FORD WSS-M4D550-A11-2013 THERMOPLASTIC POLYOLEFIN ELASTOMER (TPO) 18% TALC FILLED HIGH IMPACT MOLDED IN COLOR INTERIOR TO BE USED WITH FORD WSS-M99P1111-A .pdf

《FORD WSS-M4D550-A11-2013 THERMOPLASTIC POLYOLEFIN ELASTOMER (TPO) 18% TALC FILLED HIGH IMPACT MOLDED IN COLOR INTERIOR TO BE USED WITH FORD WSS-M99P1111-A .pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M4D550-A11-2013 THERMOPLASTIC POLYOLEFIN ELASTOMER (TPO) 18% TALC FILLED HIGH IMPACT MOLDED IN COLOR INTERIOR TO BE USED WITH FORD WSS-M99P1111-A .pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions REV 02 2013 04 25 Revised Editorial, corrected recycling code Y. Bankowski. NA 2013 03 14 Revised Complete revision Y. Bankowski, NA 2007 04 19 Activated C. Boese, M. Masserant Controlled document at www.MATS Copyright 2013, Ford Global Techn

2、ologies, LLC Page 1 of 8 THERMOPLASTIC POLYOLEFIN ELASTOMER (TPO), WSS-M4D550-A11 18% TALC FILLED HIGH IMPACT, MOLDED IN COLOR, INTERIOR 1. SCOPE The material defined by this specification is a low gloss, high impact, rigid thermoplastic polyolefin elastomer (TPO) injection molding compound, mineral

3、 (talc) filled, UV stabilized, high scratch resistant for interior applications that require low temperature ductility. 2. APPLICATION This specification was released originally for material used for the 2008 Focus instrument panel with a seamless deployable passenger airbag. 2.1 LIMITATIONS Seamles

4、s airbag applications do not allow the use of regrind. This material is not to be used in applications requiring painting because it contains an anti-scratch additive. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Company

5、s Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 Many 4D resin specifications prior to 2011, identified certain requirements with the symbol (s), which indicated that the mean and +/- 3 sigma values were to be reported. The specification minimum, maximum or range was establis

6、hed using 3 sigma data. For 2011 and beyond, refer to Table 1 for number of samples required for each test to meet specification limits. 3.1.2 This specification is based on virgin materials. Materials with post-consumer, post industrial, or repolymerised recycled materials as defined by WRS-M99P42-

7、A1 are preferred and should be used whenever feasible. 3.1.3 The use of regrind is permitted, for economic / environmental reasons, with compliance as indicated in Ford Engineering CAD and Drafting Standard E-4. 3.1.4 Materials used in interior applications must meet the requirements outlined in WSS

8、-M99P2222-D1/Latest, Performance, Vehicle Interior Environment Quality Material/Component Requirements. Data must be included in material submission package. 3.1.5 Performance Criteria: Parts using this specification shall meet the appropriate performance specification, WSS-M15P4-F/Latest for Hard,

9、Interior, Molded-in-Color component performance or WSS-M15P45-B/Latest. ENGINEERING MATERIAL SPECIFICATION WSS-M4D550-A11 Copyright 2013, Ford Global Technologies, LLC Page 2 of 8 3.2 SAMPLE PREPARATION Unless otherwise specified all tests shall be carried out on injection molded, one-end gated test

10、 specimens. The test specimens A and D shall be molded using molding conditions defined in ISO 1873-2. No annealing is allowed. See Table 1 for the number of specimens required. Specimens shall be as follows: Specimen A 150 minimum x 10 x 4.0 +/- 0.2 mm (ISO 527-2, Specimen Type 1A) Specimen B 355 x

11、 100 x 1.0 +/- 0.1 mm (ISO 3795) Specimen C 145 x 60 x 3.2 +/- 0.2 mm Specimen D Center of Specimen A. 80 x 10 x 4.0 +/- 0.2 mm Specimen E 100 mm diameter x 3.2 mm Specimen F 80 mm diameter x 3.2 mm Specimen G 90 mm x 200 mm Specimen H 50 +/- 1 mm diameter x 3.2 +/- 0.2 mm Specimen I 100 mm x 150 mm

12、, min 3.3 APPEARANCE 3.3.1 Weathering Resistance Rating 4 min (FLTM BO 116-01, 3609.6 kJ/m2 exposure Specimen C from smooth polished mold, ISO 105-A02 / AATCC Evaluation Procedure 1) Every 526.4kJ/m2 remove the samples from the weatherometer and allow them to cool for one hour. Conduct a tactile eva

13、luation and report any tackiness. Visually evaluate and report any spewing or other exudation. After exposure the material shall show no fading or color change in excess of specified AATCC rating. In addition, there shall be no cracking, crazing or other deterioration. Use regional choice colors for

14、 initial approval and report color house used. See Table 2 for additional color durability submission requirements. 3.3.2 Resistance to Scratch and Mar (FLTM BO 162-01, Specimen I) Scratch Rating 2 at 2N, max Whitening/Color Change Rating 1 at 15N, max Marring Rating 2 at 2N, max These values are de

15、rived from colored and grained samples in agreement with Materials Engineering. Details regarding color house, let down ratio, colors, grain, etc can be found in the approval package. 3.4 MATERIAL PROPERTIES 3.4.1 Filler Content 16 - 20, % (ISO 3451-1, Method A) 3.4.2 Density 1.00 1.05 g/cm3 (ISO 11

16、83, Method A) ENGINEERING MATERIAL SPECIFICATION WSS-M4D550-A11 Copyright 2013, Ford Global Technologies, LLC Page 3 of 8 3.4.3 Tensile Strength at Yield 16 MPa min (ISO 527-1 Flow 4.8 E-5 mm/mm/ C 3.5.4 Coefficient of Linear Thermal Expansion; Across Flow 8.8 E-5 mm/mm/ C 3.5.5.1 Impact Strength, N

17、otched Izod at 23 +/- 2 C 56 kJ/m2 3.5.5.2 Impact Strength ,Notched Izod at -40 +/- 2 C 9 kJ/m2 3.5.6.1 Impact Strength, Multiaxial; Max Load Energy at 23 +/- 2 C 21 J 3.5.6.2 Impact Strength, Multiaxial; Max Load Energy at -40 +/- 2 C 25 J 3.5.7 Poissons Ratio 0.4 N/A 4.2 MATERIAL IDENTIFICATION FO

18、R RECYCLING PURPOSES TPO-(PP+EPM)-TD18 (ISO 1043/11469/18064) ENGINEERING MATERIAL SPECIFICATION WSS-M4D550-A11 Copyright 2013, Ford Global Technologies, LLC Page 6 of 8 5. SUMMARY OF REVISIONS 2013 04 25 Corrected recycling code 2013 03 14 -Updated Title, Scope and Limitations section, revised form

19、at to global resin template. -Melt Flow, Multiaxial Impact Impact Strength and Izod Impact moved to report only -Added Odor Test -Revised Resistance to Scratch and Mar test method -Removed Hardness and Instrument Impact after Heat Aging ENGINEERING MATERIAL SPECIFICATION WSS-M4D550-A11 Copyright 201

20、3, Ford Global Technologies, LLC Page 7 of 8 Table 1: Number of Specimens Required Initial Approval New Manufacturing Location for Previously Approved Material Para. Test Minimum Lots Specimens per lot Total Test Specimens Lots Specimens per lot Total Test Specimens 3.1 WSS-M99P1111-A 3.1.3 WSS-M99P

21、2222-D1/Latest Total Carbon, Hazardous Substances, Formaldehyde, Acraldehyde, Acetaldehyde (See below for odor and fogging) 1 1 1 per test 3.1.4 WSS-M15P4-F/Latest or WSS-M15P45-B/Latest Reference Performance Specification 3.3.1 Weathering Resistance 1 1 1 3.3.2 Resistance to Scratch and Mar 1 1 1 3

22、.4.1 Filler Content* 3 1 3 3 1 3 3.4.2 Density 1 3 3 3.4.3 Tensile Strength at Yield* 3 5 15 1 5 5 3.4.4 Tensile Modulus 1 10 10 3.4.5 Flexural Modulus* 3 10 30 1 10 10 3.4.6 Impact Strength, Notched Charpy, (per condition)* 3 10 30 1 10 10 3.4.7 Heat Deflection Temperature* 3 2 6 1 2 2 3.4.8 Heat A

23、ged Properties 3.4.8.1 Tensile Strength at Yield Change 1 5 5 3.4.8.2 Impact Strength, Notched Charpy, Change 1 10 10 3.4.9 Odor 1 9 9 3.4.10 Fogging 1 3 3 3.4.11 Flammability 1 5 5 3.5.1 Melt Flow Rate 1 1 1 3.5.2 Elongation at Yield 3 5 15 1 5 5 3.5.3 Mold Shrinkage 1 5 5 3.5.4 Coefficient of Line

24、ar Thermal Expansion (per condition) 1 3 3 3.5.5 Impact Strength, Notched Izod (per condition) 1 10 10 3.5.6 Impact Strength, Multiaxial 3 10 30 1 10 10 3.5.7 Poissons Ratio 1 1 1 * For these requirements, the 3 Sigma value from the raw data is used to set the requirement max or min. ENGINEERING MAT

25、ERIAL SPECIFICATION WSS-M4D550-A11 Copyright 2013, Ford Global Technologies, LLC Page 8 of 8 Table 2: Minimum Color Property Testing Contact Materials Engineering for Color Test Work Plan Para. Test Lots Specimens per Lot Total Test Specimens Color Test Direction 3.3.1 Weathering Resistance 1 1 1 Ev

26、ery Color 3.3.2 Resistance to Scratch and Mar 1 3 3 As directed by Materials Engineering 3.4.3 Tensile Strength at Yield 1 5 5 As directed by Materials Engineering 3.4.5 Flexural Modulus 1 10 10 As directed by Materials Engineering 3.4.6 Impact Strength, Notched Charpy at 23 +/- 2 C 1 10 10 As directed by Materials Engineering 3.4.9 Odor 1 9 9 As directed by Materials Engineering 3.4.10 Fogging Photometric 1 3 3 As directed by Materials Engineering 3.4.11 Flammability 1 5 5 Every Color