FORD WSS-M2F156-B2-2009 FABRIC VINYL COATED (PVC) CAST EXPANDED TO BE USED WITH FORD WSS-M99P1111-A 《铸件 延展料用乙烯基涂层（PVC）织物 与标准FORD WSS-M99P1111-A一起使用 ［使用 FORD WSS-M2F156-B FORD W.pdf

《FORD WSS-M2F156-B2-2009 FABRIC VINYL COATED (PVC) CAST EXPANDED TO BE USED WITH FORD WSS-M99P1111-A 《铸件 延展料用乙烯基涂层（PVC）织物 与标准FORD WSS-M99P1111-A一起使用 ［使用 FORD WSS-M2F156-B FORD W.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M2F156-B2-2009 FABRIC VINYL COATED (PVC) CAST EXPANDED TO BE USED WITH FORD WSS-M99P1111-A 《铸件 延展料用乙烯基涂层（PVC）织物 与标准FORD WSS-M99P1111-A一起使用 ［使用 FORD WSS-M2F156-B FORD W.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 06 03 N-STATUS Replaced by WSS-M2F156-B and added 2.1 M. Dumitrescu, NA 2005 08 09 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1 of 3 FABRIC, VINYL COATED (PVC) CAST/EXPANDED

2、WSS-M2F156-B2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a laminate consisting of a top solid vinyl film, an expanded vinyl layer, a texturized polyester fabric, and coated with a non-chalking topcoat finish. 2. APPLICATION This specification was released or

3、iginally for material used in interior trim as a front seat side facing/seat back and as a covering for automotive seat cushions and backs for second/third row seat of Escape. Any other application requires new qualification 2.1 LIMITATIONS This specification categorizes lower weight vinyl. This mat

4、erial is NOT to be used for class A surfaces or outboard side facing due to reduced wear resistance. For seats, this material can only be used for seat backs, inboard side facings and head rests. 3. REQUIREMENTS In addition to the requirements listed herein, this material shall meet all requirements

5、 of the WSB-M8P3-C, PERFORMANCE, FLEXIBLE POLYMERIC FILM, INTERIOR QUALITY material performance specification. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 AP

6、PEARANCE (FLTM BI 109-01) The color, pattern, gloss level and finish shall match the approved Corporate Design master sample, or shall be as specified on the engineering drawing. 3.3 BACKING FABRIC The backing fabric shall be knitted from a good grade of polyester yarn Circular knit fabric 100% Poly

7、ester Yarn size 167dtex/f48 Yarn count ENGINEERING MATERIAL SPECIFICATIONWSS-M2F156-B2 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 3 Warp 120/100mm Fill 120/100mm Weight g/m2125 +/- 10 3.4 VINYL COATED FABRIC WEIGHT, g/m2(ASTM D 751, sample method) 664 +/-

8、 40 3.5 RESISTANCE TO TEAR (Trapezoid), N, min (ASTM D 5733, Integration Method*) LSL Warp 115 (145 average) Fill 100 (125 average) *As approved by the Materials Engineering Activity. 3.6 BREAKING STRENGTH, N, min (ASTM D 751, grab method) LSL Warp 500 (550 average) Fill 500 (550 average) The vinyl

9、coating shall not fail before the specified minimum breaking values are obtained. 3.7 SEAM STRENGTH, N, min (FLTM BN 119-01, except use lockstitch with 6 stiches/25 mm, 5 sample average in each direction.) LSL Warp 460 (560 average) Fill 570 (640 average) 3.8 ADHESION OF VINYL FILM TO BACKING FABRIC

10、, N/25 mm, width min (ISO 2411, standard method, 300 mm/minute) LSL Warp 15.3 (32.8 average) Fill 13.1 (21.9 average) 3.9 STRETCH AND SET, %, range (SAE J885) Stretch Set LSL USL Warp 20 60 0 10 of warp stretch Fill 20 60 0 10 of fill stretch ENGINEERING MATERIAL SPECIFICATIONWSS-M2F156-B2 Printed c

11、opies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 3 of 3 3.10 STIFFNESS, max (ASTM D 747, direct reading at 60 angle with a 0.01 N-m moment weight) USL Warp 8 (9 average) Fill 11 (13.0 average) 3.11 ABRASION RESISTANCE (FLTM BN 108-02, CS-10 wheels, 1000 cycles, 1000 g load)

12、The abraded area must exhibit compatible color and appearance with the adjacent unabraded area. The abrasion resistance of production material shall be equal to or better than the master sample approved by the Materials Engineering Activity. 3.12 SEAM FATIGUE RESISTANCE, max (FLTM BN 106-02) Needle hole length after test. 3.0 mm 3.13 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 RECYCLING CODE PVC+PET