SAE AMS 5046E-2017 Carbon Steel Sheet Strip and Plate (SAE 1020 and 1025) (UNS G10200 and G10250).pdf

《SAE AMS 5046E-2017 Carbon Steel Sheet Strip and Plate (SAE 1020 and 1025) (UNS G10200 and G10250).pdf》由会员分享，可在线阅读，更多相关《SAE AMS 5046E-2017 Carbon Steel Sheet Strip and Plate (SAE 1020 and 1025) (UNS G10200 and G10250).pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、 _ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising ther

2、efrom, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2017 SAE International All rights reserved. No part of this

3、publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-49

4、70 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/standards.sae.org/AMS5046E AEROSPACE MATERIAL SPECIFICATION AMS5046 REV. E Issued 1985-10 Revised 2017-05 Supers

5、eding AMS5046D Carbon Steel, Sheet, Strip, and Plate (SAE 1020 and 1025) (Composition similar to UNS G10200 and G10250) RATIONALE AMS5046E results from a Five-Year Review and update of this specification and revises grain size testing requirements (3.1.1 and 3.3.3), allows additional heat treatments

6、 (3.2), prohibits cutting bar from plate (3.2.2), and revises classification of tests (4.2) and reporting (4.4). 1. SCOPE 1.1 Form This specification covers two types of carbon steel in the form of sheet, strip, and plate. 1.2 Application These products have been used typically for use in fabricatio

7、n of fittings, but usage is not limited to such applications. These products are not typically used for deep forming or cupping operations. 1.3 Classification The steels covered by this specification are classified as follows: Type 1 0.17 to 0.23 Carbon (SAE 1020) Type 2 0.22 to 0.28 Carbon (SAE 102

8、5) 1.3.1 Unless a specific type is ordered, either type may be supplied. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a doc

9、ument unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. SAE INTERNATIONAL AMS5046E Page 2 of 5 2.1 SAE Publications Available from SAE International, 40

10、0 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or +1 724-776-4970 (outside USA), www.sae.org. AMS2232 Tolerances Carbon Steel, Sheet, Strip, and Plate AMS2259 Chemical Check Analysis Limits Wrought Low-Alloy and Carbon Steels AMS2370 Quality Assurance Samp

11、ling and Testing Carbon and Low-Alloy Steel Wrought Products and Forging Stock AMS2807 Identification Carbon and Low-Alloy Steels, Corrosion and Heat-Resistant Steels and Alloys Sheet, Strip, Plate, and Aircraft Tubing AMSH6875 Heat Treatment of Steel Raw Materials ARP1917 Clarification of Terms Use

12、d in Aerospace Metals Specifications 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM A370 Mechanical Testing of Steel Products ASTM E112 Determining Average Grain Size ASTM E290 Ben

13、d Testing of Material for Ductility ASTM E350 Chemical Analysis of Carbon Steel, Low-Alloy Steel, Silicon Electrical Steel, Ingot Iron, and Wrought Iron 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accord

14、ance with ASTM E350, by spectrochemical methods, or by other analytical methods acceptable to purchaser. Table 1 - Composition Grade 1020 1020 1025 1025 Element Type 1 Min Type 1 Max Type 2 Min Type 2 Max Carbon Manganese Phosphorus Sulfur 0.17 0.30 - - 0.23 0.60 0.040 0.050 0.22 0.30 - - 0.28 0.60

15、0.040 0.050 3.1.1 Aluminum is an optional grain refining element and need not be determined or reported unless used to satisfy the average grain size requirements of 3.3.3. 3.1.2 Check Analysis Composition variations shall meet the applicable requirements of AMS2259. 3.2 Condition The product shall

16、be supplied in the conditions as stated in 3.2.1 and 3.2.2; annealing, when used, shall be performed in accordance with AMS-H-6875 as specified for alloy 1025 for both Type 1 and Type 2. SAE INTERNATIONAL AMS5046E Page 3 of 5 3.2.1 Sheet and Strip Hot or cold rolled, annealed, sub-critically anneale

17、d or normalized, and cold finished. 3.2.2 Plate Hot rolled, annealed, sub-critically annealed or normalized, and descaled. 3.2.2.1 If allowed by the purchaser, cold rolled, annealed, sub-critically annealed or normalized if necessary and descaled as necessary, having hardness not higher than 25HRC,

18、or equivalent (see 8.2). 3.3 Properties The product shall conform to the following requirements; tensile tests shall be performed in accordance with ASTM A370: 3.3.1 Tensile Properties Shall be as shown in Table 2: Table 2 - Minimum tensile properties Property Value Tensile Strength Yield Strength a

19、t 0.2% Offset Elongation in 2 inches (50.8 mm) or 4D 55 ksi (379 MPa) 36 ksi (248 MPa) 22% 3.3.1.1 For each 2 ksi (13.8 MPa) in excess of 55 ksi (379 MPa) tensile strength, a reduction in elongation of 1% to a minimum of 10% is permissible. 3.3.2 Bending Sheet and strip shall be tested in accordance

20、 with ASTM E290 using a sample prepared nominally 0.75 inch (19.0 mm) in width with its axis of bending parallel to the direction of rolling and shall withstand without cracking when bending at room temperature through the angle and bend radius shown in Table 3. In case of dispute, the results of te

21、sts using the guided bend test of ASTM E290 shall govern. Table 3 - Bend requirements Bend Angle Degrees Bend Radius t = nominal thickness 180 1/2t 3.3.3 Average Grain Size Average grain size shall be determined by either 3.3.3.1 or 3.3.3.2. 3.3.3.1 Shall be ASTM No. 5 or finer, determined in accord

22、ance with ASTM E112. 3.3.3.2 The product of a heat shall be considered to have an ASTM No. 5 or finer austenitic grain size if one or more of the following are determined by heat analysis (see 8.5): 3.3.3.2.1 A total aluminum content of 0.020 to 0.050%. 3.3.3.2.2 An acid soluble aluminum content of

23、0.015 to 0.050%. SAE INTERNATIONAL AMS5046E Page 4 of 5 3.4 Quality The product, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the product. 3.5 Tolerances Shall conform to all applicable requ

24、irements of AMS2232. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The producer of the product shall supply all samples for producers tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory t

25、esting deemed necessary to ensure that the product conforms to specified requirements. 4.2 Classification of Tests All technical requirements are acceptance tests and shall be performed on each heat or lot as applicable. If grain refining elements (3.3.3.2) are not present, the ASTM E112 grain size

26、test (3.3.3.1) shall be conducted on each lot. 4.2.1 If aluminum as a grain refining element (3.3.2.2) is present, the ASTM E112 grain size test (3.3.2.1) shall be conducted on a periodic basis and shall be performed at a frequency selected by the producer (not to exceed one year) unless frequency o

27、f testing is specified by purchaser. 4.3 Sampling and Testing Shall be in accordance with AMS2370 and the following: 4.3.1 When a statistical sampling plan has been agreed upon by purchaser and producer, sampling shall be in accordance with such plan in lieu of sampling as in 4.3, and the report of

28、4.4 shall state that such plan was used. 4.4 Reports 4.4.1 The producer of the product shall furnish with each shipment a report showing the producer identity, results of tests for composition of each heat and for tensile properties, bending and average grain size, if measured, of each lot, and stat

29、ing that the product conforms to the other technical requirements. This report shall include the purchase order number, heat and lot numbers, AMS5046E, Type and SAE “grade”, size, product form, and quantity. If the grain size requirement of 3.3.3.2 is met by the aluminum, the aluminum content shall

30、be reported and a statement that the chemistry satisfies the grain size requirement shall be included. 4.4.2 Report the nominal metallurgically worked cross sectional size and the cut size, if different (also see 3.2.1). 4.5 Resampling and Retesting Shall be in accordance with AMS2370. 5. PREPARATIO

31、N FOR DELIVERY 5.1 Identification Shall be in accordance with AMS2807 including Type and SAE “grade”. 5.2 Protective Treatment Product shall be protected from corrosion prior to shipment. SAE INTERNATIONAL AMS5046E Page 5 of 5 5.3 Packaging The product shall be prepared for shipment in accordance wi

32、th commercial practice and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the product to ensure carrier acceptance and safe delivery. 6. ACKNOWLEDGMENT A producer shall include this specification number and its revision letter in all

33、quotations and when acknowledging purchase orders. 7. REJECTIONS Product not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. 8. NOTES 8.1 Revision Indicator A change bar (l) located in the left margin is for the convenience of the user in

34、locating areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, including technical revisions. Change bars and (R) are not used in original publicati

35、ons, nor in documents that contain editorial changes only. 8.2 Terms used in AMS are clarified in ARP1917. 8.3 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate eq

36、uivalents of the primary units and are presented only for information. 8.4 Purchase documents should specify not less than the following: AMS5046E Type number of composition desired Product form and size of product desired Quantity of product desired 8.5 Grain size The average grain size resulting f

37、rom using the appropriate test procedures per ASTM E112 will satisfy an ASTM No. 5 or finer grain size when the element defined in 3.3.2.2 as grain refiner is present. Other technical societies have adopted the verification of fine grain steel based on chemistry alone. Included are ASTM International (Documents A6, A20, and A29); American Society of Mechanical Engineers (Documents SA6, SA20, and SA29); American Bureau of Shipping; CSA Group (Canada); EuroNorm documents; American Association of State Highway and Transportation Officials. PREPARED BY AMS COMMITTEE “E“