《BS 3338-11-1961 Methods for the sampling and analysis of tin and tin alloys - Method for the determination of tin in solders (nickel coil reduction method)《锡及锡合金取样及分析方法 第11部分 焊料中锡含.pdf》由会员分享，可在线阅读，更多相关《BS 3338-11-1961 Methods for the sampling and analysis of tin and tin alloys - Method for the determination of tin in solders (nickel coil reduction method)《锡及锡合金取样及分析方法 第11部分 焊料中锡含.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD BS3338-11: 1961 Method for The determination of tin in solders (Nickel coil reduction method)BS3338-11:1961 This British Standard, having been approved by the Non-ferrous Metals Industry Standards Committee and endorsed by the Chairman oftheEngineering Divisional Council, was publis

2、hed undertheauthority of the GeneralCouncil on 17February1961 BSI12-1999 The following BSI references relate to the work on this standard: Committee references NFE/27, NFE/27/1 Draft for comment AA(NFE)1391 ISBN 0 580 03117 9 Co-operating organizations The Non-ferrous Metals Industry Standards Commi

3、ttee, under whose supervision this British Standard was prepared, consists of representatives from the following Government departments and scientific and industrial organizations: Admiralty* Institution of Mining and Metallurgy Aluminium Development Association Institution of Structural Engineers A

4、luminium Industry Council Lead Development Association Association of Bronze and Brass Founders Lead Sheet and Pipe Manufacturers Association of Consulting Engineers Federation (Incorporated) Light Metal Founders Association British Bronze and Brass Ingot Manufacturers London Metal Exchange* Associa

5、tion Magnesium Industry Council British Electrical and Allied Manufacturers Ministry of Aviation* Association* National Brassfoundry Association British Non-ferrous Metals Federation Non-ferrous Metal Stockists British Non-ferrous Metals Research Post Office* Association* Royal Institute of British

6、Architects Cable Makers Association* Society of British Aircraft Constructors Copper Development Association Society of Motor Manufacturers and Crown Agents for Oversea Governments and Traders Ltd.* Administrations Tin Research Institute* High Commission of India War Office* High Conductivity Copper

7、 Association Zinc Development Association Institute of British Foundrymen Individual manufacturers Institute of Metals Institution of Mechanical Engineers (Automobile Division) The Government departments and scientific and industrial organizations marked with an asterisk in the above list, together

8、with the following, were directly represented on the committee entrusted with the preparation of this British Standard: British Railways, The British Transport Solder Makers Association Commission Tinplate Conference(1925) British Tin Box Manufacturers Federation Tin Producers Association Electronic

9、 Engineering Association White Metal Bearing Manufacturers Gas Council Individual manufacturers Institution of Gas Engineers London Transport Executive, The British Transport Commission Amendments issued since publication Amd. No. Date CommentsBS3338-11:1961 BSI 12-1999 i Contents Page Co-operating

10、organizations Inside front cover Foreword ii Introduction 1 Apparatus 1 Solutions required 1 Sampling 1 Procedure 1 Standardization 1 Figure 1 Assembly for reduction of tin 2BS3338-11:1961 ii BSI 12-1999 Foreword This standard makes reference to the following BritishStandards: BS219, Soft solders. B

11、S3338, Methods for the sampling and analysis of tin and tin alloys Part12:Sampling of solders. This method for the determination of tin in solders, is the eleventh of a series of methods which will form a complete British Standard under the collective title “Methods for the sampling and analysis of

12、tin and tin alloys”, each method being published as a separate part. The preparation of this series of methods has been authorized by the Non-ferrous Metals Industry Standards Committee as part of a general programme for the standardization of methods for the sampling and analysis of non-ferrous met

13、als. Other methods in the series are as follows: Part1: Sampling of ingot tin; Part2: Determination of tin in ingot tin; Part3: Determination of antimony in ingot tin; Part4: Determination of copper in ingot tin and tin-lead solders; Part5: Determination of lead in ingot tin and tin-antimony solders

14、; Part6: Determination of copper in high purity ingot tin; Part7: Determination of silver in solders; Part8: Determination of bismuth in ingot tin, tin-lead solders and white metal bearing alloys; Part9: Determination of arsenic in ingot tin, tin-lead solders and white metal bearing alloys; Part10:

15、Determination of iron in ingot tin, tin-lead solders and white metal bearing alloys; Part12: Sampling of solders. The complete British Standard methods will be found suitable for the grades of metals covered by BS3252, “Ingot tin”, BS219, “Soft solders”, and BS3332,“White metal bearing alloy ingots”

16、. In the methods for determining impurities, sample weights and aliquots have been chosen to cover the range of impurity content usually found in commercial tin ingots, solders and white metal bearing alloy ingots. For amounts of impurity outside this range, sample weights of aliquots should be adju

17、sted accordingly. The methods have been found to give reliable and reproducible results, and, while in some instances they may appear to be lengthy, it should be realized that they are put forward as “referee” methods to be used in cases of dispute. A British Standard does not purport to include all

18、 the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pagesi andii

19、, pages1 and2 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover.BS3338-11:1961 BSI 12-1999 1 Introduction a) Principle. Tin is determined volumetrically with potassiu

20、m iodate after reduction with nickel. b) Range. For tin contents exceeding1percent. c) Reproducibility. 0.1percent of tin present. Apparatus a) Any volumetric glassware used shall be of Class A accuracy as defined in the appropriate British Standards, or where no British Standard exists, as describe

21、d in the National Physical Laboratory Publication “Volumetric Tests on Volumetric Glassware”. b) A suitable form of apparatus is illustrated in Figure 1. The nickel coil should be etched before use by boiling in hydrochloric acid(50per cent v/v) containing20per cent of sodium chloride. Wash well in

22、cold water and leave immersed in cold water until required. Solutions required All reagents shall be of the highest purity obtainable and distilled water shall be used throughout. Solutions shall be freshly prepared and, where necessary filtered. Standard potassium iodate/iodide (1mlN 0.01g of tin).

23、 Dissolve6.05g of potassium iodate (previously dried at105110 C) in400ml of water containing1g of sodium hydroxide. Add30g of potassium iodide and dilute to1litre in a graduated flask. Standard potassium iodate/iodide (1mlN 2mg of tin). Dilute200ml of the above solution to1litre in a graduated flask

24、. Bromine-hydrochloric acid. Add20ml of bromine to2litres of hydrochloric acid (sp. gr.1.161.18). Hydrochloric acid (50per cent v/v). Dilute50ml of hydrochloric acid (sp. gr.1.161.18) to100ml. Sodium hydrogen carbonate. Saturated solution. Starch. Make a suspension of0.5g of starch in a10ml of water

25、. Add to90ml of boiling water. Cool and dilute to100ml. Prepare freshly each day. Sampling Recommended methods of obtaining a suitable sample for the analytical procedure given below are described in BS3338-12, “Sampling of solders”. Procedure Weigh accurately triplicate portions of1.00g of sample a

26、nd transfer each to a500ml beaker. To each add100ml of bromine-hydrochloric acid and warm gently until dissolved, ensuring that bromine is always in excess, if necessary by the addition of a further25ml of bromine-hydrochloric acid. Add a few pieces of porous pot and boil to expel excess bromine (No

27、te1), then add100ml of water, and2g of iron powder. Heat gently until the reaction ceases. Filter through a small paper-pulp pad into a500ml flask, washing three times with hydrochloric acid(50per cent). Transfer the residue and the pad to the original beaker, and boil for5minutes with20ml of bromin

28、e-hydrochloric acid. Add2g of iron powder, and when the reaction ceases, filter through a small pad of paper-pulp into the first filtrate. Wash four times with hydrochloric acid(50per cent). Fill the reservoir of the Contat-Gckel trap with sodium hydrogen carbonate solution (saturated), introduce th

29、e nickel coil and Contat-Gckel assembly, close the flask and boil gently for30minutes. Cool slightly and close the outlet tube with a rubber cap. Cool in running water, remove the nickel coil and wash with water into the solution. Add5ml of starch solution, and titrate quickly, with a minimum of sti

30、rring, with standard potassium iodate/iodide solution(1mlN 0.01g of tin) (Note2) to a permanent blue colour. Standardization Weigh accurately triplicate portions of0.4g of pure tin foil, and transfer to500ml flasks. Add100ml of bromine-hydrochloric acid and heat gently until dissolved, ensuring that

31、 bromine is always in excess. Add a few pieces of porous pot and boil to expel the excess bromine (see Note1). Add50ml of hydrochloric acid (sp. gr.1.161.18),100ml of hot water, and2g of iron powder. Boil gently until the iron is dissolved. Introduce the nickel coil and Contat-Gckel assembly. Close

32、the flask and boil gently for30minutes. Cool in running water and titrate as described in the procedure. NOTE 1The solution should not be boiled longer than is necessary. The use of a boiling rod will facilitate rapid removal of bromine. NOTE 2For silver bearing solders, e.g.BS219, “Soft solders”,1S

33、 and5S, standard potassium iodate/iodide(1mlN 2mg of tin) should be used.BS3338-11:1961 2 BSI 12-1999 Figure 1 Assembly for reduction of tinblankBS3338-11: 1961 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandardsInstitution BSI is the independent national body responsible for preparing Brit

34、ishStandards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments or editions. It is the

35、 constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover

36、. Tel:02089969000. Fax:02089967400. BSI offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Custom

37、er Services. Tel:02089969001. Fax:02089967001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise requested. Information on standards BSI provides a wide range of information on

38、national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel:02089967111. Fax:02089967048. Subscr

39、ibing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:02089967002. Fax:02089967001. Copyright Copyright subsists in all BSI publications

40、. BSI also holds the copyright, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocop

41、ying, recording or otherwise without prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel:02089967070.