ASTM C91-2005 Standard Specification for Masonry Cement《砌筑水泥标准规范》.pdf

《ASTM C91-2005 Standard Specification for Masonry Cement《砌筑水泥标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM C91-2005 Standard Specification for Masonry Cement《砌筑水泥标准规范》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C 91 05Standard Specification forMasonry Cement1This standard is issued under the fixed designation C 91; the number immediately following the designation indicates the year of originaladoption or, in the case of revision, the year of last revision. A number in parentheses indicates the

2、 year of last reapproval. A superscriptepsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This specification covers three types of masonry cementfor use where mortar for masonry

3、is required.1.2 The values stated in SI units are to be regarded as thestandard. Values in SI units shall be obtained by measurementin SI units or by appropriate conversion of measurements madein other units, using the Rules for Conversion and Roundinggiven in IEEE/ASTM SI 10.1.3 The text of this st

4、andard refers to notes and footnoteswhich provide explanatory material. These notes and footnotes(excluding those in tables and figures) shall not be consideredas requirements of the standard.1.4 The following safety hazards caveat pertains only toSections 16 and 17 of this specification. This stand

5、ard does notpurport to address all of the safety concerns, if any, associatedwith its use. It is the responsibility of the user of this standardto establish appropriate safety and health practices anddetermine the applicability of regulatory limitations prior touse. (WarningFresh hydraulic cementiti

6、ous mixtures arecaustic and may cause chemical burns to skin and tissue uponprolonged exposure.)22. Referenced Documents2.1 ASTM Standards:3C 109/C 109M Test Method for Compressive Strength ofHydraulic Cement Mortars (Using 2-in. or 50-mm CubeSpecimens)C 151 Test Method for Autoclave Expansion of Hy

7、draulicCementC 183 Practice for Sampling and the Amount of Testing ofHydraulic CementC 185 Test Method for Air Content of Hydraulic CementMortarC 187 Test Method for Normal Consistency of HydraulicCementC 188 Test Method for Density of Hydraulic CementC 219 Terminology Relating to Hydraulic CementC

8、266 Test Method for Time of Setting of Hydraulic Ce-ment Paste by Gillmore NeedlesC 270 Specification for Mortar for Unit MasonryC 305 Practice for Mechanical Mixing of Hydraulic CementPastes and Mortars of Plastic ConsistencyC 430 Test Method for Fineness of Hydraulic Cement bythe 45-m (No. 325) Si

9、eveC511 Specification for Mixing Rooms, Moist Cabinets,Moist Rooms, and Water Storage Tanks Used in theTesting of Hydraulic Cements and ConcretesC 778 Specification for Standard SandC 1506 Test Method for Water Retention of HydraulicCement-Based Mortars and PlastersIEEE/ASTM SI 10 Standard for Use o

10、f the InternationalSystem of Units (SI): The Modern Metric System3. Terminology3.1 Definitions:3.1.1 masonry cementa hydraulic cement, primarily usedin masonry and plastering construction, consisting of a mixtureof portland or blended hydraulic cement and plasticizingmaterials (such as limestone, hy

11、drated or hydraulic lime)together with other materials introduced to enhance one ormore properties such as setting time, workability, water reten-tion, and durability.3.1.2 Other terms used in this specification are defined inTerminology C 219.4. Classification4.1 Type NFor use in preparation of Spe

12、cification C 270Type N mortar without further addition of cements or hydratedlime, and for use in preparation of Specification C 270 Type S1This specification is under the jurisdiction of ASTM Committee C01 onCement and is the direct responsibility of Subcommittee C01.11 on MasonryCement.Current edi

13、tion approved September 15, 2005. Published October 2005. Origi-nally approved in 1932. Last previous edition approved in 2003 as C 91 03a.2Annual Book of ASTM Standards, Vol 04.01. See the section on SafetyPrecautions in the Manual of Cement Testing.3For referenced ASTM standards, visit the ASTM we

14、bsite, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United St

15、ates.or Type M mortar when cement is added in accordance with therequirements of C 270.4.2 Type SFor use in preparation of Specification C 270Type S mortar without further addition of cements or hydratedlime.4.3 Type MFor use in preparation of Specification C 270Type M mortar without further additio

16、n of cements or hydratedlime.5. Physical Properties5.1 Masonry cement shall conform to the applicable re-quirements prescribed in Table 1 for its classification.6. Sampling6.1 The masonry cement shall be sampled in accordancewith Practice C 183.7. Temperature and Humidity7.1 The temperature and rela

17、tive humidity of the air in thevicinity of the mixing slab and dry materials, molds, baseplates, and mixing bowl shall conform to the requirements ofTest Method C 109/C 109M.7.2 The moist cabinet or moist room shall conform to therequirements of Specification C511.8. Fineness8.1 Determine the residu

18、e on the 45-m (No. 325) sieve inaccordance with Test Method C 430.9. Normal Consistency9.1 Determine normal consistency by the Vicat apparatus inaccordance with Test Method C 187.10. Autoclave Expansion10.1 Determine autoclave expansion in accordance withTest Method C 151. After molding, store the b

19、ars in the moistcabinet or room for 48 h 6 30 min before removal from themolds for measurement and testing in the autoclave. Calculatethe difference in length of the test specimen before and afterautoclaving to the nearest 0.01 % of the effective gauge lengthand report as the autoclave expansion of

20、the masonry cement.11. Time of Setting11.1 Determine the time of setting by the Gillmore needlemethod in accordance with Test Method C 266.12. Density12.1 Determine the density of the masonry cement inaccordance with Test Method C 188, using kerosine as theliquid. Use the density so determined in th

21、e calculation of theair content of the mortars.13. Blended Sand13.1 The sand shall be a blend of equal parts by weight ofgraded standard sand and standard 2030 sand conforming toSpecification C 778.14. Preparation of Mortar14.1 Proportions for MortarMortar for air entrainment,compressive strength, a

22、nd water retention tests shall be pro-portioned to contain 1620 g of sand and a mass of cement, ingrams, in accordance with Table 2. The sand shall consist of810 g of graded standard sand and 810 g of 2030 standardsand (Note 1). The quantity of water, measured in millilitresshall be such as to produ

23、ce a flow of 110 6 5 as determined byTest Method C 109/C 109M.NOTE 1Historically, field-mixed mortar has been proportioned byvolume measured in increments or fractions of ft3. The comparable wholeSI-unit volume to 1 ft3is 28 L. The specified mortar proportionsapproximate the 1:3 nominal proportions

24、by volume, commonly specifiedfor construction, on the basis of the following assumed mass and volumerelationships:The mass of dry sand in 28 L of loose damp sand is 36 kg.28 L Type N masonry cement has a mass of 32 kg.28 L Type S masonry cement has a mass of 34 kg.28 L Type M masonry cement has a ma

25、ss of 36 kg.For example, the amount of cement needed to provide a 1:3volume proportion of cement to sand using a Type N masonrycement is as follows:A 5 1620 3 C/B! 5 1620 3 32/108! 5 480 (1)TABLE 1 Physical RequirementsMasonry Cement Type N S MFineness, residue on a 45-m (No. 325) sieve, max, % 24 2

26、4 24Autoclave expansion, max, % 1.0 1.0 1.0Time of setting, Gillmore method:Initial set, minutes, not less than 120 90 90Initial set, minutes, not more than 1000 1000 1000Compressive strength (average of 3 cubes):The compressive strength of mortar cubes, composed of 1part cement and 3 parts blended

27、sand (half graded standardsand, and half standard 2030 sand) by volume, prepared andtested in accordance with this specification shall be equal to orhigher than the values specified for the ages indicated below:7 days, MPa (psi) 3.4 (500) 9.0 (1300) 12.4 (1800)28 days, MPa (psi) 6.2 (900) 14.5 (2100

28、) 20.0 (2900)Air content of mortar, prepared and tested in accordance withrequirements of this specification:Min, volume % 88 8Max, volume % 21 19 19Water retention value, min, % of original flow 70 70 70C91052where:A = number of grams of cement to be used in the mortarwith 1620 g of sand,B =33 36 =

29、 108 kg, the mass of dry sand in 84 (or 3 328) L of loose damp sand, andC = mass of Type N masonry cement per 28 L.14.2 Mixing of MortarsMix the mortar in accordancewith Practice C 305.15. Air Entrainment15.1 ProcedureIf the mortar has the correct flow, use aseparate portion of the mortar for the de

30、termination of en-trained air. Determine the mass of 400 mL of mortar inaccordance with Test Method C 185.15.2 CalculationCalculate the air content of the mortarand report it to the nearest 1 % as follows:D 5 W11 W21 Vw!/W1/S1! 1 W2/S2! 1 Vw# (2)A 5 100 2 Wm/4D!where:D = density of air-free mortar,

31、g/cm3,W1= mass of cement, g,W2= mass of sand, g,Vw= millilitres-grams of water used,S1= density of cement, g/cm3S2= density of standard sand, 2.65 g/cm3,A = volume percent of entrained air, andWm= mass of 400 mL of mortar, g.16. Compressive Strength16.1 Test Specimens:16.1.1 MoldingImmediately after

32、 determining the flowand mass of 400 mL of mortar, return all of the mortar to themixing bowl and remix for 15 s at the medium speed. Thenmold the test specimens in accordance with Test MethodC 109/C 109M, except that the elapsed time for mixing mortar,determining flow, determining air entrainment,

33、and starting themolding of cubes shall be within 8 min.16.1.2 StorageImmediately after molding, store all testspecimens in the molds on plane plates in a moist cabinet ormoist room for 48 to 52 h in such a manner that the uppersurfaces shall be exposed to the moist air. Then remove thecubes from the

34、 molds, and place them in the moist cabinet ormoist room for 5 days in such a manner as to allow freecirculation of air around at least five faces of the specimens. Atthe age of 7 days, immerse the cubes for the 28-day tests insaturated lime water in storage tanks of noncorrodible materi-als.16.2 Pr

35、ocedure:16.2.1 Test the cube specimens immediately after theirremoval from the moist cabinet or moist room for 7-dayspecimens, and immediately after their removal from storagewater for all other specimens. If more than one specimen at atime is removed from the moist cabinet or moist room for7-day te

36、sts, cover these cubes with a damp cloth until the timeof testing.16.2.2 The remainder of the testing procedure shall conformto Test Method C 109/C 109M.17. Water Retention17.1 Water retention shall be determined in accordance withthe procedures in Test Method C 1506.18. Storage18.1 The cement shall

37、 be stored in such a manner as topermit easy access for the proper inspection and identificationof each shipment, and in a suitable weathertight building thatwill protect the cement from dampness and minimize ware-house set.19. Inspection19.1 Every facility shall be provided to the purchaser for the

38、necessary inspection and sampling.19.2 All packages shall be in good condition at the time ofinspection.20. Rejection20.1 At the option of the purchaser, the cement shall berejected if it fails to meet any of the requirements of thisspecification.20.2 At the option of the purchaser, packages more th

39、an 2 %below the mass marked thereon shall be rejected. At the optionof the purchaser, the entire shipment represented shall berejected if the average mass of packages in any shipment asshown by weighing fifty packages taken at random is less thanthat marked on the packages.20.3 At the option of the

40、purchaser, cement remaining instorage prior to shipment for a period greater than six monthsafter testing shall be retested and, at the option of the purchasershall be rejected if it fails to meet any of the requirements ofthis specification.21. Manufacturers Certification21.1 Upon request of the pu

41、rchaser in the contract or order,a manufacturers report shall be furnished at the time ofshipment stating the results of the tests made on samples of thematerial taken during production or transfer and certifying thatthe applicable requirements of this specification have been met.22. Packaging and P

42、ackage Marking22.1 When masonry cement is delivered in packages, thebrand, name of the manufacturer, type of masonry cement, andnet mass of the package in kilograms (see Note 2) shall beindicated plainly thereon. Similar information shall be pro-vided in the shipping documents accompanying the shipm

43、entof masonry cement in bulk.NOTE 2To facilitate the change to SI units, a standard SI package sizeof 32 kg for Type N, 34 kg for Type S, and 36 kg for Type M will provideconvenient mass increments reasonably similar to the traditional 70-, 75-,and 80-lb packages.TABLE 2 Cement in Laboratory Batch o

44、f MortarMasonry Cement Type Mass of Cement, gN 480S 510M 540C9105323. Keywords23.1 masonry; masonry cement; mortarASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly adv

45、ised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either

46、 reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. I

47、f you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).C91054