《EN ISO 9539-2010 en Gas welding equipment - Materials for equipment used in gas welding cutting and allied processes (Incorporates Amendment A1 2013)《气焊设备 气体焊接 切割和相关工艺过程用设备的材料［代替 C.pdf》由会员分享，可在线阅读，更多相关《EN ISO 9539-2010 en Gas welding equipment - Materials for equipment used in gas welding cutting and allied processes (Incorporates Amendment A1 2013)《气焊设备 气体焊接 切割和相关工艺过程用设备的材料［代替 C.pdf（10页珍藏版）》请在麦多课文档分享上搜索。

1、BS EN ISO9539:2010ICS 25.160.20; 25.160.30NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBRITISH STANDARDGas welding equipment Materials forequipment used in gaswelding, cutting andallied processes (ISO9539:2010)BS EN ISO 9539:2010 +A1:2013BS EN ISO 9539:2010+A1:2013ISBN 978 0

2、 580 78105 6Amendments/corrigenda issued since publicationDate Comments28 February 2014 Implementation of ISO amendment 1:2013 with CEN endorsement A1:2013This British Standard was published under the authority of the Standards Policy and Strategy Committee on 28 February 2010 The British Standards

3、Institution 2014. Published by BSI Standards Limited 2014National forewordThis British Standard is the UK implementation of EN ISO 9539:2010+A1:2013. It is identical to ISO 9539:2010, incorporating amendment 1:2013. It supersedes BS EN ISO 9539:2010, which is withdrawn.The start and finish of text i

4、ntroduced or altered by amendment is indicated in the text by tags. Tags indicating changes to ISO text carry the number of the ISO amendment. For example, text altered by ISO amendment 1 is indicated by .The UK participation in its preparation was entrusted to Technical Committee WEE/18, Gas weldin

5、g and cutting appliances.A list of organizations represented on this committee can be obtained on request to its secretary.The publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application.Compliance with a British Standard cann

6、ot confer immunity from legal obligations.EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 9539 January 2010 ICS 25.160.20 Supersedes EN 29539:1992English Version Gas welding equipment - Materials for equipment used in gas welding, cutting and allied processes (ISO 9539:2010) Matriel de soud

7、age aux gaz - Matriaux utiliss pour le matriel de soudage aux gaz, coupage et techniques connexes (ISO 9539:2010) Gasschweigerte - Werkstoffe fr Gerte fr Einrichtungen zum Gasschweien, Schneiden und verwandte Prozesse (ISO 9539:2010) This European Standard was approved by CEN on 9 January 2010. CEN

8、members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on appli

9、cation to the CEN Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN Management Centre h

10、as the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway,

11、Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2010 CEN All rights of exploitation in any form and

12、by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 9539:2010: EEN ISO 9539:2010+A1December 2013BS EN ISO 9539:2010EN ISO 9539:2010 (E) 3 Foreword This document (EN ISO 9539:2010) has been prepared by Technical Committee ISO/TC 44 “Welding and allied processes“ in collaboration

13、 with Technical Committee CEN/TC 121 “Welding”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by July 2010, and conflicting national standards shall be with

14、drawn at the latest by July 2010. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 29539:1992. According to

15、 the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Lat

16、via, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. Endorsement notice The text of ISO 9539:2010 has been approved by CEN as a EN ISO 9539:2010 without any modification. iiBS EN ISO 9539:2010+A1:201

17、3EN ISO 9539:2010+A1:2013 (E)EN ISO 9539:2010/A1:2013 (E) 3 Foreword This document (EN ISO 9539:2010/A1:2013) has been prepared by Technical Committee ISO/TC 44 “Welding and allied processes” in collaboration with Technical Committee CEN/TC 121 “Welding” the secretariat of which is held by DIN. This

18、 Amendment to the European Standard EN ISO 9539:2010 shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by June 2014, and conflicting national standards shall be withdrawn at the latest by June 2014. Attention is drawn to the

19、 possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countr

20、ies are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Pola

21、nd, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. Endorsement notice The text of ISO 9539:2010/AMD 1:2013 has been approved by CEN as EN ISO 9539:2010/A1:2013 without any modification. Foreword to amendment A1BS EN ISO 9539:2010INTERNATIONAL STANDA

22、RD ISO 9539:2010(E) ISO 2010 All rights reserved 1Gas welding equipment Materials for equipment used in gas welding, cutting and allied processes 1 Scope This International Standard specifies the general, and some of the special, requirements on materials used for the construction of equipment used

23、in gas welding, cutting and allied processes. Additional requirements on materials for some equipment are given in other standards. This International Standard is not applicable to materials used for the construction of welding hoses which are specified in ISO 3821. 2 Normative references The follow

24、ing referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 554, Standard atmospheres for conditioning and/or testi

25、ng Specifications ISO 1817, Rubber, vulcanized Determination of the effect of liquids 3 General requirements Materials liable to come into contact with the process gases shall be resistant to the chemical, mechanical and thermal action of these gases under all operating conditions (see for example I

26、SO 11114-1 and ISO 11114-2). The properties of the materials shall be such that the function for which they are intended can be performed correctly within the temperature range of 20 C to +60 C. Where dissimilar materials are in direct contact, steps shall be taken to prevent corrosion. 4 Specific r

27、equirements 4.1 Metallic materials 4.1.1 For use with acetylene and gases with similar chemical properties Because of the risk of forming explosive acetylides, the copper content of materials liable to come into contact with such gases shall not exceed 70 % (mass fraction). The manufacturer shall no

28、t use any procedure resulting in copper enrichment of the surface. Nozzles and necks of blowpipes are an exception to this requirement. NOTE International and national regulations may require different maximum copper contents than those specified here, but these remain generally within this range. T

29、he likelihood of the formation of copper acetylides depends on metallic corrosion and contamination which can be caused by many factors, e.g. moisture. ISO 9539:2010+A1:2013 (E)BS EN ISO 9539:2010+A1:2013 ISO 2010 All rights reservedISO 1817, Rubber, vulcanized or thermoplastic Determination of the

30、effect of liquidsBS EN ISO 9539:2010ISO 9539:2010(E) 2 ISO 2010 All rights reservedMetal flame-arresting elements (including sintered metal elements) shall be manufactured from copper-free materials. Where brazing alloys containing silver and copper are used, the silver content shall not exceed 46 %

31、 (mass fraction) and the copper content shall not exceed 37 % (mass fraction). The brazing connection shall be designed and completed in such a way that, as far as practicable, the area where acetylene is liable to come into contact with the brazing alloy will be small and all residues of flux will

32、be removed. 4.1.2 For use with oxygen Metallic materials for components intended to be used with oxygen shall be selected according to their resistance to ignition and the release of ignition energy. NOTE 1 Materials that burn in air will burn violently in pure oxygen, and many materials that do not

33、 burn in air will do so in pure oxygen, particularly under pressure. Similarly, materials that can be ignited in air require less energy to ignite in oxygen. Many such materials can be ignited by friction at a valve seat or stem packing or by adiabatic compression produced when oxygen at high pressu

34、re is rapidly introduced into a system initially at low pressure. Aluminium or aluminium alloys shall not be used for components whose surfaces come into contact with oxygen at a working pressure greater than 30 bar, except aluminium sealing washers for pressure gauges. Materials for filters whose s

35、urfaces come into contact with gas at cylinder pressure shall be non-inflammable under the conditions of use. The selection of the material of the filter is particularly important to reduce the probability of ignition. Springs and other moving parts liable to come into contact with oxygen shall be m

36、ade of materials that resist oxidation and they shall not be coated. NOTE 2 Plating could come off. All components in contact with oxygen shall be subjected to appropriate cleaning procedures so that their surfaces do not exceed the following hydrocarbon contamination levels: a) for applications in

37、the pressure range of 50 kPa to 3 000 kPa: no greater than 550 mg/m2; b) for applications at a pressure greater than 3 000 kPa: no greater than 220 mg/m2and no particles of size 100 m. These requirements shall be met by using either an appropriate method of manufacture or an appropriate cleaning pro

38、cedure. Compliance shall be checked either by verification of the cleanliness of the components or by validation of the cleaning procedure or the manufacturing process. NOTE 3 ISO 15001 provides guidance on suitable cleaning procedures. 4.2 Non-metallic materials 4.2.1 Resistance to solvents for non

39、-metallic materials in contact with fuel gases Non-metallic materials (e.g. those used for seals and lubricants) liable to come into contact with acetylene shall be adequately resistant to the solvents acetone and dimethylformamide (DMF). Non-metallic materials (e.g. those used for seals and lubrica

40、nts) liable to come into contact with propane, butane and methylacetylene-propadiene mixtures shall be adequately resistant to n-pentane. BS EN ISO 9539:2010+A1:2013ISO 9539:2010+A1:2013 (E)2 ISO 2010 All rights reservedNon-metallic materials (e.g. those used for seals and lubricants) liable to come

41、 into contact with acetylene shall be adequately resistant individually to acetone and dimethylformamide (DMF) solvents.Non-metallic materials (e.g. those used for seals and lubricants) liable to come into contact with propane, butane and methylacetylene-propadiene mixtures shall be adequately resis

42、tant to n-pentane.For the purposes of this International Standard, the term “adequate resistance” (to solvents) will be taken to mean that the material shall fulfill the following conditions.BS EN ISO 9539:2010ISO 9539:2010(E) ISO 2010 All rights reserved 3For the purposes of this International Stan

43、dard, the term “adequate resistance” (to solvents) will be taken to mean that the material shall fulfil the following conditions. a) The change in mass (resistance to swelling) shall not exceed 15 % and the change in hardness shall not exceed 15 IRHD after the material has been stored under the foll

44、owing conditions: (168 2) h (i.e. 7 d) in an atmosphere saturated with solvent vapour (acetone and DMF) or in liquid (n-pentane) at (23 2) C. b) A subsequent period in air for (70 2) h at (40 2) C. c) (24 2) h at standard atmosphere 23/50 as specified in ISO 554. These tests shall be carried out in

45、accordance with ISO 1817. 4.2.2 Resistance to oxygen 4.2.2.1 Resistance to ignition Ignition resistance in oxygen of non-metallic materials and lubricants shall have been established by an appropriate test procedure. NOTE This test is described in several standards, e.g. ISO 11114-3. 4.2.2.2 Resista

46、nce to ageing Non-metallic sealing materials for use with air and oxygen shall be capable of withstanding an ageing sensitivity test (e.g. ISO 2440). 4.2.2.3 Cleanliness and lubricants All components in contact with oxygen shall be free from substances that may react violently with oxygen under norm

47、al operating conditions, e.g. hydrocarbon-based solvents, oils, greases and detergents. Only lubricants suitable for use in oxygen at maximum operating pressure and temperature shall be used. BS EN ISO 9539:2010+A1:2013ISO 9539:2010+A1:2013 (E)3 ISO 2010 All rights reservedThe change in mass shall n

48、ot exceed 15 % and the change in hardness shall not exceed 15 IRHD after the material has been conditioned as follows:a) (168 2) h in an atmosphere saturated with solvent as specified above at (23 2) C;b) a subsequent period in air for (70 2) h at (40 2) C;c) a subsequent period (24 2) h at standard

49、 atmosphere 23/50 as specified in ISO 554.The measurement of change of mass and hardness shall be carried out after test step c) in accordance with ISO 1817.BS EN ISO 9539:2010ISO 9539:2010(E) 4 ISO 2010 All rights reservedBibliography 1 ISO 2440, Flexible and rigid cellular polymeric materials Accelerated ageing tests 2 ISO 3821, Gas welding equipment Rubber hoses for welding, cutting and allied processes 3 ISO 11114-1, Transportable gas cylinders Compatibility of cylinder and valve mate