ASTM B582-2007(2013) Standard Specification for Nickel-Chromium-Iron-Molybdenum-Copper Alloy Plate Sheet and Strip《镍铬铁钼铜合金板材、薄板材及带材的标准规格》.pdf

《ASTM B582-2007(2013) Standard Specification for Nickel-Chromium-Iron-Molybdenum-Copper Alloy Plate Sheet and Strip《镍铬铁钼铜合金板材、薄板材及带材的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM B582-2007(2013) Standard Specification for Nickel-Chromium-Iron-Molybdenum-Copper Alloy Plate Sheet and Strip《镍铬铁钼铜合金板材、薄板材及带材的标准规格》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B582 07 (Reapproved 2013)Standard Specification forNickel-Chromium-Iron-Molybdenum-Copper Alloy Plate,Sheet, and Strip1This standard is issued under the fixed designation B582; the number immediately following the designation indicates the year oforiginal adoption or, in the case of rev

2、ision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 The specification2covers plate, sheet, and strip ofnickel-chromium-iron-molybdenum-copper alloys (U

3、NSN06007, N06975, N06985, and N06030)* as shown in Table 1,for use in general corrosive service.1.2 The following products are covered under this specifi-cation:1.2.1 Sheet and StripHot or cold rolled, solution annealed,and descaled unless solution anneal is performed in an atmo-sphere yielding a br

4、ight finish.1.2.2 PlateHot or cold rolled, solution annealed, anddescaled.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.4 This st

5、andard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided b

6、y the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3B906 Specification for General Requirements for Flat-Rolled Nickel and Nickel Alloys Plate, Sheet, and Strip3. Ter

7、minology3.1 Definitions of Terms Specific to This Standard:3.1.1 cold-rolled plate, nmaterial316 to38 in. (4.76 to9.52 mm), inclusive, in thickness.3.1.2 hot-rolled plate, nmaterial316 in. (4.76 mm) andover in thickness.3.1.3 plate, nmaterial316 in. (4.76 mm) and over inthickness.3.1.4 sheet and str

8、ip, nmaterial under316 in. (4.76 mm) inthickness.4. General Requirements4.1 Materials furnished to this specification shall conform tothe applicable requirements of Specification B906 unlessotherwise provided herein.5. Ordering Information5.1 It is the responsibility of the purchaser to specify allr

9、equirements that are necessary for material ordered under thisspecification. Examples of such requirements include, but arenot limited to, the following:5.1.1 AlloyTable 1,5.1.2 DimensionsThickness (in decimals of an inch),width, and length (inch or fractions of an inch),5.1.3 Optional Requirement,

10、PlateHow the plate is to becut (see 8.1 and Specification B906, Table A2.3),5.1.4 CertificationState if certification or a report of testresults is required (Specification B906),5.1.5 Purchaser InspectionState which tests or inspec-tions are to be witnessed (Specification B906), and5.1.6 Samples for

11、 Product (Check) AnalysisState whethersamples should be furnished (Section 6).6. Chemical Composition6.1 Heat AnalysisThe material shall conform to the com-position limits specified in Table 1.6.2 Product (Check) AnalysisIf a product (check) analysisis made by the purchaser, the material shall confo

12、rm to therequirements specified in Table 1 subject to the permissibletolerances in Specification B906.1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloy

13、s.Current edition approved Feb. 1, 2013. Published February 2013. Originallyapproved in 1973. Last previous edition approved in 2007 as B582 07. DOI:10.1520/B0582-07R13.2For ASME Boiler and Pressure Vessel Code applications, see related Specifi-cation SB-582 in Section II of that Code.* New designat

14、ion established in accordance with ASTM E527 and SAE J1086,Practice for Numbering Metals and Alloys (UNS).3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standa

15、rds Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States17. Mechanical Properties and Other Requirements7.1 Tensile PropertiesThe material shall conform to themechanical property requirements prescr

16、ibed in Table 2.7.2 HardnessThe hardness values given in Table 2 areinformative only.8. Edges8.1 Plates shall have sheared or cut machined, abrasive cut,powder cut, or inert arc cut edges, as specified.8.2 Sheet and strip shall have sheared or slit edges.9. Permissible Variations in Dimensions9.1 We

17、ightFor calculation of mass or weight, the follow-ing densities shall be used:DensityAlloy lb/in.3g/cm3N06007 0.300 8.31N06975 0.295 8.17N06985 0.300 8.31N06030 0.297 8.229.2 Thicknesses:9.2.1 PlateThe permissible variations in thickness of plateshall be as prescribed in Specification B906, Table A2

18、.1.9.2.2 Sheet and StripThe permissible variations in thick-ness of sheet and strip shall be as prescribed in SpecificationB906, Table A2.2. The thickness shall be measured with themicrometer spindle38 in. (9.52 mm) or more from any edge formaterial 1 in. (25.4 mm) or over in width and at any place

19、onmaterial under 1 in. (25.4 mm) in width.9.3 Width:TABLE 1 Chemical RequirementsElementComposition Limits, %Alloy N06007 Alloy N06975 Alloy N06985 Alloy N06030Nickel remainderA47.0 to 52.0 remainderAremainderAChromium 21.0 to 23.5 23.0 to 26.0 21.0 to 23.5 28.0 to 31.5Iron 18.0 to 21.0 remainderA18

20、.0 to 21.0 13.0 to 17.0Molybdenum 5.5 to 7.5 5.0 to 7.0 6.0 to 8.0 4.0 to 6.0Copper 1.5 to 2.5 0.70 to 1.20 1.5 to 2.5 1.0 to 2.4Manganese 1.0 to 2.0 1.0 max 1.0 max 1.5 maxCobalt, max 2.5 . 5.0 5.0Carbon, max 0.05 0.03 0.015 0.03Tungsten 1.0 max . 1.5 max 1.5 to 4.0Silicon, max 1.0 1.0 1.0 0.8Phosp

21、horus, max 0.04 0.03 0.04 0.04Sulfur, max 0.03 0.03 0.03 0.02Columbium + tantalum 1.75 to 2.50 . 0.50 max 0.30 to 1.50Titanium . 0.701.50 . .AThe composition of the remainder element shall be determined arithmetically by difference.TABLE 2 Mechanical Property RequirementsAlloy Thickness, in. (mm)Ten

22、sile Strengthmin, psi (MPa)Yield Strength(0.2 % Offset),min, psi (MPa)Elongation in2 in. or 50.8 mmor 4DAmin, %Rockwell Hardness,BmaxAnnealed PlateN06007316 to34 (4.76 to 19.05), incl 90 000 (621) 35 000 (241) 35 100 HRBOver34 to 212 (19.05 to 63.5), incl 85 000 (586) 30 000 (207) 30 100 HRBN0697531

23、6 to 212 (4.76 to 63.5), incl 85 000 (586) 32 000 (221) 40 100 HRBN06985316 to34 (4.76 to 19.05), incl 90 000 (621) 35 000 (241) 45 100 HRBOver34 to 212 (19.05 to 63.5), incl 85 000 (586) 30 000 (207) 35 100 HRBN06030 . 85 000 (586) 35 000 (241) 30 .Annealed SheetN06985 Over 0.020 (0.51) 90 000 (621

24、) 35 000 (241) 45 100 HRBAnnealed Sheet and StripN06007N06975Over 0.020 (0.51)Over 0.020 (0.51)90 000 (621)85 000 (586)35 000 (241)32 000 (221)4040100 HRB100 HRBN06030 Over 0.020 (0.51) 85 000 (586) 35 000 (241) 30 .AD refers to the diameter of the tension specimen.BHardness values are shown for inf

25、ormation purposes only and are not to be used as a basis for rejection or acceptance. For approximate hardness conversions, seeSpecification B906.B582 07 (2013)29.3.1 PlateThe permissible variations in width of rectan-gular plates shall be as prescribed in Specification B906,Table A2.3.9.3.2 Sheet a

26、nd StripThe permissible variations in widthfor sheet and strip shall be as prescribed in Specification B906,Table A2.4.9.4 Length:9.4.1 PlatePermissible variations in the length of rectan-gular plate shall be as prescribed in Specification B906,Table A2.3.9.4.2 Sheet and StripSheet and strip may be

27、ordered to cutlengths, in which case a variation of18 in. (3.18 mm) over thespecified length shall be permitted, with a 0 minus tolerance.9.5 StraightnessThe edgewise curvature (depth of cord)of sheet, strip, and plate shall not exceed 0.05 in./ft (4.2mm/m).9.6 Squareness (Sheet)For sheets of all th

28、ickness andwidths of 6 in. (152.4 mm) or more, the angle between adjacentsides shall be 90 6 0.15 (116 in. in 24 in. or 2.6 mm/m).9.7 FlatnessPlate, sheet, and strip shall be commerciallyflat.10. Product Marking and Package Marking10.1 Each plate, sheet, or strip shall be marked on one facewith the

29、specification number, heat number, manufacturersidentification, and size. The markings shall have no deleteriouseffect on the material or its performance and shall be suffi-ciently stable to withstand normal handling.10.2 Each bundle or shipping container shall be markedwith the name of the material

30、; this specification number; alloy;the size; gross, tare, and net weight; consignor and consigneeaddress; contract or order number; and such other informationas may be defined in the contract or order.11. Keywords11.1 plate; sheet; strip; N06007; N60975; N06985; N06030APPENDIX(Nonmandatory Informati

31、on)X1. HEAT TREATMENTX1.1 Proper heat treatment during or subsequent to fabrica-tion is necessary for optimum performance, and the manufac-turer shall be consulted for details.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item menti

32、onedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee a

33、nd must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting

34、of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Bo

35、x C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).B582 07 (2013)3