《FORD ESW-M1C168-A-2008 GREASE INORGANIC - HIGH MELTING POINT - NLGI NO 2 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI No 2高熔点无机润滑脂 与标准FORD WSS-M99P1111-A一起使用 ［使用 FORD WSS-M13P13-A.pdf》由会员分享，可在线阅读，更多相关《FORD ESW-M1C168-A-2008 GREASE INORGANIC - HIGH MELTING POINT - NLGI NO 2 TO BE USED WITH FORD WSS-M99P1111-A 《NLGI No 2高熔点无机润滑脂 与标准FORD WSS-M99P1111-A一起使用 ［使用 FORD WSS-M13P13-A.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 10 10 N-STATUS Replaced by WSS-M13P13-A L. Schmalz, FNA 2004 02 18 Revised Para 3.0 inserted; para 3.9, 3.11, 4 deleted 1974 02 14 Released CW10C-WC-702332 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page

2、 1 of 2 GREASE, INORGANIC - HIGH MELTING POINT - NLGI NO. 2 ESW-M1C168-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The grease defined by this specification has a mineral oil with an inorganic thickening agent. 2. APPLICATION This specification was released originally for material used as a lubricant fo

3、r anti-friction bearings operating continuously at 150 oC or intermittently at 175 oC. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 COLOR Dark

4、 amber 3.2 ODOR Not unpleasant 3.3 DROPPING POINT, min 260 oC (ASTM D 566) 3.4 PENETRATION 270 - 300 (ASTM D 217, worked 60 strokes) 3.5 OXIDATION STABILITY, Pressure Drop max 25 psi (172 kPa) (ASTM D 942, 500 hrs.) 3.6 COPPER CORROSION, max 1A (ASTM D 130) 3.7 MINERAL OIL 3.7.1 Viscosity At 37.8 oC

5、, min 324 cSt (mm2/s) (ASTM D 445) 3.7.2 Viscosity At 98.9 oC 30 - 33 cSt (ASTM D 445) (mm2/s) 3.8 STORAGE STABILITY The worked penetration of the material after being stored for a six month period at a temperature of 38 oC +/- 2 oC in an oil tight container shall not have changed from the original

6、worked penetration of the material by more than 30 points. ENGINEERING MATERIAL SPECIFICATIONESW-M1C168-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.10 REAR AXLE BEARING FATIGUE MACHINE TEST During each model year, Product Engineering shall perform wh

7、eel bearing dynamometer fatigue tests in which twelve bearings shall be tested simultaneously. The load sequence shall simulate car operation. The test shall be halted at the first failure of any one of the twelve bearings. The remaining eleven bearings shall be examined. They shall show no deterioration nor separation of the grease.