FORD WSB-M1C245-A-2008 GREASE SYNTHETIC HYDROCARBON INORGANICALLY GELLED NLGI 2 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI 2无机凝胶状的合成烃润滑脂 与标准FORD WSS-M99P1111-A一起使用 [使用 FORD WSS-.pdf

《FORD WSB-M1C245-A-2008 GREASE SYNTHETIC HYDROCARBON INORGANICALLY GELLED NLGI 2 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI 2无机凝胶状的合成烃润滑脂 与标准FORD WSS-M99P1111-A一起使用 [使用 FORD WSS-.pdf》由会员分享，可在线阅读，更多相关《FORD WSB-M1C245-A-2008 GREASE SYNTHETIC HYDROCARBON INORGANICALLY GELLED NLGI 2 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI 2无机凝胶状的合成烃润滑脂 与标准FORD WSS-M99P1111-A一起使用 [使用 FORD WSS-.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 10 15 N-STATUS Replaced by WSS-M13P12-A L. Schmalz, FNA 2004 04 30 Revised Para 3.0 inserted; para 3.1, 3.2, 3.3, 3.6 & 4 deleted 1993 11 30 Released NB00I10043054299 J. M. Showalter Printed copies are uncontrolled Copyright 2008, Ford Gl

2、obal Technologies, LLC Page 1 of 5 GREASE, SYNTHETIC HYDROCARBON, WSB-M1C245-A INORGANICALLY GELLED, NLGI 2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is an inorganically gelled, nonmelting, noncorrosive, shear stable, NLGI 2 grease based on a synthetic hydroca

3、rbon oil. The lubricant operating temperature range is -40 to 121 C. 2. APPLICATION This specification was released originally to lubricate the electrical light switch rheostat-resistor assembly. Note: This grease shall be formulated so that it will not stain or soften painted exterior or interior a

4、utomotive finishes, when evaluated according to FLTM BJ 126-01. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Materials suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 Initial Qualifications The sup

5、plier must furnish to the affected Materials Engineering activity a completed and certified copy of the attached Supplement A and test reports demonstrating the capability of the process for the listed critical properties. 3.1.2 Ongoing verification Plan In addition to the control plan, the supplier

6、 and affected Materials Engineering activity shall establish a mutually agreed upon ongoing product verification plan which will be listed on Supplement B. 3.4 CONSISTENCY Material shall be a smooth homogenous product free from abrasive particles, it shall be consistent in color and texture, and fre

7、e from objectionable odors during normal storage. It shall be suitable for the intended application. 3.5 FUNCTIONAL APPROVAL Materials being evaluated for approval to this specification shall be subjected to a production trial. Functional trial results must be approved by the affected assembly opera

8、tion and Design Engineering. Results shall be made available to Materials Engineering prior to material approval and release. ENGINEERING MATERIAL SPECIFICATIONWSB-M1C245-APrinted copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 5 5. GENERAL INFORMATION The information

9、 below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 TYPICAL PROPERTIES The information shown is to provide data on products which have been qualified to this specification. The values shown do not constitute part of the requirements for initial

10、qualification. 5.1.1 Color Clear to yellow 5.1.2 Appearance Smooth 5.1.3 Evaporation at 100 C 0.59% (ASTM D 972, 24 h) 5.1.4 Oil Separation 1.53 wt % (ASTM D 1742, 24 h) 5.1.5 Penetration (ASTM D 217) Unworked 266 After 60 strokes 265 - 295 5.1.6 Dropping Point, min 260 C (ASTM D 2265) 5.1.7 Oxidati

11、on Stability, max 20 kPa (ASTM D 942, 168 h) 5.2 SUPPLEMENT C This is to be used for additional information required for initial qualification. ENGINEERING MATERIAL SPECIFICATIONWSB-M1C245-APrinted copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 3 of 5 Supplement A INITIAL

12、 QUALIFICATION Supplier_ Date_ Product Name_ NLGI Grade_ Product Code_ Batch No._ Manufacturing Plant Location(s)_ Test Results Mfg. Limits Physical/Chemical/Performance Properties (Mean, Std. Dev., (of 99.994% Sample Size) of Production) Base Oil Viscosity at 100 C mm2/s ASTM D 445 _ _ Viscosity at

13、 40 C mm2/s ASTM D 445 _ _ Viscosity at -40 C mPa.s ASTM D 2983 _ _ Viscosity Index ASTM D 2270 _ _ Flash Point,C ASTM D 92/IP 36/84 _ _ Pour Point,C ASTM D 97 _ _ Specific Gravity ASTM D 1298 _ _ ASTM D 4052 _ _ Grease _ _ Penetration mm/10 ASTM D 217 _ _ Worked after 60 strokes _ _ Worked after 10

14、0,000 strokes _ _ Moisture Content % ASTM D 95 _ _ Soap Content % FLTM AJ 106-02 _ _ Water Washout at 38 C ASTM D 1264 _ _ Dropping Point ASTM D 566 _ _ Oxidation Stability FLTM BJ 113-02 _ _ Pressure Drop After 100 Hours Oil Separation % ASTM D 1742 _ _ Copper Strip Corrosion ASTM D 130 _ _ Specifi

15、c Gravity ASTM D 4052 _ _ Four Ball OK Load ASTM D 2266 _ _ Corrosion IP 220 (DIN 51802) _ _ Refractive Index ASTM D 1218 _ _ Evaporation, 24 h, 150 C ASTM D 972 _ _ Others (Elementals etc) Signature_ Title_ MATERIAL ENGINEERING CONCURRENCE_ ENGINEERING MATERIAL SPECIFICATIONWSB-M1C245-APrinted copi

16、es are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 4 of 5 Supplement B ONGOING PRODUCT VERIFICATION PLAN Supplier_ Date_ Product Name_ NLGI Grade_ Product Code_ Batch No._ Manufacturing Plant Location(s)_ Approved Physical/Chemical/Performance Properties Manufacturing Sample Size

17、/Limits Frequency Penetration after ASTM D 217 _ _ 60 strokes 100,000 strokes _ _ Four Ball, OK load ASTM D 2266 _ _ Timken, OK load ASTM D 2509 _ _ Wheel Bearing Leakage ASTM D 1263 mod. _ _ Oil Separation ASTM D 1742 _ _ Dropping Point ASTM D 566 _ _ Oxidation Stability ASTM D 942 _ _ Pressure Dro

18、p After 1,000 hours Water Washout at ASTM D 1264 At 38 C _ _ At 80 C _ _ Corrosion IP 220 (DIN 51802) _ _ Low Temperature Properties Low Temperature Torque IP 186 at -30 C _ _ or Flow Pressure at -30 C DIN 51805 _ _ Remarks_ _ SUPPLIER SIGNATURE_ TITLE_ MATERIAL ENGINEERING CONCURRENCE_ ENGINEERING

19、MATERIAL SPECIFICATIONWSB-M1C245-APrinted copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 5 of 5 Supplement C Supplier_ Date_ Product Name_ NLGI Grade_ Product Code_ Manufacturing Plant Location(s)_ BASE OIL Manufacturing Limits Nominal Viscosity Range, mm2/s Type Vol. % 1

20、00 C 40 C A _ _ _ _ B _ _ _ _ C _ _ _ _ D _ _ _ _ Thickener Filler/Structure Modifier/Solid Lubricant Supplier Type/Function Name Code Description A _ _ _ _ B _ _ _ _ C _ _ _ _ D _ _ _ _ E _ _ _ _ Additives Carrier Additive Type/ Supplier /Type in Final Function Name Code Description % Product % A _ _ _ B _ _ _ C _ _ _ D _ _ _ Signature_ Title_