FORD S-M99J4500-C-2006 MARKING INK TO BE USED WITH FORD WSS-M99P1111-A 《标记墨水 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD S-M99J4500-C-2006 MARKING INK TO BE USED WITH FORD WSS-M99P1111-A 《标记墨水 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD S-M99J4500-C-2006 MARKING INK TO BE USED WITH FORD WSS-M99P1111-A 《标记墨水 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 02 17 Revised Inserted 3.0; Deleted 3.12 and 4 1994 12 19 Revised and Retyped Was 5 pages 1982 08 13 Released B/656707 TP Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 MARKING INK S-M99J4500-C 1

2、. SCOPE The material defined by this specification is a fast drying marking ink. 2. APPLICATION The material is generally used as in identification on steel parts. 3. REQUIREMENTS Material specification requirements are to be used for initial qualification of materials. 3.0 STANDARD REQUIREMENTS FOR

3、 PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 COLORS (similar to) RAL 9002 or BS 2660, No. 9-102 White RAL 6010 or BS 381 C, No. 221 Green RAL 1012 or BS 381 C, No. 355 Yellow RAL 3000 or

4、BS 381 C, No. 537 Red RAL 2000 or BS 381 C, No. 557 Orange RAL 9005 or BS 381 C, No. 642 Black RAL 5009 or BS 381 C, No. 107 Blue RAL 4001 or BS 381 C, No. 796 Violet 3.2 NON-VOLATILE (FLTM BI 102-01) Minimum 25% Min 30% Black Green Red Yellow Orange White Violet Blue 3.3 VEHICLE Synthetic resins an

5、d nitrocellulose. 3.4 VISCOSITY AS RECEIVED (FLTM BI 111-01) 90 +/- 10 s; FC-4 at 25 C. Suitable for application by brush. ENGINEERING MATERIAL SPECIFICATIONS-M99J4500-CPrinted copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.5 STABILITY After 2 months storage at r

6、oom temperature there shall be no gelling and/or heavy pigment sedimentation in the closed can. 3.6 ADHESION Adequate adhesion to degreased steel. 3.7 TOXICITY The material shall not contain toxic components, e.g. lead, or lead compounds, benzene, chlorinated hydrocarbons etc., in excess of that per

7、mitted by the safety regulations currently prevailing in the country or plant where the material shall be used. The use of cadmium is prohibited. 3.8 FLASH POINT The flash point shall conform to the safety regulations applicable to the plant and/or country where the material shall be used. 3.9 GLOSS No requirements 3.10 HIDING POWER One application by brush to degreased steel shall completely hide the substrate. 3.11 DRYING TIME Tack Free: Maximum 10 minutes at room temperature Completely Dry: Maximum 15 minutes at room temperature.