《ASTM B936-2008 Standard Specification for Copper-Chromium-Iron-Titanium Alloy Plate Sheet Strip and Rolled Bar《铜铬铁钛合金板、薄板、带材和轧制棒材的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM B936-2008 Standard Specification for Copper-Chromium-Iron-Titanium Alloy Plate Sheet Strip and Rolled Bar《铜铬铁钛合金板、薄板、带材和轧制棒材的标准规范》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B 936 08Standard Specification forCopper-Chromium-Iron-Titanium Alloy Plate, Sheet, Stripand Rolled Bar1This standard is issued under the fixed designation B 936; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the yea

2、r of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification establishes the requirements for Cop-per Alloy UNS No. C18080 for plate, sheet, strip, and ro

3、lledbar in alloy.NOTE 1Since Copper Alloy UNS No. C18080 is frequently used in avariety of applications where yield strength and stress-corrosion resistancemay be critical, it is recommended that drawings or samples of the part tobe fabricated and details of application be submitted for use in estab

4、lishingtemper and treatment of material.NOTE 2Copper Alloy UNS No. C18080 is covered by a patent.Interested parties are invited to submit information regarding the identi-fication of an alternative(s) to this patented item to ASTM Internationalheadquarters. Your comments will receive careful conside

5、ration at ameeting of the responsible technical committee,1which you may attend.1.2 UnitsThe values stated in inch-pound units are to beregarded as standard. The values given in parentheses aremathematical conversions to SI units that are provided forinformation only and are not considered standard.

6、2. Referenced Documents2.1 The following documents of the issue in effect on thedate of material purchase form a part of this specification to theextent referenced herein:2.2 ASTM Standards:2B 248 Specification for General Requirements for WroughtCopper and Copper-Alloy Plate, Sheet, Strip, and Roll

7、edBarB 248M Specification for General Requirements forWrought Copper and Copper-Alloy Plate, Sheet, Strip, andRolled Bar (Metric)B 601 Classification for Temper Designations for Copperand Copper AlloysWrought and CastB 846 Terminology for Copper and Copper AlloysE 8/E 8M Test Methods for Tension Tes

8、ting of MetallicMaterialsE62 Test Methods for Chemical Analysis of Copper andCopper Alloys (Photometric Methods)E76 Test Methods for ChemicalAnalysis of Nickel-CopperAlloys3E 255 Practice for Sampling Copper and Copper Alloys forthe Determination of Chemical CompositionE 478 Test Methods for Chemica

9、l Analysis of CopperAlloysE 1473 Test Methods for Chemical Analysis of Nickel,Cobalt, and High-Temperature Alloys3. General Requirements3.1 The following sections of Specification B 248 constitutea part of this specification:3.1.1 TerminologyDefinitions,3.1.2 Materials and Manufacturing,3.1.3 Workma

10、nship, Finish, and Appearance,3.1.4 Sampling, except for chemical analysis,3.1.5 Number of Tests and Retests,3.1.6 Specimen Preparation,3.1.7 Test Methods, except for chemical analysis,3.1.8 Significance of Numerical Limits,3.1.9 Inspection,3.1.10 Rejection and Rehearing,3.1.11 Certification,3.1.12

11、Test Reports (Mill),3.1.13 Packaging and Package Marking, and3.1.14 Supplementary Requirements.3.2 In addition, when a section with a title identical to thatreferenced in 3.1 appears in this specification, it containsadditional requirements which supplement those appearing inSpecification B 248.4. T

12、erminology4.1 DefinitionsFor definitions of terms used in this speci-fication, refer to Terminology B 846.5. Ordering Information5.1 Contracts or purchase orders for product under thisspecification should include the following information:1This specification is under the jurisdiction ofASTM Committe

13、e B05 on Copperand CopperAlloys and is the direct responsibility of Subcommittee B05.01 on Plate,Sheet, and Strip.Current edition approved Oct. 1, 2008. Published November 2008. Originallyapproved in 2004. Last previous edition approved in 2005 as B 936 041.2For referenced ASTM standards, visit the

14、ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Withdrawn. The last approved version of this historical standard is referencedon www.astm.org.1*A Summ

15、ary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.1.1 ASTM designation and year of issue (for example, B936 XX),5.1.2 Copper Alloy UNS No. designation (for example,C18080),5.1

16、.3 Temper (see Section 8),5.1.4 Dimensions, that is, thickness, width, length, and soforth (see Section 13),5.1.5 Form, that is, plate, sheet, strip, or rolled bar,5.1.6 How furnished, that is, coils, specific lengths or stocklengths, with or without ends,5.1.7 Quantity, that is, total weight each f

17、orm, temper, andsize, and5.1.8 Whether material is purchased for agencies of the U.S.government (see Section 12).5.2 The following options are available under this specifi-cation and should be specified in the contract or purchase orderwhen required:5.2.1 Type of edge, that is, slit, sheared, sawed,

18、 squarecorners, round corners, rounded edges, or full rounded edges,and5.2.2 Width and straightness tolerances (see Section 13).6. Materials and Manufacture6.1 Material:6.1.1 The material of manufacture shall be a cast bar, cake,slab, and so forth, of Copper Alloy UNS No. C18080 of suchpurity and so

19、undness as to be suitable for process in to theproducts prescribed herein.6.1.2 In the event heat identification or traceability isrequired, the purchaser shall specify the details desired.NOTE 3Due to the discontinuous nature of the processing of castingsinto wrought products, it is not always prac

20、tical to identify a specificcasting analysis with a specific quantity of finished material.6.2 Manufacture:6.2.1 The product shall be manufactured by such hot work-ing, cold working, and annealing processes as to produce auniform wrought structure in the finished product.6.2.2 The product shall be h

21、ot- or cold-worked to thefinished size and subsequently annealed, when required, tomeet the temper properties specified.6.2.3 EdgesSlit edges shall be furnished unless otherwisespecified in the contract or purchase order.7. Chemical Composition7.1 The material shall conform to the chemical compositi

22、onrequirements specified in Table 1.7.2 These composition limits do not preclude the presenceof other elements. Limits may be established and analysisrequired for unnamed elements by agreement between themanufacturer and the purchaser.7.3 For alloys in which copper is listed as “Remainder,”copper is

23、 the difference between the sum of results of allelements determined and 100 %. When all elements in Table 1are determined, the sum of the results shall equal at least99.8 %.8. Temper8.1 Products fabricated from these alloys are available in thetempers listed in Table 2 as defined in Classification

24、B 601.8.1.1 Mill Hardened (TM)The standard tempers for mill-hardened material are as designated in Table 2 with the prefix“TM”. Former designations and the standard designations asdefined in Classification B 601 are shown.8.1.2 Precipitation Heat Treated, Cold Worked, and Ther-mal Stress Relieved (T

25、R)The standard tempers for precipi-tation heat treated, cold worked, and thermal stress relievedmaterial are designated in Table 2 with the prefix “TR.” Formerdesignations and the standard designations as defined inClassification B 601 are shown.NOTE 4The properties for product in special or nonstan

26、dard tempersare subject to negotiation between the manufacturer and the purchaser.9. Physical Properties9.1 The electrical resistivity and conductivity of CopperAlloy UNS No. C18080 is listed in Table 3 for informationonly.9.2 The density of Copper Alloy UNS No. C18080 is givenin Specifications B 24

27、8 and B 248M.10. Mechanical Properties10.1 Yield Strength Requirements:10.1.1 Product furnished under this specification will con-form to the 0.2 % offset yield strength requirements prescribedin Table 2 when tested in accordance with Test MethodsE 8/E 8M.10.1.2 Acceptance or rejection based upon me

28、chanicalproperties shall depend only on 0.2 % offset yield strength.10.2 Tensile Strength Requirements:10.2.1 The approximate Tensile Strength values given inTable 2 are for general information and shall not be used as abasis for product rejection.10.3 Rockwell Hardness Requirements:10.3.1 The appro

29、ximate Rockwell hardness values given inTable 2 are for general information and assistance in testingand shall not be used as a basis for product rejection.TABLE 1 Chemical RequirementsElementComposition, %Copper Alloy UNS No.C18080Copper RemainderChromium 0.20-0.7Silicon 0.01-0.10Titanium 0.01-0.15

30、Silver 0.01-0.30Iron 0.02-0.20TABLE 2 Yield Strength Requirements for Copper Alloy UNS No.C18080TemperDesignationApproximateTensileStrengthYield Strengthat 0.2 % OffsetApproximateRockwellHardnessKsiA(MPaB) KsiA(MPaB)min.Rockwell B Superficial 30Tmin. maxTM04 70 (480) 81 (560) 65 (450) 76-86 67-74TM0

31、8 78 (540) 91 (630) 75 (520) 80-89 70-76TR08 75 (520) 91 (630) 72 (500) 78-89 69-76Aksi = 1000 psi.BSee Appendix X1.B936082NOTE 5The Rockwell hardness test offers a quick and convenientmethod of checking for general conformity to the specification require-ments for temper, tensile strength, and grai

32、n size.11. Other Requirements11.1 Purchases for U.S. Government AgenciesWhenidentified in the contract or purchase order, product purchasedfor agencies of the U.S. government shall conform to thespecial government requirements stipulated in the supplemen-tal requirements given in Specification B 248

33、.12. Dimension, Mass, and Permissible Variations12.1 The dimensions and tolerances for product describedby this specification shall be as specified in Specification B 248with particular reference to the following tables and relatedparagraphs in that specification:12.1.1 ThicknessTolerances, Table 1.

34、12.1.2 Width:12.1.2.1 Tolerances for Slit Metal and Slit Metal with RolledEdgesTable 4.12.1.2.2 Tolerances for Square Sheared MetalTable 5.12.1.2.3 Tolerances for Sawed MetalTable 6.12.1.3 Length:12.1.3.1 Tolerances for Straight LengthsTable 7.12.1.3.2 Schedule of Minimum Lengths with EndsTable 8.12

35、.1.3.3 Tolerances for Square Sheared MetalTable 9.12.1.3.4 Tolerances for Sawed MetalTable 10.12.1.4 Straightness:12.1.4.1 Tolerances for Slit Metal or Slit Metal EitherStraightened or Edge RolledTable 11,12.1.4.2 Tolerances for Squared-Sheared MetalTable 12.12.1.4.3 Tolerances for Sawed MetalTable

36、13.12.1.5 Edges:12.1.5.1 Tolerances for Radius of Square EdgesTable 14.12.1.5.2 Tolerances for Radius of Round CornersTable 15.12.1.5.3 Tolerances for Radius of Rounded EdgesTable 16.12.1.5.4 Tolerances for Radius of Full-Rounded EdgesTable 17.13. Sampling13.1 Chemical Analysis:13.1.1 The sample for

37、 chemical analysis shall be taken fromthe pieces selected and combined into one composite sample inaccordance with Practice E 255 for product in its final form.The minimum weight of the composite sample shall be 150 g.13.1.2 Instead of sampling in accordance with Practice E255, the manufacturer shal

38、l have the option of taking samplesat the time the castings are poured or by taking samples fromthe semi-finished product.13.1.2.1 When composition of the material has been deter-mined during the course of manufacture, sampling of thefinished product by the manufacturer is not required.13.1.3 The nu

39、mber of samples to be taken for determinationof chemical composition shall be as follows:13.1.3.1 When sampled at the time the castings are poured,at least one sample shall be taken for each group of castingspoured from the same source of molten metal.13.1.3.2 When sampled from the semi-finished pro

40、duct, atleast one sample shall be taken to represent each 10 000 lb, orfraction thereof, except that not more than one sample shall berequired per piece.13.1.3.3 Only one sample need be taken from the semi-finished product of one cast bar from a single furnace meltcharge continuously processed.14. T

41、est Methods14.1 Chemical AnalysisChemical composition shall, incase of disagreement, be determined as follows:Element ASTM Test MethodChromium E 1473Titanium E 1473Copper E 478Iron E76(AA)Silicon E62Silver E 47814.1.1 Test method(s) to be followed for the determinationof element(s) resulting from co

42、ntractual or purchase orderagreement shall be as agreed upon between the manufacturerand the purchaser.15. Keywords15.1 copper-chromium-iron-titanium alloy plate; copper-chromium-iron-titanium alloy rolled bar; copper-chromium-iron-titanium alloy sheet; copper-chromium-iron-titanium al-loy strip; UN

43、S No. C18080TABLE 3 Electrical ResistivityTemper Copper Alloy UNS No. C18080Electrical Resistivityat 20C (68 F),Equivalent Conductivityat 20C (68 F),Vg/m % IACSTM04, TM08, TR08 0.19165 nominal 80 nominalB936083APPENDIX(Nonmandatory Information)X1. METRIC EQUIVALENTSX1.1 The SI unit for strength prop

44、erties now shown is inaccordance with the International System of Units (SI). Thederived SI unit for force is the newton (N), which is defined asthat force which when applied to a body having a mass of onekilogram gives it an acceleration of one metre per secondsquared (N = kgm/s2). The derived SI u

45、nit for pressure orstress is the newton per square metre (N/m2), which has beennamed the pascal (Pa) by the General Conference on Weightsand Measures. Since 1 ksi = 6 894 757 Pa the metricequivalents are expressed as megapascal (MPa), which is thesame as MN/m2and N/mm2.SUMMARY OF CHANGESCommittee B0

46、5 has identified the location of selected changes to this standard since the last issue(B 936 041) that may impact the use of this standard. (Approved Oct. 1, 2008.)(1) Corrected typographical errors throughout the standard.(2) A definition that is now in B 846 was removed fromSection 4.(3) The TR T

47、emper designation was added in paragraph 8.1.2.(4) Mechanical Properties (paragraphs 10.1.1 and 10.1.2) wererevised to show that product furnished under this specificationwill conform to 0.2 % offset yield strength and not tensilestrength.(5) The Cr range was revised from 0.20 0.70 to 0.20 0.7 tobe

48、consistent with CDA.(6) Table 2 was revised to show it is for Yield StrengthRequirements, TR08 temper values were added, 0.2 % offsetyield strength values were added for all tempers, and the tensilestrength ranges were modified for TM04 and TM08 tempers.(7) Table 3 was revised to add TR08 temper, th

49、e electricalresistivity value was modified, and the electrical conductifityvalue was modified.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every