ASTM F484-2008(2013) Standard Test Method for Stress Crazing of Acrylic Plastics in Contact with Liquid or Semi-Liquid Compounds《丙烯塑料在与液态或半液态化合物接触中产生的应力裂纹的标准试验方法》.pdf
《ASTM F484-2008(2013) Standard Test Method for Stress Crazing of Acrylic Plastics in Contact with Liquid or Semi-Liquid Compounds《丙烯塑料在与液态或半液态化合物接触中产生的应力裂纹的标准试验方法》.pdf》由会员分享,可在线阅读,更多相关《ASTM F484-2008(2013) Standard Test Method for Stress Crazing of Acrylic Plastics in Contact with Liquid or Semi-Liquid Compounds《丙烯塑料在与液态或半液态化合物接触中产生的应力裂纹的标准试验方法》.pdf(3页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: F484 08 (Reapproved 2013)Standard Test Method forStress Crazing of Acrylic Plastics in Contact with Liquid orSemi-Liquid Compounds1This standard is issued under the fixed designation F484; the number immediately following the designation indicates the year of originaladoption or, in the
2、 case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscriptepsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 T
3、his test method covers determination of the crazingeffect that a liquid or semi-liquid test compound will have ontransparent acrylic plastic material that is under bending stress.1.2 Three types of acrylic material are covered. One, two, orall of the materials shall be used in the test, as specified
4、 by theprocuring agency. When not specified otherwise, all three typesof acrylic shall be used in the test.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are no
5、t considered standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior
6、to use.2. Referenced Documents2.1 ASTM Standards:2D1193 Specification for Reagent Water2.2 Military Standards:MIL-PRF-5425 Plastic Sheet, Acrylic, Heat Resistant3MIL-PRF-8184 Plastic Sheet, Acrylic, Modified3MIL-PRF-25690 Plastic, Sheets and Formed Parts, ModifiedAcrylic-Basic, Monolithic, Crack Pro
7、pagation Resistant33. Terminology3.1 Definitions:3.1.1 crazea minute surface crack, sometimes hairline insize.NOTE 1Hairline craze cracks are very difficult to see except withcareful inspection under properly oriented light.3.1.2 cracka fracture or tear.4. Types4.1 Type A, cast acrylic material shal
8、l conform to MIL-PRF-5425, Finish A.4.2 Type B, cast acrylic material shall conform to MIL-PRF-8184, Finish B.4.3 Type C, stretched acrylic material shall conform toMIL-PRF-25690.5. Apparatus5.1 Stress ApparatusThe means of stressing the acrylicplastic test specimen bars shall be as shown in Fig. 1.
9、6. Test Specimens6.1 The test specimens shall be machined from 0.25 60.025 in. (6.4 6 0.64 mm) thick polished acrylic plastic sheetconforming to the applicable specification.6.2 The test specimens shall be 1 6 0.03 in. (25.4 6 0.8mm) wide by 7 6 0.05 in. (177.8 6 1.27 mm) long by 0.25 60.025 in. (6.
10、4 6 0.64 mm) thick. Edges shall be a smoothmachined surface without cracks.7. Conditioning7.1 Do not anneal Type C acrylic specimens.7.2 Anneal Type A and Type B acrylic test specimens aftermachining by heating in a circulating air oven at 195 6 5F (916 3C) for 512 h. Cool the specimens to room temp
11、erature inthe oven using a uniform cooling rate of 50F (28C)/h.7.3 Condition all specimens at 75 6 10F and 50 6 5%relative humidity for a minimum of 24 h just before testing.8. Procedure8.1 Test two specimens of each acrylic material specified foreach of the test compounds being evaluated.1This test
12、 method is under the jurisdiction of ASTM Committee F07 onAerospace and Aircraft and is the direct responsibility of Subcommittee F07.07 onQualification Testing of Aircraft Cleaning Materials.Current edition approved Dec. 1, 2013. Published December 2013. Originallyapproved in 1977. Last previous ed
13、ition approved in 2008 as F484 08. DOI:10.1520/F0484-08R13.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3A
14、vailable from Standardization Documents Order Desk, Bldg. 4 Section D, 700Robbins Ave., Philadelphia, PA 19111-5098, Attn: NPODS.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States18.2 Conduct the test at a temperature of 75 6 10F (23 65C
15、).8.3 Carefully load the acrylic specimen as a cantilever beamas shown in Fig. 1. Unless otherwise specified, the followingare recommended stress levels:8.3.1 Type A specimens shall be stressed to an outer fiberstress of 3000 psi (20 685 kPa).8.3.2 Type B specimens shall be stressed to an outer fibe
16、rstress of 3500 psi (24 132 kPa).8.3.3 Type C specimens shall be stressed to an outer fiberstress of 4500 psi (31 027 kPa).8.4 Allow the specimen to remain under the designatedstress for 10 min; then examine under the lighting and visualinspection conditions shown in Fig. 1 to be sure no crazing has
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
5000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMF48420082013STANDARDTESTMETHODFORSTRESSCRAZINGOFACRYLICPLASTICSINCONTACTWITHLIQUIDORSEMILIQUIDCOMPOUNDS
链接地址:http://www.mydoc123.com/p-536770.html