1、 AEROSPACE STANDARD NUT, SELF-LOCKING, DOUBLE HEXAGON, SOLID FILM LUBRICATED, COUNTERBORED, 160 KSI, 800 F, UNS S66286 AS3564Copyright 2017 SAE International All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means,

2、electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org ISSUE

3、D1995-10REVISED2017-08THIRD ANGLE PROJECTION CUSTODIAN: E-25 REV.E FEDERAL SUPPLY CLASS 5310 AS3564 SHEET 1 OF 2 REV. E PROCUREMENT SPECIFICATION: AS4393 /2/ SAE Technical Standards Board Rules provide that: “This report is published by SAEtoadvance thestate of technicaland engineering sciences. The

4、 useof this report is entirely voluntary, and its applicability andsuitability for any particularuse, includingany patent infringement arisingtherefrom,is thesole responsibility of theuser.” SAE reviews eachtechnical reportatleast every fiveyears at whichtime it may be revised, reaffirmed, stabilize

5、d, or cancelled. SAE invites your written comments and suggestions.SAE values your input. To provide feedback on this Technical Report, please visit http:/standards.sae.org/AS3564E RATIONALE FIGURE REDRAWN FOR CLARITY, NOTE ADDED FOR USE OF EXISTING STOCK, NOTES UPDATED. L NA F T E R F O R M I N G L

6、 O C K I N G F E A T U R EM L X 9 0 - 1 2 0 P R I O RT O F O R M I N G L O C K I N G F E A T U R E A B. 0 0 5 Z2 8 M I NTHKT O L P Z FT O L A HN O C O N V E X I T Y63T H R E A D DP E R A S 8 8 7 9WR E N C H I N G C O N F I G U R A T I O NP E R A S 8 7 0 - X X F O R T H I S D I S T A N C E B ET O L R

7、 ZM A R K P A R T N U M B E RA N D M A N U F A C T U R E R SI D E N T I F I C A T I O N P E RA S 4 7 8 C L A S S CF O R M O U T O F R O U N D I N I N T H I S A R E A T O A C H I E V ES E L F L O C K I N G R E Q U I R E M E N T( T O O L I N G M A R K S P E R M I S S I B L E )ZT O L R ZR A D I U S O R

8、 C H A M F E RT O FFIGURE 1 - NUT TABLE 1 TABLE 1A - DIMENSIONS PART NUMBER THREAD D B NOM AS870 DASH NO. E MAX F MIN AB H MIN K MAX AS3564-09 .1900-32UNJF-3B .2500 08 .340 .325 .200-.210 .125 .400 AS3564-10 .2500-28UNJF-3B .3125 10 .450 .410 .260-.270 .170 .510 AS3564-11 .3125-24UNJF-3B .3750 12 .5

9、25 .495 .323-.333 .175 .580 AS3564-12 .3750-24UNJF-3B .4375 14 .600 .560 .385-.395 .195 .645 AS3564-13 .4375-20UNJF-3B .5625 18 .690 .650 .448-.458 .220 .745 AS3564-14 .5000-20UNJF-3B .6250 20 .780 .740 .510-.525 .240 .830 AS3564-15 .5625-18UNJF-3B .6875 22 .880 .840 .573-.583 .270 .928 AS3564-16 .6

10、250-18UNJF-3B .7812 25 .970 .925 .635-.645 .290 1.020 AS3564-17 .7500-16UNJF-3B .9375 30 1.230 1.180 .760-.770 .320 1.222 AEROSPACE STANDARD AS3564 SHEET 2 OF 2 REV. E NUT, SELF-LOCKING, DOUBLE HEXAGON, SOLID FILM LUBRICATED, COUNTERBORED, 160 KSI, 800 F, UNS S66286 TABLE 1B - DIMENSIONS PART NUMBER

11、 L M N MAX T MIN P R AH APPROX MASS LB/100 AS3564-09 .190-.210 .085-.105 .262 .082 .004 .006 .0014 .44 AS3564-10 .250-.270 .100-.120 .326 .130 .005 .007 .0014 .77 AS3564-11 .312-.332 .115-.135 .392 .170 .005 .008 .0016 1.22 AS3564-12 .375-.395 .115-.135 .458 .210 .005 .009 .0016 1.90 AS3564-13 .438-

12、.458 .140-.160 .588 .230 .005 .010 .0020 3.31 AS3564-14 .500-.520 .140-.160 .654 .260 .006 .012 .0020 4.42 AS3564-15 .562-.582 .160-.180 .720 .320 .006 .014 .0020 7.96 AS3564-16 .625-.645 .160-.180 .817 .370 .007 .015 .0020 10.80 AS3564-17 .750-.770 .180-.200 .980 .500 .007 .016 .0020 19.57 NOTES 1.

13、 MATERIAL: CORROSION AND HEAT RESISTANT STEEL PER AMS5731 OR AMS5734 (UNS S66286). HEAT TREATMENT: AFTER FORMING, NUTS SHALL BE HEAT TREATED PER AMS2759/3 TO MEET THE HARDNESS SPECIFIED IN NOTE 3. /2/ PROCUREMENT SPECIFICATION: AS4393 EXCEPT AS FOLLOWS: a. COATING: SOLID FILM LUBRICANT PER AS1701, T

14、YPE VI, IN LIEU OF SILVER PLATE PER AMS2411. b. PRETREATMENT: PRIOR TO APPLYING THE SOLID FILM LUBRICANT, NUTS MAY BE PLATED WITH COPPER (AMS2418) OR NICKEL (AMS2403) OR BOTH TO .00025 MAXIMUM THICKNESS. c. DIMENSIONS APPLY AFTER PRETREATMENT PLATING AND BEFORE COATING WITH SOLID FILM LUBRICANT. d.

15、BAKE AT 800 F 15 F IN LIEU OF 1200 F FOR NUTS TESTED AFTER BAKE. 3. HARDNESS: 32 TO 42 HRC. 4. BREAK SHARP EDGES .003 TO .015, UNLESS OTHERWISE SPECIFIED. 5. FLUORESCENT PENETRANT INSPECTION PER ASTM E1417/E1417M, TYPE 1, SENSITIVITY LEVEL 2 MINIMUM, PRIOR TO PRETREATMENT OR COATING. ACCEPTANCE CRIT

16、ERIA PER AS3071. 6. SURFACE TEXTURE: SYMBOLS PER ASME Y14.36M. REQUIREMENTS PER ASME B46.1. UNLESS OTHERWISE SPECIFIED, SURFACES TO BE 125 MICROINCHES Ra. 7. DIMENSIONING AND TOLERANCING: ANSI Y14.5M-1982 (ASME PUBLICATION). 8. DIMENSIONS ARE IN INCHES. 9. DO NOT USE UNASSIGNED NUMBERS. 10. CLASSIFI

17、CATION: a. 160 KSI MINIMUM AXIAL STRENGTH AT ROOM TEMPERATURE. b. 800 F MAXIMUM BAKE TEMPERATURE FOR NUTS TESTED AFTER BAKING. 11. UNLESS OTHERWISE SPECIFIED, PART INVENTORY MANUFACTURED TO PREVIOUS REVISIONS OF THE APPLICABLE DRAWING OR SPECIFICATION MAY BE PROCURED AND USED UNTIL STOCK IS DEPLETED

18、. 12. REVISION INDICATOR: A CHANGE BAR (I) LOCATED IN THE LEFT MARGIN IS FOR THE CONVENIENCE OF THE USER IN LOCATING AREAS WHERE TECHNICAL REVISIONS, NOT EDITORIAL CHANGES, HAVE BEEN MADE TO THE PREVIOUS ISSUE OF THIS DOCUMENT. AN (R) SYMBOL TO THE LEFT OF THE DOCUMENT TITLE INDICATES A COMPLETE REV

19、ISION OF THE DOCUMENT, INCLUDING TECHNICAL REVISIONS. CHANGE BARS AND (R) ARE NOT USED IN ORIGINAL PUBLICATIONS, NOR IN DOCUMENTS THAT CONTAIN EDITORIAL CHANGES ONLY. AS AND AMS ARE SAE INTERNATIONAL PUBLICATIONS. ASTM IS ASTM INTERNATIONAL PUBLICATION. ASME IS AMERICAN SOCIETY OF MECHANICAL ENGINEERS PUBLICATION.