BS EN 13589-2008 Bitumen and bituminous binders - Determination of the tensile properties of modified bitumen by the force ductility method《沥青和沥青粘合剂 使用压力延展法测定改良沥青的拉伸性能》.pdf

《BS EN 13589-2008 Bitumen and bituminous binders - Determination of the tensile properties of modified bitumen by the force ductility method《沥青和沥青粘合剂 使用压力延展法测定改良沥青的拉伸性能》.pdf》由会员分享，可在线阅读，更多相关《BS EN 13589-2008 Bitumen and bituminous binders - Determination of the tensile properties of modified bitumen by the force ductility method《沥青和沥青粘合剂 使用压力延展法测定改良沥青的拉伸性能》.pdf（12页珍藏版）》请在麦多课文档分享上搜索。

1、Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 19/11/2008 08:17, Uncontrolled Copy, (c) BSIg49g50g3g38g50g51g60g44g49g42g3g58g44g55g43g50g56g55g3g37g54g44g3g51g40g53g48g44g54g54g44g50g49g3g40g59g38g40g51g55g3g36g54g3g51g40g53g48g44g55g55g40g39g3g37g60g3g38g50g51g60g53g44g42g43g55g3g47g36g58t

2、ensile properties of modified bitumen by the force ductility methodICS 75.140; 91.100.50Bitumen and bituminous binders Determination of the BRITISH STANDARDBS EN 13589:2008 BS 2000-520:2008BS EN 13589:2008Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 19/11/2008 08:17, Uncontrolled Copy, (c)

3、 BSIThis British Standard was published under the authority ofthe Standards Policy and Strategy Committee on 29 August 2008 BSI and Energy Institute 2008ISBN 978 0 580 59464 9contract. Users are responsible for its correct application.Compliance with a British Standard cannot confer immunity from le

4、gal obligations.Amendments/corrigenda issued since publicationDate CommentsBS 2000, and all BS EN petroleum test methods that would be Part of BS 2000, both in its annual publication Standard methods for analysis and testing of petroleum and related products and British Standard 2000 Parts and indiv

5、idually.Further information is available from: Energy Institute, 61 New Cavendish Street, London W1G 7AR. Tel: 020 7467 7100. Fax: 020 7255 1472.This publication does not purport to include all the necessary provisions of a National forewordThis British Standard is the UK implementation of EN 13589:

6、2008. It supersedes BS EN 13589:2003/BS 2000-520:2003 which is withdrawn. The UK participation in its preparation was entrusted to Technical Committee PTI/13, Petroleum testing and terminology.A list of organizations represented on this committee can be obtained on request to its secretary.Energy In

7、stitute, under the brand of IP, publishes and sells all Parts of EUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 13589March 2008ICS 91.100.50 Supersedes EN 13589:2003 English VersionBitumen and bituminous binders - Determination of the tensileproperties of modified bitumen by the force ductility m

8、ethodBitumes et liants bitumineux - Dtermination descaractristiques de traction des bitumes modifis par lamthode de force-ductilitBitumen und bitumenhaltige Bindemittel - Bestimmung derStreckeigenschaften von modifiziertem Bitumen mit demKraft-Duktilitts-VerfahrenThis European Standard was approved

9、by CEN on 21 January 2008.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstanda

10、rds may be obtained on application to the CEN Management Centre or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to t

11、he CEN Management Centre has the same status as theofficial versions.CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherl

12、ands, Norway, Poland, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: rue de Stassart, 36 B-1050 Brussels 2008 CEN All rights of exploitation in an

13、y form and by any means reservedworldwide for CEN national Members.Ref. No. EN 13589:2008: ELicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 19/11/2008 08:17, Uncontrolled Copy, (c) BSI2 Contents page Foreword3 1 Scope 4 2 Normative references 4 3 Terms and definitions .4 4 Principle5 5 Appara

14、tus .5 6 Preparation and conservation of samples for testing .6 7 Procedure .7 8 Expression of results 7 9 Precision.7 10 Test report 7 Bibliography 9 BS EN 13589:2008EN 13589:2008 (E) Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 19/11/2008 08:17, Uncontrolled Copy, (c) BSI3 Foreword This

15、document (EN 13589:2008) has been prepared by Technical Committee CEN/TC 336 “Bituminous binders”, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by Septem

16、ber 2008, and conflicting national standards shall be withdrawn at the latest by September 2008. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such pate

17、nt rights. This document supersedes EN 13589:2003. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,

18、Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. BS EN 13589:2008EN 13589:2008 (E) Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 19/

19、11/2008 08:17, Uncontrolled Copy, (c) BSI4 1 Scope This European Standard specifies a method for determining the tensile properties of a bituminous binder, in particular those of polymer-modified bitumens by means of a force ductility test. The work done during the force ductility test is a criterio

20、n for assessing the quality of these materials. WARNING The use of this European Standard may involve hazardous materials, operations and equipment. This European Standard does not purport to address all of the safety problems associated with its use. It is the responsibility of the user of this Eur

21、opean Standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited a

22、pplies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 58, Bitumen and bituminous binders Sampling bituminous binders EN 1431, Bitumen and bituminous binders Determination of recovered binder and oil distillate from bitumen emulsions by d

23、istillation EN 12594, Bitumen and bituminous binders Preparation of test samples EN 13074, Bitumen and bituminous binders Recovery of binder from bitumen emulsions by evaporation EN 13398, Bitumen and bituminous binders Determination of the elastic recovery of modified bitumen EN 13703, Bitumen and

24、bituminous binders Determination of deformation energy EN 14895, Bitumen and bituminous binders - Stabilisation of binder from bituminous emulsion or from cut-back and fluxed bituminous binders 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. 3.1

25、tensile force force undergone by a specimen subjected to extension, expressed in N 3.2 elongation increase in length of a specimen, expressed in metres NOTE Elongation is also expressed in % from the initial length. It is calculated as (new length initial length)/initial length 100 and. 3.3 tensile

26、stress for a given elongation tensile stress required to perform a given elongation to the significant part of a specimen BS EN 13589:2008EN 13589:2008 (E) Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 19/11/2008 08:17, Uncontrolled Copy, (c) BSI5 NOTE In general, the given elongation is an

27、 elongation of 1333 %, corresponding to an elongation of 400 mm. 3.4 brittle break every rupture before 1333 % of elongation performing the force ductility test 4 Principle A tensile test is carried out either on: the bituminous binder, or the recovered binder in accordance with EN 13074, or the res

28、idual binder after distillation in accordance with EN 1431, or the aged binder in accordance with the EN 14895. NOTE 1 EN 13074 and EN 14895 are currently under revision, revised draft ENs are respectively numbered prEN 13074-1 and prEN 13074-2. A moulded test specimen is extended in ductilometer at

29、 the test temperature and at constant speed until fracture or an elongation of at least 1333 % (400 mm) is achieved. NOTE 2 The specimen is a symmetrical shaped block of bitumen (Figure 1). 5 Apparatus 5.1 Ductilometer The ductilometer consists of a traction device (5.1.1) and a water bath (5.1.2).

30、5.1.1 Traction device 5.1.1.1 The traction device shall be capable of maintaining a constant speed of the moving elements at (50 2,5) mm/min. 5.1.1.2 The specimen attachment device located at both ends of the specimen shall not exert on any part of the ends of specimen, localised stresses liable to

31、cause tearing or fracture of the specimen. 5.1.1.3 Appropriate facilities shall permit the following measurements to be made: a) tensile force exerted on the specimen over the range from 1 N to 300 N, to an accuracy of 0,1 N; b) elongation of the specimen, either by following the movement of the att

32、achment points or by means of an optical extensiometer over the range 1 mm to not less than 450 mm to an accuracy of 1 mm. 5.1.2 Water bath, temperature-controlled, capable of maintaining the specimen and the attachment device at the specified temperature throughout the test to an accuracy of 0,5 C,

33、 provided with a means of checking the test temperature. When the test is performed at 0C (see Clause 7) or at a lower temperature, the liquid bath shall be water added with 15 % mass fraction of ethanol. BS EN 13589:2008EN 13589:2008 (E) Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 19/11/

34、2008 08:17, Uncontrolled Copy, (c) BSI6 5.2 Recording device, for force applied and elongation of the test specimen. 5.3 Specimen moulding equipment The moulds shall be made of metal, shall consist of four parts (2 side halves and 2 clips), and shall have the dimensions given in Figure 1. The ends f

35、or the moulds are known as clips and are similar to those specified in EN 13398. The inner radius of the clips should be of (15,5 0,1) mm, the opening width (20,0 0,2) mm and the inner length of the clips should be (22,8 0,2) mm. While testing, both clips of a mould shall be kept in place by two dia

36、metrically opposed sliding pins. Whilst the test specimens are being cast and kept on test temperature, the moulds shall be placed on a base plate, also made of metal, and they shall be pressed together with a knurled screw. Key A 36,5 mm 2,0 mm E 10,0 mm 0,1 mm B 30,0 mm 0,1 mm F 7,3 mm 0,1 mm C 20

37、,0 mm 0,2 mm R 15,5 mm 0,1 mm D 5,5 mm thickness 10,0 mm 0,1 mm Figure 1 Symmetrical mould 6 Preparation and conservation of samples for testing Take the sample in accordance with EN 58 and prepare the sample in accordance with EN 12594. Coat the base plate and the interior side of the lateral walls

38、 of the side parts of the mould with a release agent consisting of one part by mass of dextrine (or mineral talc) and one part by mass of glycerine, or with silicone. Assemble the parts of the three moulds and place them on the base plate. Press both halves of the moulds together using the knurled s

39、crew. BS EN 13589:2008EN 13589:2008 (E) Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 19/11/2008 08:17, Uncontrolled Copy, (c) BSI7 Add the amount of sample needed for three test specimen to a melting dish and heat it as described in EN 13398. Immediately fill the three moulds using a backw

40、ard and forward motion in the longitudinal direction of the mould, in order to give a uniform sample distribution in the mould, until a convex meniscus is obtained. Keep the moulded specimens for about 1 h at room temperature then remove the excess sample using a heated knife. Reject any specimens e

41、xhibiting defects. Place the moulded specimens in the water bath maintained at the test temperature for (90 10) min, before testing. Testing shall be carried out on the same day. 7 Procedure Run the test specimen by specimen. NOTE 1 If the traction and recording device allow the individual addressin

42、g of several specimen at once, more than one specimen may be tested at the same time. Once the level filled moulds have been kept at the test temperature for (90 10) min, remove the moulded specimen from the base plate, transfer the test specimen to the traction plates and remove the sides of mould.

43、 Then stretch the specimen at the usual test temperature, i.e. (5,0 0,5)C and at a speed of (50,0 2, 5) mm/min up to an elongation of 1 333 % (400 mm). Repeat any test in which a brittle break occurs. If the second specimen also breaks, raise the temperature by steps of 5 C until the test is complet

44、e without brittle break. As mentioned above, the test temperature is generally (5,0 0,5) C. However, in case of: soft bituminous binders, the test may be performed at a lower temperature, e. g. (0,0 C 0,5 C), and hard PMBs, the test should be performed at (10,0 0,5) C, or even at (15,0 0,5) C. NOTE

45、2 In general for hard PMB (i.e. PMB 10/30 63 and similar), no brittle break occurs at 10 C. If necessary the test should be run at 15 C. 8 Expression of results Calculate the result according to EN 13703. 9 Precision Since the result is calculated according to EN 13703, precision data from round rob

46、in test are indicated in EN 13703. 10 Test report The test report shall contain at least the following information: a) type and complete identification of the sample under test; b) reference to this European Standard; c) identity of the tester; d) results of the test (see Clause 8); BS EN 13589:2008

47、EN 13589:2008 (E) Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 19/11/2008 08:17, Uncontrolled Copy, (c) BSI8 e) any deviation by agreement or otherwise, from the procedure specified; f) test temperature and the used speed; g) date of the test. BS EN 13589:2008EN 13589:2008 (E) Licensed Cop

48、y: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 19/11/2008 08:17, Uncontrolled Copy, (c) BSI9 Bibliography 1 prEN 13074-1, Bitumen and bituminous binders - Recovery of binder from bituminous emulsion or cut-back or fluxed bitumen by evaporation 2 prEN 13074-2, Bitumen and bituminous binders - Stabilisati

49、on of binder from bituminous emulsion or cut-back or fluxed bitumen after recovery BS EN 13589:2008EN 13589:2008 (E) Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 19/11/2008 08:17, Uncontrolled Copy, (c) BSILicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 19/11/2008 08:17, Uncontrolled Copy, (c) BSIBS 2000 Series Energy InstituteBuying Parts of BS 2000Orders for BS 2000 publications should be addressed to either:Energy Institute Library and Information Ser