《ASTM D2714-1994(2014) Standard Test Method for Calibration and Operation of the Falex Block-on-Ring Friction and Wear Testing Machine《环块摩擦试验机和磨损试验机校准和操作的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D2714-1994(2014) Standard Test Method for Calibration and Operation of the Falex Block-on-Ring Friction and Wear Testing Machine《环块摩擦试验机和磨损试验机校准和操作的标准试验方法》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D2714 94 (Reapproved 2014)Standard Test Method forCalibration and Operation of the Falex Block-on-RingFriction and Wear Testing Machine1This standard is issued under the fixed designation D2714; the number immediately following the designation indicates the year oforiginal adoption or,

2、in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scop

3、e1.1 This test method covers the calibration and operation ofa block-on-ring friction and wear testing machine.1.2 The values in SI units are to be regarded as standard.The values given in parentheses are mathematical conversionsto SI units that are provided for information only.1.3 This standard do

4、es not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Terminology2.1 Definitions:2.1.1

5、 coeffcient of friction, or fin tribology, the dimen-sionless ratio of the friction force (F) between two bodies to thenormal force (N) pressing these two bodies together. or f 5 F/N! (1)2.1.1.1 DiscussionA distinction is often made betweenstatic coeffcient of friction and kinetic coeffcient of fric

6、tion.2.1.2 friction forcethe resisting force tangential to theinterface between two bodies when, under the action of anexternal force, one body moves or tends to move relative to theother.2.1.3 kinetic coeffcient of frictionthe coefficient of fric-tion under conditions of macroscopic relative motion

7、 betweentwo bodies.2.1.4 weardamage to a solid surface, generally involvingprogressive loss of material, due to relative motion betweenthat surface and a contacting substance or substances.3. Summary of Test Method3.1 The test machine is operated using a steel test ringrotating against a steel test

8、block, the specimen assembly beingpartially immersed in the lubricant sample. The velocity of thetest ring is 7.9 6 0.16 m/min (26 6 0.52 ft/min) which isequivalent to a spindle speed of 72 6 1 rpm. The specimens aresubjected to 68 kg (150 lb) normal load applied by 6.8 kg(15 lb) of dead weight on t

9、he 10:1 ratio lever system. Testduration is 5000 cycles.3.2 Three determinations are made: (1) The friction forceafter a certain number of revolutions, (2) the average width ofthe wear scar on the stationary block at the end of the test, and(3) the weight loss for the stationary block at the end of

10、the test.4. Significance and Use4.1 This test method is used for the calibration of ablock-on-ring testing machine by measuring the friction andwear properties of a calibration fluid under the prescribed testconditions.4.2 The user of this test method should determine to his orher own satisfaction w

11、hether results of this test procedurecorrelate with field performance or other bench test machines.If the test conditions are changed, wear values can change andrelative ratings of fluids can be different.5. Apparatus5.1 Falex Block-on-Ring Test Machine,2shown in Fig. 1and Fig. 2 and described in de

12、tail in Annex A1.NOTE 1Consult the instruction manual for each machine to determinerespective capabilities and limitations.5.2 Analytical Balance, capable of weighing to the nearest0.1 mg.5.3 Measuring Magnifier Glass, with SI or inch-poundcalibration so that the scar width can be measured with apre

13、cision of 0.01 mm, or equivalent.1This test method is under the jurisdiction of ASTM Committee D02 onPetroleum Products, Liquid Fuels, and Lubricants and is the direct responsibility ofSubcommittee D02.L0.05 on Solid Lubricants.This test method was prepared under the joint sponsorship of the America

14、nSociety of Lubrication Engineers with the cooperation of the Coordinating ResearchCouncil, Inc. (CRC) Aviation Committee on Bonded Solid-Film Lubricants.Accepted by ASLE September 1968.Current edition approved May 1, 2014. Published July 2014. Originally approvedin 1968. Last previous edition appro

15、ved in 2009 as D271494(2009). DOI:10.1520/D2714-94R14.2Trademarked and manufactured by Falex Corp., 1020 Airpark Dr., SugarGrove, IL 60554.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States16. Reagents and Materials6.1 Test Rings, Falex

16、Type S-10,2SAE 4620 carburizedsteel, having a hardness of 58 to 63 HRC. The test ring has awidth of 8.15 mm (0.321 in.), a diameter of 35 mm (1.3775 in.)and a maximum radial run out of 0.013 mm (0.0005 in.). Thesurface roughness shall be 0.15 to 0.30 m (6 to 12 in.) rms.6.2 Test Blocks, Falex Type H

17、-30,2SAE 013tool steelhaving two ground test surfaces of 0.10 to 0.20 m (4 to 8 in.)rms. The test block has a test surface width of 6.35 mm(0.250 in.) and a length of 15.76 mm (0.620 in.). The test blockhas a hardness of 27 to 33 HRC.6.3 Solvents, safe, nonfilming, nonchlorinated.NOTE 2Each user sho

18、uld select a solvent that can meet the applicablesafety standards and still thoroughly clean the parts.6.4 Calibration Fluid, consisting of white mineral oil con-forming to U. S. Pharmacopeia XVII, p. 399, and with aviscosity at 37.8C (100F) of 63 to 65 cSt.7. Preparation of Apparatus7.1 Before each

19、 test, thoroughly clean the specimen holderand chamber as well as the tapered section, threaded section,lock nut, lock washer, a new test ring and block using solventsselected in 6.3.7.2 Weigh each test ring and test block to the nearest 0.1 mgon the analytical balance. Then store the specimens in a

20、desiccator until ready for use.7.3 Place the block holder on the block and carefully placeblock and holder in upper specimen holder in test chamber.Mount the test ring on the test shaft, taking care not to touchthe test area. Tighten the test ring on the shaft with 440 N(100 lbf) as measured on the

21、friction force meter on the digitalinstrument unit.7.4 Place the heater door in position and fill the chamberwith test fluid to about halfway on the spindle (half of the testring is immersed). This volume must be measured (approxi-mately 100 mL) and the same amount used for each test. Setthe tempera

22、ture control of the oil reservoir to 43.3C (110F).It is preferable to control the temperature of the liquid beingtested, but if the machine is not equipped with a temperaturecontroller indicator, then record the liquid temperature.8. Calibration8.1 A machine shall be judged to be in acceptable condi

23、tionwhen the results obtained on the calibration fluid fall within thefollowing limits:8.1.1 Wear measurement is between 1.70 and 2.90 mm.8.1.2 Friction force after 4500 revolutions is between 66and 97 N (15.0 and 22.0 lbf).9. Procedure9.1 With the revolution counter set at zero, gently place a6.78-

24、kg (15-lb) load on the bale rod, being very careful toavoid shock-loading. When the fluid reaches temperature of43.3C (110F) start the machine and bring the speed to72 rpm. Record the friction force and the temperature of theliquid at 200, 400, 600, and 4500 revolutions and check thespeed at each of

25、 these times. Stop the machine at 5000revolutions. Remove the test block and test ring and clean themthoroughly using solvents selected in 6.3. Remove any excesswear particles that have accumulated on the side of the scar bybrushing with a camels hair brush; weigh the test ring and testblock to the

26、nearest 0.1 mg and measure the width of the wearscar of the test block at three points: in the center and 1 mmaway from each edge as shown in Fig. 3. Four tests are requiredto establish a satisfactory average.3SAE 01 is also known as Starrett 496 or Marshall Oil-crat.FIG. 1 Falex Block-On-Ring Varia

27、ble Drive Testing MachineFIG. 2 Falex Block-On-Ring Test Machine with MicroprocessorData Acquisition and Control SystemFIG. 3 Test Specimen Wear Scar MeasurementD2714 94 (2014)210. Calculation and Report10.1 Report the friction force at 200, 400, 600, and 4500revolutions, the weight loss for the tes

28、t block and test ring, andthe average wear scar width. Fig. 3.10.2 Calculate the coefficient of friction values from thefriction force value as follows:f 5 F/W (2)where:f = coefficient of friction,F = measured friction force, kg (lb), andW = normal load, kg (lb).11. Precision and Bias11.1 The follow

29、ing criteria should be used for judging theacceptability of results (95 % confidence):11.1.1 Wear Measurement:11.1.1.1 RepeatabilityThe difference between successivetest results, obtained by the same operator with the sameapparatus under constant operating conditions on identical testmaterial would,

30、 in the long run, and in the normal and correctoperation of the test method, exceed the following value onlyin one case in twenty:Repeatability 5 0.73 mm (3)11.1.1.2 ReproducibilityThe difference between two,single and independent results, obtained by different operatorsworking in different laborato

31、ries on identical test materialwould, in the long run, and in the normal and correct operationof the test method, exceed the following values only in onecase in twenty:Reproducibility 5 1.20 mm (4)11.1.2 Friction Force after 4500 Revolutions:11.1.2.1 RepeatabilityThe difference between successivetes

32、t results, obtained by the same operator with the sameapparatus under constant operating conditions on identical testmaterial would, in the long run, and in the normal and correctoperation of the test method, exceed the following values onlyin one case in twenty:Repeatability 5 29 N 6.6 lbf! (5)11.1

33、.2.2 ReproducibilityThe difference between two,single and independent results, obtained by different operatorsworking in different laboratories on identical test materialwould, in the long run, and in the normal and correct operationof the test method, exceed the following values only in onecase in

34、twenty:Reproducibility 5 31 N 7.0 lbf! (6)11.2 BiasSince there is no accepted reference materialsuitable for determining the bias for the procedure in TestMethod D2714 for measuring friction and wear, no statementon bias is being made.12. Keywords12.1 block-on-ring; coefficient of friction; friction

35、; wearANNEX(Mandatory Information)A1. DESCRIPTION OF THE FALEX BLOCK-ON-RING FRICTION AND WEAR TESTING MACHINEA1.1 A stationary rectangular test block is pressed with apredetermined load, maximum 584 kg (1300 lb), against arotating ring (Fig. A1.1). The load is accurately maintainedthroughout the te

36、st. Bearing pressures (average Hertz pres-sures) in the line contact area between the rectangular speci-men and the rotating ring can range up to 758 MN/m2(110 000 psi).A1.3 Resulting friction is indicated throughout the test by adigital indicator. A counter records the number of revolutionsof the t

37、est specimen. One criterion in the test is a preselectedmaximum for friction. For this purpose an automatic cutoff onthe friction indicator can be set for any preselected value offriction and the machine will shut off upon reaching it.A1.4 In a substitute method, a thermocouple is embedded inthe spe

38、cimen and a temperature recorder controller terminatesthe test when the temperature of the test block reaches apreviously set value.A1.5 The test shaft of the machine is supported by tworoller bearings, and the mandrel end of the shaft protrudesthrough the front panel of the machine where the test s

39、peci-mens are mounted. The test block, which is held stationaryagainst the revolving ring, is restrained from horizontal move-ment. The design of this block holder allows the test block toalign itself automatically in a manner prescribed by ASTMspecifications for compression-loaded specimens. This m

40、ain-tains uniform loading throughout the area of contact betweenthe specimens regardless of the force existing between them.A1.6 The normal force between the test specimens isproduced by hanging dead weights on the lower end of a leversystem that is designed in such a way as to allow the full valueo

41、f the friction force to be transmitted to the frictional load pickup device.A1.7 Speed ranges with variable speed control are availablefrom 0.5 to 7200 rpm. Fluid lubricants can be tested up to aD2714 94 (2014)3maximum of 204C (400F). With optional equipment, the testchamber can be pressurized to 1.

42、03 MPa (150 psi) run inspecial atmospheres or run in vacuum.A1.8 The friction force indicator is direct reading in poundsor kilograms and is fitted with an infinitely adjustable limitcontrol that allows the operator to preset the value of friction atwhich the machine will stop.A1.9 An electronic six

43、-digit cycle counter is mounted on thefront of the digital instrumentation unit. It is equipped with anautomatic cut-off.A1.10 A completely automated version is available incor-porating a computer interface to automatically control load,speed, temperature, and duration.ASTM International takes no po

44、sition respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibi

45、lity.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to A

46、STM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the addres

47、s shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 61

48、0-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ A1.1 Functional Diagram of the Falex Block-On-Ring Testing MachineD2714 94 (2014)4