1、Designation: C 467 97 (Reapproved 2008)Standard Classification ofMullite Refractories1This standard is issued under the fixed designation C 467; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in

2、 parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This classification covers refractory products consistingpredominantly of mullite (3 Al2O32 SiO2) crystals that areformed by either converting a

3、ny of the sillimanite group ofminerals, or synthesizing from appropriate materials in a meltor sinter process.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are

4、 not considered standard.2. Referenced Documents2.1 ASTM Standards:2C16 Test Method for Load Testing Refractory Shapes atHigh TemperaturesNOTE 1Chemical analysis of refractory products are determined by acombination of x-ray fluorscence (XRF) and inductively coupled plazma(ICP) using standard refere

5、nce materials (SRM), including various typesof minerals and refractory materials which are available from the NationalInstitute of Standards and Technology and other appropriate sources.C 832 Test Method of Measuring Thermal Expansion andCreep of Refractories Under Load3. Significance and Use3.1 The

6、 mullite content of an alumina-silica refractorymaterial has an important influence on volume stability, loadbearing properties, and its satisfactory use in refractory appli-cations. This classification is considered useful for purchasespecifications and quality control.4. Properties4.1 The refracto

7、ry products falling within the scope of thisclassification are classified by chemical and physical tests tomeet the following requirements:Alumina content, %Impurities,Amax, %Deformation,Bmax, %56 to 7955AImpurities refer to metal oxides other than those of aluminum and silicon.BWhen tested in accor

8、dance with 6.1.2.5. Test Specimens5.1 Testing for compliance with this classification shall beperformed on 9 by 412 by 212-in. (228 by 114 by 64-mm)rectangular brick as made, or on specimens of this size cutfrom larger shapes, utilizing existing plane surfaces as much aspossible.6. Test Methods6.1 T

9、he properties enumerated in this classification shall bedetermined in accordance with the following ASTM meth-ods:6.1.1 Alumina ContentXRF and ICP.6.1.2 Load TestSchedule 6 of Table 1 in Test MethodC16.6.1.3 Thermal Expansion and CreepMethod C 832.7. Retests7.1 Because of possible variables that may

10、 result fromsampling or an unsatisfactory reproducibility of tests bydifferent laboratories, the material may be resampled andretested at the request of either the manufacturer or thepurchaser. This could apply where the first test results may notconform to the requirements prescribed in this classi

11、fication.Therefore, the final results to be used shall be the average of atleast two series of tests, each of which has been obtained byfollowing the specified testing procedures in detail.8. Keywords8.1 alumino-silicate; classification; mullite; refractories1This classification is under the jurisdi

12、ction of the ASTM Committee C08 onRefractories and is the direct responsibility of Subcommittee C08.92 on The JosephE. Kopanda Subcommittee for Editorial, Terminology, and Classification.Current edition approved Aug. 1, 2008. Published September 2008. Originallyapproved in 1961. Last previous editio

13、n approved in 2002 as C 467 97 (2002).2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM Interna

14、tional, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determinatio

15、n of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdra

16、wn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your c

17、omments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).C 467 97 (2008)2