AECMA PREN 2516-1996 Aerospace Series Passivation of Corrosion Resistant Steels and Decontamination of Nickel Base Alloys Edition 1《航空航天系列.防腐钝化钢和镍基净化合金1板》.pdf

《AECMA PREN 2516-1996 Aerospace Series Passivation of Corrosion Resistant Steels and Decontamination of Nickel Base Alloys Edition 1《航空航天系列.防腐钝化钢和镍基净化合金1板》.pdf》由会员分享，可在线阅读，更多相关《AECMA PREN 2516-1996 Aerospace Series Passivation of Corrosion Resistant Steels and Decontamination of Nickel Base Alloys Edition 1《航空航天系列.防腐钝化钢和镍基净化合金1板》.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、AECMA STANDARD NORME AECMA AECMA NORM prEN 2516 Edition I January 1996 PUBLISHED BY THE EUROPEAN ASSOCIATION OF AEROSPACE INDUSTRIES (AECMA) Gulledelle 94 - B-I 200 BRUXELLES - Tel. (32) 2 775 81 10 - Fax. (32) 2 775 81 11 ICs : 49.040.40 Descriptors : Aircraft industry, corrosion resistant steels,

2、decontamination, nickel alloys ENGLISH VERSION Aerospace series Passivation of corrosion resistant steels and decontamination of nickel base alloys Srie arospatiale Passivation des aciers resistant la corrosion et dcontamination des alliages base nickel Luft- und Raumfahrt Passivieren von korrosions

3、bestndigen Sthlen und Dekontaminierung von Nickellegierungen This “Aerospace series“ Standard has been drawn up under the responsibility of AECMA (The European Association of Aerospace Industries). It is published on yell0 w paper in three equivalent versions (English, French, German). It will be su

4、bmitted as a draft European Standard to CEN (European Committee for Standardization) for formal vote. Edition approved for publication - 1996-01-31 _- The equivalent versions in French and German languages can be supplied by B.N.A.E. - Technopolis 54 - 199, rue Jean-Jacques Rousseau 921 38 ISSY - LE

5、S - MOULINEAUX CEDEX - FRANCE Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 3 EN 2516 : 1996 1 Scope This standard specifies several chemical me

6、thods of passivation for corrosion resistant steels (austenitic, ferritic, martensitic and precipitation hardenable) and of decontamination for nickel base alloys. 2 Purpose of process To improve the corrosion resistant characteristics of a part after such treatments as machining, forming, tumbling

7、and shot peening by removing foreign metal contamination due to these operations. Passivation shall not be used on castings, welded or brazed parts, carburized or nitrided surfaces nor on parts with mating surfaces when entrapment of acids may occur. 3 Normative references This European Standard inc

8、orporates by dated or undated reference provisions from other publications. These normative references are cited at the appropriate places in the text and the publications are listed hereafter. For dated references, subsequent amendments to or revisions of any of these publications apply to this Eur

9、opean Standard only when incorporated in it by amendment or revision. For undated references the latest edition of the publication referred to applies. IS0 9227 Corrosion tests in artificial atmospheres - Salt spray tests EN 2000 Aerospace series - Quality assurance - EN aerospace products - Approva

10、l of the quality system of manufacturers Aerospace series - Metallic materials - Part 1 : Designation 2, EN 2032-1 4 Classification The process class to be used depending on the material type unless otherwise specified between the manufacturer and the purchaser is given in table 1. The designation o

11、f the material type is defined in EN 2032-1. 1 ) Other processes (e.g. electrolytic polishing) can also produce passivated surfaces. 2) Published as AECMA Prestandard at the date of publication of this standard Previous page is blank Copyright Association Europeene des Constructeurs de Materiel Aero

12、spatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-STD-AECMA PREN 25Lb-ENGL 199b 1012311 0011205 4b4 Page 4 EN 2516 : 1996 Material type and designation Austenitic chromium-nickel steels and austeno-ferritic steels FE-PA

13、36XX, FE-PA39XX, FE-PA45XX, FE-PA47XX, FE-PA48XX, FE-PA49XX,FE-PA15XX Table 1 Process class C1 orC2 I I i Ferritic and martensitic chromium steels FE-PM15XX8 FE-PM17XX, FE-PM19XX Austenitic precipitation hardenable steels Martensitic precipitation hardenable steels High chromium martensitic steels H

14、eat resisting nickel base alloys FE-PA26XX8 FE-PA29XX, FE-PA25XX FE-PM27XX, FE-PM38XX, FE-PM35XX FE-PM39XX NI-PH 1 3XX, NI-PH18XX, NI-PH23XX8 NI-PH29XX, NI-PD73XXr NI-PH26XX c4 c1 c4 c3 C1 orC2 5 Information for the processor - Designation, see 12 ; - reference of the material standard and metallurg

15、ical condition of the latter ; - sequence of operations, if necessary ; - areas to be processed. 6 Condition of the parts prior to processing Fabrication of the parts shall have been completed. 7 Pre-treatments The parts shall be submitted to one or more of the processes (7.1 to 7.4) appropriate to

16、their degree of contamination. These processes are given for guidance. Other methods giving at least equivalent results may be applied. Unless otherwise specified, parts shall be processed from one step to the next without delay. 7.1 Degreasing 7.1.1 Organic solvents Approved products shall be used

17、either cold in liquid state or hot in vapour state. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-STD-AECMA PREN 25Lb-ENGL Lb LOL23LL 001L?rlL, 3TrJ

18、IW Page 5 EN 2516 : 1996 7.1.2 Alkaline solutions a) The composition may be as follows : Degreasing in strong alkaline solutions : - sodium hydroxide : 15 gll - sodium metasilicate pentahydrate : 40 g/l b The composition may be as follows : Degreasing in mild alkaline solutions : - sodium metasilica

19、te pentahydrate : 25 gll - sodium carbonate : 25 gll Addition of a wetting agent is possible. These solutions shall be used for immersion degreasing either anodically or not. 7.2 Abrasive cleaning a) Blasting Use a fine-grain alumina or glass beads with or without water. b) Tumbling The abrasives sh

20、all not have been used on any other type of matei., base alloys. (see ta,! 1) except i tar lum 7.3 Descaling The method shall be chosen according to the type of parts, heat treatment or hot forming. 7.4 Acid-pickling It shall only be used on steels not susceptible to pitting or sensitive to intergra

21、nular corrosion by the pickling solution which is most frequently an aqueous solution of nitric and hydrofluoric acids. The concentration can be adjusted within very wide limits by varying the proportions of the ingredients and by adjusting solution temperatures. Parts in steel of Rm (max.) 1 100 MP

22、a 3, shall be de-embrittled by heat treatment at 190 OC to 230 OC for at least 1 h. 3) Rm (max.) = maximum specified Rm Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without lice

23、nse from IHS-,-,- .- STD-AECMA PREN 25Lb-ENGL L77b = LOL23LL OOLL207 237 W Page 6 EN 2516 : 1996 8 Treatment The aqueous solutions shall be chosen from table 2 in accordance with the process class defined in table 1 for the material used to manufacture the parts. The parts shall be completely immers

24、ed in the chosen solution, then rinsed in clean water and dried. Table 2 Process class I I c2 I Step a) shall bc followed by step b) with a clean water rinse in between. 9 Required characteristics and inspection 9.1 Parts 9.1.1 Appearance When subjected to visual inspection, the surfaces shall be cl

25、ean and free from corrosion, pitting or other form of surface attack due to the treatment. A slight discolouration is allowed. 9.1.2 Absence of iron Contamination Surfaces of type parts or test specimens shall not show any iron contamination indicated by rust after a salt spray test according to IS0

26、 9227 for 2 h. 9.2 Process 9.2.1 Air used for drying or any other operation shall be dry and free from oil. 9.2.2 content less than 0,l g/l. The iron content in the solutions indicated in table 2 shall be less than 5 g/l and the chloride The nitric acid and sodium dichromate concentration shall be w

27、ithin the limits indicated in table 2. Chemical analyses of the solutions indicated in table 2 shall be carried out at regular intervals to determine the contents of nitric acid, sodium dichromate, chloride and iron. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided

28、by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-STD*AECMA PREN 25Lb-ENGL L77b 101231l 001L208 173 = Page 7 EN 2516 : 1996 10 Quality assurance 1 O. 1 See EN 2000. Approval of the processor 10.2 Process qualification Before beginning p

29、roduction, the processor shall submit a series of type parts and test pieces from the first batch treated under series conditions, which shall be tested according to 9.1. If the process is different from that described in this standard, it shall be qualified as follows : At least one specimen of eac

30、h material type to which the process is applicable (see table 11, with a surface roughness of Ra 5 1,6 pm, shall be treated according to the process to be qualified. After visual inspection to 9.1.1 each specimen shall be subjected to a salt spray test in accordance with IS0 9227 for 24 h. The expos

31、ed surface shall then show not more than a few isolated spots of rust. 10.3 Acceptance The parts shall have the required characteristics (see 9.1 1. Frequency of inspection shall be agreed between the purchaser and processor. 10.4 Fault sanction The parts not meeting the requirements shall be reject

32、ed. After agreement of the purchaser, these parts may be reprocessed (see 7 and 81. 11 Health, safety and environmental aspects The locally applicable regulations and laws shall be observed. 12 Designation EXAMPLE : EN251 6C1 Process class (see table 1) Number of this standard NOTE : If the classes of this standard are not used (see 4), the designation shall be limited to EN 2516. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-