FORD WSB-M5B280-C2-2009 PRIMER CLEANER GLASS SILANE TRANSPARENT RED TO BE USED WITH FORD WSS-M99P1111-A 《玻璃用红色透明底漆 清洁剂 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSB-M5B280-C上[使用 FORD.pdf

《FORD WSB-M5B280-C2-2009 PRIMER CLEANER GLASS SILANE TRANSPARENT RED TO BE USED WITH FORD WSS-M99P1111-A 《玻璃用红色透明底漆 清洁剂 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSB-M5B280-C上[使用 FORD.pdf》由会员分享，可在线阅读，更多相关《FORD WSB-M5B280-C2-2009 PRIMER CLEANER GLASS SILANE TRANSPARENT RED TO BE USED WITH FORD WSS-M99P1111-A 《玻璃用红色透明底漆 清洁剂 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSB-M5B280-C上[使用 FORD.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 05 29 C2 N-STATUS Replaced by WSS-M5B280-C5 M. Mehandru, FNA 2008 11 06 Revised Completely revised; Updated 2.1 and deleted Table 1 and Table 2, Inactivated C & C3 See summary of Revisions. Mukta Mehandru, FNA 1990 02 08 Released NB00E001

2、79051000 K. King, E. R. Rezendes Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1 of 4 PRIMER/CLEANER, GLASS, SILANE, TRANSPARENT YELLOW INACTIVE WSB-M5B280-C PRIMER/CLEANER, GLASS, SILANE, TRANSPARENT RED N-STATUS WSB-M5B280-C2 PRIMER/CLEANER, GLASS, SILANE, NON-

3、PHOTOCHEMICALLY INACTIVE WSB-M5B280-C3 REACTIVE TRANSPARENT RED 1. SCOPE The materials defined by these specifications are glass cleaners/adhesion promoters that deposit monomolecular films and also remove surface contaminates. 2. APPLICATION These specifications were released originally for materia

4、ls used to clean and condition windshield glass prior to the application of adhesion promoting primer ( WSS-M2G314-B2). (These primers should be applied by means of a brush, felt or other suitable applicator. 2.1 MANUFACTURING PROCESS RECOMMENDATION These primers are moisture sensitive and require s

5、pecial handling for manual and automated process. Please contact supplier or the Material Engineering for current process standards. Approved suppliers are responsible for maintaining the accuracy and relevancy of these process parameters (in their Process Standard). Approved suppliers must submit a

6、ny changes to these process parameters in a timely manner (within 30 days) for review and approval by Materials Engineering, Vehicle Operation, and Product Development Engineer. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to t

7、he Companys Standard Requirements For Production Materials (WSS-M99P1111-A). ENGINEERING MATERIAL SPECIFICATION WSS-M5B280-C/C3 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 4 3.2 COLOR WSB-M5B280-C Transparent Yellow WSB-M5B280-C2 Transparent Red WSB-M5B280

8、-C3 Transparent Red 3.3 VISCOSITY, max (FLTM BI 111-01, No. 4, Ford Cup) WSB-M5B280-C 25 - 40 s WSB-M5B280-C2 25 - 40 s WSB-M5B280-C3 25 - 40 s 3.4 WEIGHT PER VOLUME (ASTM D 1475) The weight tolerance for any one supplier shall be +/- 0.075 kg/L based on the weight of the original approved productio

9、n sample (see para 4.3). 3.5 DRYING RATE, max WSB-M5B280-C 1 minute WSB-M5B280-C2 1 minute WSB-M5B280-C3 10 minutes Test Method: Apply a 0.008 - 0.013 mm film of primer 25 mm wide to a 75 x 75 mm clean glass plate. To determine the primer drying rate, immediately at rapid intervals, dab the primer f

10、ilm with a wad of absorbent cotton. Observe if any of the cotton fibers adhere to the primed surface. Record the drying rate, as the time elapsed from the initial primer application until the cotton fibers do not adhere to the primer. Note: The drying rate is longer for the C3 suffix material due to

11、 the type of solvent. C4 is a one step clear primer and thus has a different drying rate. Actual differences in drying rate as processed through the assembly plant are negligible. 3.9 STORAGE STABILITY Shall be stored at ambient room temperature below 35 C, away from all sources of heat such as oven

12、s, direct sunlight etc. The material should not be stored outside. Under these storage conditions, the maximum shelf life of the material in unopened containers shall be six (4) months from date of receipt at Ford Motor Co. Material may not be used after the expiration date unless the supplier has g

13、iven written documentation to Materials Engineering and the affected Manufacturing Plant that the material conforms to requirements outlined in the material control plan. The supplier shall also indicate in the letter the number of additional days the material will be usable. ENGINEERING MATERIAL SP

14、ECIFICATION WSS-M5B280-C/C3 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 3 of 4 3.10 QUALITY The material shall be a smooth, homogenous mixture free from foreign materials and properties detrimental to normal production operations. 3.11 NON-INTERCHANGEABILITY OF

15、 MATERIALS Only approved urethane adhesive WSB-M2G316-B, or WSS-M2G316-B2/B3/B4/B5, Glass Cleaner WSS-M5B280-C5, or WSS-M5B280-C4 Glass Primer WSS-M2G314-B2, Metal Primer WSB-M2G234-C/C2/C3 all from the same production source shall be used in conjunction with one another. Note that WSS-M5B280-C4 mus

16、t be used with WSS-M2G316-B4. 3.12 FUNCTIONAL APPROVAL Materials being evaluated for approval to this specification shall be subjected to a production trial. Functional trial results must be approved by the affected assembly operation and Design Engineering. Results shall be made available to Materi

17、als Engineering prior to material approval and release. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 FLASH POINT, Max. WSB-M5B280-C, C2 2 C (ASTM D 3278, Setaflash Closed Cup) WSB-M5B280-C3 13 C

18、 (ASTM D 3278, Setaflash Closed Cup) 4.2 FLAMMABILITY AND/OR TOXICITY These materials represent potential fire and/or health hazards. The Manufacturing Engineering Department shall notify both the Plant Security and the Safety Units of their presence in the Plant to assure that proper fire and/or he

19、alth precautions are provided. The location in which they are used or stored shall be included in the notifications. 4.3 WEIGHT PER VOLUME (ASTM D 816) Materials conforming to this specification and found satisfactory in production, range from 0.65 - 0.96 kg/L. ENGINEERING MATERIAL SPECIFICATION WSS

20、-M5B280-C/C3 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 4 of 4 4.4 RELATED MATERIALS AND PROCEDURE 4.4.1 Glass Primer WSS-M2G314-B2 4.4.2 Metal Primer WSB-M2G234-C WSB-M2G234-C3 4.4.3 Urethane Adhesive WSS-M2G316-B2/B3/B4/B5/B6 4.4.5 Performance Spec WSS-M11P5

21、7-A5 4.5 ODOR Shall be free form objectionable odors, both at “as received“ and application temperatures. 5.0 SUMMARY OF REVISIONS 2008 11 06 1. Seprarated the C4 Spec. 2. Revised Application to reflect the new specification for black out primer. 3. Revised Manufacturing Process Recommendation and deleted Tables 1, and 2. 4. Deleted Shear Adhesion Requirement. 5. Revised Storage Stability.