ASTM B162-1999(2009) Standard Specification for Nickel Plate Sheet and Strip《镍板、薄板及带材的标准规范》.pdf

《ASTM B162-1999(2009) Standard Specification for Nickel Plate Sheet and Strip《镍板、薄板及带材的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM B162-1999(2009) Standard Specification for Nickel Plate Sheet and Strip《镍板、薄板及带材的标准规范》.pdf（9页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B 162 99 (Reapproved 2009)Standard Specification forNickel Plate, Sheet, and Strip1This standard is issued under the fixed designation B 162; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A

2、 number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This specification2covers rolled nickel (UNS N02200)a

3、nd low-carbon nickel (UNS N02201)* plate, sheet, and strip.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not

4、 purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufactu

5、rer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3B 160 Specification for Nickel Rod and BarB 880 Specification for General Requirements for ChemicalCheck Analysis Limits for Nick

6、el, Nickel Alloys andCobalt AlloysE8 Test Methods for Tension Testing of Metallic MaterialsE10 Test Method for Brinell Hardness of Metallic Materi-alsE18 Test Methods for Rockwell Hardness of MetallicMaterialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with Specifi

7、cationsE39 Test Methods for Chemical Analysis of Nickel4E112 Test Methods for Determining Average Grain SizeE 140 Hardness Conversion Tables for Metals RelationshipAmong Brinell Hardness, Vickers Hardness, RockwellHardness, Superficial Hardness, Knoop Hardness, andScleroscope HardnessF 155 Test Meth

8、od for Temper of Strip and Sheet Metals forElectronic Devices (Spring-Back Method)43. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 The terms given in Table 1 shall apply.4. Ordering Information4.1 It is the responsibility of the purchaser to specify allrequirements that are ne

9、cessary for the safe and satisfactoryperformance of material ordered under this specification.Examples of such requirements include, but are not limited to,the following:4.1.1 AlloyName and UNS number. (See Table 2.)4.1.2 ASTM designation, including year of issue.4.1.3 Condition (See 6.1, 6.2, and A

10、ppendix X1.)4.1.4 Finish (See Appendix X1.)4.1.5 DimensionsThickness, width, and length.4.1.6 Quantity.4.1.7 Optional Requirements:4.1.7.1 Sheet and Strip Whether to be furnished in coil, incut straight lengths, or in random straight lengths.4.1.7.2 StripWhether to be furnished with commercial slite

11、dge, square edge, or round edge.4.1.7.3 PlateWhether to be furnished specially flattened(see 7.7.2); also how plate is to be cut (see 7.2.1 and 7.3.2).4.1.8 Fabrication DetailsNot mandatory but helpful tothe manufacturer.4.1.8.1 Welding or BrazingProcess to be employed.4.1.8.2 PlateWhether material

12、is to be hot-formed.4.1.9 CertificationState if certification or a report of testresults is required (see Section 15).1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt

13、 and Their Alloys.Current edition approved Oct. 1, 2009. Published October 2009. Originallyapproved in 1941. Last previous edition approved in 2005 as B 162 99 (2005)1.2For ASME Boiler and Pressure Vessel Code applications, see related Specifi-cation SB-162 in Section II of that Code.* New designati

14、on established in accordance with ASTM E 527 and SAE J1086,Practice for Numbering Metals and Alloys (UNS).3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standa

15、rds Document Summary page onthe ASTM website.4Withdrawn.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.1.10 Samples for Product (Check) AnalysisWhethersamples for product (check) analysis should be furnished (see5.2).4.1.11 Purcha

16、ser InspectionIf the purchaser wishes towitness tests or inspection of material at the place of manu-facture, the purchase order must so state indicating which testsor inspections are to be witnessed (see Section 13).5. Chemical Compositions5.1 The material shall conform to the requirements as toche

17、mical composition prescribed in Table 2.5.2 If a product (check) analysis is performed by thepurchaser, the material shall be done per Specification B 880and the material shall conform to the product (check) analysisvariations defined in Table 1 of Specification B 880.6. Mechanical and Other Require

18、ments6.1 Mechanical PropertiesThe material shall conform tothe requirements for mechanical properties prescribed in Table3.6.2 Deep-Drawing and Spinning Quality Sheet and StripThe material shall conform to the requirements for grain sizeand hardness properties prescribed in Table 4.6.2.1 The mechani

19、cal properties of Table 3 do not apply todeep-drawing and spinning quality sheet and strip.7. Dimensions and Permissible Variations7.1 Thickness and Weight:7.1.1 PlateFor plate up to 2 in. (50.8 mm), inclusive, inthickness, the permissible variation under the specified thick-ness and permissible exc

20、ess in overweight shall not exceed theamounts prescribed in Table 5.7.1.1.1 For use with Table 5, plate shall be assumed toweigh 0.321 lb/in.3(8.89 g/cm3).7.1.2 PlateFor plate over 2 in. (50.8 mm) in thickness, thepermissible variations over the specified thickness shall notexceed the amounts prescr

21、ibed in Table 6.7.1.3 Sheet and StripThe permissible variations in thick-ness of sheet and strip shall be as prescribed in Table 7. Thethickness of strip and sheet shall be measured with themicrometer spindle38 in. (9.5 mm) or more from either edgefor material 1 in. (25.4 mm) or over in width and at

22、 any placeon the strip under 1 in. in width.7.2 Width and Diameter:7.2.1 PlateThe permissible variations in width of rectan-gular plates and diameter of circular plates shall be asprescribed in Table 8 and Table 9.7.2.2 Sheet and StripThe permissible variations in widthfor sheet and strip shall be a

23、s prescribed in Table 10.7.3 Length:7.3.1 Sheet and strip of all sizes may be ordered to cutlengths, in which case a variation of18 in. (3.2 mm) over thespecified length shall be permitted.7.3.2 Permissible variations in length of rectangular plateshall be as prescribed in Table 11.7.4 Straightness:

24、7.4.1 The edgewise curvature (depth of chord) of flat sheet,strip, and plate shall not exceed 0.05 in. multiplied by thelength in feet (0.04 mm multiplied by the length in centime-tres).7.4.2 Straightness for coiled material is subject to agree-ment between the manufacturer and the purchaser.7.5 Edg

25、es:7.5.1 When finished edges of strip are specified in thecontract or order, the following descriptions shall apply:7.5.1.1 Square-edge strip shall be supplied with finishededges, with sharp, square corners, and without bevel orrounding.7.5.1.2 Round-edge strip shall be supplied with finishededges,

26、semicircular in form, and the diameter of the circleforming the edge being equal to the strip thickness.7.5.1.3 When no description of any required form of stripedge is given, it shall be understood that edges such as thoseresulting from slitting or shearing will be acceptable.7.5.1.4 Sheet shall ha

27、ve sheared or slit edges.7.5.1.5 Plate shall have sheared or cut (machined, abrasive-cut, powder-cut, or inert-arc-cut) edges, as specified.7.6 Squareness (Sheet)For sheets of all thicknesses, theangle between adjacent sides shall be 90 6 0.15 (116 in. in 24in.) (1.6 mm in 610 mm).7.7 Flatness:7.7.1

28、 There shall be no flatness requirements for “deepdrawing quality,” “spinning quality,” or “as rolled,” sheet andstrip (see X1.4).TABLE 1 Product DescriptionProduct Thickness, in. (mm)Width, in.(mm)Hot-rolled plateA 316 and over (Table 5 andTable 6)(Table 8)BHot-rolled sheetA0.018 to 0.250 (0.46 to

29、6.4),incl (Table 7)(Table 10)Cold-rolled sheetC0.018 to 0.250 (0.46 to 6.4),incl (Table 7)(Table 10)Cold-rolled stripC0.005 to 0.250 (0.13 to 6.4),incl (Table 7)(Table 10)AMaterial316 to14 in. (4.8 to 6.4 mm), incl, in thickness may be furnished assheet or plate provided the material meets the speci

30、fication requirements for thecondition ordered.BHot-rolled plate, in widths 10 in. (254 mm) and under, may be furnished ashot-finished rectangles with sheared or cut edges in accordance with SpecificationB 160, provided the mechanical property requirements of this specification aremet.CMaterial unde

31、r 48 in. (1219 mm) in width may be furnished as sheet or stripprovided the material meets the specification requirements for the conditionordered.TABLE 2 Chemical RequirementsElementComposition,%Nickel(UNSN02200)Low-CarbonNickel(UNSN02201)Nickel,Amin 99.0 99.0Copper, max 0.25 0.25Iron, max 0.40 0.40

32、Manganese, max 0.35 0.35Carbon, max 0.15 0.02Silicon, max 0.35 0.35Sulfur, max 0.01 0.01AElement shall be determined arithmetically by difference.Corrected editorially.B 162 99 (2009)27.7.2 Standard flatness tolerances for plate shall conform tothe requirements prescribed in Table 12. “Specially fla

33、ttened”plate, when so specified, shall have permissible variations inflatness as agreed upon between the manufacturer and thepurchaser.8. Workmanship, Finish, and Appearance8.1 The material shall be uniform in quality and temper,smooth, commercially straight or flat, and free of injuriousimperfectio

34、ns.TABLE 3 Mechanical Properties for Plate, Sheet, and Strip (All Thicknesses and Sizes Unless Otherwise Indicated)Condition (Temper)Tensile Strength, min, psi(MPa)YieldAStrength (0.2 %offset), min, psi (MPa)Elongation in 2in.or50mm,or 4D,min,%Rockwell Hardness(B Scale)B,CNickel (UNS N02200) Hot-Rol

35、led PlateAnnealedAs-rolledD,E55 000 (380)55 000 (380)15 000 (100)20 000 (135)4030.Nickel (UNS N02200) Hot-Rolled SheetAnnealed 55 000 (380) 15 000 (100) 40F.Nickel (UNS N02200) Cold-Rolled SheetAnnealed 55 000 (380) 15 000 (100) 40F.Quarter-hard . . . 70 to 80Half-hard . . . 79 to 86Hard 90 000 (620

36、) 70 000 (480) 2 .Nickel (UNS N02200) Cold-Rolled StripAnnealed 55 000 (380)G15 000 (100) 40F,G.Skin-hard . . . 64 to 70Quarter-hard . . . 70 to 80Half-hard . . . 79 to 86Three-quarter-hard . . . 85 to 91Hard 90 000 (620)G70 000 (480) 2G.Spring temper . . . 95 minLow-Carbon Nickel (UNS N02201) Hot-R

37、olled PlateAnnealedAs-rolledD,E50 000 (345)50 000 (345)12 000 (80)12 000 (80)4030.Low-Carbon Nickel (UNS N02201) Hot-Rolled SheetAnnealed 50 000 (345) 12 000 (80) 40F.Low-Carbon Nickel (UNS N02201) Cold-Rolled SheetAnnealed 50 000 (345) 12 000 (80) 40F.Low-Carbon Nickel (UNS N02201) Cold-Rolled Stri

38、pAnnealed 50 000 (345)G12 000 (80) 40F,G.AYield strength requirements do not apply to material under 0.020 in. (0.51 mm) in thickness.BFor Rockwell or equivalent hardness conversions see Hardness Conversion Tables E 140.CCaution should be observed in using the Rockwell test on thin material, as the

39、results may be affected by specimen thickness. For thicknesses under 0.050 in. (1.3mm), the use of the Rockwell superficial or the Vickers hardness test is suggested.DAs-rolled plate may be given a stress-relieving heat treatment subsequent to final rolling.EAs-rolled plate specified “suitable for h

40、ot forming” shall be furnished from heats of known good hot-malleability characteristics (see X1.2.2). There are no applicabletensile or hardness requirements for such material.FSheet and strip 0.010 to 0.049 in. (0.25 to 1.2 mm), inclusive, in thickness shall have an elongation of 30 % minimum. She

41、et and strip 0.050 to 0.109 in. (1.3 to 2.7mm), inclusive, in thickness shall have an elongation of 35 % minimum.GNot applicable for thickness under 0.010 in. (0.25 mm).TABLE 4 Grain Size and Hardness for Cold-Rolled, Deep-Drawing, and Spinning Quality Sheet and StripThickness, in. (mm)Calculated Di

42、ameter of Average Grain Section,maxCorresponding ASTMMicro-Grain Size No.Rockwell BA,BHardness, maxmm in.Nickel (UNS N02200) SheetC(56 in. (1420 mm) Wide and Under)0.050 (1.3) and lessOver 0.050 to 0.250 (1.3 to 6.4), incl0.1100.1200.00430.00473.53.06464Nickel (UNS N02200) Strip (12 in. (305 mm) Wid

43、e and Under)D0.005Eto 0.010 (0.13 to 0.25), incl 0.025 0.0010 7.5F70FOver 0.010 to 0.024 (0.25 to 0.61), incl 0.065 0.0026 5.0 68Over 0.024 to 0.125 (0.61 to 3.2), incl 0.110 0.0043 3.5 64Low-Carbon Nickel (UNS N02201) Strip (12 in. (305 mm) Wide and Under)D0.005Eto 0.010 (0.13 to 0.25), incl 0.030

44、0.0012 7.0F66FOver 0.010 to 0.024 (0.25 to 0.61), incl 0.075 0.0030 4.5 64Over 0.024 to 0.125 (0.61 to 3.2), incl 0.110 0.0043 3.5 64AFor Rockwell or equivalent hardness conversions see Hardness Conversion Tables E 140.BCaution should be observed in using the Rockwell test on thin material, as the r

45、esults may be affected by specimen thickness. For thicknesses under 0.050 in. (1.3mm), the use of the Rockwell superficial or the Vickers hardness test is suggested.CThere are no applicable grain size requirements for low-carbon nickel (UNS N02201) sheet. The hardness of low-carbon nickel (UNS N0220

46、1) sheet shall be not overRockwell B64, or equivalent.DSheet requirements in Table 4 apply to strip thicknesses over 0.125 in. (3.2 mm), and for all thicknesses of strip over 12 in. (305 mm) in width.EFor ductility evaluations for strip under 0.005 in. (0.13 mm) in thickness, the spring-back test, s

47、uch as that described in Test Method F 155, is often used and themanufacturer should be consulted.FAccurate grain size and hardness determinations are difficult to make on strip under 0.005 in. (0.13 mm) in thickness and are not recommended.B 162 99 (2009)38.2 Sheet, Strip, and PlateSheet, strip, an

48、d plate suppliedin the conditions and finishes as listed in the appendix may beground or machined to remove surface imperfections, providedsuch removal does not reduce the material below the minimumspecified dimensions. Surface eliminated depressions shall befaired smoothly into the surrounding mate

49、rial. The removal ofa surface imperfection shall be verified by the method origi-nally used to detect the imperfection.TABLE 5 Permissible Variations in Thickness and Overweight of Rectangular PlatesNOTE 1All plates shall be ordered to thickness and not to weight per square foot. No plates shall vary more than 0.01 in. (0.25 mm) under thethickness ordered, and the overweight of each lotAin each shipment shall not exceed the amount given in the table. Spot grinding is permitted to removesurface imperfections, such spots not to exceed 0.01 in. (0.25