ASTM D4707-2009(2017) Standard Test Method for Measuring Paint Spatter Resistance During Roller Application《测量辊压机应用防油漆飞溅的标准试验方法》.pdf

《ASTM D4707-2009(2017) Standard Test Method for Measuring Paint Spatter Resistance During Roller Application《测量辊压机应用防油漆飞溅的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D4707-2009(2017) Standard Test Method for Measuring Paint Spatter Resistance During Roller Application《测量辊压机应用防油漆飞溅的标准试验方法》.pdf（10页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D4707 09 (Reapproved 2017)Standard Test Method forMeasuring Paint Spatter Resistance During RollerApplication1This standard is issued under the fixed designation D4707; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, t

2、he year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the determination of the ten-dency of a paint to spatter when applied with a paint

3、roller toa substrate.1.2 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior t

4、o use.1.3 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarri

5、ers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2D3924 Specification for Environment for Conditioning andTesting Paint, Varnish, Lacquer, and Related Materials(Withdrawn 2016)3D3925 Practice for Sampling Liquid Paints and RelatedPigmented Coatings2.2 Other Document:Pictorial S

6、tandards of Paint Roller Spatter43. Summary of Test Method3.1 The test paint is applied to a black plastic panel bydraw-down. The coated plastic panel is immediately mountedon an essentially vertical surface above a sheet of paper used tocatch any spatter. A specially designed notched spool roller(s

7、ee 5.1) is rolled through the film following a definedprocedure, tending to generate spatter. Any spatter falls uponthe spatter catch paper and, after drying, is rated against thepictorial standards.4. Significance and Use4.1 Paint spatter generated by roller application is depen-dent on the propert

8、ies of both the paint being applied and thepaint roller cover used for the application. To eliminate theinfluence of the paint roller cover as a variable, and thus restrictthe spatter-inducing variable to the paint under test only, thepaint roller cover is replaced by a standard notched spool roller

9、to generate spatter by a mechanism that simulates that of apaint-applying roller cover.4.2 Although most of the development work to establish thistest method was undertaken using latex paints, sufficient workwas also done to show its applicability to solvent-reduciblepaints.4.3 Tests during the deve

10、lopment of this test methodshowed that the spattering properties of paints, like otherphysical properties, may in time change. Therefore, the resultsof this test are valid only for the time when the test is run.5. Apparatus5.1 Notched Spool Test Roller (Fig. 1).5,65.2 Glass Plateat least 230 by 485

11、mm (9 by 19 in.) by 6mm (0.25 in.) thick.5.3 U-shaped Film Caster,7,6having a 175-m (7-mil) clear-ance by 135 mm (5.25 in.) wide.5.4 Metronome, adjusted to 80 beats per min.1This test method is under the jurisdiction of ASTM Committee D01 on Paintand Related Coatings, Materials, and Applications and

12、 is the direct responsibility ofSubcommittee D01.42 on Architectural Coatings.Current edition approved June 1, 2017. Published June 2017. Originallyapproved in 1987. Last previous edition approved in 2013 as D4707 09 (2013).DOI: 10.1520/D4707-09R17.2For referenced ASTM standards, visit the ASTM webs

13、ite, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.4Copies of the pictorial pho

14、tographic reference standards are contained inPictorial Standards of Coatings Defects and may be obtained from the Federationof Societies For Coatings Technology, 492 Norristown Rd., Blue Bell, PA 19422.5The sole source of supply for the notched spool test roller known to thecommittee at this time i

15、s Precision Gage and Tool Co., 28 Volkenand Ave., Dayton,OH 45410.6If you are aware of alternative suppliers, please provide this information toASTM International Headquarters. Your comments will receive careful consider-ation at a meeting of the responsible technical committee,1which you may attend

16、.7The sole source of supply for the Dow film caster known to the committee atthis time is BYKGardner, Inc., Gardner Laboratory, 2435 Linden Lane, SilverSpring, MD 20910.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international

17、 standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1

18、6. Materials6.1 Black Plastic Panels,8,6165 by 430 mm (6.5 by 17 in.).6.2 Flannel Cloth.6.3 Masking Tape, 25 mm (1 in.) wide.6.4 Spatter Catch Paper, minimum size 190 by 240 mm (7.5by 9.5 in.). This paper can be any convenient paper to whichthe spatter droplets will adhere and of a color to contrast

19、 thatof the paint under test.7. Sampling and Conditioning7.1 Sample the material in accordance with Practice D3925.7.2 Prior to testing, the samples shall be conditioned inaccordance with the standard atmosphere described in Speci-fication D3924. The testing shall take place under the sameconditions

20、.8. Procedure8.1 Clean the top of the glass plate and both sides of theblack plastic panel to ensure that they are free of specks. Placethe black plastic panel on the glass plate and tape the narrowend at the top to the glass plate. Smooth the panel along theplate to ensure a close fit.8.2 Stir the

21、paint under test thoroughly and strain to removeall skins and particles. Place the film caster with the 175-m(7.0-mil) side down immediately below the taped portion of theblack plastic panel. Turn on the metronome. Into the wellformed by the film caster, pour sufficient paint that the well isfilled

22、from corner to corner. Draw down the paint the fulllength of the black plastic panel until the film caster is fullybeyond the far edge. The rate of application should be fairlyslow, 3 to 4 seconds from end to end, to prevent pinholes orholidays in the paint film.8.3 Immediately upon completion of th

23、e draw-down, re-move the black plastic panel from the glass plate, keeping themasking tape intact, and tape, with the long direction verticalto a surface that is vertical or nearly vertical (within 5 ofvertical, top sloping away from the operator) with the bottomof the black plastic panel about 25 m

24、m (1 in.) above thelaboratory bench or table (Fig. 2). It is desirable that the surfaceunder the black plastic panel be firm but with a little resilience.A backing of 6-mm (14-in.) thick fiberboard is ideal as veryhard surfaces make proper performance of the test difficult.Center the spatter catch p

25、aper on the laboratory bench or table8The sole source of supply for the dull black plastic panels, Leneta P-121-10N,612 by 17 in. by 10 mil (production tolerance 61 mil) (165 by 430 by 250 m) insize known to the committee at this time is Leneta Company, 15 Whitney Rd.,Mahwah, NJ 07430.Dimensionsin.

26、mmA Flange thickness 0.063 0.005 1.60 0.13B Space between flanges 0.343 0.005 8.71 0.13C Total diameter 1.600 0.015 40.16 0.38D Diameter under notches 1.400 0.015 35.56 0.38E Hole diameter 0.281 0.005 7.14 0.13FIG. 1 Notched Spool RollerD4707 09 (2017)2under the black plastic panel with the short si

27、de of the catchpaper closest to the black plastic panel.8.4 Using the clean, notched spool roller, start in one of theupper corners and roll downward and upward through the paintfilm. Always keep the notched spool in contact with the blackplastic panel, not removing the roller from the film whenchan

28、ging directions. Make ten passes in each direction (20passes total), 380 6 15 mm (15 612 in.) per pass, progres-sively moving sideways from one edge of the film to the other(Fig. 3). Each pass should coincide with a beat of themetronome and the motion should be continuous, not jerky.Use the metronom

29、e for accurate timing since the speed of therolling of the notched spool roller through the paint film hasbeen found to be the only variable significantly affecting theresults of the test. Make sure that all four flanges of the notchedspool roller are within the draw-down area at all times. Usesuffi

30、cient pressure to maintain constant contact between thenotched spool roller and the black plastic panel. Note that aslong as constant contact is maintained, pressure variations havenot been found to affect the results noticeably.8.5 Remove the spatter catch paper and lay it in a suitableplace to dry

31、.8.6 Repeat the test with a second plastic panel after cleaningthe apparatus.9. Grading Procedure9.1 Carefully cut an area 190 by 240 mm (7.5 by 9.5 in.) outof the front edge (edge nearest the paint) of the spatter catchpaper. The shorter side will be the front edge. Center the areawith respect to t

32、he spatter so a maximum of spatter is on thissheet (Fig. 4).FIG. 2 Test Set-Up SchematicDimensionsin. mmA Notched spool pass length 15 12 38015B Drawdown width (determined byblade)514 140C Panel width 612 165D Panel length 17 430FIG. 3 Test Pattern SchematicFIG. 4 Cutting Out Section of Spatter Catc

33、h paper for EvaluationD4707 09 (2017)39.2 Compare the cut-out area to the pictorial standards.Assign the rating that most closely matches a standard,interpolating as needed for ratings (0poor spatter resistance,2, 4, 6, 8, and 10no spatter).NOTE 1Figs. 5-9 are duplications thereof for sample purpose

34、s and arenot meant to be used for test grading purposes.9.3 In rating the paints using the photographic standards,consider the population of spatter droplets of greater impor-tance than the average size of the spatter droplets.9.4 If the ratings of two tests do not agree within 1 unit,repeat until s

35、uch precision is obtained.10. Precision and Bias10.1 In an interlaboratory study of this test method in whichone operator in each of three laboratories tested six paints witha broad range in spattering properties, one operator in twoother laboratories tested three of the paints and one operator inon

36、e laboratory tested only two paints, the between-laboratoriesstandard deviation was found to be 0.17 rating units (see Note2) with 18 df, with no results discarded. Based on this standarddeviation, the following criteria should be used for judging theacceptability of results at the 95 % confidence l

37、evel:10.1.1 RepeatabilityIntralaboratory precision is normallybetter than interlaboratory precision. However, when rating isinvolved, it is difficult to establish reliability because of thenatural tendency for bias when operators know the samematerial is being tested again.NOTE 2When the results wer

38、e ranked, the agreement among the sixoperators was perfect. This might not occur if some paints with lessdistinct differences in spattering properties were included in a similarstudy.10.1.2 ReproducibilityTwo results obtained by operatorsin different laboratories should be considered suspect if they

39、differ by more than 0.5 units.10.2 BiasBias can not be determined for this test methodbecause there is no standard reference material.11. Keywords11.1 paint spatter resistance; resistancepaint spatter; rollerapplication; spatteringD4707 09 (2017)4FIG. 5 Paint Spatter Resistance to Roller Application

40、 Rating Standard No. 1D4707 09 (2017)5FIG. 6 Paint Spatter Resistance to Roller Application Rating Standard No. 3D4707 09 (2017)6FIG. 7 Paint Spatter Resistance to Roller Application Rating Standard No. 5D4707 09 (2017)7FIG. 8 Paint Spatter Resistance to Roller Application Rating Standard No. 7D4707

41、 09 (2017)8FIG. 9 Paint Spatter Resistance to Roller Application Rating Standard No. 9D4707 09 (2017)9ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that de

42、termination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved

43、or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel t

44、hat your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprint

45、s (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 09 (2017)10