SAE AS 22759 35-2000 WIRE ELECTRICAL FLUOROPOLYMER-INSULATED CROSSLINKED MODIFIED ETFE NORMAL WEIGHT SILVER-COATED HIGH-STRENGTH COPPER ALLOY 200C 600 VOLT《600伏、200℃、高强度铜合金、镀银、标准重量.pdf

《SAE AS 22759 35-2000 WIRE ELECTRICAL FLUOROPOLYMER-INSULATED CROSSLINKED MODIFIED ETFE NORMAL WEIGHT SILVER-COATED HIGH-STRENGTH COPPER ALLOY 200C 600 VOLT《600伏、200℃、高强度铜合金、镀银、标准重量.pdf》由会员分享，可在线阅读，更多相关《SAE AS 22759 35-2000 WIRE ELECTRICAL FLUOROPOLYMER-INSULATED CROSSLINKED MODIFIED ETFE NORMAL WEIGHT SILVER-COATED HIGH-STRENGTH COPPER ALLOY 200C 600 VOLT《600伏、200℃、高强度铜合金、镀银、标准重量.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、Copyright 2000 Society of Automotive Engineers, Inc. Printed in the U.S.A.All rights reserved. .TO PLACE A DOCUMENT ORDER: (724) 776-4970 FAX: (724) 776-0790 SAE WEB ADDRESS: http:/www.sae.org400 Commonwealth Drive, Warrendale, PA 15096-0001SAE Technical StandardsBoard Rulesprovidethat:“Thisreport i

2、s published by SAEtoadvance thestateoftechnical and engineeringsciences. The useofthis reportisentirelyvoluntary, and its applicabilityand suitability for any particularuse, includingany patent infringement arising therefrom, isthe soleresponsibility of the user.”SAE reviews each technical report at

3、 least every five years at whichtime it maybereaffirmed, revised, or cancelled. SAE invites your writtencomments and suggestions.SHEET 1 OF 6AS22759/35THIRD ANGLE PROJECTIONAEROSPACE STANDARDAS22759/35ISSUED2000-04WIRE, ELECTRICAL, FLUOROPOLYMER-INSULATED, CROSS-LINKED MODIFIED ETFE, NORMAL WEIGHT,

4、SILVER-COATED,HIGH-STRENGTH COPPER ALLOY, 200C, 600 VOLTPREPARED BY SAE SUBCOMMITTEE AE-8DFEDERAL SUPPLY CLASS 6145NOTICETHIS DOCUMENT HAS BEEN TAKEN DIRECTLY FROM U.S. MILITARY SPECIFICATION MIL-W-22759/35D, AMENDMENT 1 AND CONTAINS ONLY MINOR EDITORIAL AND FORMAT CHANGES REQUIRED TO BRING IT INTO

5、CONFORMANCE WITH THE PUBLISHING REQUIREMENTS OF SAE TECHNICAL STANDARDS. THE INITIAL RELEASE OF THIS DOCUMENT IS INTENDED TO REPLACE MIL-W-22759/35D, AMENDMENT 1. ANY PART NUMBERS ESTABLISHED BY THE ORIGINAL SPECIFICATION REMAIN UNCHANGED.THE ORIGINAL MILITARY SPECIFICATION WAS ADOPTED AS AN SAE STA

6、NDARD UNDER THE PROVISIONS OF THE SAE TECHNICAL STANDARDS BOARD (TSB) RULES AND REGULATIONS (TSB 001) PERTAINING TO ACCELERATED ADOPTION OF GOVERNMENT SPECIFICATIONS AND STANDARDS. TSB RULES PROVIDE FOR (A) THE PUBLICATION OF PORTIONS OF UNREVISED GOVERNMENT SPECIFICATIONS AND STANDARDS WITHOUT CONS

7、ENSUS VOTING AT THE SAE COMMITTEE LEVEL, AND (B) THE USE OF THE EXISTING GOVERNMENT SPECIFICATION OR STANDARD FORMAT.UNDER DEPARTMENT OF DEFENSE POLICIES AND PROCEDURES, ANY QUALIFICATION REQUIREMENTS AND ASSOCIATED QUALIFIED PRODUCTS LISTS ARE MANDATORY FOR DOD CONTRACTS. ANY REQUIREMENT RELATING T

8、O QUALIFIED PRODUCTS LISTS (QPLS) HAS NOT BEEN ADOPTED BY SAE AND IS NOT PART OF THIS SAE TECHNICAL DOCUMENT.Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-400 Commonwealth Drive, Warrendale, PA 15096

9、-0001WIRE, ELECTRICAL, FLUOROPOLYMER-INSULATED, CROSS-LINKED MODIFIED ETFE, NORMAL WEIGHT, SILVER-COATED,HIGH-STRENGTH COPPER ALLOY, 200C, 600 VOLTAEROSPACE STANDARD AS22759/35SHEET 2 OF 6AS22759/35THE REQUIREMENTS FOR ACQUIRING THE WIRE DESCRIBED HEREIN SHALL CONSIST OF THIS SPECIFICATION AND THE L

10、ATEST ISSUE OF MIL-W-22759.FIGURE 1. GENERAL CONFIGURATION.TABLE I. CONSTRUCTION DETAILS.Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-400 Commonwealth Drive, Warrendale, PA 15096-0001WIRE, ELECTRICA

11、L, FLUOROPOLYMER-INSULATED, CROSS-LINKED MODIFIED ETFE, NORMAL WEIGHT, SILVER-COATED,HIGH-STRENGTH COPPER ALLOY, 200C, 600 VOLTAEROSPACE STANDARD AS22759/35SHEET 3 OF 6AS22759/35TABLE II. PERFORMANCE DETAILS.RATINGS:Temperature rating: 200C (392F) maximum continuous conductor temperature.Voltage rat

12、ing: 600 volts (rms) at sea level.ADDITIONAL REQUIREMENTS:Acid resistance: No requirement.Blocking: 230C 3C (446F 5.4F).Color: In accordance with MIL-STD-104, class 1; white preferred. Conformity of color to the limits of MIL-STD-104 shall not be required after crosslinking proof test or life cycle

13、oven exposure.Color striping or banding durability: 125 cycles (250 strokes) (min), 500 grams weight.Crosslinking proof test: 7 hours at 300C 3C (572F 5.4F). Quality conformance test, group II. Requirements and procedures as for life cycle except for time and temperature.Dielectric test after immers

14、ion: 2,500 volts (rms), 60 Hz.Flammability: Quality conformance test, group II. For requirements and procedures see below.Humidity resistance: After humidity exposure, wire shall meet the requirements for initial insulation resistance.Identification of product: Not required for size 24 and smaller.

15、Color code designator not required.Identification durability: 125 cycles (250 strokes) (min), 500 grams weight.Immersion: For procedure see below.Impulse dielectric test: 8.0 kilovolts (peak), 100 percent test.Insulation resistance, initial: 5,000 megohms for 1,000 feet (min).Insulation thickness:0.

16、003 inch (min) for primary insulation.0.004 inch (min) for outer jacket.0.008 inch (min) for total insulation.Life cycle: 500 hours at 230C 3C (446F 5.4F). Dielectric test, 2,500 volts (rms), 60 Hz. Procedure to use mandrels coated with polytetrafluoroethylene in the form of either enamel or wrapped

17、 tape, such that the diameter of the mandrels, after coating, still conform to the requirements of performance details, table II.Low temperature (cold bend):Bend temperature, -65C 3C (-85F 5.4F).Dielectric test, 2,500 volts (rms), 60 Hz.Copyright SAE International Provided by IHS under license with

18、SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-400 Commonwealth Drive, Warrendale, PA 15096-0001WIRE, ELECTRICAL, FLUOROPOLYMER-INSULATED, CROSS-LINKED MODIFIED ETFE, NORMAL WEIGHT, SILVER-COATED,HIGH-STRENGTH COPPER ALLOY, 200C, 600 VOLTAEROSPACE STANDARD AS2275

19、9/35SHEET 4 OF 6AS22759/35Physical properties of insulation: Pulled at 2 inches per minute. Primary insulation shall be separated from the outer jacket for determination of primary insulation tensile strength and elongation.Tensile strength, 5,000 lbf/in2 (min) for primary insulation, 500 lbf/in2 (m

20、in) for total insulation (primary insulationand jacket).Elongation, 125 percent (min) for primary insulation, 75 percent (min) for total insulation (primary insulationand jacket).Propellant resistance: No dielectric breakdown. For procedure see below.Shrinkage: 0.125 inch (max) at 230C 3C (446F 5.4F

21、).Smoke: 250C 5C (482F 9F); no visible smoke.Solderability: All conductors shall be tested in accordance with MIL-STD-202, method 208 without steam aging.Spark test of primary insulation: 1500 volts (rms), 60 Hz.Surface resistance: 500 megohms - inches (min), initial and final readings.Thermal shock

22、 resistance:Oven temperature, 200C 3C (392F 5.4F).Maximum change in measurement, 0.060 inch.Wicking: Procedure II; weight increase, no requirement. Dye travel between layers of insulation, 2.25 inches (max) from end of specimen.Wire length requirements: Schedule B.Wrap test:Wrap back test.Oven tempe

23、rature, 313C 3C (595F 5.4F).Flammability requirements and procedure:The flammability test of MIL-W-22759 shall be modified for the wire of this specification sheet as follows: The specified test burner shall be used without the wing top flame spreader and shall be adjusted to furnish a 3-inch conica

24、l flame with an inner cone approximately 1 inch in height and a temperature of 955C 30C (1751F 54F) at its hottest point. A sheet of facial tissue conforming to UU-T-450 shall be suspended taut and horizontal 9-1/2 inches below the marked point on the wire specimen in the test chamber and at least 1

25、/2 inch above the floor of the chamber. The period of application of the hot flame tip to the marked point on the wire specimen shall be 30 seconds for all sizes of wire. Observations shall include time of burning after removal of the test flame, final distance of flame travel on the wire above the

26、test mark, and presence or absence of flame in the facial tissue due to incendiary drip from the specimen. Requirements shall be:Breaking of the wire specimen in size 24 or smaller shall not be considered as failure provided the requirements for duration of flame, final distance of flame travel, and

27、 absence of incendiary dripping are met.One specimen shall be tested from each sample unit. The post-flame dielectric test of MIL-W-22759 is not required for wire of this specification sheet.Immersion procedure:A 24-inch specimen, for each test fluid in table III, shall have its diameter measured an

28、d shall then be immersed to within 6inches of each end for the time and temperature specified. During immersion, the radius of bend of the wire shall be not less than 14 nor more than 35 times the specified maximum diameter of the wire under test. Upon removal from the test fluid, the specimen shall

29、 be wiped dry and then remain for 1 hour in free air at room temperature. The diameter shall be measured and compared to the initial diameter. The insulation shall be removed for a distance of 1/2 inch from each end of the specimen. The specimen shall then be subjected to the bend test and dielectri

30、c test specified in the procedure for life cycle testing.Duration of after-flame 3 seconds (max)Flame travel 3.0 inches (max)No flaming of tissueCopyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-400 Comm

31、onwealth Drive, Warrendale, PA 15096-0001WIRE, ELECTRICAL, FLUOROPOLYMER-INSULATED, CROSS-LINKED MODIFIED ETFE, NORMAL WEIGHT, SILVER-COATED,HIGH-STRENGTH COPPER ALLOY, 200C, 600 VOLTAEROSPACE STANDARD AS22759/35SHEET 5 OF 6AS22759/35TABLE III. IMMERSION TEST FLUIDSPropellant resistance procedure: (

32、Initial qualification test only)Specimens of finished wire, 24 inches long, shall be immersed to within 1-1/2 inches of each end in the following propellants for the specified time at normal room temperature, using a separate specimen for each propellant.Copyright SAE International Provided by IHS u

33、nder license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-400 Commonwealth Drive, Warrendale, PA 15096-0001WIRE, ELECTRICAL, FLUOROPOLYMER-INSULATED, CROSS-LINKED MODIFIED ETFE, NORMAL WEIGHT, SILVER-COATED,HIGH-STRENGTH COPPER ALLOY, 200C, 600 VOLTAEROSPA

34、CE STANDARD AS22759/35SHEET 6 OF 6AS22759/35During immersion, the radius of bend of the wire shall be not less than 14 nor more than 35 times the specified maximum diameter of the wire under test. Upon removal from the liquids, the specimens shall remain for no more than 48 hours in free air at room

35、 temperature. The insulation shall be removed for a distance of 1 inch from each end of the specimens, and the specimens shall be subjected to the dielectric test specified for life cycle testing.Qualifying activity: The activity responsible for the qualified products covered by this specification s

36、heet is Naval Avionics Center, Code B/714, 6000 East 21st Street, Indianapolis, IN 46219-2189.Propellant Immersion timea. MIL-P-26536, Propellant, Hydrazine 30 minutesb. MIL-P-26539, Propellant, Nitrogen Tetroxide 1 minutec. MIL-P-27402, Propellant, Hydrazine - Uns-Dimethylhydrazine (50 percent N2H4 - 50 percent UDMH)30 minutesCopyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-