ASTM A659 A659M-2010 Standard Specification for Commercial Steel (CS) Sheet and Strip Carbon (0 16 Maximum to 0 25 Maximum Percent) Hot-Rolled《碳素(最大含量为0 16%至0 25%)薄板材和带材热轧型钢(CS)用标准.pdf

《ASTM A659 A659M-2010 Standard Specification for Commercial Steel (CS) Sheet and Strip Carbon (0 16 Maximum to 0 25 Maximum Percent) Hot-Rolled《碳素(最大含量为0 16%至0 25%)薄板材和带材热轧型钢(CS)用标准.pdf》由会员分享，可在线阅读，更多相关《ASTM A659 A659M-2010 Standard Specification for Commercial Steel (CS) Sheet and Strip Carbon (0 16 Maximum to 0 25 Maximum Percent) Hot-Rolled《碳素(最大含量为0 16%至0 25%)薄板材和带材热轧型钢(CS)用标准.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A659/A659M 10Standard Specification forCommercial Steel (CS), Sheet and Strip, Carbon (0.16Maximum to 0.25 Maximum Percent), Hot-Rolled1This standard is issued under the fixed designation A659/A659M; the number immediately following the designation indicates the yearof original adoption

2、 or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scop

3、e*1.1 This specification covers hot-rolled carbon steel (CS)sheet and strip, in coils and cut lengths, in which the maximumof the specified carbon range is over 0.15 and not over 0.25 %and the maximum of the specified manganese range is not over0.90 %. This material is ordered to chemical compositio

4、n.1.2 This specification is not applicable to the steels coveredby Specification A635/A635M.1.3 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used indepen

5、dently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.2. Referenced Documents2.1 ASTM Standards:2A568/A568M Specification for Steel, Sheet, Carbon, Struc-tural, and High-Strength, Low-Alloy, Hot-Rolled andCold-Rolled, General Requirements forA635/A6

6、35M Specification for Steel, Sheet and Strip,Heavy-Thickness Coils, Hot-Rolled, Alloy, Carbon, Struc-tural, High-Strength Low-Alloy, and High-Strength Low-Alloy with Improved Formability, General RequirementsforA749/A749M Specification for Steel, Strip, Carbon andHigh-Strength, Low-Alloy, Hot-Rolled

7、, General Require-ments forE527 Practice for Numbering Metals and Alloys in theUnified Numbering System (UNS)2.2 Society of Automotive Engineers Standard:3J 1086 Numbering Metals and Alloys3. Ordering Information3.1 It is the purchasers responsibility to specify in thepurchase order all ordering inf

8、ormation necessary to purchasethe needed material. Examples of such information include butare not limited to the following:3.1.1 ASTM specification number and year of issue,3.1.2 Name of material (hot-rolled commercial steel (CS)sheet, or hot-rolled commercial steel (CS) strip),3.1.3 Grade designat

9、ion or chemical composition, or both,3.1.4 Copper-bearing steel (if required),3.1.5 Condition (as-rolled, pickled, or blast cleaned) (see4.1),3.1.5.1 Material to this specification is furnished in thehot-rolled condition. Pickled (or blast cleaned) must be speci-fied if required,3.1.6 Oiling (see 7.

10、2),3.1.7 Edges (see 7.1),3.1.8 Dimensions (thickness, width, and whether cut lengthsor coils),NOTE 1Not all producers are capable of meeting all of the limitationsof the thickness tolerance tables in Specification A568/A568M. Thepurchaser should contact the producer regarding possible limitations pr

11、iorto placing an order.3.1.9 Coil size (must include inside diameter, outside diam-eter, and maximum mass),3.1.10 Quantity,3.1.11 Application (show part identification and descrip-tion),3.1.12 Cast or heat analysis report (request, if required),3.1.13 Special requirements (if required).3.1.13.1 When

12、 the purchaser requires thickness tolerancesfor 3/8 in. 10 mm minimum edge distance (see Supplemen-tary Requirement in Specification A568/A568M), this require-ment shall be specified in the purchase order or contract.NOTE 2A typical ordering description is as follows:1This specification is under the

13、 jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.19 on Steel Sheet and Strip.Current edition approved April 1, 2010. Published April 2010. Originallyapproved in 1972. Last previous edition approved in 2008 as A659/A65

14、9M 08.DOI: 10.1520/A0659_A0659M-10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from Society of

15、 Automotive Engineers (SAE), 400 CommonwealthDr., Warrendale, PA 15096-0001, http:/www.sae.org.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.“ASTM A659-XX or A659M-X

16、X, Hot-Rolled Commercial Steel (CS)Sheet, Grade 1017, Pickled and Oiled, Cut Edge, 0.075 by 36 in. or 1.85by 900 mm, by coil, ID 24 in., OD 48 in., max weight 11 250 lb max orID 600 mm, OD 1200 mm, max, weight 7500 kg, max, 100 000 lb or 45000 kg for Part No. 6509, Shelf Leg, Cast or heat analysis r

17、eportrequired.”4. Materials and Manufacture4.1 ConditionUnless otherwise specified, the material isfurnished in the as-rolled condition (not annealed or pickled).5. Chemical Composition5.1 The Cast or Heat Analysis of the steel shall conform tothe chemical requirements shown in Table 1, or chemicalc

18、ompositions can be specified from carbon 0.16 maximum to0.25 % maximum, inclusive, and manganese 0.90 % maxi-mum, inclusive, which conform to the standard chemicalranges and limits tables in the Appendixes of SpecificationsA568/A568M and A749/A749M.5.1.1 Unspecified elements may be present. Limits o

19、n ele-ments shall be as stated in Table 2.5.1.1.1 Each of the elements listed in Table 2 shall beincluded in the report of the heat analysis. When the amount ofcopper, nickel, chromium, or molybdenum is less than 0.02 %,the analysis may be reported as “0.02 %.” When the amountof vanadium or columbiu

20、m is less than 0.008 %, the analysismay be reported as “0.008 %.”5.2 Where material is used for fabrication by welding, caremust be exercised in selection of the chemical composition toassure compatibility with the welding process and its effect onaltering the properties of the steel.6. Bending Prop

21、erties6.1 The minimum forming radius (radii) that steel coveredby this specification can be expected to sustain is listed in theappendix and is discussed in more detail in SpecificationsA568/A568M, and A749/A749M. When tighter bend radii arerequired, or curved or offset bends are involved, or whenst

22、retching or drawing are also a consideration, the producersshall be consulted.7. Workmanship, Finish, and Appearance7.1 Edge:7.1.1 Sheet can be supplied with mill edge or cut edge.7.1.2 Strip can be supplied with mill edge or slit (cut) edge.7.2 OilingHot-rolled, non-pickled material is commonlyfurn

23、ished not oiled, while hot-rolled pickled (or blast cleaned)material is commonly furnished oiled. When required, pickled(or blast cleaned) material may be specified to be furnished notoiled, and non-pickled material may be specified to be fur-nished oiled.8. General Requirements for Delivery8.1 Mate

24、rial furnished under this specification shall con-form to the applicable requirements of the current edition ofSpecification A568/A568M for sheet, and Specification A749/A749M for strip, unless otherwise provided herein.9. Certification and Reports9.1 When requested, the producer shall furnish copie

25、s of areport showing test results of the cast or heat analysis. Thereport shall include the purchase order number, the ASTMdesignation number, and the cast or heat number representingthe material.10. Keywords10.1 carbon steel sheet; carbon steel strip; hot rolled steelsheet; hot rolled steel strip;

26、steel sheet; steel stripTABLE 1 Typical Grade Designations and Chemical CompositionsAGrade Designation Carbon, % Manganese, % Phosphorus, max, % Sulfur, max, %1015 0.130.18 0.300.60 0.030 0.0351016 0.130.18 0.600.90 0.030 0.0351017 0.150.20 0.300.60 0.030 0.0351018 0.150.20 0.600.90 0.030 0.0351020

27、0.180.23 0.300.60 0.030 0.0351021 0.180.23 0.600.90 0.030 0.0351023 0.200.25 0.300.60 0.030 0.035ACopper, when specified, shall have a minimum content of 0.20 % by cast or heat analysis.TABLE 2 Limits on Unspecified Elements (see 5.1.1)Copper, max %AHeat analysisProduct analysis0.200.23Nickel, max %

28、AHeat analysisProduct analysis0.200.23Chromium, max %AHeat analysisProduct analysis0.150.19Molybdenum, max %AHeat analysisProduct analysis0.060.07Vanadium, max % Heat analysisProduct analysis0.0080.018Columbium, max % Heat analysisProduct analysis0.0080.018AThe sum of copper, nickel, chromium, and m

29、olybdenum shall not exceed0.50 % on heat analysis. When one or more of these elements are specified, thesum does not apply; in which case, only the individual limits on the remainingunspecified elements will apply.A659/A659M 102APPENDIX(Nonmandatory Information)X1. BENDING PROPERTIESX1.1 Table X1.1

30、shows suggested minimum inside radii forcold bending.SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A659/A659M 08) that may impact the use of this standard. (Approved April 1, 2010.)(1) Section 3.1.8.1 deleted.(2) Reversed order

31、of 3.1.12 and 3.1.13 and added new section3.1.13.1.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent righ

32、ts, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for

33、revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing

34、you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may

35、be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).TABLE X1.1 Sugges

36、ted Minimum Inside Radii for Cold BendingANOTE 1(t) equals a radius equivalent to the steel thickness.NOTE 2The suggested radii should be used as minimums for 90bends in actual shop practice.Maximum of SpecifiedManganese Range, %Minimum Inside Radius for ColdBendingTo 0.60 incl. 2 tOver 0.60 to 0.90 incl. 212 tAMaterial that does not perform satisfactorily, when fabricated in accordancewith the above requirements, may be subject to rejection pending negotiation withthe steel supplier.A659/A659M 103