ASTM D4708-2012 Standard Practice for Preparation of Uniform Free Films of Organic Coatings《有机涂层均匀游离膜制备的标准实施规程》.pdf
《ASTM D4708-2012 Standard Practice for Preparation of Uniform Free Films of Organic Coatings《有机涂层均匀游离膜制备的标准实施规程》.pdf》由会员分享,可在线阅读,更多相关《ASTM D4708-2012 Standard Practice for Preparation of Uniform Free Films of Organic Coatings《有机涂层均匀游离膜制备的标准实施规程》.pdf(2页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: D4708 12Standard Practice forPreparation of Uniform Free Films of Organic Coatings1This standard is issued under the fixed designation D4708; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A
2、 number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This practice covers the preparation of free films oforganic coatings for use in determining the physical propertiesof the coatings.
3、Procedures are given for preparing free filmson three alternative substrates. These substrates are treated FEP(fluorinated ethylene-propylene) sheet, silicone coated paper,and halosilane coated glass plates.1.2 The values stated in SI units are to be regarded as thestandard. The values given in pare
4、ntheses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitati
5、ons prior to use.2. Referenced Documents2.1 ASTM Standards:2D823 Practices for Producing Films of Uniform Thicknessof Paint, Varnish, and Related Products on Test PanelsD1005 Test Method for Measurement of Dry-Film Thick-ness of Organic Coatings Using MicrometersD1653 Test Methods for Water Vapor Tr
6、ansmission of Or-ganic Coating FilmsD2370 Test Method for Tensile Properties of Organic Coat-ingsE96/E96M Test Methods for Water Vapor Transmission ofMaterials3. Summary of Test Method3.1 Free films are prepared by depositing a uniform wetcoating of the test material on a release substrate. The appl
7、iedfilms are dried or baked, cut into appropriate size for theintended physical property test, and then stripped from therelease substrate.4. Significance and Use4.1 Free films are required for conducting tests to evaluatephysical and mechanical properties such as tensile and elon-gation (Test Metho
8、ds D2370 and E96/E96M), moisture vaporpermeability (Test Methods D1653), and other physical prop-erties of organic coatings where the substrate may interferewith the determination.5. Apparatus and Materials5.1 Equipment, for applying films of uniform thickness asdescribed in Practices D823.5.2 Micro
9、meter Film Thickness Gage, as described in TestMethod D1005.5.3 Alternative Release Substrates:5.3.1 Sheet of FEP(polyhexafluoropropylene), preferably50-m (2-mils) thick, coated with a thin film of a drylubricant.3,45.3.2 Sheet of Silicone Coated Paper, preferably 125-m(5-mil) thick.5,45.3.3 Glass P
10、lates, coated with halosilane compound.5.3.4 Steel Panelwrapped with Tedlar6polyvinyl fluoridefilm, preferably 25 to 50m 9 (1 to 2 mils) thick.NOTE 1Other substrates that may be suitable are 250-m (10-mil)thick polyethylene, polypropylene sheet, photographic paper, polishedsteel, and fluoropolymer c
11、oated metal panels.5.4 Precision Specimen Cutter, having a double blade with afoot to hold the sample.7,41This practice is under the jurisdiction of ASTM Committee D01 on Paint andRelated Coatings, Materials, and Applications and is the direct responsibility ofSubcommittee D01.23 on Physical Propert
12、ies of Applied Paint Films.Current edition approved July 1, 2012. Published August 2012. Originallyapproved in 1987. Last previous edition approved in 2007 as D4708 07. DOI:10.1520/D4708-12.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at servi
13、ceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The sole source of supply of dry lubricant (MS-122 Fluorocarbon ReleaseAgent) known to the committee at this time is Miller-Stephenson Chemical Co.,Inc., 55 Backus Ave.,
14、Danbury, CT 06810.4If you are aware of alternative suppliers, please provide this information toASTM International Headquarters. Your comments will receive careful consider-ation at a meeting of the responsible technical committee,1which you may attend.5The sole source of supply of silicone coated r
15、elease paper, Form RP-1K, size858 by 1114 in., known to the committee at this time is the Leneta Co., 15 WhitneyRd., Mahwah, NJ 07430.6Tedlar is a registered trademark of E. I. du Pont de Nemours and Company.7The sole source of supply of the JDC Precision Sample Cutter known to thecommittee at this
16、time is the Thwing-Albert Instrument Co., 14 West Collins Ave.,West Berlin, NJ 08091.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States16. Procedure6.1 Prepare the free fil
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMD47082012STANDARDPRACTICEFORPREPARATIONOFUNIFORMFREEFILMSOFORGANICCOATINGS 有机 涂层 均匀 游离 制备 标准 实施 规程
链接地址:http://www.mydoc123.com/p-517773.html