《ANSI ASTM F718-2007 Standard Specification for Shipbuilders and Marine Paints and Coatings Product Procedure Data Sheet《造船厂和船舶漆及涂料制品 工艺数据单用规范》.pdf》由会员分享，可在线阅读，更多相关《ANSI ASTM F718-2007 Standard Specification for Shipbuilders and Marine Paints and Coatings Product Procedure Data Sheet《造船厂和船舶漆及涂料制品 工艺数据单用规范》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F718 07 (Reapproved 2017) An American National StandardStandard Specification forShipbuilders and Marine Paints and Coatings Product/Procedure Data Sheet1This standard is issued under the fixed designation F718; the number immediately following the designation indicates the year of orig

2、inaladoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscriptepsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department o

3、f Defense.1. Scope1.1 The Shipbuilders and Marine Paints and CoatingsProduct/Procedure Data Sheet2provides on one sheet neededinformation concerning the characteristics of a specific paint orcoating to include generic description, physical properties,surface preparation requirements, application req

4、uirements,and safety. The front side of the sheet contains four major,numbered paragraphs and a highlighted section for SpecialSafety Precautions. These paragraphs are as follows:I. Generic Type and DescriptionII. Manufacturers DataIII. PropertiesIV. Surface Preparation Minimum RequirementsThe back

5、side of the page contains the following paragraphs:V. Mixing ProcedureVI. Application1.2 The completed data sheets can be used by technicalpersonnel to help evaluate the technical acceptability of aproposed material, by production personnel to evaluate pro-duction compatibility of proposed materials

6、 and to provideapplication instructions for selected paints and coatingsmaterials, and by quality control personnel to verify attributesof materials.1.3 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision

7、 on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:3D56 Test Method for Flash Point by Tag Closed Cup TesterD93 Test Methods for Flash Po

8、int by Pensky-MartensClosed Cup TesterD523 Test Method for Specular GlossD1475 Test Method For Density of Liquid Coatings, Inks,and Related ProductsD1640 Test Methods for Drying, Curing, or Film Formationof Organic CoatingsD1650 Test Methods for Sampling and Testing ShellacVarnish (Withdrawn 1997)4D

9、2697 Test Method for Volume Nonvolatile Matter in Clearor Pigmented CoatingsD3278 Test Methods for Flash Point of Liquids by SmallScale Closed-Cup Apparatus2.2 ASTM Adjunct:Shipbuilders and Marine Paints and Coatings Product/Procedure Data Sheets22.3 U.S. EPA Method:524 U.S. Environmental Protection

10、 Agency, 40 CFR Ch. 1,Part 60, Appendix A, Determination of Volatile MatterContent, Density, Volume Solids, and Weight Solids ofSurface Coatings3. Instructions for Completing Data Sheet3.1 When filling out the Product/Procedure Data Sheet (seeFigs. 1 and 2) remember that the information contained th

11、ereinwill be utilized by both technical and production personnel.1This standard is under the jurisdiction of ASTM Committee F25 on Ships andMarine Technology and is the direct responsibility of Subcommittee F25.01 onStructures.Current edition approved May 1, 2017. Published June 2017. Originallyappr

12、oved in 1981. Last previous edition approved in 2011 as F718 07 (2011)1.DOI: 10.1520/F0718-07R17.2Available from ASTM International Headquarters. Order Adjunct No.ADJF0718. Original adjunct produced in 1993.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer

13、 Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4The last approved version of this historical standard is referenced onwww.astm.org.5Available from U.S. Government Printing Office, Superintendent ofDocu

14、ments, 732 N. Capitol St., NW, Washington, DC 20401-0001, http:/www.access.gpo.gov.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on st

15、andardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1FIG. 1 Data Sheet (Front)F718 07 (2017)2FIG. 2 Data Sheet (Back)F718 07 (2017)3Keep it

16、 simple and brief but complete. The following instruc-tions are organized by paragraph numbers contained within thedata sheet.3.2 Paragraph IGeneric Type and Description Use onlyknown and industry-accepted generic descriptions. Also, listany specification specific terminology (for example, MIL-PRF-2

17、3236 Type I, Class 2, etc.). See Fig. 1.3.3 Paragraph IIManufacturers DataThis section isself-explanatory with the possible exception of subparagraph(f). This can be as complete or as brief as the concerned partiesdesire. For example, a separate attached list of compatible andincompatible topcoats o

18、r acceptable cargo exposures could beincluded. See Fig. 1.3.4 Paragraph IIIPropertiesThis section is also self-explanatory with the following exceptions:3.4.1 Subparagraph (a)If agreed upon by the concernedparties, a different method for determining volume solids(theoretical coverage) may be substit

19、uted. The form should beamended to show method.3.4.2 Subparagraph (e)If the specification requires anedge-retentive paint to be used, the % edge retention and testmethod used should be listed.3.4.3 Subparagraph (g)Use an agreed upon standard forviscosity (for example, ASTM, etc.). Also, for two part

20、coatings, state whether the requirement is for each individualcomponent, the mixed coating, or all three.3.4.4 Subparagraph (n)any special properties (forexample, stain resistance, low temperature cure, etc.) should belisted, and any specific differences in handling, application ormaintenance proced

21、ures to maintain that property should belisted. See Fig. 1.3.5 Paragraph IVSurface Preparation Minimum Require-ments:3.5.1 Subparagraphs (a) and (b)Use an agreed-upon stan-dard for example, ASTM, SSPC, Swedish, NACE, SNAME,etc. See Fig. 1.3.5.2 Subparagraph (c)Surface profile data is required.The pr

22、ofile listed must be given as a range for the average ofall profile measurements. The method of measurement must beagreed upon by all parties concerned.3.5.3 Subparagraph (d)Any specific requirements for, orprohibitions on, the type of abrasives that can be used shall beentered in subparagraph (d),

23、Special Instructions. See Fig. 1.3.5.4 Subparagraph (f) and (g)List commercial industrystandard(s), or test method(s), or both, for conductivity andflash rust.3.6 Special Safety PrecautionsThis section should containspecific instructions of what to do in the event of skin or eyecontact or accidental

24、 ingestion, or both. Reference should alsobe made to the appropriate manufacturers Material SafetyData Sheet. See Fig. 1.3.7 Paragraph VMixing ProcedureThis section is self-explanatory with the possible exceptions of subparagraphs (c)and (f). Subparagraph (c) should preferably contain a genericsolve

25、nt as opposed to a proprietary one. Subparagraph (f)should, as a minimum, contain the mesh size of the strainingmaterial and special procedures governing which componentshould be added to the other. Subparagraph (b), if appropriate,should include length of induction time given as a function ofvariou

26、s temperatures. See Fig. 2.3.8 Paragraph VIApplicationThis section is one of themost important of the entire form. It must be filled outaccurately and completely using all blocks in every paragraph.3.8.1 Subparagraph (c), “Dry Times”Provide either agraph or a chart showing the following cure times a

27、t aminimum:(1) dry to recoat(2) dry to handle (that is, time until personnel can walk on,inspect, touch-up coat)(3) maximum recoat(4) cure to full serviceThe graph or chart shall have at a minimum each of thesefour cure times at the stated minimum and maximum ambienttemperatures, and at least one da

28、ta point in between (forexample, if a product can be applied as low as 40F, and ashigh as 100F, the chart or graph may need; to dry, to recoat,dry to handle, max recoat and cure to full service times for40F, 100F, and 70F).Maximum recoat times should be expressed in hours, days,weeks, or months.3.8.

29、2 Subparagraph (d)Equipment requirements shouldbe brief.3.8.3 Subparagraph (e)Special Instructions should in-clude mitigation steps to be followed when above conditionsnot met (for example, if max overcoat window is missed), andrequire special handling to correct. See Fig. 2.4. Keywords4.1 data shee

30、t; marine coatings; marine paints; proceduredata sheet; product data sheetF718 07 (2017)4ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination o

31、f the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn.

32、 Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comm

33、ents have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or

34、multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 07 (2017)5