clamp. If the strain at break is independent of the clamping forc

42、e, then no slipping in the clamps occurs. The applied tensile force shall be parallel to the test piece centre-line, in the direction of the test piece, within an angle of 1. The distance between the clamping lines (the test span) shall be 100 mm 0,5 mm. The apparatus shall have means of recording t

43、he elongation and the force as follows: Property Elongation Force Tensile strength to an accuracy of 1,0 % of the true force Strain at break to an accuracy of 0,1 mm Tensile energy absorption to an accuracy of 0,1 mm to an accuracy of 1,0 % of the true force Tensile stiffness to an accuracy of 0,01

44、mm, in the range 0 to 1 mm to an accuracy of 1,0 % of the true force The elongation shall be calculated from the change in distance between the clamps, or by the use of an extensometer. Clamping lines parallel to each other within an angle of 1 Centre-line of test piece perpendicular to clamping lin

45、e within an angle of 1 Tensile force parallel to the test piece centre-line within an angle of 1 Figure 1 Clamping line and test piece relationship NOTE 3 If the elongation is calculated from the movement of the moving clamp, the deflection of the load-cell and of the testing machine must be taken i

46、nto consideration and adjusted for. 5.2 Device for cutting test pieces to the dimensions required (see 7.3). BS ISO 1924-3:20054 6 Calibration and adjustment of apparatus The apparatus shall be calibrated according to the instructions given by the manufacturer. Ensure that the criteria stated in the

47、 Table in 5.1 are fulfilled. Position the clamps so that the test span is 100 mm 0,5 mm. Check the test span by measuring the two impressions produced by the clamps when strips of, for example, thin aluminium foil are clamped. Adjust the rate of separation of the clamps to 100 mm/min 10 mm/min. Adju

48、st the clamping force so that there is neither slipping of, nor damage to, the test piece. 7 Sampling and preparation of test pieces 7.1 Sampling If the tests are being made to evaluate a lot, the sample shall be selected in accordance with ISO 186. If the tests are made on another type of sample, m

49、ake sure that the test pieces are representative of the sample received. 7.2 Conditioning Condition the specimens of paper and board as specified in ISO 187. Keep them in the conditioning atmosphere throughout the test. This test, like other mechanical tests, is very sensitive to changes in the moisture content of the test piece. Handle the test pieces carefully, and avoid touching with a bare hand the part of the test piece to be placed