ASTM F487-2013(2018) Standard Specification for Fine Aluminum&x2013 1&x2009 % Silicon Wire for Semiconductor Lead-Bonding《优质铝标准规范&x2013 1&x2009 %硅导线用于半导体引线键合》.pdf

《ASTM F487-2013(2018) Standard Specification for Fine Aluminum&x2013 1&x2009 % Silicon Wire for Semiconductor Lead-Bonding《优质铝标准规范&x2013 1&x2009 %硅导线用于半导体引线键合》.pdf》由会员分享，可在线阅读，更多相关《ASTM F487-2013(2018) Standard Specification for Fine Aluminum&x2013 1&x2009 % Silicon Wire for Semiconductor Lead-Bonding《优质铝标准规范&x2013 1&x2009 %硅导线用于半导体引线键合》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F487 13 (Reapproved 2018)Standard Specification forFine Aluminum1 % Silicon Wire for Semiconductor Lead-Bonding1This standard is issued under the fixed designation F487; the number immediately following the designation indicates the year of originaladoption or, in the case of revision,

2、the year of last revision. A number in parentheses indicates the year of last reapproval. A superscriptepsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers aluminum1 % silicon alloywire for internal connections in semiconductor devices

3、and islimited to wire of diameter up to and including 76 m (0.003in.). For diameters larger than 76 m (0.003 in.), the specifi-cations are to be agreed upon between the purchaser and thesupplier.1.2 The values stated in SI units are to be regarded as thestandard, regardless of whether they appear fi

4、rst or second in atable. Values given in parentheses are for information only.1.3 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides an

5、d Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2F16 Test Methods for Measuring Diameter or Thickness ofWire and Ribbon for Electronic Devices and LampsF219 Test Methods of Testing Fine Round and Flat Wire

6、 forElectron Devices and Lamps2.2 Military Standard:3MIL-STD-105 Sampling Procedures and Tables for Inspec-tion by Attributes3. Ordering Information3.1 Orders for material under this specification shall includethe following information:3.1.1 Quantity,3.1.2 Size (see Section 5),3.1.3 Breaking load an

7、d elongation (see Section 4),3.1.4 Packaging and marking (see Section 11), and3.1.5 Special requirements, such as for certificate of com-pliance (see Section 10).4. Physical Requirements4.1 Elongation and breaking-load ranges for the wire shallbe specified by the purchaser. The maximum ranges of the

8、semechanical properties are listed in Table 1.4.2 Mechanical property requirements in ranges smallerthan those listed in Table 1 may be specified upon agreementbetween the purchaser and the supplier.NOTE 1The nature of aluminum1 % silicon alloy is such that themechanical properties of both as-drawn

9、and annealed wires overlapconsiderably. It is also possible to alter the properties of hard wire byvarying the manufacturing parameters and procedures. For these reasons,no distinction is made between the two types of wire in this specification.5. Dimensions, Weights, and Permissible Variations5.1 W

10、ire size shall be expressed in terms of wire diameter indecimal fractions of millimetres (inches). Tolerances for vari-ous size ranges are specified in Table 2.5.2 When wire size is expressed in terms of weight, thefollowing values shall be used:5.2.1 Density of Aluminum1 % Silicon2.7 g/cm3.5.2.2 We

11、ight of a 200-mm Length of Wire 25.4 m inDiameter0.274 mg.6. Surface Finish6.1 The wire surface shall be clean and free of finger oils,lubricant residues, stains, and particulate matter.6.2 Mechanical damage to the wire surface, such as nicks,scratches, and kinks, shall be held to a minimum.6.3 The

12、inspection shall be carried out by electronic, optical,or other inspection method is agreed upon between thepurchaser and the supplier. The nature and extent of defectspermitted to be present on the surface of the wire shall beagreed upon between the purchaser and the supplier.1This specification is

13、 under the jurisdiction of ASTM Committee F01 onElectronics and is the direct responsibility of Subcommittee F01.03 on MetallicMaterials, Wire Bonding, and Flip Chip.Current edition approved March 1, 2018. Published April 2018. Originallyapproved in 1977. Last previous edition approved in 2013 as F4

14、87 13. DOI:10.1520/F0487-13R18.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from Standardizatio

15、n Documents Order Desk, Bldg. 4 Section D, 700Robbins Ave., Philadelphia, PA 19111-5094, Attn: NPODS.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognize

16、d principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.17. Chemical Requirements7.1 The alloy composition shall be 1.00 6 0.

17、15 % silicon,and between 98.84 and 99.15 % aluminum. All other elementsare considered impurities.7.2 No single impurity shall exceed 0.0050 % and the totalof all detectable impurities shall not exceed 0.01 %.7.3 Any lower or higher impurity content shall be as agreedupon between the purchaser and th

18、e supplier as part of thepurchase contract.7.4 Larger aluminum wire diameters often include nickel orother impurities or both to minimize corrosion in plasticpackages. Such wire is not covered by this specification.8. Sampling8.1 Unless otherwise agreed upon by the purchaser and thesupplier, conform

19、ance with Section 4 shall be determined byMIL-STD-105.9. Test Methods9.1 Elongation and Breaking Load Determine elongationand breaking load in accordance with Test Methods F219.9.2 Dimensional MeasurementDetermine the wire diam-eter by one of the following methods:9.2.1 Measure the diameter directly

20、 in accordance with TestMethods F16.9.2.2 Measure the diameter by optical means agreed uponbetween the purchaser and the supplier.NOTE 2Optical methods for measuring wire diameter are underdevelopment by Committee F-1 on Electronics.9.3 Chemical AnalysisVerify that the chemical require-ments are sat

21、isfied by means of spectrographic analysis orother means agreed upon between the purchaser and thesupplier.10. Certification10.1 When agreed upon in writing by the purchaser and thesupplier, a certification shall be made the basis of acceptance ofthe material. This shall consist of a copy of the man

22、ufacturerstest report or a statement by the supplier, accompanied by acopy of the test results, that the material has been sampled,tested, and inspected in accordance with the provisions of thisspecification. Each certification so furnished shall be signed byan authorized agent of the supplier or th

23、e manufacturer.11. Packaging (Spooling) and Package Marking11.1 The type of spool shall be specified as agreed uponbetween the purchaser and the supplier. (For aging propertiessee the shelf life aging test, in Appendix X1.)NOTE 3Types of spools recommended for fine lead-bonding wire willbe agreed up

24、on by purchaser and manufacturer that are compliant with theusers intended bonding machines.11.2 The maximum and minimum length of wire on a spoolshall be as specified by the purchaser.11.3 The wire shall be wound so that it despools freely andwill be free of kinks and nicks. Spools shall be free of

25、 nicks,burrs, and dents. The beginning and end of the wind shall beclearly identified. The method of termination shall be as agreedupon between the purchaser and the supplier.11.4 The wire shall be protected against damage in normalhandling and shipping. The outer container shall bear markingsindica

26、ting“ fragile” contents and designating the proper end tobe “up” in order to maintain spool axes horizontal duringshipping. The outer container shall also be marked “Extremesof Temperature Must Be Avoided.”NOTE 4Other package marking should be specified by the purchaserif required.11.5 The basic pac

27、king unit shall be legibly marked with thefollowing information:11.5.1 Material description,11.5.2 Diameter, in. (or mm),11.5.3 Length, metres (or feet),11.5.4 Elongation and breaking-load specifications,11.5.5 Melt or bar number,11.5.6 Date of packaging,11.5.7 Users part number, and11.5.8 Manufactu

28、rers name and product designation, if any.12. Keywords12.1 silicon aluminum wire; wire bondingTABLE 1 Typical Elongation and Breaking Load ofAluminum1 % Silicon Alloy WireNOTE 1Select the desired nominal breaking load and elongation forthe wire by specifying a range of mechanical properties that inc

29、ludes thedesired values.ANominal Diameter,in. (mm)Breaking Load, g Elongation, %Min MaxMaxRangeBMin MaxMaxRangeC0.0007 (0.018) 3 12 2 0.5 3.0 2.00.0010 (0.025) 12 22 3 0.5 4.0 2.50.0012 (0.030) 14 30 3 0.5 4.0 2.50.00125 (0.032) 15 32 3 0.5 4.0 3.00.0015 (0.038) 20 50 4 0.5 4.0 3.00.0020 (0.051) 32

30、90 6 1.0 4.0 3.0AExample: Wire of 25-m (0.001-in.) diameter with a breaking load of 16 g and anelongation of 2.0 % is desired. Specify a breaking-load range of 14 to 18 g (16 2 g) and an elongation range of 1.0 to 3.5 % (2.0 + 1.5 %, 2.0 1.0 %). (NoteSmaller ranges are acceptable; for this example,

31、ranges of 15 to 17 g and 1.0 to3.0 % could be specified. For diameters larger than 0.0020 in. (0.051 mm), thespecifications are to be agreed upon between the purchaser and the supplier.)BA range of permissible breaking strength of no more than the number of gramsshown shall be selected from within t

32、he overall range designated by the minimumand maximum values for the given diameter.CA range of permissible elongation of no more than the number of percentagepoints shown shall be selected from within the overall range designated by theminimum and maximum values for the given diameter.TABLE 2 Dimen

33、sional TolerancesNominal Diameter, in. (mm)DiameterTolerance, % ofnominalWeightTolerance, % ofnominal0.0005 to 0.0020 (0.013 to 0.051), incl 3 6F487 13 (2018)2APPENDIX(Nonmandatory Information)X1. SHELF LIFE AGING TEST 19831985X1.1 PurposeX1.1.1 To determine the effect of room temperature agingon th

34、e stress-strain characteristics of bonding wires of severalcompositions and tempers.X1.2 Test parametersX1.2.1 EnvironmentTypical stock room, 22.8 6 1.7C(73 6 3F).X1.2.2 Spooling2-in. diameter, Aluminum, 100 ft/spool.X1.2.3 InstrumentInstron type, 1 in./min., 10 in. length.X1.2.4 SamplingAverage of

35、five readings per notation.X1.2.5 TimeIntervals shown on charts, see Fig. X1.1.X1.2.6 Wire SizeAll specimens, 25-m (0.001-in.)diameter.NOTE 1These data were taken in the 1980s. However, the metal-lurgy of 2012 Al-Si wire is unchanged and the data are consideredcorrect for this purpose today.FIG. X1.

36、1 Aging Chart 1 % Silicon Aluminum Bonding Wire AlloyF487 13 (2018)3ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any

37、 such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are in

38、vited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not receive

39、d a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of t

40、his standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 13 (2018)4