NAVY MIL-E-24355 B (1)-1987 ELECTRODES WELDING BARE SOLID NICKEL-MANGANESE-CHROMIUM-MOLYBDENUM ALLOY STEEL FOR PRODUCING HY-130 WELDMENTS FOR AS-WELDED APPLICATIONS《为制造HY-130焊接应用无遮.pdf

《NAVY MIL-E-24355 B (1)-1987 ELECTRODES WELDING BARE SOLID NICKEL-MANGANESE-CHROMIUM-MOLYBDENUM ALLOY STEEL FOR PRODUCING HY-130 WELDMENTS FOR AS-WELDED APPLICATIONS《为制造HY-130焊接应用无遮.pdf》由会员分享，可在线阅读，更多相关《NAVY MIL-E-24355 B (1)-1987 ELECTRODES WELDING BARE SOLID NICKEL-MANGANESE-CHROMIUM-MOLYBDENUM ALLOY STEEL FOR PRODUCING HY-130 WELDMENTS FOR AS-WELDED APPLICATIONS《为制造HY-130焊接应用无遮.pdf（1页珍藏版）》请在麦多课文档分享上搜索。

1、N-Q3-iB MIL-E-24355B(SH) AMENDMENT 1 26 March 1987 Figure number 2 3 MILITARY SPECIFICATION Preheat and interpass Heat input temperature (joules per (OF) inch) 275 to 300 40,000 to 45,000 150 to 175 25,000 to 30,000 ELECTRODES, WELDING, BARE, SOLID, NICKEL-MANGANESE- CHROMIUM-MOLYBDENUM ALLOY STEEL

2、FOR PRODUCING HY-130 WELDMENTS FOR AS-WELDED APPLICATIONS This amendment forms a part of MIL-E-24355B(SH), dated 16 April 1982, and is approved for use by all Departments and Agencies of the Depart- ment of Defense. PAGE 14 Table X: Delete and substitute: “TABLE X. Cooling rate parameters. Type MIL-

3、140s-1 Nominal weld- ment plate thickness (inch) 1 Cooling rate Low High Preparing activity: Navy - SH ( Pro j e c t 3 4 3 9 -N 6 4 5 ) AMSC NIA FSC 3439 DISTRIBUTION STATEMENT A Approved for public re-lease; distributipn unlimited ,- -. THIS DOCUMENT CONTAINS PAGES. -_ _ . fl - -_ - - Il Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-