SAE AMS 4013G-2014 Aluminum Sheet Laminated Surface Bonded《表面结合层压铝片》.pdf

《SAE AMS 4013G-2014 Aluminum Sheet Laminated Surface Bonded《表面结合层压铝片》.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 4013G-2014 Aluminum Sheet Laminated Surface Bonded《表面结合层压铝片》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、_SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising theref

2、rom, is the sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions.Copyright 2013 SAE InternationalAll rights reserved. No part of this publi

3、cation may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE.TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada)Tel: +1 724-776-4970 (out

4、side USA)Fax: 724-776-0790Email: CustomerServicesae.orgSAE WEB ADDRESS: http:/www.sae.orgSAE values your input. To provide feedbackon this Technical Report, please visithttp:/www.sae.org/technical/standards/AMS4013GAEROSPACE MATERIAL SPECIFICATIONAMS4013 REV. GIssued 1958-01Reaffirmed 2012-09Revised

5、 2014-02Superseding AMS4013EAluminum Sheet, LaminatedSurface BondedRATIONALEAMS4013G revises the Title to more clearly indicate the product and to align it with that of AMS-DTL-22499 which is for a similar product, revises Fabrication (3.2.1), and is a Five Year Review and update of this specificati

6、on.1. SCOPE1.1 FormThis specification covers aluminum and aluminum alloy foil in the form of laminated sheet.1.2 ApplicationThis product has been used typically for shims in which thickness is to be adjusted by removal of laminations as required, but usage is not limited to such applications.2. APPL

7、ICABLE DOCUMENTSThe issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document

8、 has been cancelled and no superseding document has been specified, the last published issue of that document shall apply.2.1 SAE PublicationsAvailable from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA),

9、www.sae.org.AMS4016 Aluminum Alloy Sheet and Plate, 2.5Mg - 0.25Cr (5052-H32), Strain Hardened, Quarter-Hard, and StabilizedAMS4017 Aluminum Alloy Sheet and Plate, 2.5Mg - 0.25Cr (5052-H34), Strain Hardened, Half-Hard, and StabilizedAMS4041 Aluminum Alloy Sheet and Plate, Alclad, 4.4Cu - 1.5Mg - 0.6

10、0Mn (Alclad 2024 and 1-1/2% Alclad 2024, -T3 Flat Sheet; 1-1/2% Alclad 2024-T351 Plate)SAE INTERNATIONAL AMS4013G Page 2 of 52.2 ASTM PublicationsAvailable from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org.ASTM B 660 Pack

11、aging/Packing of Aluminum and Magnesium Products3. TECHNICAL REQUIREMENTS3.1 Composition3.1.1 LaminationsShall be AA1100, AA1145, AA3003, or AA5052 aluminum alloy foil. The choice of alloy shall be at the discretion of the producer unless a specific alloy is specified by purchaser.3.1.2 Solid BaseSh

12、all be AMS4041 aluminum alloy sheet, except that when laminations are AA5052 aluminum alloy foil the base shall be AMS4016 or AMS4017 aluminum alloy sheet.3.1.3 AdhesiveShall be a composition which will meet the fabrication and quality requirements of 3.2, 3.3, and 3.4.3.2 FabricationLaminated shim

13、stock shall be fabricated from hard or extra hard laminations, in combination with a solid base, when required. Laminations shall be 0.0030 inch 0.0003 (0.076 mm 0.008) thick unless thickness of 0.0020 inch + 0.0002 (0.051 mm + 0.005) is specified. The thickness of each layer of adhesive shall not e

14、xceed 0.0003 inch (0.008 mm).3.2.1 Laminations and solid base when applicable, shall be bonded together throughout the surface area in a manner which will permit peeling of laminations for adjustment of shim thickness without separation of the remaining laminations and solid part. Laminations shall

15、be bonded together so that any shape can be cut from the material using suitable tools, without separation. Material shall remain intact without separation during normal handling. Requirements shall be applicable to laminations not less than eight hours after completion of bonding.3.2.2 Surface Roug

16、hnessFlat surfaces of laminations, and solid stock when applicable, shall have a maximum roughness of 63 RA (microinches) on original surfaces and on metallic surfaces after peeling.3.2.3 Water ResistanceSheet shall withstand immersion in tap water at 120 F 5 (49 C 3) for not less than 3 hours witho

17、ut separation of laminations or any evidence of corrosion.3.3 SizesSheet shall be of the thicknesses and combinations of laminations and solid base specified in Table 1.SAE INTERNATIONAL AMS4013G Page 3 of 5TABLE 1 - LAMINATION THICKNESS/COMBINATIONSNominal Thickness of Shim StockAll Laminated,All L

18、aminated,Half Solid, Half Laminated,Half Solid, Half Laminated,Three-Quarters Solid, One Quarter Laminated,Three-Quarters Solid, One Quarter Laminated,Inch mm0.002 inch (0.05 mm)0.003 inch (0.08 mm)0.002 inch (0.05 mm)0.003 inch (0.08 mm)0.002 inch (0.05 mm)0.003 inch (0.08 mm)0.006 0.15 X0.008 0.20

19、 X0.010 0.25 X0.012 0.30 X0.015 0.38 X X0.016 0.41 X X0.020 0.51 X X0.021 0.53 X X0.032 0.81 X X0.033 0.84 X X0.047 1.19 X X0.048 1.22 X X0.062 1.58 X X X X0.063 1.60 X X X X0.078 1.98 X X X X0.080 2.03 X X X X0.093 2.36 X X X X0.094 2.39 X X X X0.109 2.77 X X X X0.121 3.07 X X X X X X0.125 3.18 X X

20、 X X X X3.4 QualitySheet, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from dents, creases, and other imperfections detrimental to usage of the sheet.3.5 TolerancesShall be as specified in Table 2.TABLE 2A - TOLERANCES, INCH/POUND UN

21、ITSNominal ThicknessInchesTolerance, InchPlusTolerance, InchMinusUp to 0.008, incl 0.001 0.005Over 0.008 to 0.010, incl 0.0015 0.005Over 0.010 to 0.016, incl 0.0015 0.001Over 0.016 to 0.021, incl 0.002 0.001Over 0.021 to 0.033, incl 0.003 0.002Over 0.033 to 0.048, incl 0.005 0.002Over 0.048 to 0.063

22、, incl 0.006 0.002Over 0.063 to 0.080, incl 0.007 0.002Over 0.080 to 0.094, incl 0.009 0.003Over 0.094 to 0.109, incl 0.010 0.003Over 0.109 to 0.125, incl 0.012 0.003Over 0.125 to 0.156, incl 0.015 0.003Over 0.156 to 0.187, incl 0.018 0.003Over 0.187 to 0.190, incl 0.018 0.005SAE INTERNATIONAL AMS40

23、13G Page 4 of 5TABLE 2B - TOLERANCES, SI UNITSNominal ThicknessMillimetersTolerance, mmPlusTolerance, mmMinusUp to 0.20, incl 0.025 0.013Over 0.20 to 0.25, incl 0.038 0.013Over 0.25 to 0.41, incl 0.038 0.03Over 0.41 to 0.53, incl 0.05 0.03Over 0.53 to 0.84, incl 0.08 0.05Over 0.84 to 1.22, incl 0.13

24、 0.05Over 1.22 to 1.60, incl 0.15 0.05Over 1.60 to 2.03, incl 0.17 0.05Over 2.03 to 2.39, incl 0.23 0.08Over 2.39 to 2.77, incl 0.25 0.08Over 2.77 to 3.18, incl 0.30 0.08Over 3.18 to 3.96, incl 0.38 0.08Over 3.96 to 4.75, incl 0.46 0.08Over 4.75 to 4.83, incl 0.46 0.134. QUALITY ASSURANCE PROVISIONS

25、4.1 Responsibility for InspectionThe vendor of sheet shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the sheet conforms to spe

26、cified requirements.4.2 Classification of TestsAll technical requirements are acceptance tests and shall be performed on each heat or lot as applicable.4.3 Sampling and TestingSufficient sheet shall be selected at random from each inspection lot to perform all required tests. The number of determina

27、tions for each requirement shall be not less than two.4.4 ReportsThe vendor of sheet shall furnish with each shipment a report showing the results of tests for composition of each alloy used and stating that the sheet conforms to the other technical requirements. This report shall include the purcha

28、se order number, lot number, AMS4013G, shim stock thickness, foil thickness, percentage of total thickness which is laminated, size, and quantity. The report shall also identify the producer and lot identity.4.5 Resampling and RetestingIf any specimen used in the above tests fails to meet the specif

29、ied requirements, disposition of the sheet may be based on the results of testing two additional specimens for each original nonconforming specimen. Failure of any retest specimen to meet the specified requirements shall be cause for rejection of the sheet represented. Results of all tests shall be

30、reported.5. PREPARATION FOR DELIVERY5.1 IdentificationLaminated sheet shall be marked with not less than the nominal total thickness, thickness of each lamination, percentage of total thickness which is laminated, and AMS4013G.SAE INTERNATIONAL AMS4013G Page 5 of 55.2 PackagingProduct shall be prepa

31、red for shipment in accordance with ASTM B 660 and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the sheet to ensure carrier acceptance and safe delivery.6. ACKNOWLEDGMENTA vendor shall mention this specification number and its revis

32、ion letter in all quotations and when acknowledging purchase orders.7. REJECTIONSSheet not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection.8. NOTES:8.1 A change bar (|) located in the left margin is for the convenience of the user in locati

33、ng areas where technical revisions, not editorial changes, have been made to the previous issue of a document. An (R) symbol to the left of the document title indicates a complete revision of the document, including technical revision. Change bars and (R) are not used in original publications, nor i

34、n documents that contain editorial changes only.8.2 Terms used in AMS are clarified in ARP1917.8.3 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of

35、 the primary units and are presented only for information.8.4 Purchase documents should specify not less than the following:AMS4013GForm and size or part number of laminated sheet desiredQuantity of laminated sheet desired.8.5 Similar SpecificationsAMS-DTL-22499, Composition 1, is listed for information only and shall not be construed as an acceptable alternate unless all requirements of this AMS are met.PREPARED BY AMS COMMITTEE “D“