1、Designation: B967/B967M 11Standard Specification forCopper-Zinc-Tin-Bismuth Alloy Rod, Bar and Wire1This standard is issued under the fixed designation B967/B967M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of last re

2、vision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification establishes the requirements forcopper-zinc-tin-bismuth alloy rod, bar and wire of alloy UNSNos. C49255,

3、C49260, C49300, C49340, C49350, and C49360intended for use in plumbing applications and drinking watersystems.1.2 Typically, rod and bar product made to this specificationis furnished as straight lengths. Wire (H04) 0.08-0.3 in. 2-8mm inclusive is furnished in coil form, and H50 shapes.1.3 UnitsThe

4、values stated in either SI units or inch-pound units are to be regarded separately as standard. Thevalues stated in each system may not be exact equivalents;therefore, each system shall be used independently of the other.Combining values from the two systems may result in non-conformance with the st

5、andard.1.4 The following safety hazard caveat pertains only to thetest method(s) described in this specification.1.4.1 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate

6、safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2B249/B249M Specification for General Requirements forWrought Copper and Copper-Alloy Rod, Bar, Shapes andForgingsB250/B250M Specification for General Require

7、ments forWrought Copper Alloy WireB846 Terminology for Copper and Copper AlloysE8/E8M Test Methods for Tension Testing of MetallicMaterialsE54 Test Methods for ChemicalAnalysis of Special Brassesand Bronzes3E62 Test Methods for Chemical Analysis of Copper andCopper Alloys (Photometric Methods)3E92 T

8、est Method for Vickers Hardness of Metallic Materi-als3E478 Test Methods for ChemicalAnalysis of CopperAlloys2.2 Other Standards:ISO No. 3110 (AA) Copper Alloys Determination of Alu-minum as an Alloying Element Volumetric4(Interna-tional Organization of Standardization)JIS H 1068:2005 Method for Det

9、ermination of Bismuth inCopper and Copper Alloys5(Japanese Industrial Stan-dards)3. General Requirements3.1 The following sections of Specifications B249/B249Mor B250/B250M constitute a part of this specification:3.1.1 Terminology,3.1.2 Materials and Manufacture,3.1.3 Sampling,3.1.4 Number of Tests

10、and Retests,3.1.5 Specimen Preparation,3.1.6 Certification,3.1.7 Test Reports.3.2 In addition, when a section with a title identical to thatreferenced in X.1, above, appears in this specification, itcontains additional requirements which supplement those ap-pearing in Specifications B249/B249M or B2

11、50/B250M.4. Terminology4.1 For definitions of terms related to copper and copperalloys, refer to Terminology B846.5. Ordering Information5.1 Include the following information when placing ordersfor product under this specification, as applicable:5.1.1 ASTM designation and year of issue,1This specifi

12、cation is under the jurisdiction ofASTM Committee B05 on Copperand Copper Alloys and is the direct responsibility of Subcommittee B05.02 on Rod,Bar, Wire, Shapes and Forgings.Current edition approved April 1, 2011. Published May 2011. Originallyapproved in 2009. Last previous edition approved in 201

13、0 as B967/B967M 10a.DOI: 10.1520/B0967_B0967M-11.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Withdrawn.

14、The last approved version of this historical standard is referencedon www.astm.org.4Available from International Organization of Standards, http:/www.ISO.org/ISO/store.htm5Japanese Industrial Standard, available through http:/www.JIS.or.jp/1*A Summary of Changes section appears at the end of this st

15、andard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.1.2 Copper Alloy UNS designation,5.1.3 Temper (Section 8),5.1.4 Dimensions, diameter, or distance between parallelsurfaces,5.1.5 How furnished: straight lengths or coils,5.1.6 Q

16、uantity: total weight or total length or number ofpieces of each size,5.1.7 If product is purchased for agencies of the U.S.Government (see the Supplementary Requirements section ofSpecifications B249/B249M or B250/B250M for additionalrequirements, if specified).5.1.8 ShapesWhen product is shapes, t

17、he dimensionaltolerances shall be as agreed upon between the manufacturer orsupplier and purchaser and shall be specified (see 11.1.7).5.2 The following options are available and should bespecified at the time of placing of the order when required:5.2.1 Heat identification or traceability details,5.

18、2.2 Certification, and5.2.3 Mill Test Report.6. Materials and Manufacture6.1 Materials:6.1.1 The material of manufacture shall be a form of CopperAlloy UNS Nos. C49255, C49260, C49300, C49340, C49350,and C49360 of such purity and soundness as to be suitable forprocessing into the products prescribed

19、 herein.6.1.2 In the event heat identification or traceability isrequired, the purchaser shall specify the details desired.NOTE 1Due to the discontinuous nature of the processing of castingsinto wrought products, it is not always practical to identify a specificcasting analysis with a specific quant

20、ity of finished material.6.2 Manufacture:6.2.1 The product shall be manufactured by such hot work-ing, cold working, and annealing processes as to produce auniform wrought structure in the finished product.6.2.2 The product shall be hot or cold worked to the finishedsize, and subsequently annealed w

21、hen required, to meet thetemper properties specified.7. Chemical Composition7.1 The material shall conform to the chemical compositionrequirements in Table 1 for the copper alloy UNS Numbersspecified in the ordering information.7.2 These composition limits do not preclude the presenceof other elemen

22、ts. By agreement between the manufacturer andpurchaser, limits may be established and analysis required forunnamed elements.7.3 For alloys in which zinc is listed as “remainder,” eithercopper or zinc may be taken as the difference between the sumof results of all elements determined and 100 %. When

23、allelements in Table 1 are determined, the sum of results shall be99.5 % min.7.4 For alloys in which copper is listed as “remainder”,copper is the difference between the sum of results of allelements determined and 100%. When all elements in Table 1are determined, the sum of results shall be 99.5% m

24、in.8. Temper8.1 The standard tempers for products described in thisspecification are given in Table 2.8.1.1 Hot Extruded and Annealed: O308.1.2 Annealed: 061 for rod and bar8.1.3 As Hot Extruded: M30 for rod and bar8.1.4 Cold drawn half hard temper: H02 for rod and bar8.1.5 Cold drawn hard temper: H

25、04 for wire8.1.6 Hot extruded and drawn: H50 for Shapes in all sizes.9. Mechanical Property Requirements9.1 Tensile Strength Requirements:9.1.1 Product furnished under this specification shall con-form to the tensile requirements prescribed in Table 2, whentested in accordance with Test Methods E8/E

26、8M.9.1.2 Acceptance or rejection shall be based upon the tensileproperties prescribed in Table 2.10. Other Requirements10.1 Purchases for the U.S. Government Product pur-chased for agencies of the U.S. Government shall conform tothe additional requirements prescribed in the SupplementaryRequirements

27、 section of Specifications B249/B249M or B250/B250M.11. Dimensions, Mass, and Permissible Variation11.1 The dimensions and tolerances for product describedby this specification shall be as specified in SpecificationB249/B249M or B250/B250M for wire as noted, with particu-lar reference to the followi

28、ng Tables and related paragraphs:11.1.1 Diameter or Distance Between Parallel Surfaces11.1.1.1 Rod, Cold-Drawn, H02, H04 Table 1, B249/B249M.11.1.1.2 Hot Extruded and Annealed, O30 Table 4, B249/B249M.11.1.1.3 Rod and Bar, As Extruded, O61 Table 4, B249/B249M.TABLE 1 Chemical CompositionCopper Alloy

29、UNS No.Copper LeadmaxIronmaxTin Zinc PhosphorusmaxAluminummaxAntimonymaxBismuth ManganesemaxNickelmax, incl CoSeleniummaxSiliconmaxC49255 58.0- 60.0A0.01 0.10 0.50 max Rem 0.10 . . . . . . 1.7-2.9 . . . 0.10-0.30 0.02-0.07 0.10C49300 58.062.0 0.01 0.10 1.01.8 Rem 0.20 0.50 0.50 .502.0 0.03 1.5 0.20

30、0.10C49260B58.063.0 0.09 0.50 0.50 Rem 0.050.15 . . . . . . 0.501.8 . . . . . . . . . 0.10C49340B60.0-63.0 0.09 0.12 0.50-1.5 Rem 0.050.15 . . . . . . 0.502.0 . . . . . . . . . 0.10C49350 61.063.0 0.09 0.12 1.53.0 Rem 0.040.15 . . . 0.02-0.10 0.502.5 . . . . . . . . . 0.30C49360 Rem 0.09 1.0-2.0 19.

31、0-22.0 0.10 . . . . . . 0.50-1.5 . . . . . . . . . 2.0-3.5AIncludes cadmium 0.01 max.BIncludes Cadmium 0.001 max.B967/B967M 11211.1.1.4 Wire Cold Drawn Hard, H04 Table 1, B250/B250M.11.1.2 Thickness Tolerance for Rectangular and Square Bar,Table 8, B249/B249M.11.1.3 Width Tolerance for Rectangular B

32、ar, Table 10,B249/B249M.11.1.4 Length: Table 13, Full Length Tolerances for Rod,Bar, and Table 15, Schedule of Lengths with Ends for Rod andBar, B249/B249M.11.1.5 Straightness: Table 16, Straightness Tolerances forRod, Bar, For General Use section, B249/B249M.11.1.6 Edge Contour: Refer to Edge Conto

33、urs section inB249/B249M or B250/B250M.11.1.7 Shapes: The dimensional tolerances for shapes shallbe agreed upon between the manufacturer or supplier and thepurchaser and shall be specified in the order or purchasecontract.12. Workmanship, Finish, and Appearance12.1 The product shall be free of defec

34、ts, but blemishes ofa nature that do not interfere with the intended application areacceptable.13. Sampling13.1 Refer to sampling section in Specifications B249/B249M or B250/B250M.14. Number of Tests and Retests14.1 Test:14.1.1 Chemical AnalysisChemical composition shall bedetermined in accordance

35、with the element mean of the resultsfrom at least two replicate analyses of the sample(s).TABLE 2 Mechanical Property Requirements Round and Hexagonal Rod, BarAand WireTemper Diameter or DistanceBetween Parallel Surfaces,in. (mm)Tensile Strength,ksi (MPa)minYield Strength0.2 offsetksi (MPa)minElonga

36、tionin 4 3 dia.%minVickers Hardness5000 gmsTyp.Code NameCopper Alloys UNS No. C49260, C49300, and C49340M30 As Hot Extruded 1 to 4.375 incl. (25 110) incl. 50 (345) 20 (140) 18O61 Annealed .3 1 incl. (8 25) incl.1 2.5 incl. (26 65) incl.50 (345)48 (330)20 (140)16 (110)15158080H0212 Hard .3 1 incl. (

37、8 25) incl.1 2.5 incl. (26 65) incl.55 (380)50 (345)25 (170)20 (140)15158080H04 Hard Wire .08 .3 incl. (2 8) incl. 67 (460) 45 (310) 3H50 Hot extruded and Drawn All Sizes 50 (345) 20 (140)Copper Alloy UNS No C49350M30 As Hot extruded 1 4.375 incl. (25-110 incl.) 50 (345) 20 (140) 15O61 Annealed .3 2

38、.5 incl. (8-25 incl.) 48 (330) 16 (110) 12AFor rectangular bar, the Distance Between Parallel Surfaces refers to thickness.TABLE 3 Mechanical Property Requirements UNS Alloy No. C49255 RodTemper Diameteror DistanceBetween ParallelSurfaces, in.(mm)TensileStrength, ksi(MPa) minYield Strength0.2 offset

39、 ksi(MPa) minElongation in4 3 dia. % minVickers Hardness5000 gms Typ.Code NameM30 As HotExtruded1 to 4.375 incl.(25 110) incl.46 (315) . . . 15 . . .O30 Hot Extrudedand Annealed0.33incl.(8 75) incl.49 (335) . . . . . . 80TABLE 4 Mechanical Property Requirements UNS Alloy No. C49360 Round and Hexagon

40、al Rod and BarATemper Diameteror DistanceBetweenParallel Surfaces,in. (mm)Tensile Strength,ksi (MPa) minYield Strength0.2 offsetksi (MPa) minElongation in4 3 dia. % minVickers Hardness5000 gms Typ.Code NameM30 As Hot Extruded 1 to 3.15 incl.(26 80) incl.50 (345) 22 (150) 15 . . .O61 Annealed 0.41inc

41、l.(10 25) incl.50 (345) 22 (150) 12 . . .AFor rectangular bar, the distance between parallel surfaces refers to thickness.B967/B967M 11314.2 Retest:14.2.1 When requested by the manufacturer or supplier, aretest shall be permitted when results of tests obtained by thepurchaser fail to conform to the

42、requirements of the productspecification.14.2.2 The retest shall be as directed in the product speci-fication for the initial test, except the number of test specimensshall be twice that normally required for the specified test.14.2.3 All test specimens shall conform to the productspecification requ

43、irement(s) in retest. Failure to conform shallbe cause for rejection.15. Test Methods15.1 Chemical Analyses:15.1.1 In cases of disagreement, the resolution of thedispute shall be subject to agreement between the manufactureror supplier and purchaser. The following methods may be used:Element MethodC

44、opper E478Aluminum ISO No. 3110 (AA)Phosphorus E62Nickel E478Tin E478Zinc E478Bismuth JIS H 1068: 2005Lead E478Iron E478Silicon E5415.1.2 Test method(s) to be followed for the determinationof element(s) resulting from contractual or purchase orderagreement shall be as agreed upon between the manufac

45、turer orsupplier and purchaser.15.2 Other Tests:15.2.1 The product furnished shall conform to specifiedrequirements when subjected to test in accordance with thefollowing table:Test MethodTensile Properties E8/E8MHardness, Vickers E9215.2.2 Yield StrengthThe yield strength shall be deter-mined by th

46、e 0.2 % offset method of Test Methods E8/E8M.When test results are obtained from both full-size and ma-chined specimens, and they differ, the test results from thefull-size specimens shall prevail.16. Significance of Numerical Limits16.1 For the purpose of determining compliance with thespecified li

47、mits for requirements of the properties listed in thefollowing table and for dimensional tolerances, an observedvalue or a calculated value shall be rounded as indicated inaccordance with the rounding method of Practice E92:Property Rounded Unitfor Observed orCalculated ValueChemical CompositionHard

48、nessNearest unit in the last right-handsignificant digit used inexpressing the limiting valueTensile StrengthYield StrengthNearest ksi 5 MPaElongation Nearest 1 %17. Inspection17.1 The manufacturer, or supplier, shall inspect and maketests necessary to verify the furnished product conforms tospecifi

49、cation requirements.17.2 Source inspection of the product by the purchaser maybe agreed upon between the manufacturer, or supplier, and thepurchaser as part of the purchase order. In such case, the natureof the facilities needed to satisfy the inspector, representing thepurchaser, that the product is being furnished in accordancewith the specification shall be included in the agreement. Alltesting and inspection shall be conducted so as not to interfereunnecessarily with the operation of the works.17.3 When mutually