《NAVY MIL-S-22698 C-1988 STEEL PLATE SHAPES AND BARS WELDABLE ORDINARY STRENGTH AND HIGHER STRENGTH STRUCTURAL《可焊性普通强度和高强度碳素钢板和型材结构》.pdf》由会员分享，可在线阅读，更多相关《NAVY MIL-S-22698 C-1988 STEEL PLATE SHAPES AND BARS WELDABLE ORDINARY STRENGTH AND HIGHER STRENGTH STRUCTURAL《可焊性普通强度和高强度碳素钢板和型材结构》.pdf（38页珍藏版）》请在麦多课文档分享上搜索。

1、29 June 1988 SUPERSEDING MIL-S-22698B(SH) 10 April 1981 (See 6.4 and 6.8) MILITARY SPECIFICATION STEEL PLATE, SHAPES AND BARS, WELDABLE ORDINARY STRENGTH AND HIGHER STRENGTH: STRUCTURAL This specification is approved for use within the Naval Sea Systems Command, Department of the Navy, and is availa

2、ble for use by all Departments and Agencies of the Department of Defense. 1. SCOPE 1.1 Scope. This specification covers ordinary strength and higher strength steel plate, shapes and bars. 1.2 Classification. 1.2.1 Grades. Plates, shapes and bars covered by this specification shall be of the followin

3、g grades, as specified (see 6.2.1): Ordinary strength structural steel Plate A: ABS grade A - 1/2 inch or less in thickness B: ABS grade B - up through 1 inch in thickness D: ABS grade D E: ABS grade E Shapes A: ABS grade A - shapes with web 3/4 inch and less in thickness B: ABS grade B - shapes wit

4、h web up through 2 inches in thickness B ar A: ABS grade A - 3/4 inch or less in thickness B: ABS grade B Beneficial comments (recommendations, additions, deletions) and any pertinent data which may be of use in improving this document should be addressed to: Commander, Naval Sea Systems Command, SE

5、A 5523, Department of the Navy, Washington, DC 20362-5101 by using the self-addressed Standardization Document Improvement Proposal (DD Form 1426) appearing at the end of this document or by letter. AMSC N/A FSC 9515 DISTRIBUTION STATEMENT A Approved for public release; distribution unlimited Provid

6、ed by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Higher strength structural steel Plate AH-36T: ABS grade AH-36 with ultrasonic (UT) testing AH-36TZ: ABS grade AH-36 with through thickness properties and UT testing DH-36: ABS grade DH-36 EH-36Z: ABS grade E

7、H-36 with through thickness properties EH-36T: ABS grade EH-36 with UT testing EH-36TZ: ABS grade EH-36 with through thickness properties and UT testing Shapes AH-36: ABS grade AH-36 with web 2 inches and less in thickness AH-36T: ABS grade AH-36 with web 2 inches and less in thickness and with fine

8、 grain practice and UT testing AH-36TZ: ABS grade AH-36 with web 2 inches and less in thickness with fine grain practice, UT testing, and through thick- ness properties Bar AH-36: ABS grade AH-36 AH-36T: ABS grade AH-36 with UT testing AH-36TZ: ABS grade AH-36 with through thickness properties and E

9、H-36: ABS grade EH-36 UT testing 1.2.2 Classes. Surface finish of plates, shapes and bars covered by this specification shall be! of the following classes, as specified (see 6.2.1): Class P - Descaled and painted Class U - Nil1 finish (hot rolled or normalized) 2. APPLICABLE DOCUMENTS 2.1 Government

10、 documents. 2.1.1 Standard. The following standard forms a part of this specification to the extent specified herein. Unless otherwise specified, the issue of this document shall be that listed in the issue of the Department of Defense Index of Specifications and Standards (DoDISS) and supplement th

11、ereto, cited in the solicitation. STANDARD MILITARY MIL-STD-271 - Requirements for Nondestructive Testing Methods. (Copies of standards and other Government documents required by contractors in connection with specific acquisition functions should be obtained from the contracting activity or as dire

12、cted by the contracting activity.) 2 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-NIL-S-22678C 75 U 7797706 OLL8040 4 U 2.2 Other publications. The following documents form a part of ths specification to the extent specified herein. Unless otherwi

13、se specified, the issues of the documents which are DoD adopted shall be those listed in the issue of the DoDISS specified in the solicitation. Unless otherwise specified, the issues of documents not listed in the DoDISS shall be the issue of the nongovernment documents which is current on the date

14、of the solicitation. AMERICAN BUREAU OF SHIPPING (ABS) ABS Rules for Building and Classing Steel Vessels. (Application for copies should be addressed to the American Bureau of Shipping, 45 Eisenhower Drive, Paramus, NJ 07652.) AMERICAN SOCIETY FOR TESTING AND MATERIALS (ASTM) A 6 - Standard Specific

15、ation for General Requirements for Rolled Steel Plates, Shapes, Sheet Piling, and Bars for Structural Use. (DoD adopted) A 370 - Standard Test Methods and Definitions for Mechanical Testing of Steel Products. (DoD adopted) A 505 - Standard Specification for Steel, Sheet and Strip, Hot- Rolled and Co

16、ld-Rolled, General Requirements for. (DoD adopted) Methods for Steel Products for Domestic Shipment. (DoD adopted) Testing of Steel Plates for Special Applications. (DoD adopted) mine Nil-Ductility Transition Temperature of Ferritic Steels. A 700 - Standard Practices for Packaging, Marking, and Load

17、ing A 770 - Standard Specification for Through-Thickness Tension E 208 - Standard Method for Conducting Drop-Weight Test to Deter- Test from (Application for copies should be addressed to the American Society for ing and Materials, 1916 Race Street, Philadelphia, PA 19103.) (Nongovernment standards

18、and other publications are normally available the organizations which prepare or which distribute the documents. . These documents also may be available in or through libraries or other informational services. ) 2.3 Order of precedence. In the event of a conflict between the text of this specificati

19、on and the references cited herein (except for associated detail specifications, specification sheets or MS standards), the text of this specifi- cation shall take precedence. Nothing in this specification, however, shall supersede applicable laws and regulations unless a specific exemption has been

20、 obtained. 3. REQUIREMENTS 3.1 First article. When specified in the contract or purchase order, a sample shall be subjected to first article inspection (see 4.3, 6.2.1, and 6.3). 3 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-3.2 General. Unless o

21、therwise specified (see 1.2.1 and 6.2.1), steel plates, shapes, and bars shall be in accordance with section 43, ABS Rules for Building and Classing Steel Vessels. Additional requirements may be specified for particular U.S. Navy applications. 3.2,1 Extrusions. Extrusions shall consist of one piece,

22、 reduced from a billet to the final section in a one pass hot-extrusion operation. Hot-wrought materials shall be produced by hot forming ingots, billets, or other semi- finished forms to the final product. 3,2.2 Weld repair. Weld repair of plate, shape, or bar defects shall be in accordance with se

23、ction 43 of the ABS rules and with the following additional requirements. Weld repairs shall be magnetic particle inspected in accordance with MIL-STD-271 and shall be free of relevant linear indications longer than 1/8 inch. After weld repair, the area of the repair shall be inspected by the same n

24、ondestructive method as revealed the original indication. 3.3 Dimensional tolerances, Unless otherwise specified (see 6.2.1), dimen- sional tolerances shall be in accordance with section 43 of the ABS Rules. Where dimensional tolerances are not delineated in section 43 of the ABS Rules, they shall b

25、e in accofdance with ASTN A 6 or ASTW A 505, as applicable. 3.3.1 Dimensional tolerances for EH-36T and EH-36TZ. Dimensional tolerances for EH-36T and EH-36TZ shall be in accordance with table I. 4 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-

26、S-2269BG 75 W 7999706 OLL8042 B W MIL-S-22698C (SH) INNNNNNNNNNNNCOLnLnnnnnnnLnnLnnLnnv- IfjfnnnnLnv)u3v)v)u3bbbaJCOCOmmooorrcjn 1OOOOOOOOOOOOOOOOOOOoooccv-rt- I IO . O . O bbbbbbbbnLnNNNNNNNNNNNNNCOCOnnnnn NNNNNNNNmmjffjfLnnLnLnv)v)v)v)v)v)bbFbj 00000000000000000000ooooooooorv- O . . O rrrrrbbbnnnN

27、NNNNNNNNNCOCOnLnmn NNNNNNNNNmmmfjfLnnnnv)v)v)v)v)v)bbbboN 00000000000000000000000000000 O . . O . O c a, c, u) a, u) u) 4Jm .P na, -m nm r-= a, .P- v) -0u)s 4-c a, 5 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-3.4 Fine grain practice for AH-36T a

28、nd AH-36TZ shapes, plates and bars. AH-36T and AH-36TZ shapes, plates and bars shall be produced using a fine grain practice in accordance with section 43 of the ABS Rules. 3.5 Chernical composition. Unless otherwise specified (see 6.2.1), the chemical composition shall conform to section 43 of the

29、ABS Rules. 3.5.1 Chemical composition of EH-36Z and EH-36TZ. The chemical composi- tion (heat analysis) of EH-362 and EH-36TZ shall conform to the higher strength steel composition with the following additional limitations: (a) The maximum sulfur content shall be 0.010 percent. (b) Additions of elem

30、ents that result in control of the shape of (c) When product analysis is specified, chemical tolerances shall be nonmetallic inclusions (sulfide shape control) shall be made. in accordance with ASTM A 6 and shall be applied with the excep- tion that the upper maximum tolerance limit for sulfur and p

31、hos- phorus shall be 0.003 percent weight. 3.5,2 Recovered materials. Unless otherwise specified herein, all material incorporated in the products covered by this specification shall be new and may be fabricated using materials produced from recovered materials to the maximum extent practicable with

32、out jeopardizing the intended use. The term “recovered materials“ means materials which have been collected or recovered from solid waste and reprocessed to become a source of raw materjals, as opposed to virgin raw materials. None of the above shall be interpreted to mean that the use of used produ

33、cts is allowed under this specification unless otherwise specifically specified. 3.6 Surface finish, Unless otherwise specified (see 6.2.1), plates, shapes, and bars shall be furnished class P (see 1.2.2). 3.7 Internal soundness. Plates ordered to condition T and TZ shall be inspected as specified i

34、n appendix A and shall meet the acceptance criteria as specified in appendix A. Shapes and bars ordered to condition T and TZ shall not have a complete loss or transposition of back reflection by more than a total of 6 inches (150 millimeters (mm) in any 3 feet (1 meter) of scan when tested in accor

35、dance with 4.5.2. 3.8 Mechanical properties. Every grade of material shall be tested and certified in accordance with the provisions of section 43 of the ABS Rules. Test results shall meet all mechanical property requirements specified in section 43 of the ABS Rules. 3.8.1 Properties test direction.

36、 The mechanical properties shall be obtained in the transverse direction unless size limitations require obtaining them in the longitudinal direction. 3.8.2 Through thickness properties of EH-36Z and EH-36TZ. The reduction in area shall be not less than 20 percent when tested as specified in 4.5.3.

37、6 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-S-22678C 75 W 7797906 OLL8044 L m MIL-S-22698C(SH) 3.9 Identification. Each grade of material shall be marked in accbrdance with section 43 of the ABS Rules and in accordance with the following ad

38、ditional requirements: (a) Steel plates, shapes, and bars over 3/8 inch in thickness shall be steel die stamped with the appropriate classification (see l. 2) and with the letters “AB“. (b) Plates 3/8 inch and .less in thickness shall be stencilled with. the appropriate classification (see 1.2). (c)

39、 Shapes and bars less than 3/8 inch in thickness shall be iden- tified by stencilling or tagging, depending on the available surface area. The specification number shall be included on each plate, shape, 0.r bar. For materials over 3/8 inch in thickness, the specification number shall be stamped or

40、stencilled. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for inspection. Unless otherwise specified in the contract or purchase order, the contractor is responsible for the performance of all inspection requirements as specified herein. Except as otherwise speci- fied in the contract or purcha

41、se order, the contractor may use his own or any other facilities suitable for the performance of the inspection requirements specified herein, unless disapproved by the Government. The Government reserves the right to perform any of the inspections set forth in the specification where such inspectio

42、ns are deemed necessary to assure supplies and services conform to prescribed requirements. 4.1.1 Responsibility for compliance. All items must meet all requirements of sections 3 and 5. The inspection set forth in this specification shall become a part of the contractors overall inspection system o

43、r quality program. The absence of any inspection requirements in the specification shall not relieve the contractor of the responsibility of assuring that all products or supplies sub- mitted to the Government for acceptance comply with all requirements of the con- tract. Sampling in quality conform

44、ance does not authorize submission of known defective material, either indicated or actual, nor does it commit the Government to acceptance of defective material. 4.1.2 Certification of quality conformance. When specified in the contract or order, certification data for level 1 material shall be pre

45、pared (see 6.2.2 and appendix C). 4.2 Classification of inspections. The inspection requirements specified herein are classified as follows: (a) First article inspection (see 4.3). (b) Quality conformance inspection (see 4.4). 4.3 First article inspection. First article inspection shall be conducted

46、 in accordance with section 43 of the ABS Rules which requires data in support of mechanical properties, weldability, and compliance with the rules when new or 7 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-special steel or production methods are

47、proposed or when new steel mills begin production. Approval by ABS to produce a particular grade of ABS steel also approves the facility to produce the same grade of steel to this specification. 4.3.1 First article inspection report. When specified in the contract or order, a first article inspectio

48、n procedure and report shall be prepared (see 6.2.2). 4.3.2 First article inspection of Z grades. First artjcle inspectio? shall be performed on each type and thickness range of Z and TZ grades of steel to approve any contractor who has not previously supplied these grades to this speci- fication. F

49、irst article inspection shall include all tests specified in section 43 of the ABS Rules and the additional tests specified in 4.3.2.1 through 4.3.2.3. Thickness ranges shall be up to 1 inch (25 mm), over 1 inch (25 mm) to 2 inches (51 mm), over 2 inches (51 mm) to 4 inches (102 mm), and over 4 inches (102 mm) to 6 inches (152 mm). First article inspection will be verified by the ABS surveyor. 4,3.2.1 Tensile tests. Tensile tests s