1、Designation: A 809 08Standard Specification forAluminum-Coated (Aluminized) Carbon Steel Wire1This standard is issued under the fixed designation A 809; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A n

2、umber in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification covers soft, medium, and hard tempe

3、rcarbon steel wire coated with aluminum by a hot-dip process,supplied in coils for general use.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered

4、 standard.2. Referenced Documents2.1 ASTM Standards:2A 370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA 428/A 428M Test Method for Weight Mass of Coatingon Aluminum-Coated Iron or Steel ArticlesA 700 Practices for Packaging, Marking, and LoadingMethods for Steel Products for

5、 ShipmentE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with Specifications2.2 U.S. Military Standards:3MIL-STD-129 Marking for Shipment and StorageMIL-STD-1188 Commercial Packaging of Supplies andEquipment2.3 U.S. Federal Standard:Fed. Std. No. 123 Marking for Shipme

6、nt (Civil Agencies)33. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 carbon steelsteel is considered to be carbon steel (1)when no minimum content is specified or required for alumi-num, chromium, cobalt, columbium, molybdenum, nickel,titanium, tungsten, vanadium, or zirconium

7、or any otherelement is added to obtain a desired alloying effect; (2) whenthe specified minimum copper content does not exceed 0.40 %;or (3) when the maximum specified content for any of thefollowing elements does not exceed these percentages: man-ganese 1.65, silicon 0.60, or copper 0.60.3.1.2 alum

8、inum-coated (aluminized) wirealuminum-coated (aluminized) wire is produced by passing individualwires through a bath of molten aluminum, after first beingproperly preheated, cleaned, and pickled.3.1.3 temperas applied to aluminum-coated (aluminized)wire, pertains to stiffness or resistance to bendin

9、g. It hascustomarily been expressed by tensile strength as shown in thethree ranges given in Table 1. The temper of a given chemicalcomposition can be controlled by the use of a different thermaltreatment for each temper. Different properties can also beobtained by varying the chemical composition f

10、or a giventhermal treatment. A thorough understanding of the end use ofthe wire, which involves both tensile strength and ductility,should be reached between the user and the manufacturer of thealuminum-coated (aluminized) wire. Requirements for bothchemical composition and mechanical properties may

11、 betechnologically impracticable.4. Ordering Information4.1 Orders for material under this specification shouldinclude the following information:4.1.1 Quantity (weight in pounds (kilograms),4.1.2 Coated wire diameter, expressed to 0.001 in. (0.025mm),4.1.3 Name of material (aluminum-coated carbon st

12、eelwire),4.1.4 Temper (soft, medium, or hard) (Table 1),4.1.5 Packaging requirements, and4.1.6 ASTM designation and year of issue.1This specification is under the jurisdiction of ASTM Committee A05 onMetallic-Coated Iron and Steel Products and is the direct responsibility ofSubcommittee A05.12 on Wi

13、re Specifications.Current edition approved May 1, 2008. Published May 2008. Originallyapproved in 1983. Last previous edition approved in 2003 as A 809 03.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTM

14、Standards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from Standardization Documents Order Desk, Bldg. 4, Section D,700 Robbins Ave., Philadelphia, PA 19111-5094, Attn: NPODS.1*A Summary of Changes section appears at the end of this standard.Copyrig

15、ht ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.NOTE 1A typical ordering description is as follows: 40 000 lb,0.148-in. aluminum-coated carbon steel wire, medium temper, in 500- to600-lb catch-weight coils on tubular carriers to ASTM A 80988

16、.5. Materials and Manufacture5.1 The steel rod from which the wire is produced shall bemanufactured by any commercially accepted steel makingpractice.5.2 The ingot or pig aluminum used for coating shallconform to the following impurity limits:max, %CopperIron0.100.506. Mechanical Properties6.1 The a

17、luminum-coated wire shall meet the tensilestrength in accordance with Table 1 when tested in accordancewith Test Methods and Definitions A 370.6.2 Test specimens containing a weld or an obvious defectshall be discarded and another test specimen obtained to verifyconformance to the tensile strength r

18、equirements.7. Dimensions and Tolerances7.1 The permissible variation in diameter of the aluminum-coated wire as represented by the test specimens shall be inaccordance with Table 2.8. Weight of Coating8.1 The aluminum-coated wire as represented by the testspecimens tested in accordance with Test Me

19、thod A 428, shallhave a minimum weight of aluminum coating in accordancewith Table 2.9. Adherence of Coating9.1 The aluminum-coated wire as represented by the testspecimens shall be capable of being wrapped in a close helix ata rate not exceeding 15 turns/min around a cylindrical steelmandrel having

20、 a diameter equal to three times the nominaldiameter of the coated wire under test, without cracking orflaking the aluminum coating to such an extent that anyaluminum can be removed by rubbing with the bare fingers.9.2 Loosening or detachment during the adhesion test ofsuperficial, small particles o

21、f aluminum formed by mechanicalpolishing of the surface of the aluminum-coated wire shall notbe considered cause for rejection.10. Workmanship10.1 The aluminum-coated wire shall be free of slivers,scale, and other imperfections not consistent with good com-mercial practice. The coating shall be cont

22、inuous and reason-ably uniform. To ensure large continuous length coils, weldsmay be present in the finished wire.11. Number of Tests and Retests11.1 Alot shall consist of all of the coils of wire of the samesize, type and class, and shall be offered for inspection at onetime. A wire sample of suffi

23、cient length, approximately 4 ft.(1.2 m), shall be cut from either end of each coil selected fortests described in Sections 6, 8, and 9.11.2 The number of test specimens taken from the ends ofcoils during production to assure compliance with Sections 6and 7 varies with the quality control procedures

24、 and themanufacturing facilities of each manufacturer, but is generallynot less than 10 % of the coils produced. For the purpose offinal product testing, one specimen from every ten coils orfraction thereof in a lot shall be selected at random, or a totalof seven specimens, whichever is less.11.3 Sh

25、ould one or more of the wire specimens fail anyrequirement, the lot shall be subjected to retest. For retestpurposes the original lot shall be regrouped into 50 coil lots orfractions thereof. Each lot shall be tested for the property inwhich the original sample failed to comply at a frequency of10 %

26、 or more so that the total number of tests is at least doublethe original. Any lot that exhibits a failure shall be rejected. Ifduring retesting an additional quality parameter is observed tobe defective, the lot of 50 is subject to rejection for that cause.The manufacturer may test each coil in the

27、 failed lot for theproperty in which failure occurred and reject only the noncon-forming coils.12. Inspection12.1 Unless otherwise specified in the contract or purchaseorder, the manufacturer is responsible for the performance ofall inspection and test requirements specified in this specifica-tion.

28、Except as otherwise specified in the contract or purchaseTABLE 1 Tensile Strength for Temper DesignationWire Diameter, in.(mm)Tensile Strength, ksi (MPa)ASoft Temper Medium Temper Hard Temper0.080 to under 0.106(2.03 to 2.69)75 max(515 max)70 to 95(485 to 655)85 to 115(585 to 795)0.106 to 0.176, inc

29、l(2.69 to 4.47)70 max(485 max)65 to 90(450 to 620)80 to 110(550 to 760)Over 0.176(over 4.47)70 max(485 max)60 to 85(415 to 585)75 to 105(515 to 725)AFor the purpose of determining conformance with this specification, anobserved value shall be rounded to the nearest 1 ksi in accordance with theroundi

30、ng method of Practice E29.TABLE 2 Dimensions, Tolerances, and Minimum Weight ofAluminum Coating per Unit Area of Uncoated Wire SurfaceSpecified Wire Diameter, in.(mm)ATolerance, 6in. (mm)BMinimumWeight of AluminumCoating, oz/ft2(g/m2)0.080 to under 0.092(2.03 to under 2.34) 0.004 (0.10) 0.30 (92)0.0

31、92 to under 0.106(2.34 to under 2.69) 0.004 (0.10) 0.32 (98)0.106 to under 0.148(2.69 to under 3.76) 0.004 (0.10) 0.35 (107)0.148 to under 0.244(3.76 to under 6.20) 0.004 (0.10) 0.40 (122)0.244(6.20) 0.005 (0.13) 0.40 (122)AFor the purpose of determining conformance with this specification, anobserv

32、ed value shall be rounded to the nearest 0.001 in., in accordance with therounding method of Practice E29.BIt is recognized that the surfaces of heavy aluminum coatings, particularlythose produced by the hot dip process, are not perfectly smooth. If the tolerancesshown in this table are rigidly appl

33、ied to such irregularities that are inherent to theproduct, unjustified rejections of wire that would actually be satisfactory for usecould occur. Therefore, it is intended that these tolerances be used in gaging theuniform areas of the aluminized wire.A809082order, the manufacturer may use his own

34、or any other suitablefacilities for the performance of the inspection and testrequirements, unless disapproved by the purchaser at the timethe order is placed. The purchaser shall have the right toperform any of the inspections and tests set forth in thisspecification when such inspections and tests

35、 are deemednecessary to assure that the material conforms to prescribedrequirements.13. Rejection and Rehearing13.1 Material that fails to conform to the requirements ofthis specification may be rejected. Rejections should be re-ported to the producer or supplier promptly and in writing. Incase of d

36、issatisfaction with the results of the test, the produceror supplier may make claim for a rehearing.13.2 The material must be adequately protected and cor-rectly identified in order that the producer or supplier maymake a proper investigation.14. Packaging, Marking, and Loading14.1 Marking shall be

37、by a tag securely attached to each coilof wire and shall show the identity of the producer, name ofproduct, temper, and ASTM designation.14.2 Packaging of the coils of wire shall be by agreementbetween the producer and the purchaser. This agreement shallinclude coil dimensions and mass.14.3 Unless o

38、therwise specified, the packaging, marking,and loading shall be in accordance with Practices A 700.14.4 For procurement by or direct shipment to the U.S.Government, marking for shipment, in addition to the require-ments specified in the contract or order, shall be in accordancewith MIL-STD-129 for m

39、ilitary agencies and with Fed. Std.No. 123 for civil agencies.14.5 When specified in the contract or order, and for directprocurement by or direct shipment to the U.S. Government,commercial packaging shall be in accordance with MIL-STD-1188.15. Keywords15.1 aluminized wire; aluminum-coated carbon st

40、eel wire;steel wire; wireSUMMARY OF CHANGESCommitteeA05 has identified the location of selected changes to this standard since the last issue (A 809 - 03)that may impact the use of this standard. (May 1, 2008)(1) Deleted reference to Mil Std 163 in 2.2 and 14.5.ASTM International takes no position r

41、especting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.Thi

42、s standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM Inte

43、rnational Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown

44、below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).A809083