BS EN 61068-2-1997 Polyester fibre woven tapes - Methods of test《聚酯纤维机织带 第2部分 试验方法》.pdf

《BS EN 61068-2-1997 Polyester fibre woven tapes - Methods of test《聚酯纤维机织带 第2部分 试验方法》.pdf》由会员分享，可在线阅读，更多相关《BS EN 61068-2-1997 Polyester fibre woven tapes - Methods of test《聚酯纤维机织带 第2部分 试验方法》.pdf（10页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD BS EN 61068-2:1997 IEC 61068-2: 1991 Specification for Polyester fibre woven tapes Part 2: Methods of test The European Standard EN 61068-2:1997 has the status of a British Standard ICS 29.035.20BSEN61068-2:1997 This British Standard, having been prepared under the directionof the E

2、lectrotechnical Sector Board, was published underthe authority of the Standards Board and comesintoeffect on 15November1997 BSI 04-2000 ISBN 0 580 28494 8 National foreword This British Standard is the English language version of EN61068-2:1997. It is identical with IEC61068-2:1991. It supersedes BS

3、780-2:1995 which is withdrawn. The UK participation in its preparation was entrusted by Technical Committee GEL/15, Insulating materials, to Subcommittee GEL/15/3, Material specifications, which has the responsibility to: aid enquirers to understand the text; present to the responsible international

4、/European committee any enquiries on the interpretation, or proposals for change, and keep the UK interests informed; monitor related international and European developments and promulgate them in the UK. A list of organizations represented on this subcommittee can be obtained on request to its secr

5、etary. From 1 January 1997, all IEC publications have the number60000added to the old number. For instance, IEC27-1 has been renumbered as IEC60027-1. For a period of time during the change over from one numbering system to the other, publications may contain identifiers from both systems. Cross-ref

6、erences Attention is drawn to the fact that CEN and CENELEC Standards normally include an annex which lists normative references to international publications with their corresponding European publications. The British Standards which implement these international or European publications may be fou

7、nd in the BSI Standards Catalogue under the section entitled “International Standards Correspondence Index”, or by using the “Find” facility of the BSI Standards Electronic Catalogue. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standard

8、s are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pagesi andii, theEN title page, pages2 to4 and a back cover. This standard has

9、 been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover. Amendments issued since publication Amd. No. Date CommentsBSEN61068-2:1997 BSI 04-2000 i Contents Page National foreword Inside front cover Foreword 2

10、 Text of EN 61068-2 3ii blankEUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 61068-2 August 1997 ICS 29.035.20 Descriptors: Electrical insulating materials, solid electrical insulating materials, tapes, weaving, polyester fibres, tests, determination, thickness, width, retractibility, tensile s

11、trength, testing conditions English version Specification for polyester fibre woven tapes Part2:Methods of test (IEC 61068-2:1991) Spcification pour rubans tisss en fibresdepolyester Partie 2: Mthodes dessai (CEI 61068-2:1991) Bestimmung fr gewebte Bnder aus Polyesterfilamenten Teil2: Prfverfahren (

12、IEC 61068-2:1991) This European Standard was approved by CENELEC on 1997-07-01. CENELEC members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists an

13、d bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CENELEC member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the respon

14、sibility of a CENELEC member into its own language and notified to the Central Secretariat has the same status as the official versions. CENELEC members are the national electrotechnical committees of Austria, Belgium, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, N

15、etherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom. CENELEC European Committee for Electrotechnical Standardization Comit Europen de Normalisation Electrotechnique Europisches Komitee fr Elektrotechnische Normung Central Secretariat: rue de Stassart 35, B-1050 Brussels 1997

16、CENELEC All rights of exploitation in any form and by any means reserved worldwide for CENELEC members. Ref. No. EN 61068-2:1997 EEN61068-2:1997 BSI 04-2000 2 Foreword The text of the International Standard IEC61068-2:1991, prepared by SC15C, Specifications, of IECTC15, Insulating materials, was sub

17、mitted to the formal vote and was approved by CENELEC as EN61068-2 on1997-07-01 without any modification. The following dates were fixed: Endorsement notice The text of the International Standard IEC61068-2:1991 was approved by CENELEC as a European Standard without any modification. Contents Page F

18、oreword 2 1 Scope 3 2 Normative references 3 3 Tests 3 latest date by which the EN has to be implemented at national level by publication of an identical national standard or by endorsement (dop) 1998-06-01 latest date by which the national standards conflicting with the EN have to be withdrawn (dow

19、) 1998-06-01EN61068-2:1997 BSI 04-2000 3 1 Scope This part of IEC1068 specifies requirements for tapes woven on shuttleless looms for continuous filament polyester fibres. This part gives methods of test to demonstrate compliance with the general requirements of Part1 and the specific requirements o

20、f Part3 of the standard. Other parts of IEC 1068 are: Part 1: Definitions, designation and general requirements; Part 3: Specifications for individual materials. 2 Normative references The following standards contain provisions which, through reference in this text, constitute provisions of this par

21、t. At the time of publication, the editions indicated were valid. All standards are subject to revision, and parties to agreements based on this part are encouraged to investigate the possibility of applying the most recent editions of the standards listed below. Members of IEC and ISO maintain regi

22、sters of currently valid International Standards. ISO 5081:1977, Textiles Woven fabrics Determination of breaking strength and elongation (Strip method). ISO 5084:1977, Textiles Determination of thickness of woven and knitted fabrics (other than textile floor coverings). 3 Tests 3.1 Determination of

23、 number of warp ends The ends shall be counted across the full width ofthe tape under ordinary room conditions anddivided by the nominal width to obtain the ends/10mm of nominal width. 3.2 Determination of number of picks The picks shall be counted over not less than20mm length of tape under ordinar

24、y room conditions and the average value shall be calculated from not less than three individual tests made at three different places along the tape. NOTEIn most constructions, two threads equal one pick (seethe definition of “pick” in Part1). 3.3 Determination of thickness The thickness shall be det

25、ermined generally by the method given in ISO5084, modified as below: 3.3.1 Test pieces Take five rolls of tape selected at random. 3.3.2 Conditioning Condition the rolls in an atmosphere of relative humidity within the range 45% to75% and with a temperature between15 C and35 C and then measure the t

26、hickness under these conditions. 3.3.3 Test apparatus Use test apparatus as described in ISO5084. Pressure to be selected from ISO5084 to be the nearest to (100 10)kPa. 3.3.4 Test procedure Clean the surface of the reference plate and of the presser foot. Adjust the instrument to provide a pressure

27、of100kPa to200kPa. In all cases of dispute, a deadweight tester shall be used and the pressure shall be100kPa. Separate the parallel plates and place an uncreased part of the test piece without tension in contact with the reference plate. Reduce the distance between the reference plate and the press

28、er foot until contact is made gently with the tape and note the reading of the gauge as soon as the movement of the pointer has ceased and the reading is easily visible. On each of the five selected rolls make four measurements at random, one at each of the selvedges and two between the selvedges. 3

29、.3.5 Results For the five rolls there will be ten measurements at the selvedges and ten between the selvedges. The central values of the two sets of ten measurements are the thickness of the tape at the selvedges and between the selvedges, respectively. 3.4 Determination of width 3.4.1 Test pieces T

30、ake five rolls selected at random. 3.4.2 Test conditions Make the test under standard ambient conditions. 3.4.3 Procedure Unroll the tape and lay it flat on a smooth surface. Apply no more tension to the tape than is necessary to make it lie straight and flat. Measure the width of the tape by means

31、of a steel rule graduated in millimetres. Make two measurements at random on each of the five selected rolls. 3.4.4 Results Take the central value of the ten measurements at the width of the tape.EN61068-2:1997 4 BSI 04-2000 3.5 Determination of shrinkage 3.5.1 Test pieces From each of the five roll

32、s selected at random cut a test piece sufficiently long to be able to mark on it a distance of500mm. 3.5.2 Procedure Lay the test piece flat on a smooth surface. Apply no more tension to the tape than is necessary to make it lie straight and flat. Measure the marked length and width (when the shrink

33、age on width is required) to within 0,5mm. Make two measurements of each of the required dimensions on each of the five test pieces. Place the test pieces in an oven which is maintainedat155 5 C. The test pieces shall beloosely coiled to allow free circulation of air. After60min 10min at the155 C ex

34、posure, remove the test pieces and cool for 1h at15 C to35 C. Repeat the earlier measurements of length and width. 3.5.3 Results Take the central value of the ten measurements before and after heating and express the result as a percentage,i.e.: Report also the central value of the shrinkage in widt

35、h in millimetres. 3.6 Shrinkage under load (Under consideration.) 3.7 Determination of tensile strength 3.7.1 General The tensile strength shall be determined generally by the method given in ISO5081, modified as below: 3.7.2 Test pieces Take five test pieces of sufficient length to allow an unstret

36、ched length of200mm between the jaws of the testing machine. 3.7.3 Test temperature Make the test temperature between15 C and35 C at standard IEC conditions. 3.7.4 Test apparatus A constant rate of load (CRL) machine, a constant rate of traverse (CRT) machine or a constant rate of specimen extension

37、 (CRE) machine may be used. 3.7.5 Procedure Apply the load so that the time from the commencement of application of the load to the moment at which the specified minimum load is reached is 30s 5s and continue until the test piece breaks. If the test piece breaks unevenly, either in or at a jaw of th

38、e testing machine, discard the result and make a further test using another test piece. 3.7.6 Results Express the tensile strength as the central value of the five determinations in newtons per millimetre width and record the type of machine used. 3.8 Force developed when heated at150 C Test method

39、for determining the maximum force exerted by a shrinkable tape when heated to150 C 3.8.1 Test specimen Approximately150mm length of the tape. 3.8.2 Test apparatus Tensile tester with oven. 3.8.3 Procedure Fix the test piece in the tester in suitable jaws100mm apart. The jaws shall be in an oven. App

40、ly a load of nominally5% of the estimated breaking load. Raise the temperature in the oven from room temperature to155 C 5 C in10to15min. Record the maximum force exerted by the test piece. 3.8.4 Results Take the central value of three measurements. 100 length or width after heating length or width

41、before heating - 100 blankBS EN 61068-2:1997 IEC61068-2: 1991 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandardsInstitution BSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on standards in Europe and at the international level. It is

42、incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if a

43、nyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel:02089969000. Fax:02089967400. BSI offers members an individual updating service called PLUS w

44、hich ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel:02089969001. Fax:02089967001. In response to orders for international standards, i

45、t is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international standards through its Library and its Technical Help to Export

46、ers Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel:02089967111. Fax:02089967048. Subscribing members of BSI are kept up to date with standards developments and receive substantial discou

47、nts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:02089967002. Fax:02089967001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the publications of the international standardization

48、 bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior written permission from BSI. This does not preclude the

49、free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel:02089967070.