ASTM B768-2011(2016) Standard Specification for Copper-Cobalt-Beryllium Alloy and Copper-Nickel-Beryllium Alloy Strip and Sheet《铜钴铍合金和铜镍铍合金带材和薄板材的标准规格》.pdf

《ASTM B768-2011(2016) Standard Specification for Copper-Cobalt-Beryllium Alloy and Copper-Nickel-Beryllium Alloy Strip and Sheet《铜钴铍合金和铜镍铍合金带材和薄板材的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM B768-2011(2016) Standard Specification for Copper-Cobalt-Beryllium Alloy and Copper-Nickel-Beryllium Alloy Strip and Sheet《铜钴铍合金和铜镍铍合金带材和薄板材的标准规格》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B768 11 (Reapproved 2016)Standard Specification forCopper-Cobalt-Beryllium Alloy and Copper-Nickel-BerylliumAlloy Strip and Sheet1This standard is issued under the fixed designation B768; the number immediately following the designation indicates the year oforiginal adoption or, in the

2、case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 T

3、his specification establishes the requirements forcopper-cobalt-beryllium and copper-nickel-beryllium strip andsheet of the following alloys:Nominal Composition, %Copper Alloy UNS No.2Beryllium Cobalt NickelC17410 0.3 0.5 . . .C17450 0.3 . . . 0.8C17460 0.3 . . . 1.21.2 UnitsValues stated in inch-po

4、und units are to beregarded as the standard. The values given in parentheses aremathematical conversions to SI units, which are provided forinformation only and are not considered standard.1.3 The following safety hazard caveat pertains only to thetest methods described in this specification:1.3.1 T

5、his standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Docume

6、nts2.1 The following documents of the issue in effect on dateof material purchase form a part of this specification to theextent referenced herein:2.2 ASTM Standards:3B194 Specification for Copper-BerylliumAlloy Plate, Sheet,Strip, and Rolled BarB248 Specification for General Requirements for Wrough

7、tCopper and Copper-Alloy Plate, Sheet, Strip, and RolledBarB601 Classification for Temper Designations for Copper andCopper AlloysWrought and CastB846 Terminology for Copper and Copper AlloysE8/E8M Test Methods for Tension Testing of Metallic Ma-terialsE18 Test Methods for Rockwell Hardness of Metal

8、lic Ma-terialsE255 Practice for Sampling Copper and Copper Alloys forthe Determination of Chemical CompositionE527 Practice for Numbering Metals and Alloys in theUnified Numbering System (UNS)3. Terminology3.1 For definitions of terms related to copper and copperalloys, refer to Terminology B846.4.

9、General Requirements4.1 The following sections of Specification B248 constitutesa part of this specification4.1.1 Terminology.4.1.2 Materials and Manufacture.4.1.3 Workmanship, Finish, and Appearance.4.1.4 Sampling.4.1.5 Number of Tests and Retests.4.1.6 Specimen Preparation.4.1.7 Test Methods.4.1.8

10、 Significance of Numerical Limits.4.1.9 Inspection.4.1.10 Rejection and Rehearing.4.1.11 Certification.4.1.12 Test Report.4.1.13 Packaging and Marking.4.1.14 Supplementary Requirements.4.2 In addition, when a section with a title identical to thatreferenced in 5.1 appears in this specification, it c

11、ontainsadditional requirements which supplement those appearing inSpecification B248.1This specification is under the jurisdiction ofASTM Committee B05 on Copperand CopperAlloys and is the direct responsibility of Subcommittee B05.01 on Plate,Sheet, and Strip.Current edition approved Oct. 1, 2016. P

12、ublished October 2016. Originallyapproved in 1987. Last previous edition approved in 2011 as B76811. DOI:10.1520/B0768-11R16.2The UNS system for copper and copper alloys (see Practice E527) is a simpleexpansion of the former standard designation system accomplished by the additionof a prefix “C” and

13、 a suffix “00.” The suffix can be used to accommodatecomposition variations of the base alloy.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document

14、 Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States15. Ordering Information5.1 Include the following information when placing ordersfor prod

15、uct under this specification, as applicable:5.1.1 ASTM designation and year of issue,5.1.2 Copper alloy UNS No. designation (1.1),5.1.3 Form of material: strip or sheet,5.1.4 Temper (Section 8),5.1.5 Tension test, if required (Section 9),5.1.6 Dimensions: thickness and width, and length as appli-cab

16、le (Section 11),5.1.7 How furnished: rolls, stock lengths with or withoutends, specific lengths with or without ends (Section 11),5.1.8 Type of edge, if required: slit, sheared, sawed, squarecorners, rounded corners, rounded edges, or full rounded edges(see 11.6),5.1.9 Special thickness tolerances,

17、if required (Section 11),5.1.10 Hardness test, if required,5.1.11 Special marking or packaging, if required,5.1.12 Mill test report, if required,5.1.13 Special tests or exceptions, if any, and5.1.14 Certification, if required.5.2 If product is purchased for agencies of the U.S. Gov-ernment (see the

18、Supplementary Requirements as defined inthe current issue of Specification B248 for additionalrequirements, if specified).6. Materials and Manufacture6.1 MaterialsThe material of manufacture shall be castbillets or slabs of one of the alloys cited in Section 1 of thisspecification. The cast material

19、 shall be of such soundness andpurity as to be suitable for processing into the productsprescribed herein.6.2 Manufacture:6.2.1 The product shall be manufactured by such hotworking, cold working, and annealing processes as to producea uniform wrought structure in the finished product.6.2.2 The produ

20、ct shall be hot or cold worked to the finishsize, and heat-treated when required, to meet the temperproperties specified.7. Chemical Composition7.1 The material shall conform to the chemical compositionrequirements in Table 1 for the copper alloy UNS No.designation specified in the ordering informat

21、ion.7.2 These composition limits do not preclude the presenceof other elements. By agreement between the manufacturer andpurchaser, limits may be established and analysis required forunnamed elements.7.3 For alloys in which copper is given as remainder, copperis the difference between the sum of all

22、 the elements analyzedand 100 %. When all the elements in Table 1 are analyzed, thesum of results shall be 99.5 % minimum.8. Temper8.1 The standard tempers for products described in thisspecification are given in Table 2.8.1.1 Copper Alloy UNS No. C17410 Strip and Sheet isoffered in the TH02 (12 HT)

23、 and TH04 (HT) tempers.8.1.2 Copper Alloy UNS No. C17450 Strip and Sheet isoffered in TH02 (12 HT) Temper.8.1.3 Copper Alloy UNS No. C17460 Strip and Sheet isoffered in the TH03 (34 HT) and TH04 (HT) tempers.9. Physical Properties9.1 Electrical Conductivity:9.1.1 The product furnished shall conform

24、to the electricalconductivity prescribed in Table 3.10. Mechanical Properties10.1 Tensile Strength Requirements:10.1.1 Product under 0.075 in. (1.905 mm) in thicknessfurnished under this specification shall conform to the tensilerequirements prescribed in Table 2, when tested in accordancewith Test

25、Methods E8/E8M.10.1.2 Tensile test specimens shall be taken so that theirlongitudinal axis is parallel to the direction of rolling.10.1.3 Acceptance or rejection, under 0.075 in. (1.905 mm)in thickness, based upon mechanical properties shall dependonly on tensile strength.10.2 Rockwell Hardness Requ

26、irements:10.2.1 Product 0.075 in. (1.905 mm) and over in thicknessfurnished under this specification shall conform to the Rock-well hardness requirements prescribed in Table 2, when testedin accordance with Test Methods E18.10.2.2 Acceptance or rejection, 0.075 in. (1.905 mm) andover in thickness, b

27、ased upon mechanical properties shalldepend only on Rockwell hardness.11. Dimensions and Permissible Variations11.1 The dimensions and tolerances for product describedby this specification shall be as specified in Specification B248,with particular reference to the following tables and relatedparagr

28、aphs:11.2 ThicknessSee 5.2.2, Table 2, and for specialtolerances, Table 3.11.3 Width:11.3.1 Slit Metal and Slit Metal With Rolled EdgesSee5.3.1 and Table 4.TABLE 1 Chemical RequirementsElementComposition, %Copper Alloy UNS NumberC17410 C17450 C17460Beryllium 0.150.50 0.150.50 0.150.50Cobalt 0.350.6

29、. .Nickel . 0.501.0 1.01.4Iron, max 0.20 0.20 0.20Zirconium, max . 0.50 0.50Tin, max . 0.25 0.25Silicon, max 0.20 0.20 0.20Aluminum, max 0.20 0.20 0.20copper remainder remainder remainderCopper + sum ofnamed elements99.5 % min 99.5 % min 99.5 % minB768 11 (2016)211.4 Length:11.4.1 Specific and Stock

30、 Lengths With and Without EndsSee 5.4.1.11.4.2 Schedule of Lengths (Specific and Stock) With EndsSee 5.4.2 and Table 8.11.5 Straightness:11.5.1 Slit Metal or Edge-Rolled MetalSee 5.5.1 andTable 11.11.6 EdgesSee 5.6.11.6.1 Square EdgesSee 5.6.1 and Table 15.11.6.2 Rounded CornersSee 5.6.2 and Table 1

31、6.11.6.3 Rounded EdgesSee 5.6.3 and Table 17.11.6.4 Full-Rounded EdgesSee 5.6.4 and Table 18.12. Workmanship, Finish, and Appearance12.1 The product shall be free of defects, but blemishes ofa nature that do not interfere with the intended application areacceptable.13. Sampling13.1 SamplingThe lot s

32、ize, portion size, and selection ofsamples pieces shall be as follows:13.1.1 Lot SizeAn inspection lot shall be 10 000 lb or lessmaterial of the same mill form, alloy, temper, and nominaldimensions, subject to inspection at one time or shall be theproduct of one cast bar from a single melt charge, w

33、hoseweight shall not exceed 25 000 lb that has been continuouslyprocessed and subject to inspection at one time.13.1.2 Portion SizeA portion shall be two representativesamples taken from the product of one cast bar that has beencontinually processed to the finished temper and dimensions.13.1.3 Chemi

34、cal Analysissample pieces for chemicalanalysis shall be in accordance with section 7.1.2.1 of Speci-fication B248.14. Number of Tests and Retests14.1 The number of tests and retests shall be in accordancewith Section 8 of Specification B248.15. Specimen Preparation15.1 Chemical AnalysisSample prepar

35、ation shall be inaccordance with Practice E255.15.2 Tensile TestsSample preparation shall be in accor-dance with Section 9 of Specification B248.15.3 Rockwell HardnessThe test specimens shall be of asize and shape to permit testing by the available test equipmentand shall be taken to permit testing

36、in a plane parallel to thedirection of deformation given to the product.15.3.1 The surface of the test specimens shall be sufficientlysmooth and even to permit the accurate determination ofhardness.15.3.2 The specimen shall be free of scale and foreignmatter and care shall be taken to avoid any chan

37、ge in condition,that is, heating or cold working.16. Test Methods16.1 The test methods for determining the mechanical andphysical properties are detailed in Specification B248.16.2 The test method for determining chemical analysis forcompliance and preparation to certifications and test reportsshall

38、 be at the discretion of the reporting laboratory.16.2.1 In case of dispute, the test method in the Annex ofSpecification B194 shall be used for determining chemicalrequirements in Table 1.16.3 When analysis for unnamed or residual elements isrequired in the purchase order, the method of analysis sh

39、all bemutually agreed upon between the manufacturer or supplierand the purchaser.17. Keywords17.1 beryllium copper strip; copper UNS number C17410;copper UNS number C17450; copper UNS number C17460TABLE 2 Mechanical Property Requirements for Strip and Sheet Precipitation Heat TreatedCopper AlloyUNS

40、No.Temper Designation Tensile Strength,ksi (MPa)Yield Strength, ksi (MPa),0.2 % offsetElongation, 2 in.(50 mm), %Rockwell HardnessStandard Former B 30TC17410 TH0212 HT 95-115 80-100 10-20 89-98 76-81(655-790) (550-690)TH04 HT 110-130 100-120 7-17 95-100 79-86(760-895) (690-830)C17450 TH0212 HT 95-11

41、5 80-100 12 min 88-99 75-82(655-790) (550-690)C17460 TH0334 HT 115-135 95-115 11 min 98-105 81-88(790-930) (655-790)TH04 HT 120-140 105-125 10 min 99-106 82-89(825-965) (720-860)TABLE 3 Electrical ConductivityCopper Alloy UNS No. Temper Percent IACS, minC17410 TH02, TH04 45C17450 TH02 50C17460 TH03,

42、 TH04 50B768 11 (2016)3SUMMARY OF CHANGESCommittee B05 has identified the principal changes to this specification that have been incorporated since the1999 (2004) issue as follows:(1) This specification received an editorial five-year update.Rewording and additions were made in accordance with thene

43、w “Outline of Form.”(2) Copper remainder was added to Table 1.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such

44、patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited

45、either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fa

46、ir hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this st

47、andard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 11 (2016)4