EN ISO 6506-4-2014 en Metallic materials - Brinell hardness test - Part 4 Table of hardness values《金属材料 布氏硬度试验 第4部分 硬度数值表(ISO 6506-4 2014)》.pdf

《EN ISO 6506-4-2014 en Metallic materials - Brinell hardness test - Part 4 Table of hardness values《金属材料 布氏硬度试验 第4部分 硬度数值表(ISO 6506-4 2014)》.pdf》由会员分享，可在线阅读，更多相关《EN ISO 6506-4-2014 en Metallic materials - Brinell hardness test - Part 4 Table of hardness values《金属材料 布氏硬度试验 第4部分 硬度数值表(ISO 6506-4 2014)》.pdf（20页珍藏版）》请在麦多课文档分享上搜索。

1、BSI Standards PublicationBS EN ISO 6506-4:2014Metallic materials Brinellhardness testPart 4: Table of hardness valuesBS EN ISO 6506-4:2014 BRITISH STANDARDNational forewordThis British Standard is the UK implementation of EN ISO 6506-4:2014. It supersedes BS EN ISO 6506-4:2005 which is withdrawn.The

2、 UK participation in its preparation was entrusted to Technical Committee ISE/101/5, Indentation hardness testing.A list of organizations represented on this committee can be obtained on request to its secretary.This publication does not purport to include all the necessary provisions of a contract.

3、 Users are responsible for its correct application. The British Standards Institution 2014.Published by BSI Standards Limited 2014ISBN 978 0 580 79052 2 ICS 77.040.10 Compliance with a British Standard cannot confer immunity from legal obligations.This British Standard was published under the author

4、ity of the Standards Policy and Strategy Committee on 30 September 2014.Amendments/corrigenda issued since publicationDate T e x t a f f e c t e dEUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 6506-4 September 2014 ICS 77.040.10 Supersedes EN ISO 6506-4:2005English Version Metallic materia

5、ls - Brinell hardness test - Part 4: Table of hardness values (ISO 6506-4:2014) Matriaux mtalliques - Essai de duret Brinell - Partie 4: Tableau des valeurs de duret (ISO 6506-4:2014) Metallische Werkstoffe - Hrteprfung nach Brinell - Teil 4: Tabelle zur Bestimmung der Hrte (ISO 6506-4:2014) This Eu

6、ropean Standard was approved by CEN on 30 August 2014. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references

7、concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN membe

8、r into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, Fran

9、ce, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KO

10、MITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2014 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 6506-4:2014 EBS EN ISO 6506-4:2014EN ISO 6506-4:2014 (E) 3 Foreword This document (EN ISO 65

11、06-4:2014) has been prepared by Technical Committee ISO/TC 164 “Mechanical testing of metals“ in collaboration with Technical Committee ECISS/TC 101 “Test methods for steel (other than chemical analysis)” the secretariat of which is held by AFNOR. This European Standard shall be given the status of

12、a national standard, either by publication of an identical text or by endorsement, at the latest by March 2015, and conflicting national standards shall be withdrawn at the latest by March 2015. Attention is drawn to the possibility that some of the elements of this document may be the subject of pa

13、tent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN ISO 6506-4:2005. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this Eur

14、opean Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Sl

15、ovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. Endorsement notice The text of ISO 6506-4:2014 has been approved by CEN as EN ISO 6506-4:2014 without any modification. BS EN ISO 6506-4:2014ISO 6506-4:2014(E) ISO 2014 All rights reserved iiiContents PageForeword iv1 Scope . 12 Dete

16、rmination of the Brinell hardness for testing on flat surfaces . 1BS EN ISO 6506-4:2014ISO 6506-4:2014(E)ForewordISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is norma

17、lly carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in th

18、e work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In particular the

19、different approval criteria needed for the different types of ISO documents should be noted. This document was drafted in accordance with the editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives). Attention is drawn to the possibility that some of the elements of this docume

20、nt may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of any patent rights identified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received (see www.iso.org/

21、patents). Any trade name used in this document is information given for the convenience of users and does not constitute an endorsement.For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence to the WTO pri

22、nciples in the Technical Barriers to Trade (TBT) see the following URL: Foreword - Supplementary informationThe committee responsible for this document is ISO/TC 164, Mechanical testing of metals, Subcommittee SC 3, Hardness testing.This second edition cancels and replaces the first edition (ISO 650

23、6-4:2005), which has been technically revised.ISO 6506 consists of the following parts, under the general title Metallic materials Brinell hardness test: Part 1: Test method Part 2: Verification and calibration of testing machines Part 3: Calibration of reference blocks Part 4: Table of hardness val

24、uesiv ISO 2014 All rights reservedBS EN ISO 6506-4:2014INTERNATIONAL STANDARD ISO 6506-4:2014(E)Metallic materials Brinell hardness test Part 4: Table of hardness values1 ScopeThis part of ISO 6506 gives a table of the Brinell hardness values for use in tests on flat surfaces.2 Determination of the

25、Brinell hardness for testing on flat surfacesSee Tables 1 and 2. Where the measured indentation diameter value is not given in the table, a linear interpolation between the two adjacent values and between the two corresponding hardness values should be carried out. Each hardness value is quoted to t

26、hree significant figures, but is calculated from the nominal force-diameter index rather than from the specified force value, in order to avoid variations in the hardness values calculated at a specific force-diameter index. In some cases, this calculation method leads to an error of one digit in th

27、e least significant figure.Table 1Ball indenter D mmForce-diameter index 0,102 F/D230 15 10 5 2,5 1Test force F10 29,42 kN 14,71 kN 9,807 kN 4,903 kN 2,452 kN 980,7 N5 7,355 kN 2,452 kN 1,226 kN 612,9 N 245,2 N2,5 1,839 kN 612,9 N 306,5 N 153,2 N 61,29 N1 294,2 N 98,07 N 49,03 N 24,52 N 9,807 NTable

28、 2Ball indenter D mmForce-diameter index 0,102 F/D210 5 2,5 1 30 15 10 5 2,5 1Mean diameter of the indentation d mmBrinell hardness HBW2,40 1,200 0,600 0 0,240 653 327 218 109 54,5 21,82,41 1,205 0,602 5 0,241 648 324 216 108 54,0 21,62,42 1,210 0,605 0 0,242 643 321 214 107 53,5 21,42,43 1,215 0,60

29、7 5 0,243 637 319 212 106 53,1 21,22,44 1,220 0,610 0 0,244 632 316 211 105 52,7 21,12,45 1,225 0,612 5 0,245 627 313 209 104 52,2 20,92,46 1,230 0,615 0 0,246 621 311 207 104 51,8 20,7 ISO 2014 All rights reserved 1BS EN ISO 6506-4:2014ISO 6506-4:2014(E)Ball indenter D mmForce-diameter index 0,102

30、F/D210 5 2,5 1 30 15 10 5 2,5 1Mean diameter of the indentation d mmBrinell hardness HBW2,47 1,235 0,617 5 0,247 616 308 205 103 51,4 20,52,48 1,240 0,620 0 0,248 611 306 204 102 50,9 20,42,49 1,245 0,622 5 0,249 606 303 202 101 50,5 20,22,50 1,250 0,625 0 0,250 601 301 200 100 50,1 20,02,51 1,255 0

31、,627 5 0,251 597 298 199 99,4 49,7 19,92,52 1,260 0,630 0 0,252 592 296 197 98,6 49,3 19,72,53 1,265 0,632 5 0,253 587 294 196 97,8 48,9 19,62,54 1,270 0,635 0 0,254 582 291 194 97,1 48,5 19,42,55 1,275 0,637 5 0,255 578 289 193 96,3 48,1 19,32,56 1,280 0,640 0 0,256 573 287 191 95,5 47,8 19,12,57 1

32、,285 0,642 5 0,257 569 284 190 94,8 47,4 19,02,58 1,290 0,645 0 0,258 564 282 188 94,0 47,0 18,82,59 1,295 0,647 5 0,259 560 280 187 93,3 46,6 18,72,60 1,300 0,650 0 0,260 555 278 185 92,6 46,3 18,52,61 1,305 0,652 5 0,261 551 276 184 91,8 45,9 18,42,62 1,310 0,655 0 0,262 547 273 182 91,1 45,6 18,2

33、2,63 1,315 0,657 5 0,263 543 271 181 90,4 45,2 18,12,64 1,320 0,660 0 0,264 538 269 179 89,7 44,9 17,92,65 1,325 0,662 5 0,265 534 267 178 89,0 44,5 17,82,66 1,330 0,665 0 0,266 530 265 177 88,4 44,2 17,72,67 1,335 0,667 5 0,267 526 263 175 87,7 43,8 17,52,68 1,340 0,670 0 0,268 522 261 174 87,0 43,

34、5 17,42,69 1,345 0,672 5 0,269 518 259 173 86,4 43,2 17,32,70 1,350 0,675 0 0,270 514 257 171 85,7 42,9 17,12,71 1,355 0,677 5 0,271 510 255 170 85,1 42,5 17,02,72 1,360 0,680 0 0,272 507 253 169 84,4 42,2 16,92,73 1,365 0,682 5 0,273 503 251 168 83,8 41,9 16,82,74 1,370 0,685 0 0,274 499 250 166 83

35、,2 41,6 16,62,75 1,375 0,687 5 0,275 495 248 165 82,6 41,3 16,52,76 1,380 0,690 0 0,276 492 246 164 81,9 41,0 16,42,77 1,385 0,692 5 0,277 488 244 163 81,3 40,7 16,32,78 1,390 0,695 0 0,278 485 242 162 80,8 40,4 16,22,79 1,395 0,697 5 0,279 481 240 160 80,2 40,1 16,02,80 1,400 0,700 0 0,280 477 239

36、159 79,6 39,8 15,92,81 1,405 0,702 5 0,281 474 237 158 79,0 39,5 15,82,82 1,410 0,705 0 0,282 471 235 157 78,4 39,2 15,7Table 22 ISO 2014 All rights reservedBS EN ISO 6506-4:2014ISO 6506-4:2014(E)Ball indenter D mmForce-diameter index 0,102 F/D210 5 2,5 1 30 15 10 5 2,5 1Mean diameter of the indenta

37、tion d mmBrinell hardness HBW2,83 1,415 0,707 5 0,283 467 234 156 77,9 38,9 15,62,84 1,420 0,710 0 0,284 464 232 155 77,3 38,7 15,52,85 1,425 0,712 5 0,285 461 230 154 76,8 38,4 15,42,86 1,430 0,715 0 0,286 457 229 152 76,2 38,1 15,22,87 1,435 0,717 5 0,287 454 227 151 75,7 37,8 15,12,88 1,440 0,720

38、 0 0,288 451 225 150 75,1 37,6 15,02,89 1,445 0,722 5 0,289 448 224 149 74,6 37,3 14,92,90 1,450 0,725 0 0,290 444 222 148 74,1 37,0 14,82,91 1,455 0,727 5 0,291 441 221 147 73,6 36,8 14,72,92 1,460 0,730 0 0,292 438 219 146 73,0 36,5 14,62,93 1,465 0,732 5 0,293 435 218 145 72,5 36,3 14,52,94 1,470

39、 0,735 0 0,294 432 216 144 72,0 36,0 14,42,95 1,475 0,737 5 0,295 429 215 143 71,5 35,8 14,32,96 1,480 0,740 0 0,296 426 213 142 71,0 35,5 14,22,97 1,485 0,742 5 0,297 423 212 141 70,5 35,3 14,12,98 1,490 0,745 0 0,298 420 210 140 70,1 35,0 14,02,99 1,495 0,747 5 0,299 417 209 139 69,6 34,8 13,93,00

40、 1,500 0,750 0 0,300 415 207 138 69,1 34,6 13,83,01 1,505 0,752 5 0,301 412 206 137 68,6 34,3 13,73,02 1,510 0,755 0 0,302 409 205 136 68,2 34,1 13,63,03 1,515 0,757 5 0,303 406 203 135 67,7 33,9 13,53,04 1,520 0,760 0 0,304 404 202 135 67,3 33,6 13,53,05 1,525 0,762 5 0,305 401 200 134 66,8 33,4 13

41、,43,06 1,530 0,765 0 0,306 398 199 133 66,4 33,2 13,33,07 1,535 0,767 5 0,307 395 198 132 65,9 33,0 13,23,08 1,540 0,770 0 0,308 393 196 131 65,5 32,7 13,13,09 1,545 0,772 5 0,309 390 195 130 65,0 32,5 13,03,10 1,550 0,775 0 0,310 388 194 129 64,6 32,3 12,93,11 1,555 0,777 5 0,311 385 193 128 64,2 3

42、2,1 12,83,12 1,560 0,780 0 0,312 383 191 128 63,8 31,9 12,83,13 1,565 0,782 5 0,313 380 190 127 63,3 31,7 12,73,14 1,570 0,785 0 0,314 378 189 126 62,9 31,5 12,63,15 1,575 0,787 5 0,315 375 188 125 62,5 31,3 12,53,16 1,580 0,790 0 0,316 373 186 124 62,1 31,1 12,43,17 1,585 0,792 5 0,317 370 185 123

43、61,7 30,9 12,33,18 1,590 0,795 0 0,318 368 184 123 61,3 30,7 12,3Table 2 ISO 2014 All rights reserved 3BS EN ISO 6506-4:2014ISO 6506-4:2014(E)Ball indenter D mmForce-diameter index 0,102 F/D210 5 2,5 1 30 15 10 5 2,5 1Mean diameter of the indentation d mmBrinell hardness HBW3,19 1,595 0,797 5 0,319

44、366 183 122 60,9 30,5 12,23,20 1,600 0,800 0 0,320 363 182 121 60,5 30,3 12,13,21 1,605 0,802 5 0,321 361 180 120 60,1 30,1 12,03,22 1,610 0,805 0 0,322 359 179 120 59,8 29,9 12,03,23 1,615 0,807 5 0,323 356 178 119 59,4 29,7 11,93,24 1,620 0,810 0 0,324 354 177 118 59,0 29,5 11,83,25 1,625 0,812 5

45、0,325 352 176 117 58,6 29,3 11,73,26 1,630 0,815 0 0,326 350 175 117 58,3 29,1 11,73,27 1,635 0,817 5 0,327 347 174 116 57,9 29,0 11,63,28 1,640 0,820 0 0,328 345 173 115 57,5 28,8 11,53,29 1,645 0,822 5 0,329 343 172 114 57,2 28,6 11,43,30 1,650 0,825 0 0,330 341 170 114 56,8 28,4 11,43,31 1,655 0,

46、827 5 0,331 339 169 113 56,5 28,2 11,33,32 1,660 0,830 0 0,332 337 168 112 56,1 28,1 11,23,33 1,665 0,832 5 0,333 335 167 112 55,8 27,9 11,23,34 1,670 0,835 0 0,334 333 166 111 55,4 27,7 11,13,35 1,675 0,837 5 0,335 331 165 110 55,1 27,5 11,03,36 1,680 0,840 0 0,336 329 164 110 54,8 27,4 11,03,37 1,

47、685 0,842 5 0,337 326 163 109 54,4 27,2 10,93,38 1,690 0,845 0 0,338 325 162 108 54,1 27,0 10,83,39 1,695 0,847 5 0,339 323 161 108 53,8 26,9 10,83,40 1,700 0,850 0 0,340 321 160 107 53,4 26,7 10,73,41 1,705 0,852 5 0,341 319 159 106 53,1 26,6 10,63,42 1,710 0,855 0 0,342 317 158 106 52,8 26,4 10,63

48、,43 1,715 0,857 5 0,343 315 157 105 52,5 26,2 10,53,44 1,720 0,860 0 0,344 313 156 104 52,2 26,1 10,43,45 1,725 0,862 5 0,345 311 156 104 51,8 25,9 10,43,46 1,730 0,865 0 0,346 309 155 103 51,5 25,8 10,33,47 1,735 0,867 5 0,347 307 154 102 51,2 25,6 10,23,48 1,740 0,870 0 0,348 306 153 102 50,9 25,5

49、 10,23,49 1,745 0,872 5 0,349 304 152 101 50,6 25,3 10,13,50 1,750 0,875 0 0,350 302 151 101 50,3 25,2 10,13,51 1,755 0,877 5 0,351 300 150 100 50,0 25,0 10,03,52 1,760 0 880 0 0,352 298 149 99,5 49,7 24,9 9,953,53 1,765 0,882 5 0,353 297 148 98,9 49,4 24,7 9,893,54 1,770 0,885 0 0,354 295 147 98,3 49,2 24,6 9,83Table 24 ISO 2014 All rights reservedBS EN ISO 6506-4:2014ISO 6506-4:2014(E)Ball indenter D mmForce-diameter index 0,102 F/D210 5 2,5 1 30 15 10 5 2,5 1Mean diameter of the indentation d mmBrinell hardness HBW3,55