《ASTM B937-2004(2010) Standard Specification for Copper-Beryllium Seamless Tube (UNS Nos C17500 and C17510)《铜铍无缝管的标准规格(UNS Nos C17500和C17510)》.pdf》由会员分享，可在线阅读，更多相关《ASTM B937-2004(2010) Standard Specification for Copper-Beryllium Seamless Tube (UNS Nos C17500 and C17510)《铜铍无缝管的标准规格(UNS Nos C17500和C17510)》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B937 04 (Reapproved 2010)Standard Specification forCopper-Beryllium Seamless Tube (UNS Nos. C17500 andC17510)1This standard is issued under the fixed designation B937; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, th

2、e year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification establishes the requirements forcopper-beryllium alloy seamless tube in straight lengths.

3、Copper-cobalt-beryllium alloy UNS No. C17500 and copper-nickel-beryllium alloy UNS No. C17510 will be the alloysfurnished whenever this specification is specified.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to S

4、I units that are provided for information onlyand are not considered standard.1.3 The following safety hazard caveat pertains only to thetest method(s) described in this specification. This standarddoes not purport to address all of the safety concerns, if any,associated with its use. It is the resp

5、onsibility of the user of thisstandard to establish appropriate safety and health practicesand to determine the applicability of regulatory limitationsprior to use.2. Referenced Documents2.1 The following documents of the issue in effect on dateof material purchase form a part of this specification

6、to theextent referenced herein:2.2 ASTM Standards:2B193 Test Method for Resistivity of Electrical ConductorMaterialsB194 Specification for Copper-Beryllium Alloy Plate,Sheet, Strip, and Rolled BarB251 Specification for General Requirements for WroughtSeamless Copper and Copper-Alloy TubeB601 Classif

7、ication for Temper Designations for Copperand Copper AlloysWrought and CastB846 Terminology for Copper and Copper AlloysE8 Test Methods for Tension Testing of Metallic MaterialsE18 Test Methods for Rockwell Hardness of Metallic Ma-terialsE255 Practice for Sampling Copper and Copper Alloys forthe Det

8、ermination of Chemical CompositionE1004 Test Method for Determining Electrical Conductiv-ity Using the Electromagnetic (Eddy-Current) Method3. General Requirements3.1 The following sections of Specification B251 (as noted)constitute a part of this specification:3.1.1 Workmanship, Finish, and Appeara

9、nce,3.1.2 Number of Tests and Retests,3.1.3 Significance of Numerical Limits,3.1.4 Inspection,3.1.5 Rejection and Rehearing,3.1.6 Certification,3.1.7 Mill Test Report, and3.1.8 Packaging and Package Marking.4. Terminology4.1 For definitions of terms related to copper and copperalloys, refer to Termi

10、nology B846.4.2 Definitions of Terms Specific to This Standard:4.2.1 average diameter (for round tubes only), ntheaverage of the maximum and minimum outside diameters, ormaximum and minimum inside diameters, whichever is appli-cable, as determined at any one cross section of the tube.4.2.2 lengths,

11、nstraight pieces of the product4.2.2.1 ends, nstraight pieces, shorter than the nominallength, left over after cutting the product into mill lengths,stock lengths, or specific lengths. They are subject to minimumlength and maximum weight requirements.4.2.2.2 specific, adjstraight lengths that are un

12、iform inlength, as specified, and subject to established length toler-ances.4.2.2.3 specific with ends, adjspecific lengths, includingends.4.2.2.4 stock, nstraight lengths that are mill cut and storedin advance of orders. They are usually 8, 10, 12, or 20 ft (2.44,3.05, 3.66, or 6.10 m) and subject

13、to established lengthtolerances.1This specification is under the jurisdiction ofASTM Committee B05 on Copperand Copper Alloys and is the direct responsibility of Subcommittee B05.04 on Pipeand Tube.Current edition approved Oct. 1, 2010. Published December 2010. Originallyapproved in 2004. Last previ

14、ous edition approved in 2004 as B937 04. DOI:10.1520/B0937-04R10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM webs

15、ite.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.2.2.5 stock with ends, adjstock lengths, including ends.4.2.3 tube, na hollow product of round or any other crosssection having a continuous periphery.4.2.3.1 tube, seamless, adja

16、 tube produced with a con-tinuous periphery in all stages of the operations.5. Ordering Information5.1 Include the following information when placing ordersfor product under this specification, as applicable:5.1.1 Quantity, number of pieces or pounds,5.1.2 Copper Alloy UNS No. designation (see 1.1),

17、5.1.3 Temper (see section 8)5.1.4 Dimensions, including length if applicable. For tubeor pipe specify either OD/ID, OD/wall, or ID/wall.5.1.5 How furnished: stock lengths with or without ends,specific lengths with or without ends,5.1.6 ASTM designation and year of issue,5.1.7 Special tests or except

18、ions, if any,5.1.8 Hardness tests, if required,5.1.9 Special tests such as tension test, if required,5.1.10 Special marking or packaging, if required,5.1.11 Inspection, if required (see Specification B251),5.1.12 Certification, if required (see Specification B251),5.1.13 Mill test report, if require

19、d (see Specification B251).5.2 When material is purchased for agencies of the U.S.government, this shall be specified in the contract or purchaseorder, and the material shall conform to the SupplementaryRequirements as defined in the current issue of SpecificationB251.6. Materials and Manufacture6.1

20、 Materials:6.1.1 The material of manufacture shall be UNS Alloy No.C17500 or C17510, cast and worked into tubular form, and ofsuch purity and soundness as to be suitable for processing intothe products prescribed herein.6.1.2 The tube shall have heat traceable identity.6.2 Manufacture:6.2.1 The prod

21、uct shall be manufactured by a combinationof hot working or cold working, or both; annealing; orprecipitation heat treatment, or both, as to produce a uniformwrought structure in the finished product, to meet the temperspecified.7. Chemical Composition7.1 The material shall conform to the chemical c

22、ompositionrequirements in Table 1 for the copper alloy designated in theordering information.7.2 These composition limits do not preclude the presenceof other elements. By agreement between the manufacturer andpurchaser, limits may be established and analysis required forunnamed elements7.3 For allo

23、ys in which copper is listed as “Remainder,”copper is the difference between the sum of results of allelements determined and 100 %. When all elements in Table 1are determined, the sum of results shall be 99.5 % min.8. Temper8.1 Tempers, as described in Classification B601, availableunder this speci

24、fication are: TB00 (solution treated (A), TF00(precipitation hardened (AT), TD04 (solution heat-treated andcold worked: hard (H), and TH04 (hard and precipitationheat-treated (HT). These products meet property requirementsin Table 2.9. Precipitation Heat Treatment9.1 When material is purchased in th

25、e TB00 (A) or theTD04 (H) tempers, the precipitation heat treatment is per-formed by the purchaser.9.2 Conformance to the TF00 (AT) and TH04 (HT) speci-fication limits shown in Table 2, for products supplied in theTB00 (A) or the TD04 (H) tempers, shall be determined bytesting test specimens heat-tr

26、eated at a uniform temperature of850 to 900F for the times shown in Table 3.TABLE 1 Chemical CompositionConcentration, %ElementCopper AlloyUNS No.C17500Copper AlloyUNS No.C17510Beryllium 0.4-0.7 0.2-0.6Cobalt 2.4-2.7 0.3 maxNickel 1.4-2.2Iron, max 0.10 0.10Aluminum, max 0.20 0.20Silicon, max 0.20 0.

27、20Copper Remainder RemainderTABLE 2 Tensile Strength and Rockwell Hardness RequirementsATemper Designation As SuppliedStandard FormerTensileStrengthKsiB(MPaC)RockwellHardness,B ScaleElectricalConductivityIACS min, %TB00 Solution heat-treated (A) 35-55 (240-380) 50 max 20TD04 Solution heat-treated an

28、dcold-worked hard (H)65-80 (450-550) 60-80 20After Precipitation Heat TreatmentTF00 Precipitation hardened (AT) 100-130 (690-895)D92-100 45TH04 Hard and precipitation heat-treated (HT)110-140 (760-965)D95-102 48AThese values apply to mill products. See Section 10 for exceptions in end products.Bksi

29、= 1000 psi.CSee Appendix.DThe upper limits in the tensile strength column are for design guidance only.B937 04 (2010)29.3 End products may be heat-treated at other times andtemperatures for specific applications. These special combina-tions of properties such as increased ductility, dimensionalaccur

30、acy, and endurance strength may be obtained by specialprecipitation-hardening heat treatments. The mechanical re-quirements of Table 2 do not apply to such special heattreatment. Specific test requirements as needed shall be agreedupon between the manufacturer or the supplier and the pur-chaser of t

31、he end product.9.4 TF00 (AT) and TH04 (HT) tempers as standard mill-hardened products has been precipitation heat-treated andtested by the manufacturer. An appropriate time and tempera-ture has been used to produce properties within the specifica-tion limits shown in Table 2. Table 3 does not apply.

32、 Furtherthermal treatment of these tempers is not normally required.9.5 Material may be supplied with nonstandard properties.Table 2 values would not apply. Specific test requirements asneeded shall be agreed upon between the manufacturer orsupplier and the purchaser of these end products.10. Physic

33、al Property Requirements10.1 Electrical ConductivityProduct furnished to thisspecification shall conform to the electrical conductivity re-quirement given in Table 2 for the applicable temper, whentested in accordance with Practice E1004 or by convertingfrom resistivity measured in accordance with T

34、est MethodB193.11. Mechanical Property Requirements11.1 Mechanical property requirements are specified inTable 2.11.2 Rockwell HardnessRockwell hardness is the productacceptance criteria, when tested in accordance with TestMethods E18 for product larger than38 in. (9.5 mm) innominal diameter or dist

35、ance between parallel surfaces, andother shapes having a nominal cross sectional area larger than0.141 in.2(91 mm2).11.2.1 The referee product rejection criteria shall be tensileresults, when rested in accordance with Test Methods E8.11.3 Tension TestThe tension test will be used for quali-fication

36、of all material when specifically required by thepurchaser, as in some government requirements.12. Purchases for the U.S. Government12.1 When specified in the contract or purchase order,product purchased for agencies of the U.S. government shallconform to the special government regulations specified

37、 in theSupplemental Requirements section of Specification B251.13. Dimensions, Mass, and Permissible Variation13.1 The standard method of specifying wall thickness shallbe in decimal fractions of an inch.13.1.1 For the purpose of determining conformance with thedimensional requirements prescribed in

38、 this specification, anymeasured value outside the specified values for any dimensionmay be cause for rejection.13.1.2 Tolerances on a given tube may be specified withrespect to any two, but not all three, of the following: outsidediameter, inside diameter, wall thicknessNOTE 1Blank spaces in the to

39、lerance tables indicate either that thematerial is not generally available or no tolerances have been established.13.2 Wall-Thickness Tolerances-Wall-thickness tolerancesshall be in accordance with Table 4 and Table 5.13.3 Diameter Tolerances-Diameter Tolerances shall be inaccordance with Table 6.13

40、.4 Length Tolerances-Length tolerances shall be in accor-dance with Table 713.5 Squareness-For tube in straight lengths, the departurefrom squareness of the end shall not exceed the following:Specified OutsideDiameter, in. (mm) Tolerance, in./in. (mm/mm)34 (19.1) and over 0.06213.6 Straightness-Refe

41、r to Table 7 of Specification B251.TABLE 3 Precipitation Heat-Treatment Time for Acceptance TestsTemper Designation Copper Alloy UNSNo. 17500 At900F (482C), hCopper Alloy UNSNo. C17510 At850F (454C)Ato900F (482C)A,hStandard FormerTB00 Solution heat-treated (A) 3 3TD04 Solution heat-treated and cold-

42、worked:hard (H)22ASpecific temperature used must conform with suppliers certification.TABLE 4 Wall-Thickness TolerancesTB00 (A) and TF00 (AT) TempersANOTE 1Maximum Deviation of Any PointThe following tolerances are plus and minus: if tolerances all plus or all minus are desired double thevalues give

43、n.Wall Thickness, in. (mm)Outside Diameter, in. (mm)5/8to1(15.9 to 25.4)Over 1 to 2(25.4 to 50.8)Over 2 to 4(50.8 to 102)Over 4(102)Over 0.125 (3.2) to 0.250 (6.5) incl 60.014 (0.36) 60.017 (0.43) 60.020 (0.51) 60.030 (0.76)Over 0.250 (6.5) to 0.500 (12.7) incl 60.017 (0.43) 60.023 (0.58) 60.032 (0.

44、81) 60.053 (1.35)Over 0.500 (12.7) to 1.000 (25.4) incl 60.030 (0.76) 60.053 (1.35) 60.083 (2.11)Over 1.000 (25.4) 60.068 (1.73) 60.098 (2.49)AWhen tube is ordered by outside and inside diameters, the maximum plus and minus deviation of the wall thickness from the nominal at any point shall not exce

45、edthe values given in this table more than 50 %.B937 04 (2010)314. Workmanship, Finish and Appearance14.1 The product shall be free of defects, but blemishes ofa nature that do not interfere with the intended application areacceptable.15. Sampling15.1 Refer to sampling section in Specification B251.

46、15.2 SamplingSample pieces shall be taken from a heatand lot of material processed simultaneously in the sameequipment, as follows:15.2.1 HeatA heat shall be the result of castings pouredsimultaneously from the same source of molten metal15.2.2 LotThe lot shall be a heat, or fraction thereof.16. Spe

47、cimen Preparation16.1 Chemical AnalysisSample preparation shall be inaccordance with Practice E255.16.1.1 Analytical specimen preparation shall be the respon-sibility of the reporting laboratory.16.2 Tension TestsSample preparation shall be in accor-dance with Specification B251.16.3 Rockwell Hardne

48、ssThe test specimens shall be of asize and shape to permit testing by the available test equipmentand shall permit testing in a plane parallel to the direction ofdeformation given to the product.16.3.1 The surface of the test specimens shall be sufficientlysmooth and even to permit the accurate dete

49、rmination ofhardness.16.3.2 Each specimen shall be free of scale and foreignmatter and care shall be taken to avoid change in condition,that is, heating or cold working17. Test Methods17.1 Chemical AnalysesThe chemical composition shall,in cases of disagreement, be determined in accordance with theapplicable method in Annex A1 of Specification B194.17.2 Tension TestsTension tests, when required, shall bemade according to Test Methods E8.18. Test Report18.1 When specified in the contract or purchase order, areport of test results shall