FORD WSS-M11G46-A-2009 DECORATIVE WOOD VENEER MAN-MADE FROM OBECHE- TRIPLOCHITON SCLEROXYLON FINE LINE EBONY PATTERN JAGUAR LAND ROVER ONLY TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD WSS-M11G46-A-2009 DECORATIVE WOOD VENEER MAN-MADE FROM OBECHE- TRIPLOCHITON SCLEROXYLON FINE LINE EBONY PATTERN JAGUAR LAND ROVER ONLY TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M11G46-A-2009 DECORATIVE WOOD VENEER MAN-MADE FROM OBECHE- TRIPLOCHITON SCLEROXYLON FINE LINE EBONY PATTERN JAGUAR LAND ROVER ONLY TO BE USED WITH FORD WSS-M99P1111-A .pdf（1页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 04 21 Activated A. Knell Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1 of 1 DECORATIVE WOOD VENEER, MAN-MADE FROM WSS-M11G46-A OBECHE- TRIPLOCHITON SCLEROXYLON, “FINE LINE EBONY“ PATTERN, JAGUAR LAND

2、 ROVER ONLY 1. SCOPE This specification defines man-made wood veneers, produced by a double-cut process, for use as decorative product on interior wood veneer assemblies. A = Man Made Veneer “Fine Line Ebony“ pattern, made from OBECHE- TRIPLOCHITON SCLEROXYLON. 2. APPLICATION This specification was

3、released for materials used for wooden decorative automotive components. Application of lacquer and other products will need to be considered to provide a suitable finished product. 3. REQUIREMENTS Material specification requirements are to be used for initial qualification of materials. When in the

4、 fully assembled form the veneer assembly must comply with the Material specification requirements as specified on the engineering drawing. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Mater

5、ials (WSS-M99P1111-A). 3.2 MATERIAL PROPERTIES 3.2.1 Appearance Color, feature and grain to be as per Master samples 3.2.2 Thickness Nominal thickness - 0.6mm 3.2.3 Moisture content 11 - 18% 3.2.4 Density 600 +/- 50 k/gm33.3 PERFORMANCE PROPERTIES Veneer selected for its attractive appearance should be uniform in thickness, smooth, flat, free from decay and have face grain suitable for the intended face grade.