《ASTM B850-1998(2015) Standard Guide for Post-Coating Treatments of Steel for Reducing the Risk of Hydrogen Embrittlement《对钢镀层后处理以减小氢脆变危险的标准指南》.pdf》由会员分享，可在线阅读，更多相关《ASTM B850-1998(2015) Standard Guide for Post-Coating Treatments of Steel for Reducing the Risk of Hydrogen Embrittlement《对钢镀层后处理以减小氢脆变危险的标准指南》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B850 98 (Reapproved 2015)Standard Guide forPost-Coating Treatments of Steel for Reducing the Risk ofHydrogen Embrittlement1This standard is issued under the fixed designation B850; the number immediately following the designation indicates the year oforiginal adoption or, in the case of

2、 revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.INTRODUCTIONWhen atomic hydrogen enters steel, it can cause a loss of ductility, load carrying ability, or

3、cracking(usually as submicroscopic cracks), as well as catastrophic brittle failures at applied stresses wellbelow the yield strength or even the normal design strength for the alloys. This phenomenon oftenoccurs in alloys that show no significant loss in ductility, when measured by conventional ten

4、sile tests,and is referred to frequently as hydrogen-induced delayed brittle failure, hydrogen stress cracking, orhydrogen embrittlement. The hydrogen can be introduced during cleaning, pickling, phosphating,electroplating, autocatalytic processes, porcelain enameling, and in the service environment

5、 as a resultof cathodic protection reactions or corrosion reactions. Hydrogen can also be introduced duringfabrication, for example, during roll forming, machining, and drilling, due to the breakdown ofunsuitable lubricants, as well as during welding or brazing operations.1. Scope1.1 This guide cove

6、rs procedures for reducing the suscep-tibility in some steels to hydrogen embrittlement or degrada-tion that may arise in the finishing processes.1.2 The heat treatment procedures established herein maybe effective for reducing susceptibility to hydrogen embrittle-ment. This heat-treatment procedure

7、 shall be used after platingoperations but prior to any secondary conversion coatingoperation.1.3 This guide has been coordinated with ISO/DIS 9588 andis technically equivalent.NOTE 1The heat treatment does not guarantee complete freedom fromthe adverse effects of hydrogen degradation.1.4 The values

8、 stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safet

9、y and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2A919 Terminology Relating to Heat Treatment of Metals(Withdrawn 1999)3B374 Terminology Relating to ElectroplatingB851 Specification for Automated Controlled Shot

10、Peeningof Metallic Articles Prior to Nickel, Autocatalytic Nickel,or Chromium Plating, or as Final Finish2.2 ISO Standards:ISO 2080 Electroplating and Related ProcessesVocabulary4ISO DIS 9588 Post-Coating Treatments of Iron or Steel forReducing the Risk of Hydrogen Embrittlement42.3 Federal Standard

11、:QQ-C-320 Chromium Plating (Electrodeposited)53. Terminology3.1 DefinitionsMany of the terms used in this guide can befound in Terminology B374, A919, or ISO 2080.1This specification is under the jurisdiction of ASTM Committee B08 onMetallic and Inorganic Coatingsand is the direct responsibility of

12、SubcommitteeB08.02 on Pre Treatment.Current edition approved Jan. 1, 2015. Published January 2015. Originallyapproved in 1994. Last previous edition approved in 2009 as B85098(2009). DOI:10.1520/B0850-98R15.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer

13、 Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.4Available from American National Standards Institute (ANSI), 25 W. 43

14、rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.5Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States14.

15、Requirements4.1 Heat treatment may be performed on coated metals toreduce the risk of hydrogen embrittlement. The duration ofheat treatment in all cases shall commence from the time atwhich the whole of each part attains the specified temperature.4.2 Parts made from steel with actual tensile strengt

16、hs1000 MPa (with corresponding hardness values of 300HV10kgf, 303 HB, or 31 HRC) and surface-hardened parts mayrequire heat treatment unless Class ER-0 is specified. Prepara-tion involving cathodic treatments in alkaline or acid solutionsshall be avoided. Additionally, the selection of electroplatin

17、gsolutions with high cathodic efficiencies is recommended forsteel components with tensile strengths above 1400 MPa (withcorresponding hardness values of 425 HV10kgf, 401 HB, or 43HRC).4.3 Table 1 provides a list of embrittlement-relief heat-treatment classes from which the purchaser may specify the

18、treatment required to the electroplater, supplier, or processor onthe part drawing or purchase order.NOTE 2The treatment class selected is based on experience with thepart, or similar parts, and the specific alloy used or with empirical testdata. Because of factors such as alloy composition and stru

19、cture, type ofcoating, coating thickness, size, mass, or design parameters, some partsmay perform satisfactorily with no embrittlement-relief treatment. ClassER-0 treatment is therefore provided for parts that the purchaser wishes toexempt from treatment.NOTE 3The use of inhibitors in acid pickling

20、baths may not minimizehydrogen embrittlement.4.4 The electroplater, supplier, or processor is not normallyin possession of the necessary information, such as designconsiderations, operating stresses, etc., that must be consideredwhen selecting the correct embrittlement relief treatment. It isin the

21、purchasers interest that his or her part designer,manufacturing engineer, or other technically qualified indi-vidual specify the treatment class on the part drawing orpurchase order.5. Embrittlement Relief Treatment Classes5.1 With the exception of surface-hardened parts and partsthat have been shot

22、 peened in accordance with SpecificationB851, heat treatment conditions may be selected on the basis ofactual tensile strength. When only the minimum tensilestrength is specified, or if the tensile strength is not known, theheat treatment condition may be selected by relating known ormeasured hardne

23、ss values to equivalent tensile strengths. It isrecommended that the tensile strength be supplied by thepurchaser.5.2 Steels that have been wholly or partly surface hardenedmay be considered as being in the category appropriate to thehardness of the surface-hardened layer.5.3 If the purchaser requir

24、es any tests to be performed inorder to verify adequate embrittlement relief treatment, the testmethod and the sampling plan to be used shall be specified.6. Heat Treatment After Processing6.1 The heat treatment shall commence as soon as possible,preferably within 1 h but not later than 3 h after pl

25、ating andbefore commencement of any grinding or other mechanicaloperation. For cadmium, tin, zinc, their alloys, or any othercoating receiving a chromate treatment, heat treatment shall beconducted before chromate treatment.NOTE 4Chromate coatings undergo change at temperatures above66C. The coating

26、 changes from an amorphous structure to a crystallinestructure and no longer exhibits self-healing properties. While the crys-tallized chromate coating will provide satisfactory corrosion protectionunder most natural environments, the chromate coating will no longer passaccelerated corrosion tests.N

27、OTE 5The time period referred to is the length of time between theend of the plating operation and loading of the item concerned into theheat treatment processor.6.2 For high-strength steels, the conditions given in Table 1may be applied. For steels of actual tensile strength below 1000MPa, heat tre

28、atment after plating is not essential.6.3 Electroplated steel items having surface-hardened areasand through hardened or bearing steels, which would suffer anunacceptable reduction in hardness by treatment in accordancewith Table 1 shall be heat treated at a lower temperature, butnot below 130C.6.4

29、Treatment at 440 to 480C will reduce the hardness ofchromium deposits. It shall not be applied to steels that may beaffected adversely by heat treatment at this temperature, andthe lower temperature range shall be applied. For temperedsteels, items shall not be heat treated above a temperature thats

30、hall be 50C below the tempering temperature.7. Keywords7.1 delayed brittle failure; heat treatment; hydrogen em-brittlement; hydrogen embrittlement relief; hydrogen inducedcracking; hydrogen stress cracking; post-treatments of steelTABLE 1 Classes of Embrittlement-Relief Heat Treatment (SeeSections

31、46for details on the Use of Table 1)Hydrogen Embrittlement-Relief Treatment Classes for High-Strength SteelsClass Steels of Tensile Strength (Rm), MPaTemperature,CTime, hER-0 not applicableER-1 1701 to 1800 190220 min 22ER-2 1601 to 1700 190220 min 20ER-3 1501 to 1600 190220 min 18ER-4 1401 to 1500

32、190220 min 16ER-5 1301 to 1400 190220 min 14ER-6 1201 to 1300 190220 min 12ER-7A1525 or greater 177205 min 12ER-8 1101 to 1200 190220 min 10ER-9 1000 to 1100 190220 min 8ER-10A1250 to 1525 177205 min 8ER-11A1450 to 1800 190220 min 6ER-12A1000 to 1500 177205 min 4ER-13 1000 to 1800 unpeened itemsand

33、for engineering chromiumplated items440480 min 1ER-14Asurface-hardened parts 1401 130160 min 8ER-15Asurface-hardened parts 1401 to1800 plated with cadmium, tin,zinc, or their alloys130160 min 8ER-16 surface-hardened parts 1401plated with cadmium, tin, zinc,or their alloys130160 min 16AClasses ER-7,

34、ER-10, ER-11, ER-12, ER-14, and ER-15 are traditional treat-ments used in Federal Standard QQ-C-320. They do not apply to any otherstandard.B850 98 (2015)2ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard.

35、 Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed e

36、very five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible tec

37、hnical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshoho

38、cken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 98 (2015)3