DIN EN 13523-29-2017 Coil coated metals - Test methods - Part 29 Resistance to environmental soiling (Dirt pick-up and striping) German version EN 13523-29 2017《卷材镀层金属 试验方法 第29部分 环.pdf

《DIN EN 13523-29-2017 Coil coated metals - Test methods - Part 29 Resistance to environmental soiling (Dirt pick-up and striping) German version EN 13523-29 2017《卷材镀层金属 试验方法 第29部分 环.pdf》由会员分享，可在线阅读，更多相关《DIN EN 13523-29-2017 Coil coated metals - Test methods - Part 29 Resistance to environmental soiling (Dirt pick-up and striping) German version EN 13523-29 2017《卷材镀层金属 试验方法 第29部分 环.pdf（11页珍藏版）》请在麦多课文档分享上搜索。

1、May 2017 English price group 9No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 25.220.60!%eQ8“2664621www.din.deDIN E

2、N 13523-29Coil coated metals Test methods Part 29: Resistance to environmental soiling (Dirt pickup and striping);English version EN 1352329:2017,English translation of DIN EN 13523-29:2017-05Bandbeschichtete Metalle Prfverfahren Teil 29: Bestndigkeit gegen Verschmutzung (Schmutzaufnahme und Streife

3、nbildung);Englische Fassung EN 1352329:2017,Englische bersetzung von DIN EN 13523-29:2017-05Tles prlaques Mthodes dessai Partie 29: Rsistance la pollution environnementale (salissures);Version anglaise EN 1352329:2017,Traduction anglaise de DIN EN 13523-29:2017-05SupersedesDIN EN 1352329:201007www.b

4、euth.deDocument comprises 11 pagesDTranslation by DIN-Sprachendienst.In case of doubt, the German-language original shall be considered authoritative.05.17 DIN EN 13523-29:2017-05 2 A comma is used as the decimal marker. National foreword This document (EN 13523-29:2017) has been prepared by Technic

5、al Committee CEN/TC 139 “Paints and varnishes” (Secretariat: DIN, Germany), Working Group WG 9 “Testing of coil coated metals” (Secretariat: DIN, Germany). The responsible German body involved in its preparation was DIN-Normenausschuss Beschichtungsstoffe und Beschichtungen (DIN Standards Committee

6、Coatings and Coating Materials), Working Committee NA 002-00-07 AA “General test methods for coating materials and coatings”. The European Standards referred to in this document have been published as DIN EN or DIN EN ISO Standards with the same number. Amendments This standard differs from DIN EN 1

7、3523-29:2010-07 as follows: a) the washing procedure has been corrected; b) the procedure in Clause 7 has been clarified; c) the text has been editorially revised and normative references have been updated. Previous editions DIN EN 13523-29: 2010-07 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM

8、EN 13523-29 March 2017 ICS 25.220.60 Supersedes EN 13523-29:2010English Version Coil coated metals - Test methods - Part 29: Resistance to environmental soiling (Dirt pick-up and striping) Tles prlaques - Mthodes dessai - Partie 29 : Rsistance la pollution environnementale (salissures)Bandbeschichte

9、te Metalle - Prfverfahren - Teil 29: Bestndigkeit gegen Verschmutzung (Schmutzaufnahme und Streifenbildung) This European Standard was approved by CEN on 30 December 2016. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this Europea

10、n Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (

11、English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgi

12、um, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden,

13、 Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2017 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN n

14、ational Members. Ref. No. EN 13523-29:2017 EEN 13523-29:2017 (E) 2 Contents Page European foreword . 3 1 Scope 5 2 Normative references 5 3 Terms and definitions . 5 4 Principle . 5 5 Apparatus and materials 5 6 Sample preparation 6 7 Procedure. 6 8 Evaluation 7 9 Test report . 8 Bibliography 9 DIN

15、EN 13523-29:2017-05 EN 13523-29:2017 (E) 3 European foreword This document (EN 13523-29:2017) has been prepared by Technical Committee CEN/TC 139 “Paints and varnishes”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by public

16、ation of an identical text or by endorsement, at the latest by September 2017, and conflicting national standards shall be withdrawn at the latest by September 2017. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN shall not be

17、 held responsible for identifying any or all such patent rights. This document supersedes EN 13523-29:2010. The main changes are: a) the washing procedure was corrected; b) the procedure in Clause 7 has been clarified; c) the text has been revised editorially and the normative references have been u

18、pdated. The EN 13523 series, Coil coated metals Test methods, consists of the following parts: Part 0: General introduction Part 1: Film thickness Part 2: Gloss Part 3: Colour difference Instrumental comparison Part 4: Pencil hardness Part 5: Resistance to rapid deformation (impact test) Part 6: Adh

19、esion after indentation (cupping test) Part 7: Resistance to cracking on bending (T-bend test) Part 8: Resistance to salt spray (fog) Part 9: Resistance to water immersion Part 10: Resistance to fluorescent UV radiation and water condensation Part 11: Resistance to solvents (rubbing test) Part 12: R

20、esistance to scratching Part 13: Resistance to accelerated ageing by the use of heat Part 14: Chalking (Helmen method) DIN EN 13523-29:2017-05 EN 13523-29:2017 (E) 4 Part 15: Metamerism Part 16: Resistance to abrasion Part 17: Adhesion of strippable films Part 18: Resistance to staining Part 19: Pan

21、el design and method of atmospheric exposure testing Part 20: Foam adhesion Part 21: Evaluation of outdoor exposed panels Part 22: Colour difference Visual comparison Part 23: Resistance to humid atmospheres containing sulfur dioxide Part 24: Resistance to blocking and pressure marking Part 25: Resi

22、stance to humidity Part 26: Resistance to condensation of water Part 27: Resistance to humid poultice (Cataplasm test) Part 29: Resistance to environmental soiling (Dirt pick-up and striping) According to the CEN-CENELEC Internal Regulations, the national standards organisations of the following cou

23、ntries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, P

24、oland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. DIN EN 13523-29:2017-05 EN 13523-29:2017 (E) 5 1 Scope This part of the EN 13523 series specifies a procedure for the comparative evaluation of resistance to soiling of an organic coating

25、 on a metallic substrate (coil coating) in an outdoor exposure environment, particularly the soiling defect known as “Tiger stripes”. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated

26、references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 13523-0, Coil coated metals - Test methods - Part 0: General introduction EN 13523-19:2011, Coil coated metals - Test methods - Part 19: Panel desi

27、gn and method of atmospheric exposure testing 3 Terms and definitions For the purposes of this document, the terms and definitions given in EN 13523-0 apply. 4 Principle A test panel is exposed along with known reference panels, to the effects of atmospheric dirt and rain. The dirt and rain is colle

28、cted and directed onto the surface of the panels in such a way as to channel rainwater thus creating the conditions to form stripes on the surface under test. 5 Apparatus and materials 5.1 Exposure rack design in accordance with EN 13523-19:2011, Clause 4 and Figure 4, modified as described below. T

29、he area of the rack normally used for the exposure of panels to the 5 orientation is used to install a sheet made of UV stable polymeric material (e.g. polycarbonate). This sheet forms the collector of the atmospheric soil and is angled on the upper surface of the rack at between 10 and 12 with resp

30、ect to the horizontal plane to control the rate of run-off of rainwater. The machining imparts grooves of 3 mm width and 3 mm depth at a separation of 3 mm extending along the surface and over the rounded edge to direct rainwater onto the panels in rivulets (see Figures 1 and 2). The upper row of th

31、e 90 North facing exposure area of the rack is used to fix the panels, having removed the existing overhang. Two rows are used for this exposure if the panels are longer than 200 mm. The test panels are positioned so that the top edge is in uniform contact with the bottom edge of the collector overh

32、ang. DIN EN 13523-29:2017-05 EN 13523-29:2017 (E) 6 Figure 1 Detail of grooves to be machined Top view Figure 2 Detail of grooves to be machined Side view 6 Sample preparation The test samples shall be flat and free from contamination. Sampling shall be performed in accordance with EN 13523-0. Sampl

33、e dimensions shall be 100 mm (200 mm to 400 mm). If coil production line samples are used these should be cut so as to have the longest dimension in the direction of rolling. 7 Procedure In addition to the test panel, expose two reference panels for each test campaign: one of known good and one of k

34、nown poor performance. This allows for comparative evaluation in various atmospheric conditions. The duration of the test is typically three months and shall be no longer than six months. The duration of the test shall be for a continuous period to avoid other weathering effects, e.g. corrosion, pho

35、to degradation, etc. To minimize seasonal effects, the start date should be noted. At the end of the test period there shall be sufficient separation in performance between the reference panels so as to allow a ranking of the test panels. If not, the test will be restarted with new panels. DIN EN 13

36、523-29:2017-05 EN 13523-29:2017 (E) 7 8 Evaluation Evaluate all panels as soon as possible after the exposure; intermediate examinations may be made (visual observations of the panels on the exposure rack). During handling of the panels and storage before examination, care shall be taken not to dist

37、urb the dirt on the surface. Then the test panels are compared to the reference panels and classified relative to each other and to reference panels and ranked accordingly, e.g.: better than the best reference panel; same as the best reference panel; in between of both reference panels; same as the

38、worst reference panel; worse than the worst reference panel. Changes in gloss and colour measured in accordance with EN 13523-2 and EN 13523-3 can be used to make the comparison. Record gloss and colour at points A, B and C (triplicate readings), as indicated in Figure 3. The results should be docum

39、ented by photographing the panels. To evaluate the ease with which the panels can be cleaned, they may then be subjected to a washing procedure: Wash the left half of the panel indicated in Figure 3 with water containing 0,5 % by mass of a mild non-reactive detergent (pH 6 to pH 7) at ambient temper

40、ature. Use a cloth or sponge that is non-abrasive and smooth to gently clean the surface. Rinse with water at ambient temperature and air dry at ambient temperature. A first evaluation is made by comparing the washed area of each panel with the unwashed area; the second evaluation is made by re-rank

41、ing the washed areas as above. DIN EN 13523-29:2017-05 EN 13523-29:2017 (E) 8 Dimensions in millimetres Key 1 direction of dirt/water 2 line for wash test 3, 4, 5 measuring points (triplicate reading) Figure 3 Dirt panel inspection 9 Test report The test report shall contain at least the following i

42、nformation: a) all details necessary to identify the product tested; b) a reference to this part of the EN 13523 series (EN 13523-29); c) all details necessary to identify the references; d) the geographical location of the rack; e) the test duration; f) the results of the test, as indicated in Clau

43、se 8; g) any deviation from the test procedure described; h) the date(s) of the test. DIN EN 13523-29:2017-05 EN 13523-29:2017 (E) 9 Bibliography 1 EN 1396, Aluminium and aluminium alloys - Coil coated sheet and strip for general applications - Specifications 2 EN 10169, Continuously organic coated (coil coated) steel flat products Technical delivery conditions 3 EN 13523-2, Coil coated metals - Test methods - Part 2: Gloss 4 EN 13523-3, Coil coated metals - Test methods - Part 3: Colour difference - Instrumental comparison DIN EN 13523-29:2017-05