ASTM C587-2004(2018) Standard Specification for Gypsum Veneer Plaster.pdf

《ASTM C587-2004(2018) Standard Specification for Gypsum Veneer Plaster.pdf》由会员分享，可在线阅读，更多相关《ASTM C587-2004(2018) Standard Specification for Gypsum Veneer Plaster.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C587 04 (Reapproved 2018)Standard Specification forGypsum Veneer Plaster1This standard is issued under the fixed designation C587; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in

2、parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This specification covers calcined gypsum mixed at themill

3、with other ingredients to control working quality andsetting time; specifically designed as a veneer plaster to beapplied over gypsum base for veneer plasters, masonry orconcrete surfaces to a maximum thickness of14 in. (6.4 mm)providing a surface ready for decoration.NOTE 1Specification C843 contai

4、ns application procedures for gyp-sum veneer plaster.1.2 This specification covers test methods for determiningthe physical properties of gypsum veneer plasters and sets forthminimum requirements that must be met.1.3 The values stated in inch-pound units are to be regardedas standard. The values giv

5、en in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.4 The text of this standard references notes and footnoteswhich provide explanatory material. These notes and footnotesshall not be considered as requirements of the stan

6、dard.1.5 The following safety hazards caveat applies only to theTest Methods portion, Section 5 of this specification: Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to establish appropriate sa

7、fety, health, andenvironmental practices and determine the applicability ofregulatory limitations prior to use.1.6 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of I

8、nternational Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2C11 Terminology Relating to Gypsum and Related BuildingMaterials and SystemsC473 Test Methods for Physical Testing of Gypsu

9、m PanelProductsC843 Specification for Application of Gypsum Veneer Plas-terC1396/C1396M Specification for Gypsum Board3. Terminology3.1 Definitions:3.1.1 Definitions of terms shall be in accordance withTerminology C11 and Specification C843.3.2 Definitions of Terms Specific to This Standard:3.2.1 gy

10、psum veneer plaster systems, nveneer plasterapplied in accordance with Specification C843 to gypsum basefor veneer plasters.4. Physical Properties4.1 Joint StrengthGypsum veneer plaster systems appliedin accordance with Specification C843 shall be tested inaccordance with 5.9. The breaking load shal

11、l be not less thanthe parallel to surfacing loads specified in Specification C1396/C1396M.4.2 Bond StrengthThe bond strength of the gypsum ve-neer plaster to the gypsum veneer base and, where applicable,between the base coat plaster and the finish coat shall notdelaminate when tested in accordance w

12、ith 5.6.4.3 Impact StrengthGypsum veneer plaster systems shallnot crack or lose bond beyond the impact area when tested inaccordance with 5.7.4.4 FlexureGypsum veneer plaster systems shall exhibitcrack resistance within the field of the gypsum base for veneerplasters such that radial or random crack

13、ing shall extend notmore than12 in. (13 mm) from the break line at failure when1This specification is under the jurisdiction of ASTM Committee C11 onGypsum and Related Building Materials and Systems and is the direct responsibilityof Subcommittee C11.01 on Specifications and Test Methods for Gypsum

14、Products.Current edition approved Oct. 1, 2018. Published October 2018. Originallyapproved in 1966. Last previous edition approved in 2014 as C587 04 (2014).DOI: 10.1520/C0587-04R18.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.o

15、rg. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesT

16、his international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade

17、(TBT) Committee.1tested in accordance with 5.8. At rupture of the panel theveneer plaster shall be securely bonded to the face paper.5. Test Methods5.1 MaterialsGypsum Base for Veneer Plaster, see Speci-fication C1396/C1396M.5.2 SamplingSample not less than 1 % of the packages,but not less than 5 pa

18、ckages. Select packages to be sampled atrandom. Take samples both from the outer portion and thecenter of each package. Thoroughly mix the materials soobtained to provide a composite sample of not less than 15 lb(6.8 kg). Place this composite sample immediately in a clean,dry, airtight container for

19、 delivery to the laboratory.5.3 Test Unit PreparationFrom the sample, prepare panelsof veneer plaster system and cut four 2 ft (600 mm) square, andthree 12 by 16 in. (300 by 400 mm) specimens.5.4 ConditioningCondition specimens to constant weightat a temperature of 85 6 15F (29.5 6 8.5C) and relativ

20、ehumidity of 50 6 2 % (see Note 2). Test specimens individu-ally after constant weight is reached.NOTE 2Laboratory test results indicate that conditioning temperaturesmay range from 70 to 100F (21 to 38C) without significantly affectingthe results. However, relative humidity is critical. Therefore,

21、specimensshall be tested within 10 min upon removal from the conditioningchamber.5.5 Number of TestsRun each test in triplicate.5.6 Bond Strength:5.6.1 Significance and UseThe bond strength test is de-signed to evaluate the bond of veneer plaster to veneer plasterbase and between the base coat and f

22、inish coat. The degree ofcorrelation between these test methods and service perfor-mance has not been determined.5.6.2 ProcedureSelect three 2 ft (600 mm) square speci-mens. Raise each specimen and slam the back side (face nottreated with veneer plaster) on a bare concrete floor repeatedlyuntil the

23、specimen is broken.5.6.3 ReportReport whether the sample passes or fails thebond test. The sample fails if the bond to the veneer base orbetween the finish coast and base coat delaminates on any oneof the specimens.5.6.4 Precision and BiasNo information is presentedabout either the precision or bias

24、 of the bond test since the testresult is nonquantitative.5.7 Impact Strength:5.7.1 Significance and UseThe impact strength is de-signed to test the effect of impact from a hard object on thesurface of the veneer plaster. The degree of correlation betweenthis test method and service performance has

25、not been deter-mined.5.7.2 Apparatus:5.7.2.1 A stand with a solid, flat base at least 2 ft (600 mm)square with a means of holding the steel ball and releasing itfrom a height of 36 in. above the base, without impartingadditional force.5.7.2.2 A12 in. (38 mm) diameter polished steel ball weigh-ing 7.

26、8 6 0.1 oz (221 6 3 g).5.7.3 ProcedureSelect one 2 ft (600 mm) square. Placethe specimen horizontally, with the plaster surface face up, onthe base of the apparatus . Drop the steel ball three times ontodifferent areas of the panel surface.5.7.4 ReportReport whether the sample passes or fails theimp

27、act test. The sample fails if there is a loss of bond orcracking beyond the impact area on any one of the drops.5.7.5 Precision and BiasNo information is presentedabout either the precision or bias of the impact test since thetest result is nonquantitative.5.8 Flexure:5.8.1 Significance and UseThe f

28、lexure test is designed totest the effect on the resistance to cracking and bond of theveneer plaster to the veneer plaster base while being flexed.The degree of correlation between this test method and serviceperformance has not been determined.5.8.2 ApparatusUse the apparatus described in Test Met

29、h-ods C473 for Method B.5.8.3 ProcedureSelect three 12 by 16 in. (300 by400 mm) specimens. Subject each specimen to a continuous,midpoint, loading applied at a rate of 1 in./min 6 5s(25 mm min 6 5 s) downward to the back of the panel (plastersurface in tension) supported over a clear span of 14 in.(

30、356 mm) until failure.5.8.4 ReportReport whether the sample passes or fails theflexure test. The sample fails if any one of the specimens showscracking more than12 in. (13 mm) from the break line or if thebond of the veneer plaster to the paper fails.5.8.5 Precision and BiasNo information is present

31、edabout either the precision or bias of the flexure test since thetest result is nonquantitative.5.9 Joint Strength:5.9.1 Significance and UseThe joint strength test is de-signed to test strength of the joint between two adjacentgypsum veneer panels that have been covered with veneerplaster. The deg

32、ree of correlation between this test method andservice performance has not been determined.5.9.2 ApparatusUse the apparatus described in Test Meth-ods C473 for Method B.5.9.3 Specimen PreparationCut two 8 by 12-in. (200 by300-mm) pieces of gypsum base for veneer plaster for eachspecimen to be tested

33、. One 12-in. edge of each piece shall bethe paper-bound edge. Place the two pieces of gypsum base forveneer plaster face down with the paper-bound edges formingthe joint. Apply a pregummed tape over the joint. (The tapewill keep the joint from flexing during the specimen prepara-tion.) Turn face up

34、and apply joint tape and gypsum veneerplaster in accordance with Specification C843 using themethod titled “Reinforcement Secured and Embedded withVeneer Plaster.”5.9.4 ProcedureCondition the specimen and determinethe flexural strength in accordance with Test Methods C473Method B.Apply the load para

35、llel to and directly over the backof the joint.5.9.5 ReportCalculate and report the average breakingload in pound-force or newtons, rounded to the nearest 1 lbf(N).C587 04 (2018)25.9.6 Precision and BiasThe precision and bias for mea-suring joint strength are essentially as specified in Test Meth-od

36、s C473.6. Inspection6.1 Inspection of the gypsum veneer plaster shall be agreedupon between the purchaser and the supplier as part of thepurchase agreement.7. Rejection and Rehearing7.1 Rejection of gypsum veneer plaster that fails to conformto the requirements of this specification shall be reporte

37、d to theproducer or supplier promptly and in writing. The notice ofrejection shall contain a statement documenting how thegypsum veneer plaster has failed to conform to the require-ments of this specification.8. Certification8.1 When specified in the purchase agreement, a manufac-turers or suppliers

38、 report shall be furnished at the time ofshipment certifying that the product is in compliance with thisspecification.9. Packaging and Package Marking9.1 Gypsum veneer plaster shall be dry and free from lumps,and shall be shipped in packages.9.2 When shipped for resale, the following informationshal

39、l be legibly marked on each package or on a tag of suitablesize attached thereto:9.2.1 Name of producer or supplier,9.2.2 Brand,9.2.3 Description, and9.2.4 Net or gross weight, or both, of package.10. Keywords10.1 gypsum; gypsum veneer plaster; plaster; veneer plasterASTM International takes no posi

40、tion respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibili

41、ty.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to AST

42、M International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address

43、shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 04 (2018)3