SAE AMS 5763D-2010 Steel Corrosion Resistant Bars Forgings Tubing and Rings 15Cr - 6 5Ni - 0 75Mo - 0 50Cb (Nb) - 1 5Cu Solution Heat Treated (UNS S45000)《经热处理的15Cr 6 5Ni 0 75Mo 0 .pdf

《SAE AMS 5763D-2010 Steel Corrosion Resistant Bars Forgings Tubing and Rings 15Cr - 6 5Ni - 0 75Mo - 0 50Cb (Nb) - 1 5Cu Solution Heat Treated (UNS S45000)《经热处理的15Cr 6 5Ni 0 75Mo 0 .pdf》由会员分享，可在线阅读，更多相关《SAE AMS 5763D-2010 Steel Corrosion Resistant Bars Forgings Tubing and Rings 15Cr - 6 5Ni - 0 75Mo - 0 50Cb (Nb) - 1 5Cu Solution Heat Treated (UNS S45000)《经热处理的15Cr 6 5Ni 0 75Mo 0 .pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、_SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising theref

2、rom, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2010 SAE International All rights reserved. No part of this publication ma

3、y be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: 724-776-4970 (outside USA)

4、Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.orgSAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS5763DAEROSPACEMATERIALSPECIFICATIONAMS5763 REV. D Issued 1972-12 Reaffirmed 2006-04 Revised 201

5、0-06 Superseding AMS5763C Steel, Corrosion Resistant Bars, Forgings, Tubing, and Rings 15Cr - 6.5Ni - 0.75Mo - 0.50Cb (Nb) - 1.5Cu Solution Heat Treated (Composition similar to UNS S45000) RATIONALEAMS5763D revises Table 1 and Reports (4.4), and is a Five Year Review and update of this specification

6、. 1. SCOPE 1.1 Form This specification covers a corrosion-resistant steel in the form of bars, wire, forgings, mechanical tubing, flash welded rings, and stock for forging or flash welded rings. 1.2 Application These products have been used typically for parts requiring corrosion resistance approxim

7、ating that of steels of the 18-8 types and high strength exceeding that of the 12 Cr martensitic types up to 700 F (370 C), but usage is not limited to such applications.1.3 This steel can be used in the solution heat treated condition and is capable of being precipitation heat treated to tensile st

8、rengths as high as 180 ksi (1240 MPa). 1.4 Although this steel is relatively immune to stress-corrosion cracking, reference should be made to ARP1110 for recommended practices to minimize such conditions. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purch

9、ase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published

10、issue of that document shall apply. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE AMS5763D Page 2 of 82.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale,

11、PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org.AMS2241 Tolerances, Corrosion and Heat-Resistant Steel, Iron Alloy, Titanium, and Titanium Alloy Bars and Wire AMS2243 Tolerances, Corrosion and Heat-Resistant Steel Tubing AMS2248 Chemical Check Anal

12、ysis Limits, Corrosion and Heat-Resistant Steels and Alloys, Maraging and Other Highly-Alloyed Steels, and Iron Alloys AMS2303 Steel Cleanliness, Aircraft Quality, Martensitic Corrosion-Resistant Steels, Magnetic Particle Inspection ProcedureAMS2371 Quality Assurance Sampling and Testing, Corrosion

13、and Heat-Resistant Steels and Alloys, Wrought Products and Forging Stock AMS2374 Quality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steel and Alloy Forgings AMS2750 Pyrometry AMS2806 Identification, Bars, Wire, Mechanical Tubing, and Extrusions, Carbon and Alloy Steels and Corrosio

14、n and Heat-Resistant Steels and Alloys AMS2808 Identification, Forgings AMS7490 Rings, Flash Welded, Corrosion and Heat-Resistant Austenitic Steels, Austenitic-Type Iron, Nickel, or Cobalt Alloys, or Precipitation-Hardenable Alloys ARP1110 Minimizing Stress Corrosion Cracking in Wrought Forms of Ste

15、els and Corrosion Resistant Steels and Alloys2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org.ASTM A 370 Mechanical Testing of Steel Products ASTM E 353 Chemical Analysis of Stainless, Hea

16、t-Resisting, Maraging, and Other Similar Chromium-Nickel-Iron AlloysCopyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE AMS5763D Page 3 of 83. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to

17、the percentages by weight shown in Table 1, determined by wet chemical methods in accordance with ASTM E 353, by spectrochemical methods, or by other analytical methods acceptable to purchaser. TABLE 1 - COMPOSITION Element min max Carbon - 0.05 Manganese - 1.00 Silicon - 1.00 Phosphorus - 0.030Sulf

18、ur - 0.030Chromium 14.00 16.00 Nickel 6.00 7.00 Molybdenum 0.50 1.00 Columbium (Niobium) 8 x C 0.75 Copper 1.25 1.75 3.1.1 Check Analysis Composition variations shall meet the applicable requirements of AMS2248. 3.2 ConditionThe product shall be supplied in the following condition: 3.2.1 Bars, Wire,

19、 Mechanical Tubing, Forgings, and Flash Welded Rings Solution heat treated. 3.2.1.1 Bars 3.2.1.1.1 RoundsSolution heat treated and centerless ground. 3.2.1.1.2 Squares, Hexagons, and Flats Hot finished, solution heat treated, and descaled, or solution heat treated cold drawn, and descaled.3.2.1.2 Wi

20、reSolution heat treated and cold drawn. 3.2.1.3 Mechanical Tubing Cold finished and solution heat treated. 3.2.1.4 Flash Welded Rings Shall not be supplied unless specified or permitted on purchasers part drawing. When supplied, they shall be manufactured in accordance with AMS7490. Copyright SAE In

21、ternational Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE AMS5763D Page 4 of 83.2.2 Stock for Forging or Flash Welded Rings As ordered by the forging or flash welded ring manufacturer. 3.3 Heat Treatment Bars, wire, forgi

22、ngs, mechanical tubing, and flash welded rings shall be solution heat treated by heating to 1900 F 25 (1040 C 15), holding at heat for not less than 1 hour, and cooling rapidly. Pyrometry shall be in accordance with AMS2750.3.4 Properties The product shall conform to the following requirements; hard

23、ness and tensile testing shall be conducted in accordance with ASTM A 370: 3.4.1 Bars, Wire, Forgings, Mechanical Tubing, and Flash Welded Rings Shall be as follows on product 8.0 inch (200 mm) and under in least nominal cross-sectional dimensions. 3.4.1.1 As Solution Treated 3.4.1.1.1 Tensile Prope

24、rties Shall meet the requirements shown in Table 2 and 3.4.1.1.1.2. 3.4.1.1.1.1 Bars, Forgings, Tubing, and Flash Welded Rings TABLE 2 - MINIMUM TENSILE PROPERTIES Property Value Tensile Strength 125 ksi (860 MPa) Yield Strength at 0.2% Offset 95 ksi (655 MPa) Elongation in 4D 10% Reduction of Area

25、40% 3.4.1.1.1.2 WireNot higher than 165.0 ksi (1135 MPa) or equivalent hardness (See 8.2). 3.4.1.1.2 HardnessShall be as follows: 3.4.1.1.2.1 Bars Not higher than 311 HB, or equivalent (See 8.3), determined midway between surface and center. 3.4.1.1.2.2 Tubing, Flash Welded Rings, and Forgings Not h

26、igher than 311 HB, or equivalent (See 8.3). 3.4.1.2 After Precipitation Heat Treatment The product shall have the following properties after being precipitation heat treated by heating to 900 F 15 (480 C 8), holding at heat for not less than 4 hours, and cooling in air: Copyright SAE International P

27、rovided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE AMS5763D Page 5 of 83.4.1.2.1 Tensile Properties Shall be as shown in Table 3: TABLE 3 - MINIMUM TENSILE PROPERTIES Property Value Tensile Strength 180 ksi (1240 MPa) Yield Str

28、ength at 0.2% Offset 170 ksi (1170 MPa) Elongation in 4D 10% Reduction of Area 40% 3.4.1.2.2 HardnessShall be not lower than 363 HB, or equivalent (See 8.3), but the product shall not be rejected on the basis of hardness if the tensile properties of 3.4.1.2.1 are acceptable, determined on specimens

29、taken from the same sample as that with nonconforming hardness, or from another sample with similar nonconforming hardness. 3.4.2 Forging Stock When a sample of stock is forged to a test coupon and heat treated as in 3.3 and 3.4.1.2, specimens taken from the heat treated coupon shall conform to the

30、requirements of 3.4.1.2.1 and 3.4.1.2.2. If specimens taken from the stock after heat treatment as in 3.3 and 3.4.1.2 conform to the requirements of 3.4.1.2.1 and 3.4.1.2.2, the tests shall be accepted as equivalent to tests of a forged coupon. 3.4.3 Stock for Flash Welded Rings Specimens taken from

31、 the stock after heat treatment as in 3.3 and 3.4.1.2 shall conform to the requirements of 3.4.1.2.1 and 3.4.1.2.2. 3.5 QualityThe product, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the p

32、roduct. 3.5.1 When specified, steel shall conform to AMS2303. 3.5.2 Forgings shall have substantially uniform macrostructure. Standards for acceptance may be agreed upon by purchaser and vendor. 3.5.3 Grain flow of die forgings, except in areas which contain flash-line end grain, shall follow the ge

33、neral contour of the forgings, showing no evidence of reentrant flow. 3.6 Tolerances Shall be as follows: 3.6.1 Bars and Wire In accordance with AMS2241. 3.6.2 Mechanical Tubing In accordance with AMS2243. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproductio

34、n or networking permitted without license from IHS-,-,-SAE AMS5763D Page 6 of 84. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of the product shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves

35、 the right to sample and to perform any confirmatory testing deemed necessary to ensure that the product conforms to specified requirements. 4.2 Classification of Tests 4.2.1 Acceptance Tests The following are acceptance tests and shall be performed on each heat or lot as applicable: 4.2.1.1 Composi

36、tion (3.1) of each heat. 4.2.1.2 Tensile properties (3.4.1.1) and hardness (3.4.1.1.2) of each lot of bars, wire, forgings, mechanical tubing, and flash welded rings as solution heat treated. 4.2.1.3 Macrostructure of forgings (3.5.2). 4.2.1.4 Tolerances (3.6) or bars, wire, and mechanical tubing. 4

37、.2.2 Periodic Tests The following are periodic tests and shall be performed at a frequency selected by the vendor unless frequency of testing is specified by purchaser: 4.2.2.1 Tensile properties (3.4.1.2.1) and hardness (3.4.1.2.2) of each lot of bars, wire, forgings, mechanical tubing, and flash w

38、elded rings after precipitation heat treatment, and grain flow of die forgings (3.5.3). 4.2.2.2 Ability of forging stock (3.4.2) and stock for flash welded rings (3.4.3) to develop required properties. 4.3 Sampling and Testing Shall be as follows: 4.3.1 Bars, Wire, Mechanical Tubing, Flash Welded Ri

39、ngs, Forging Stock, and Stock for Flash Welded Rings In accordance with AMS2371. 4.3.2 Forgings In accordance with AMS2374. 4.4 ReportsThe vendor of bars, wire, forgings, mechanical tubing, and flash welded rings shall furnish with each shipment a report showing the results of tests for composition

40、of each heat and for tensile properties and hardness of each lot, and stating the product conforms to the other technical requirements. This report shall include the purchase order number, heat and lot numbers, AMS5763D, product form, size, and quantity. If forgings are supplied, statement of compli

41、ance with the uniform macrostructure requirement (if agreed upon) and the size and melt source of stock used to make the forgings shall also be included. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,

42、-,-SAE AMS5763D Page 7 of 84.5 Resampling and Retesting Shall be as follows: 4.5.1 Bars, Wire, Mechanical Tubing, Flash Welded Rings, Forging Stock, and Stock for Flash Welded Rings In accordance with AMS2371. 4.5.2 Forgings In accordance with AMS2374. 5. PREPARATION FOR DELIVERY 5.1 Sizes Except wh

43、en exact lengths or multiples of exact lengths are ordered, straight bars, wire, and tubing will be acceptable in mill lengths of 6 to 20 ft (2 to 6 m) but not more than 10% of any shipment shall be supplied in lengths shorter than 10 ft (3 m). 5.2 IdentificationShall be as follows: 5.2.1 Bars, Wire

44、, and Mechanical Tubing In accordance with AMS2806. 5.2.2 ForgingsIn accordance with AMS2808. 5.2.3 Flash Welded Rings and Stock for Forging or Flash Welded Rings As agreed upon by purchaser and vendor. 5.3 PackagingThe product shall be prepared for shipment in accordance with commercial practice an

45、d in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the product to ensure carrier acceptance and safe delivery.6. ACKNOWLEDGMENT A vendor shall mention this specification number and its revision letter in all quotations and when acknowle

46、dging purchase orders. 7. REJECTIONS Material not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from

47、IHS-,-,-SAE AMS5763D Page 8 of 88. NOTES 8.1 A change bar (l) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of the document title indic

48、ates a complete revision of the document, including technical revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 Tensile strength to hardness conversions are presented in ASTM A 370. 8.3 Hardness conversion tables for metals are presented in ASTM E 140. 8.4 Terms used in AMS are clarified in ARP1917. 8.5 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and